A fracture mechanics model which shall be applied to the fatigue strength determination of weldments has to focus on various aspects such as: (a) the description of mechanical and physical short fatigue crack extension which is characterised by yielding conditions which do not permit the application of the common ΔK concept and by the gradual build-up of the crack closure effect, (b) a consistent methodology for determining the initial crack size, (c) based on this, the determination of a fatigue limit, (d) the treatment of multiple crack propagation at load levels above this limit, (e) the variation of the local geometry along the weld toe, and (f) statistical effects.The paper gives alimited overview of the work the authors did in this field during the last years within the German project cluster IBESS. A model is presented and briefly discussed which covers the questions above.
Based on a large set of 2D finite element analyses, parametric equations for weld toe stress concentration factors and through-thickness stress profiles are provided for butt-welded plates. These cover Single-Vand Double-V joints subject to tensile and bending loading. Compared to the most widespread solutions in the literature, which have also been tested against the finite element data in this work, the application range is extended particularly with respect to the weld toe radius(0.1≤ρ≤4 mm)andangle(10 °≤α≤60 °). Furthermore, two values of excess weld metal are considered (h=0.75;2.5mm). The analyses are performed for a plate thickness of 10 mm. Besides the extended validity range, the proposed equations show also an improved accuracy compared to the existing solutions.
The fatigue crack propagation threshold ΔKth is of paramount importance for any kind of damage tolerant design, but in contrast to this importance, the determination and application of the parameter is not on the firm ground as previously assumed. The paper discusses questions of its experimental determination as well as of its application to components. In both fields, new questions have been raised with the potential to challenge or modify long-standing knowledge. Against this background, the paper is an attempt to systematize the established knowledge as well as questions and open issues.
The paper deals with the prediction of the fatigue Limit of notched specimens. Some authors in the literature have shown that this issue can be solved by employing an approach based on critical distances, others used elastic fracture mechanics. In this paper the fatigue limit of notched specimens is given by the non-propagating condition of mechanically small surface cracks. According to the so-called cyclic R-curve method, the crack driving force of a growing small crack is compared to its resistance force, which incorporates the gradual build-up of crack closure. The fatigue limit is determined by that applied nominal stress, for which the tangency condition of crack driving and resistance force is satisfied. The approach has been modified to incorporate plasticity effects in the mechanically short crack Regime and it has been applied to a mild and a high-strength steel, in case of an infinite plate with circular hole under remote tensile stress. The method has been successfully applied to the evaluation of fatigue notch-sensitivity in case of surface roughness.