Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on productionsimilar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. In particular, the rimpeeling failure mode is considered as case study. A semi-circular surface crack is modelled at the most stressed region at the diaphragm of a turbine disk, with the crack plane perpendicular to the radial direction. The crack is therefore subjected to a biaxial stress state and grows under increasing rotational speed until it triggers the rim-peeling failure. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of -integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. Probabilistic aspects are also considered in the calculations.
The knowledge of fatigue crack propagation data in terms of their effective values is important for a conservative and safe life assessment of components subjected to cyclic loading. To overcome issues related to the precise consideration of the crack-closure effects on experimental data obtained at small R ratios, closure-free data have been obtained at R ≈ 0.8 by different experimental procedures. The statistical analysis of the intrinsic fatigue crack propagation threshold obtained experimentally has shown a small data scatter and good agreement between procedures. When compared with effective values obtained from analytical corrections of closure-affected data, the data obtained at R ≈ 0.8 should lead to a conservative life estimation.
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of 𝐽-integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest 𝐽 -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. In addition, probabilistic aspects are also considered in the calculations.
The present paper provides a discussion on all these topics and it offers solutions for it. The authors present an analytical solution of a Delta J based crack driving force based on an R6 type approach but modified for cyclic loading. The gradual build-up of the crack closure effect is modelled by the so-called cyclic R curve which describes the crack size dependency of the fatigue crack propagation threshold in the short crack regime. It is explained how the cyclic R curve is experimentally determined and how it can be estimated by a modified Kitagawa-Takahashi approach.
A fracture mechanics model which shall be applied to the fatigue strength determination of weldments has to focus on various aspects such as: (a) the description of mechanical and physical short fatigue crack extension which is characterised by yielding conditions which do not permit the application of the common ΔK concept and by the gradual build-up of the crack closure effect, (b) a consistent methodology for determining the initial crack size, (c) based on this, the determination of a fatigue limit, (d) the treatment of multiple crack propagation at load levels above this limit, (e) the variation of the local geometry along the weld toe, and (f) statistical effects.The paper gives alimited overview of the work the authors did in this field during the last years within the German project cluster IBESS. A model is presented and briefly discussed which covers the questions above.
A discussion is provided on the relation between non-destructive testing (NDT) and fracture mechanics. The basic tasks behind this are to guarantee the safety of a component at a potential hazard loading event, to specify inspection intervals or, alternatively, of demands on NDT for a fixed inspection regime, to plan accompanying measures for cases of temporary continued operation of structures in which cracks have been detected, and, finally, fatigue strength considerations which take into account initial defects.
Special aspects of welded components such as geometrical imperfections, inhomogeneity, strength mismatch and welding residual stresses have to be taken into account in a fracture mechanics analysis since they affect the crack driving force in the component as weil as the fracture resistance of the material. The treatment of components subjected to static loading is based on methods such as the European SINT AP procedure, which has been validated in a nurober of case studies. In the present paper the influence of strength mismatch and residual stresses on the fracture resistance and the assessment of a component are discussed.
The idea to determine the fatigue strength of weldments by means fracture mechanics was originally based on the empirical observation that the major portion of the fatigue life in weldments is frequently spent in crack propagation. The present paper gives a brief overview on the basic principles of fracture mechanics-based determination of fatigue strength and on special features which have to be considered for weldments. Based on this information, the ongoing research project IBESS is introduced and briefly reviewed.
The burst of a disc in rotating machinery can cause catastrophic damage of the equipment and, more importantly, it can represent a mortal threat to anyone in the sphere of influence of the event. In order to minimize the danger associated to a rotating component failure, burst testing is required by the authorities in order to set safety margins to the normal operating speeds. Moreover more accurate predicting tools are required for designing the components. This paper presents the results of a numerical and analytical study on the assessment of the crack driving force for discs containing surface flaws. The aim is to provide a simple, though reliable, tool in order to be able to calculate the possible dangerous in-service speed for a rotating component and, therefore, to set burst margins above the normal operating conditions of the equipment. An R6-like flaw assessment procedure is adopted considering different assumptions in the definition of the critical speed and the analytical predictions are compared with the results of elastic-plastic finite element analysis of disc. In particular, the validity and potentiality of the method is proved for surface flaws in different positions in the disc.
An analytical fracture mechanics model for predicting the finite life fatigue strength of components is presented which Combines a number of well established and newly developed approaches such as Murakami’s and McEvily's approach for describing the transient behaviour of crack closure of short cracks, the analytical (long) crack closure function of Newman, the R6 procedure modified by a method for improving the ligament yielding correction proposed by the authors and other elements. Basic assumption is the preexistence of initial flaws such that the crack initiation or nucleation stage is small and can be neglected. The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with artificial initial defects generated by FIB technology, the size of which was fixed on the basis of fractographic investigations on broken, smooth specimens.