Exposure response function for a quantitative prediction of weathering caused aging of polyethylene
(2019)
The exposure response function of the carbonyl formation over the bulk has been determined for a high-density polyethylene of a thickness of 200 μm, which was used as a weathering reference material according to ISO TR 19032. To this end, spectral sensitivity was studied by local measurement of the effect of spectrally dispersed irradiation. Both the exposure device and the methodology of determination are described.
The temperature dependency of photooxidation was determined by UV exposure at various temperatures between 23 and 80 °C. Deviations from linearity and thus reciprocity below 40 °C are discussed and assumed to be related to diffusion limitations. An Arrhenius approach –based on data of linear carbonyl formation – has been incorporated into the exposure response function. Using this exposure response function, aging in terms of the distribution of a quantitative property change over a plastic component can be predicted for a specific outdoor location with real chronologic weather data as input for the exposure. Thus, artificial and natural weathering can be linked and compared. The established exposure response function has been validated by outdoor exposure results from the literature. If an estimated diffusion limitation is taken into consideration, calculations and published data are in good agreement.
In a laboratory test, transparent high‐density polyethylene (HDPE) jerrycans have been exposed to both UV radiation and 55 wt‐% nitric acid solution at (41 ± 2)°C, for up to 20 days. For comparison, UV radiant exposure (21 days) and nitric acid exposure (up to 6 weeks) were performed separately, at nearly equal temperatures. The damages are compared with FTIR spectroscopy in ATR and HT‐gel permeation chromatography(GPC) on a molecular level and with hydraulic internal pressure testing as a component test. For the used jerrycans, relevant oxidation can only be found after the combined exposure. This is caused by the decomposition of nitric acid into nitrous gases by UV radiation, which is also observed at lower concentrations (28 wt‐%). After 6 days of laboratory exposure, this is rated as critical, which corresponds to about 1/10 year in Central Europe, according to the UV radiant exposure. The gradual increase in oxidative damage shows the reproducibility of the test.
Unpigmented HDPE jerrycans filled with nitric acid (55%) and water respectively had been exposed to outdoor conditions for one Berlin summer season. As both liquids underwent equal temperature progression, exposure effects of UV radiation and nitric acid as well as of their combination can be separated and compared. On the basis of various property changes after these exposures, synergistic action is evaluated and compared to a damaged Intermediate Bulk Container (IBC) from a transport accident.
It is found that carbonyl formation goes along with lightness increase in color measurement due to microcracking and with a worsening in mechanical behavior, all of them showing synergistic effects of UV and nitric acid exposure. In contrast, embedding nitrogen compounds goes along with yellowing of the material but cannot be correlated to oxidation.
The reason for intensified damaging is the decomposition of the 55-percent nitric acid and formation of nitrogen oxides even at ambient temperatures, caused by UV radiation. Thus, damaging effects become similar to those caused by fuming nitric acid exposure at temperatures above 60 °C, with the result of strong oxidative degradation of the polyethylene.
In contrast, exclusive exposure to the 55-percent nitric acid at 40 °C does not cause any failure.
It can therefore be assumed that also the damaged IBC had been exposed to both UV radiation and nitric acid, probably outdoors.