Full penetration high power bead-on-plate laser beam welding tests of up to 20 mm thick 2205 duplex steel plates were performed in PA position. A contactless inductive electromagnetic (EM) weld pool support system was used to prevent gravity drop-out of the melt. Welding experiments with 15 mm thick plates were carried out using IPG fiber laser YLR 20000 and Yb:YAG thin disk laser TruDisk 16002. The laser power needed to achieve a full penetration was found to be 10.9 and 8.56 kW for welding velocity of 1.0 and 0.5 m min−1, respectively. Reference welds without weld pool support demonstrate excessive root sag. The optimal value of the alternating current(AC) power needed to completely compensate the sagging on the root side was found to be ≈1.6 kW for both values of the welding velocity. The same EM weld pool support system was used in welding tests with 20 mm thick plates. The laser beam power (TRUMPF Yb:YAG thin disk laser TruDisk 16002) needed to reach a full penetration for 0.5 m min−1 was found to be 13.9 kW. Full penetration welding without EM weld pool support is not possible—the surface tension cannot stop the gravity drop-out of the melt. The AC power needed to completely compensate the gravity was found to be 2 kW.
Full penetration high power bead-on-plate laser beam welding tests of up to 20 mm thick 2205 duplex steel plates were performed in PA position. A contactless inductive electromagnetic (EM) weld pool support system was used to prevent gravity drop-out of the melt. Welding experiments with 15 mm thick plates were carried out using IPG fiber laser YLR 20000 and Yb:YAG thin disk laser TruDisk 16002. The laser power needed to achieve a full penetration was found to be 10.9 and 8.56kW for welding velocity of 1.0 and 0.5 m min(-1), respectively. Reference welds without weld pool support demonstrate excessive root sag. The optimal value of the alternating current (AC) power needed to completely compensate the sagging on the root side was found to be approximate to 1.6 kW for both values of the welding velocity. The same EM weld pool support system was used in welding tests with 20 mm thick plates. The laser beam power (TRUMPF Yb:YAG thin disk laser TruDisk 16002) needed to reach a full penetration for 0.5 m min(-1) was found to be 13.9 kW. Full penetration welding without EM weld pool support is not possible-the surface tension cannot stop the gravity drop-out of the melt. The AC power needed to completely compensate the gravity was found to be 2 kW. (C) 2016 Laser Institute of America
Im Rahmen eines AiF-Forschungsvorhabens wurde die Beeinflussung des Schweißprozesses mittels generierter Wechselstrom-Magnetfelder (ACMagnetfelder) beim Laserstrahlschweißen von Aluminiumlegierungen untersucht. Das vorrangige Augenmerk galt hierbei der Entfernung von Poren sowie der Stabilisierung der Schweißnahtoberfläche zur Vermeidung von rauen Schweißnähten. Das Schweißen mit Einsatz des AC-Magneten erzeugte im Vergleich zu den Referenznähten deutlich flachere Schweißnähte mit reduzierter Porenanzahl, die typische Schuppenstruktur wurde unterdrückt. Das Magnetfeld bewirkte bei entsprechenden Parametern der magnetischen Flussdichte und der Frequenz eine Halbierung der Rauigkeit der Schweißnahtoberfläche. Neben der Oberflächenberuhigung wurde auch die Verteilung von Poren in der Schmelze beeinflusst. Es konnte nachgewiesen werden, dass bei einer geeigneten Auswahl der Parameter von AC-Magnetfeldern die Porositätsanteile in der Schweißnaht auf ein Zehntel gegenüber den Referenzschweißnähten reduziert werden können.-----------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
Within the framework of an AiF research project, investigations were conducted into the influences exerted on the welding process using generated alternating current (AC) magnetic fields during the laser beam welding of aluminium alloys. In this respect, attention was principally paid to removing pores and to stabilising the weld surface in order to avoid rough welds. In comparison with the reference welds, welding utilising the AC magnet produced considerably flatter welds with a reduced number of pores and the typical ripple structure was suppressed. With corresponding parameters for the magnetic flux density and the frequency, the roughness of the weld surface was halved using the magnetic field. In addition to the surface stabilisation, influences were also exerted on the distribution of pores in the molten metal. It was possible to prove that, by selecting suitable parameters for AC magnetic fields, the porosity proportions in the weld can be reduced to one tenth of those in the reference welds.
Full penetration 15 kW Yb fibre laser butt welding of thick AlMg3 (AW 5754) plates was performed in PA position. A contactless inductive electromagnetic weld pool support system was used to prevent gravity dropout of the melt. The welding speed needed to achieve 20 mm penetration was ~0·5 m min-1. An ac power supply of ~244 W at 460 Hz was necessary to completely suppress gravity dropout of the melt and eliminate sagging of the weld pool root side surface. The oscillating magnetic field can suppress the Marangoni convection in the lower part of the weld pool. The system was also successfully used in the full penetration welding of 30 mm thick AlMg3 plates.
The main characteristic feature of deep penetration laser beam welding is a large temperature difference between the plasma cavity (keyhole) in the centre of the weld pool and the melting/solidification front. Large temperature gradients in the weld pool result in a very intensive thermocapillary (Marangoni) convection. The weld pool surface width becomes very large and unstable. However, an externally applied oscillating magnetic field can stabilize the surface of the melt (the Garnier-Moreau effect, 1983). In the present work this technology was used to stabilize the surface of the weld pool in partial penetration 4.4 kW Nd:YAG laser beam welding of AW-5754 alloyin PA position. The AC magnet was mounted on the laser welding head. The oscillating magnet field was oriented perpendicular to the welding direction. It was found that the AC magnet field can drastically reduce the surface roughness of welds. The analysis of the x-ray images shows a rastic reduction of porosity content in the welds. This effect can be explained as a result of electromagnetic ectification of the melt.
An oscillating (AC) magnet field was used to suppress porosity formation and to stabilize the surface of the weld pool in bead-on-plate partial penetration 4.4 kW Nd:YAG laser beam welding of AW-5754 plates in PA position. The magnet was mounted on the laser welding head. The magnet field (up to 0.4 T and 10 kHz) was oriented perpendicular the welding direction.
The analysis of the weld cross-sections and x-ray images shows a drastic reduction (up to 90%) of porosity contents in the welds. The observed effects can be explained in terms of electromagnetically (EM)
induced 'Archimedes' forces as well as the EM stirring flow in the weld pool. Moreover, usage of AC magnetic fields results in a significant reduction (up to 50%) of the surface roughness of the welds. This effect can be explained in terms of electromagnetic (EM)
contribution to the surface tension (the Garnier-Moreau effect)