Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (62)
- Vortrag (48)
- Beitrag zu einem Tagungsband (33)
- Beitrag zu einem Sammelband (20)
- Posterpräsentation (2)
- Forschungsbericht (2)
- Buchkapitel (1)
- Sonstiges (1)
Schlagworte
- Wear (21)
- Friction (16)
- Temperature (12)
- Fretting (9)
- Silicon carbide (7)
- Ceramics (6)
- Reibung (6)
- Alumina (4)
- Ceramic (4)
- Humidity (4)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (48)
This paper presents a dry sliding tribo-couple (DLC/monolithic oxide ceramics), where the tribological quantities are more or less in a wide ränge independent of the sliding speed. The DLC film is composed of a specific mixture of sp3 /sp2 hybridized carbon. Self-mated ceramic/ceramic couples of MgO-Zr02, alpha-AI203 or SSiC are with their coefficients of friction above 0.45 not so lubricious, whereas the coefficients of friction of the tribocouples MgO-Zr02/DLC and alpha-AbOVDLC ranged between 0.075 and 0.15 under dry sliding. The coefficients of friction for these tribo-couples tend to decrease with increase sliding speed from 0.03 m/s to 6 m/s. The dry wear rates of the thin film is low (<10‘7 mm3/Nm) and perfectly independent from sliding velocity.
Zero wear (Null Verschleiß)
(2013)
Zero wear (Null Verschleiß)
(2012)
Recent developments in contact mechanics and microfribology have shown that it is very important to study surface modification effects for quantification of „Zero wear“ (plastic deformation of upper parts of asperities) during sliding friction. The present work considers experimental and Simulation data on the Formation of elastic and plastic contact areas during sliding friction on rough surfaces. The Simulation of discrete contact was carried out using as a source the AFMimages of real surface topography at micro/nanoscale.
The approach for quantification of „zero wear“, proposed here, is not using common Statistical Parameters of roughness, but it considers contact areas on asperities.
In these areas some regions are undergoing plastic deformation which influences surface Transformation during sliding friction. Also, the workhardening effect was taken into account in the Simulation
of sliding friction. This enabled a rnore successful fit of experimental data. The results obtained of the Computer simulations will provide a way of studying friction force at the initial stage of the running-in process.
Three different contact geometries, ball on disk and two different settings with crossed cylinders have been investigated with regard to the agreement of the results of the tribological quantities determined by each method. The material combination was α-alumina as upper specimen and steel 100Cr6 as lower specimen. For each of the contact geometries 5 independent measurements were carried out and evaluated independently. The agreement between the single results of coefficient of friction and the coefficient of system wear as well as between the different groups and conditions are good. Largest scatter of the results were found in the dry air regime where both friction and wear depend strongly on the relative humidity. However, comparison of the absolute values of the coefficient of wear between the ball on disk contact geometry on one side and the 2 crossed cylinder contact geometries on the other side reveals a significant difference in that the ball on disk results are lower by about a factor of two. The results document also a high degree of repeatability of single wear tests.
Wear of thin steel wires
(2010)
Ceramics are of increasing interest for application in many branches of technique. In order to improve the tribological performance of ceramic materials, composites on the basis of silicon carbide with different amounts of titanium carbide, boron carbide, titanium diboride and free carbon in the form of graphite were manufactured by a reaction sintering process.
The friction and wear behaviour of these composites was investigated with oscillating sliding motion in unlubricated tests at room temperature on different levels of relative humidity. Additional tests were performed under water lubrication, revealing the superior behaviour of composites for special test conditions. A major influence of the free carbon on friction or wear behaviour was not observed. The tribological behaviour in air as well as under water is mainly dependant on the amount of titanium phases.
An extended study on tribological properties of carbon nitride coatings under oscillating sliding conditions has been carried out. The coatings were prepared by reactive magnetron sputtering with graphite target using nitrogen as reactive gas in an argon/nitrogen atmosphere during the deposition process to deposit carbon nitride, CNx. Coating thickness was about 2 µm. A 200300 nm thick Ti interlayer was used to enhance adhesion. The nitrogen flow during the deposition was varied to control the amount of nitrogen in the coating. Maximum amount of N-content was about 28 at%, achieved at a maximum N2 flow rate. Other deposition parameters were target to substrate distance, substrate temperature during deposition and bias voltage. The results show a large variation of hardness depending mainly on the nitrogen content and bias voltage. Higher bias voltage produced harder coatings as did lower nitrogen content. The tribological properties were tested unlubricated and lubricated by paraffin oil under gross slip fretting conditions at room temperature against alumina as counter material. Most coatings, but not all, showed a more or less pronounced dependence of wear on relative humidity with wear rates from 10-5 to 10-6 mm3/Nm. The best coatings with regard to a low wear rate and the least dependence upon relative humidity were carbon nitride coatings deposited at elevated substrate temperatures up to 350 °C. The wear resistance of these coatings was increased under the most severe conditions by about one order of magnitude. The results are discussed on the basis of a transfer layer formation. The results show clearly that wear is not significantly correlated to the coating hardness which itself is strongly dependant on the nitrogen content. However, under lubricated conditions with paraffin oil, wear rates were generally very low with wear coefficients at about 10-8 mm3/Nm.