The knowledge of fatigue crack propagation data in terms of their effective values is important for a conservative and safe life assessment of components subjected to cyclic loading. To overcome issues related to the precise consideration of the crack-closure effects on experimental data obtained at small R ratios, closure-free data have been obtained at R ≈ 0.8 by different experimental procedures. The statistical analysis of the intrinsic fatigue crack propagation threshold obtained experimentally has shown a small data scatter and good agreement between procedures. When compared with effective values obtained from analytical corrections of closure-affected data, the data obtained at R ≈ 0.8 should lead to a conservative life estimation.
The impact of crack closure and environmental effects on the experimental determination of the fatigue crack propagation threshold is a major problem for the assessment of cyclically loaded components, especially at low stress ratios 𝑅. In this work, the influence of the experimental procedure and air humidity on d𝑎∕d𝑁 − 𝛥𝐾 data at different 𝑅 is discussed. Unlike the results at 𝑅 = −1, the threshold values obtained at 𝑅 ≈ 0.8, i.e. under negligible crack closure levels, show a very small scatter band regardless of the variation of the test parameters and environmental conditions.
This article is an outcome of a workshop on Fatigue of Additive Manufactured Metallic Components jointly organized by the Federal Institute for Materials Research and Testing (BAM) Berlin, Germany and the National Institute of Standards and Technology (NIST) Boulder, CO, U.S.A. The aim of the workshop was a comprehensive discussion of the specific aspects of additively manufactured (AM) components in regard to failure under cyclic loading. Undoubtedly, a better understanding and the further development of approaches for damage tolerant component design of AM parts are among the most significant challenges currently facing the use of these new technologies.
This article presents a thorough overview of the workshop discussions. It aims to provide a review of the parameters affecting the damage tolerance of AM parts with special emphasis on the process parameters intrinsic to the AM technologies, the resulting defects and residual stresses. Based on these aspects, concepts for damage tolerant component design for AM are reviewed and critically discussed.