Artificial weathering of LDPE under dry conditions (<10% of relative humidity) by UV radiation was monitored
by dielectric spectroscopy. For an apolar polymer like LDPE, dielectric study yields information
about the change in structure and dynamics of the system. The fluctuations of the polar groups which
are generated as a result of photooxidation such as carbonyl groups can be monitored as characteristic
relaxation processes like the αc or β mode. The dielectric loss characterized by typical dielectric parameters
like the activation energy and dielectric strength are strongly dependent upon changes induced
by photooxidation in the amorphous and crystalline domains. This paper discusses in detail how the foil
reached its mechanical disintegration. It was found that initial stages of weathering induce chain scission
and/or crosslinking in the amorphous domains of the polymer and the motional processes in the crystalline
regions are not affected. After this induction period, an increase in the degree of crystallization was
observed by employing differential calorimetry. The increasing crystallinity is considered as one of the
reasons for embrittlement which finally leads to the complete loss of the structural integrity.
Additively manufactured test specimens made of polyamide 12 (PA 12) by Laser Sintering (LS) as well as of acrylnitril-butadien-styrol (ABS) by Fused Layer Modeling (FLM), were tested with active thermography. For this, two different excitation methods (flash and impulse excitation) were used and compared, regarding the suitability for the detection of constructed and imprinted defects. To increase the quality of the thermograms, data processing methods like thermal signal reconstruction (TSR) and Fourier-Transformation were applied. Furthermore, the long-term stability of the probes towards environmental stress, like UV-radiation, heat, water contact and frost is being investigated in the presented project with artificial weathering tests.
Polyether and -ester urethanes (PU) were exposed to artificial weathering at 40 °C and artificial UV radiation in a weathering chamber. In 3 parallel exposures, humidity was varied between dry, humid, and wet conditions. Material alteration was investigated by various analytical techniques like size exclusion chromatography
(SEC), liquid chromatography-infrared spectroscopy (LC-FTIR), thermal-desorption gas chromatography-mass spectrometry (TD-GC-MS), fluorescence mapping and dynamic mechanical analysis (DMA). Our results show that depending on the weathering conditions, different degradation effects can be observed. By means of SEC an initial strong decrease of the molar masses and a broadening of the mass distributions was found. After a material dependent time span this was followed by a plateau where molar mass changes were less significant. A minor moisture-dependent degradation effect was only found for polyester PU. Fluorescence measurements on two materials revealed an increase in the luminescence intensity upon weathering process reaching a saturation level after about 500 h. The changes in the optical properties observed after different exposure conditions and times were very similar. The TD-GC-MS data showed the fate of the stabilizers and antioxidant in the course of weathering. LC-FTIR measurements revealed a change in peak intensities and the ratio of urethane and carbonyl bands.
Additively manufactured test specimens made of polyamide 12 (PA 12) by Laser Sintering as well as of acrylonitrile butadiene styrene (ABS) by Fused Layer Modelling, were characterised with active thermography directly after manufacturing and after artificial weathering. For this, two different excitation methods (flash and pulse heating) were used and compared, regarding their suitability for the detection of constructed and imprinted defects inside the test specimens. To increase the quality of the thermograms, data processing methods like thermal signal reconstruction (TSR) and Fourier Transformation after TSR were applied. To further investigate the long-term stability of the additively manufactured test specimens towards environmental stress, like UV radiation, heat, humidity, water contact and frost with active thermography, an artificial weathering test over 2000 hours (~3 months) was applied to the specimens. The monitoring of the changes in the optical properties of the weathered plastics was supplemented by spectral reflectance and UV/VIS spectroscopy.
Different climatic conditions and weather variables during natural and artificial exposure of polymers may be reasons for an unsatisfying correlation between the ageing results. Here the main differences are discussed for:
- Global solar radiation
In weathering devices there is a constant spectral irradiance which is 5 times higher than the averaged spectral irradiance outdoors, which is strongly varying in its diurnal course. Intensified weathering using Fresnel reflectors concentrates only the direct solar radiation with a relatively low UV proportion. Problems of reciprocity may arise from the different mean of irradiance levels.
- Temperatures at specimen surfaces.
Because of the high irradiance levels mentioned above, artificial exposures may lead to high surface temperatures and large temperature differences between differently coloured specimen surfaces, if the artificial radiation source emits much VIS- and IR-radiation. Outdoors the surface temperature and temperature differences of exposed specimens are influenced by considerably lower irradiance levels and additionally by an effective radiation loss in the night.
- Relative humidity at specimen surfaces
In weathering devices the relative humidity at specimen surfaces is very low if it is uncontrolled. If controlled by ultrasonic humidifiers or spray nozzles, the additional exposure to water droplets is quite likely.
- Wetness on specimen surfaces
All usual spray programs prescribed in weathering standards recommend frequently changing of short spray/dry periods and result in total times of wetness (TOW) of the exposed specimen surfaces which is only about 30 % of the outdoor TOW.
- Acidic precipitation and bio films
Acidic precipitation and bio films are usual outdoor conditions which are only considered in special weathering tests.
Influence of weathering on the leaching behaviour of zinc and PAH from synthetic sports surfaces
(2017)
Synthetic materials used for outdoor sports grounds consist of a mix of inorganic, organic and polymeric compounds that show ageing due to weathering and a complex leaching behaviour by percolation of rainwater, which can limit its lifetime. Additionally, weathering exposure induces degradation processes in the polymers, which leads to the formation of new surfaces allowing water to access additional reservoirs of leachable compounds. A laboratory test comprising artificial weathering, ozonisation and subsequent leaching was developed to investigate this behaviour in a reproducible and controllable way. The experiments showed a general decline of Zn, polycyclic aromatic hydrocarbons (PAH) and total organic carbon (TOC) concentrations after an initial increase. Within this general trend, the course of concentration over exposure duration is very specific for individual sample materials and the analyte under investigation. The results indicate that weathering and degradation behaviour cannot be predicted from initial material conditions. Thus, weathering experiments are recommended to fill this gap of knowledge.