Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (57)
- Vortrag (40)
- Beitrag zu einem Tagungsband (32)
- Monografie (3)
- Buchkapitel (2)
- Beitrag zu einem Sammelband (2)
- Forschungsbericht (2)
Schlagworte
- Fracture mechanics (25)
- Fatigue strength (19)
- Bruchmechanik (16)
- Schwingfestigkeit (14)
- Weldments (10)
- Fatigue crack propagation (9)
- Fatigue crack propagation threshold (7)
- Short crack propagation (7)
- Short cracks (7)
- FITNET (6)
Organisationseinheit der BAM
- 9 Komponentensicherheit (52)
- 9.4 Integrität von Schweißverbindungen (49)
- 9.0 Abteilungsleitung und andere (7)
- 5 Werkstofftechnik (6)
- 5.1 Mikrostruktur Design und Degradation (5)
- 9.6 Additive Fertigung metallischer Komponenten (5)
- 8 Zerstörungsfreie Prüfung (3)
- 8.5 Röntgenbildgebung (3)
- 4 Material und Umwelt (2)
- 9.3 Schweißtechnische Fertigungsverfahren (2)
- 4.0 Abteilungsleitung und andere (1)
- 4.2 Material-Mikrobiom Wechselwirkungen (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
- 5.5 Materialmodellierung (1)
- 8.3 Thermografische Verfahren (1)
- S Qualitätsinfrastruktur (1)
- S.0 Abteilungsleitung und andere (1)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (40)
Ermüdungsrisse gehen in technischen Materialien in der Regel von Werkstoffdefekten auf oder nahe der Oberfläche aus. Bei Schweißverbindungen können Schweißnahtdefekte, z. B. oberflächennahe Schlackeneinschlüsse die Risseinleitungsphase erheblich verkürzen, so dass der Hauptteil der Lebensdauer auf die Phase der Kurzriss- und zu geringerem Anteil auf die Langrissausbreitung entfällt. Bei nichtgeschweißten Bauteilen aus technischen Werkstoffen starten Ermüdungsrisse häufig an Einschlüssen, oberflächennahen Poren oder anderen Ungänzen. Einerseits ermöglicht dies prinzipiell die Anwendung bruchmechanischer Methoden zur Ermittlung der Schwingfestigkeit, andererseits müssen die Methoden in der Lage sein, spezielle Aspekte des Kurzrisswachstums wie den graduellen Aufbau des Rissschließeffekts und die lokale Rissspitzenplastizität zu erfassen. Im Beitrag werden ein geeignetes analytisches Modell sowie erste Validierungen an Proben aus verschiedenen Aluminiumlegierungen vorgestellt. Der abschließende Teil des Beitrags geht auf Besonderheiten von Schweißverbindungen (Schweißnahtdefekte, Eigenspannungen etc.) im Kontext des vorgestellten Modells ein. Eine Erweiterung des Modells für Schweißverbindungen aus Stahl wird im Rahmen eines kürzlich gestarteten DFG-AiF-Clusterprojekts erfolgen.
An analytical fracture mechanics model for predicting the finite life fatigue strength of components is
presented which combines a number of well established and newly developed approaches such as
Murakami's and McEvily's approach for describing the transient behaviour of crack closure of short
cracks, the analytical (long) crack closure function of Newman which became part of the widely used
NASGRO approach, the R6 procedure, a method for improving the ligament yielding correction f(Lr ) of
R6 proposed by the authors of the present paper and other elements. Basic assumption is the preexistence
of initial flaws such that the crack initiation or nucleation stage is small and can be neglected.
The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with
artificial initial defects generated by FIB technology, the size of which was fixed on the basis of
fractographic investigations on broken, smooth specimens.
The net section limit load FY necessary for assessment at static loading is a key input for the accuracy of any elasticplastic flaw assessment procedure of the R6 type. Unfortunately available limit load solutions are of variable quality since they have been obtained over decades by different methods. As a consequence the results of the fracture analyses such as the critical load or crack size are limited in their accuracy and are often significantly conservative. Further, common limit load solutions based on ligament yielding are inadequate in a number of cases even for through crack configurations and should be replaced by some kind of local yielding solutions. In the present paper a simple and straightforward reference load definition is proposed instead of the limit load which strictly corresponds to a ligament yielding parameter Lr = 1 in the R6 Routine and similar approaches such as the European SINTAP and FITNET methods. This can be determined by finite element simulation for any geometry. In addition to a previous study on thin wall notched plates the method is applied to plates containing shallow semi-elliptical surface cracks. The results demonstrate that the approach provides a suitable extension and improvement of the existing methods.
In the approval procedure of transport packages for radioactive materials, the mechanical and thermal safety assessment is carried out in Germany by competent authority BAM. In recent years BAM was involved in several licensing procedures of new spent fuel and HLW package designs, where the cask body was made of Ductile Cast Iron (DCI). According to IAEA regulations package designs have to fulfill requirements for specific conditions of transport. Type B(U) packages must withstand the defined accident conditions of transport. The temperature range from -40°C up to the operational temperature has to be considered. For the cask material DCI, it is necessary to determine the brittle fracture behavior. The German guideline BAM-GGR 007 defines requirements for the fracture mechanics of DCI. Due to complex structure of the cask body and the dynamic loading a fracture mechanical assessment in an analytical kind is not always possible. Experience of recent design approval procedures show that the application of numerical calculations are applicable to determine the fracture mechanical load in the cask body. At the first step a numerical analysis has to be done to identify the loading state at the whole cask body. Secondly an analysis of a detail of the cask body is made considering the displacement boundary conditions of the global model. An artificial flaw is considered in this detailed model to calculate the fracture mechanical loading state. The finite element mesh was strongly refined in the area of flaw. The size of the artificial flaw is characterized by the ultrasonic inspection used for the quality assurance of the package. The applicant developed additional analysis tools for calculation of stress intensity factor and/or J-Integral. The assessment approach by BAM led to the decision to develop own tools to the possibility for independent check of the results.
The paper describes the authority assessment approach for the DCI fracture mechanics analysis. The validation procedure incl. the development of own tools is explained. BAM developed a post-processor called JINFEM to determine the fracture mechanical loads. The regulatory 1 m puncture bar drop test is used to give an example of the assessment procedure.
The paper provides a discussion on damage tolerance options applied to railway axles and factors influencing the residual lifetime as well as the required inspection interval. These comprise material properties such as the scatter of the da/dNΔK curve, the fatigue crack propagation threshold ΔKth and the toughness of the material. Parameters affecting axle loading such as the press fit, rotating bending, load history and mixed crack opening modes are discussed. Finally the influence of the initial crack geometry on residual lifetime is simulated.
The aim of this paper is a collection of stress intensity factor solutions for cracks in railway axle geometries which the authors of the present special issue developed and/or used for damage tolerance analyses. These solutions comprise closed form analytical as well as tabled geometry functions and they refer to solid as well as hollow axles and various crack sites such as the T- and V-notch and the axle body.
Railway structures such as rails and axles are safety relevant components since any failure includes the risk of catastrophic derailment. This paper gives a brief overview on the most important potential failure scenarios driven by fatigue crack initiation and propagation and discusses the effects of important influencing factors such as vehicle weight and speed, track quality and environmental conditions. The present paper summarizes earlier work of the authors in this field.
The net section limit load FY is a key input parameter for the accuracy of any
elastic-plastic flaw assessment procedure of the R6 type. Unfortunately available limit load
solutions are of variable quality since they have been obtained over decades by different
methods. As a consequence the results of the fracture analyses such as the critical load or
crack size are limited in their accuracy and are often significantly conservative. A further
problem is that common limit load solutions based on ligament yielding are inadequate in a
number of cases even for through crack configurations and should be replaced by some
kind of local yielding solutions. In the present paper a simple and straightforward reference
load definition is proposed instead of the limit load which strictly corresponds to a ligament
yielding parameter Lr = 1 in the R6 Routine and similar approaches such as SINTAP and
FITNET. This can be determined by finite element simulation for any geometry. In addition to
a previous study on thin wall notched plates the method is applied to plates containing
shallow semi-elliptical surface cracks. The results demonstrate that the approach provides a
suitable extension and improvement of the existing methods.