Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (57)
- Vortrag (40)
- Beitrag zu einem Tagungsband (32)
- Monografie (3)
- Buchkapitel (2)
- Beitrag zu einem Sammelband (2)
- Forschungsbericht (2)
Schlagworte
- Fracture mechanics (25)
- Fatigue strength (19)
- Bruchmechanik (16)
- Schwingfestigkeit (14)
- Weldments (10)
- Fatigue crack propagation (9)
- Fatigue crack propagation threshold (7)
- Short crack propagation (7)
- Short cracks (7)
- FITNET (6)
- IBESS (6)
- Initial crack size (6)
- Multiple crack propagation (6)
- Railway axles (6)
- S-N curve (6)
- SINTAP (6)
- Schadenstoleranz (6)
- Crack propagation (5)
- Cyclic R-curve (5)
- Fatigue (5)
- Flaw assessment (5)
- Limit load (5)
- Reference load (5)
- Crack closure (4)
- Damage tolerance (4)
- Non-metallic inclusions (4)
- R6 procedure (4)
- Additive manufacturing (3)
- Component assessment (3)
- Constraint (3)
- Cyclic J-integral (3)
- Defects (3)
- Kitagawa-Takahashi diagram (3)
- Residual stresses (3)
- Rissarrest (3)
- Safe life design (3)
- Selective Laser Melting (SLM) (3)
- Structural integrity (3)
- Turbine disk (3)
- Werkstoffeigenschaften (3)
- Zyklische R-Kurve (3)
- Ausgangsriss (2)
- Bauteilbewertung (2)
- Bruchmechanische Bauteilbewertung (2)
- Burst (2)
- Corrosion (2)
- Crack driving force (2)
- Cyclic R-curve analysis (2)
- Damage tolerance design (2)
- Endurance limit (2)
- Experimental determination (2)
- Experimental procedure (2)
- Fail-safe (2)
- Failure analysis (2)
- Fatigue crack growth (2)
- Fatigue life (2)
- Flying ballast impact (2)
- Fracture (2)
- Fracture resistance (2)
- Fracture toughness (2)
- Inclusions (2)
- Korrosion (2)
- Material defects (2)
- Mehrfachriss (2)
- Micro-shrinkages (2)
- Multiple cracks (2)
- Nichtmetallische Einschlüsse (2)
- Pores (2)
- R6 (2)
- Radsatzwellen (2)
- Railway rails (2)
- Reference stress method (2)
- Residual lifetime (2)
- Schweißverbindungen (2)
- Sichere Lebensdauer (2)
- Steinschlag (2)
- Strength mismatch (2)
- Weld toe geometry (2)
- Welded joints (2)
- Welding residual stresses (2)
- Zerstörungsfreie Inspektion (2)
- (Residual) lifetime (1)
- 316L (1)
- AM 316L stainless steel (1)
- ASTM E647 (1)
- Accompanying measures (1)
- Achsschenkel (1)
- Additive Fertigung (1)
- Additive Manufacturing (1)
- Analytisches Modell (1)
- BS 7910 (1)
- Bauteilauslegung (1)
- Biaxial loading (1)
- Biaxial tensile loading (1)
- Bruch (1)
- Bruchmechanische Auslegung (1)
- Bruchmechanische Kennwerte (1)
- Bruchmechanische Konzepte (1)
- Burst test (1)
- Butt welds (1)
- Chapetti’s and IBESS model (1)
- Characterisation (1)
- Codes and standards (1)
- Compression pre-cracking (1)
- Constraint faktor (1)
- Contact fatigue (1)
- Corrosion pits (1)
- Crack Tip Opening Displacement (CTOD) (1)
- Crack arrest (1)
- Crack closure effect (1)
- Crack closure mechanisms (1)
- Crack closure phenomenon (1)
- Crack initation (1)
- Crack-closure (1)
- Critical distance (1)
- Critical speed (1)
- Cyclic R curve (1)
- Cyclic stress-strain curve (1)
- Damage tolerant component design (1)
- Data evaluation methods (1)
- Defekte Eigenspannung (1)
- Derailment (1)
- Druckanschwingen (1)
- EPRI method (1)
- EPRI-Methode (1)
- Effective crack propagation data (1)
- Einflussfaktoren auf Rissfortschrittsdaten (1)
- Einschlüsse (1)
- Elastic follow-up (1)
- Elastic-plastic fracture mechanics (1)
- Environment (1)
- Environmental conditions (1)
- Environmental effect (1)
- Environmental effects (1)
- Ermüdungsrissausbreitung (1)
- Ermüdungsrissfortschritt (1)
- FAT class (1)
- FAT class approach (1)
- FAT class concept (1)
- FEM (1)
- FKM-Richtlinie (1)
- FORM (1)
- FORM/SORM (1)
- Fail-safe design (1)
- Failure Assessment Diagram (1)
- Failure probability (1)
- Fatigue S-N curve (1)
- Fatigue crack (1)
- Fatigue crack initiation (1)
- Fatigue crack propagation stages (1)
- Fatigue crack propagation stagesdefects (1)
- Fatigue life prediction (1)
- Fatigue loading (1)
- Fatigue strength and life (1)
- Finite element (FE) (1)
- Flaw assessment procedures (1)
- Flaw interaction (1)
- Flawed rotors (1)
- Foot crack (1)
- Fracture Mechanics (1)
- Fracture assessment (1)
- Fracture of weldments (1)
- Global stability criterion (1)
- Graphite modules (1)
- Grenzlast (1)
- HAZ (1)
- HCF (1)
- Heat affected zone (1)
- IBESS-Prozedur (1)
- ISO 12108 (1)
- Impact damage (1)
- In-situ Process Monitoring (1)
- Inclusion cluster (1)
- Inclusion size (1)
- Influencing factors (1)
- Initial flaw size (1)
- Inspection intervals (1)
- Intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung (1)
- J-Integral (1)
- J-integral (1)
- Kerbschlagarbeit (1)
- Korrelation (1)
- Kritische Last (1)
- Kurz- und Langriss-Ermüdungsbruchmechanik (1)
- Kurzrissbruchmechanik (1)
- Kurzrisswachstum (1)
- L-PBF (1)
- LCF (1)
- Lastabsenkung (1)
- Life prediction (1)
- Ligamentplastifizierung (1)
- Load decreasing (1)
- L‐PBF (1)
- Material inhomogeneity (1)
- Mechanische Bewertung (1)
- Metallic components (1)
- Mis-match (1)
- Mismatch (1)
- Monotonic and cyclic crack driving force (1)
- Multiple crack initiation (1)
- Multiple cracking (1)
- Non-destructive Materials (1)
- Non-destructive inspection (1)
- Non-destructive testing (1)
- Non-propagating cracks (1)
- Non-sharp defects (1)
- Notch fatigue (1)
- Notch sensitivity (1)
- Notches (1)
- Nuclear reactor systems (1)
- Numerische Analyse (1)
- Oberflächenschädigung (1)
- Overspeed (1)
- Oxide-induced crack closure (1)
- Peak stress method (PSM) (1)
- Pipes (1)
- Plastic collapse (1)
- Poren (1)
- Primär- und Sekundärspannungen (1)
- Process development (1)
- R-curve analysis (1)
- R6-Routine (1)
- Radioaktives Material (1)
- Railway axle (1)
- Rauheit (1)
- Reference yield load (1)
- Referenzlast (1)
- Referenzspannungsmethode (1)
- Reliability (1)
- Representative material properties (1)
- Repräsentative Werkstoffeigenschaften (1)
- Restlebensdauer (1)
- Rissausbreitung (1)
- Rissausbreitungsstadien (1)
- Rissschließeffekte (1)
- Rissschließfunktion (1)
- Rissschließphenomen (1)
- Rissspitzenbelastung (1)
- Risswiderstand (1)
- Root cause (1)
- Safety (1)
- Safety assessment (1)
- Schadenstolerante Bauteilauslegung (1)
- Schadenstolerante Bauteilauslegung, (1)
- Schadenstolerante Bauteilauslegung, Restlebensdauer, intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung (1)
- Schweißeigenspannungen (1)
- Schweißeigenspannungs-Tiefen-Profile (1)
- Schwellenwert (1)
- Schwellenwert gegen Ermüdungsrissausbreitung (1)
- Scratches (1)
- Secondary stresses (1)
- Service loading fatigue (1)
- Short crack (1)
- Short fatigue-cracks (1)
- Shrinkages (1)
- Stabilität von Eigenspannungen (1)
- Standardisation (1)
- Statistics (1)
- Steel (1)
- Steel 316L (1)
- Stiffness (1)
- Strength mis-match (1)
- Stress analysis (1)
- Stress intensity factor (1)
- Stretch-Zone (1)
- Structures (1)
- Struktur Integrität (1)
- Surface roughness (1)
- SN curve (1)
- Tearing instability (1)
- Testing parameters (1)
- Threshold (1)
- Transferability to components (1)
- Turbinenscheibe (1)
- Weld fatigue (1)
- Weld geometry (1)
- Weld toes (1)
- Werstoff- und geometrische Imperfektion (1)
- Zerstörungsfreie Prüfung (1)
- Zuverlässigkeit (1)
- damage tolerance (1)
- fatigue crack propagation (1)
- fatigue strength (1)
- fracture mechanics (1)
- inspection (1)
- probability (1)
- railway axles (1)
Organisationseinheit der BAM
- 9 Komponentensicherheit (52)
- 9.4 Integrität von Schweißverbindungen (49)
- 9.0 Abteilungsleitung und andere (7)
- 5 Werkstofftechnik (6)
- 5.1 Mikrostruktur Design und Degradation (5)
- 9.6 Additive Fertigung metallischer Komponenten (5)
- 8 Zerstörungsfreie Prüfung (3)
- 8.5 Röntgenbildgebung (3)
- 4 Material und Umwelt (2)
- 9.3 Schweißtechnische Fertigungsverfahren (2)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (40)
The paper gives an overview on safe life and damage tolerance methods applied to railway axles. It describes failure scenarios due to fatigue crack initiation and propagation. Besides common aspects of design, specific features such as corrosion and impact damage from flying ballast are discussed which may reduce the fatigue strength of axles during service. Potential effects of non-metallic inclusions from the steel manufacturing process are addressed in the context of the very high number of loading cycles railway axles are designed for. With respect to damage tolerance general lines of fracture mechanics residual lifetime analyses are introduced. More specific discussion is provided on aspects such as the threshold value of fatigue crack propagation and reliability aspects of non-destructive inspection.
An analytical fracture mechanics model for predicting the finite life fatigue strength of components is presented which Combines a number of well established and newly developed approaches such as Murakami’s and McEvily's approach for describing the transient behaviour of crack closure of short cracks, the analytical (long) crack closure function of Newman, the R6 procedure modified by a method for improving the ligament yielding correction proposed by the authors and other elements. Basic assumption is the preexistence of initial flaws such that the crack initiation or nucleation stage is small and can be neglected. The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with artificial initial defects generated by FIB technology, the size of which was fixed on the basis of fractographic investigations on broken, smooth specimens.
On July 9, 2008 a high speed train derailed in Cologne main Station, Germany at a low speed because an axle was broken. Fortunately, the derailment happened at a low speed so that nobody was injured. The reason for the broken axle was investigated and it turned out that most likely large inclusions located shortly undemeath the surface in a T-transition were the origin of the final crack. Basing on that result, a systematic investigation on existing safety assessments of railway axles was performed. This results in an analysis of the production process of axles and in a critical review of existing of existing assessments. Improvements and future developments are outlined.
The net section limit load FY is a key input parameter for the accuracy of any
elastic-plastic flaw assessment procedure of the R6 type. Unfortunately available limit load
solutions are of variable quality since they have been obtained over decades by different
methods. As a consequence the results of the fracture analyses such as the critical load or
crack size are limited in their accuracy and are often significantly conservative. A further
problem is that common limit load solutions based on ligament yielding are inadequate in a
number of cases even for through crack configurations and should be replaced by some
kind of local yielding solutions. In the present paper a simple and straightforward reference
load definition is proposed instead of the limit load which strictly corresponds to a ligament
yielding parameter Lr = 1 in the R6 Routine and similar approaches such as SINTAP and
FITNET. This can be determined by finite element simulation for any geometry. In addition to
a previous study on thin wall notched plates the method is applied to plates containing
shallow semi-elliptical surface cracks. The results demonstrate that the approach provides a
suitable extension and improvement of the existing methods.
The net section limit load FY necessary for assessment at static loading is a key input for the accuracy of any elasticplastic flaw assessment procedure of the R6 type. Unfortunately available limit load solutions are of variable quality since they have been obtained over decades by different methods. As a consequence the results of the fracture analyses such as the critical load or crack size are limited in their accuracy and are often significantly conservative. Further, common limit load solutions based on ligament yielding are inadequate in a number of cases even for through crack configurations and should be replaced by some kind of local yielding solutions. In the present paper a simple and straightforward reference load definition is proposed instead of the limit load which strictly corresponds to a ligament yielding parameter Lr = 1 in the R6 Routine and similar approaches such as the European SINTAP and FITNET methods. This can be determined by finite element simulation for any geometry. In addition to a previous study on thin wall notched plates the method is applied to plates containing shallow semi-elliptical surface cracks. The results demonstrate that the approach provides a suitable extension and improvement of the existing methods.
The safety assessment of railway axles is based on a two-stage approach: fatigue strength design and regular inspections which, in terms of a general safety philosophy refer to safe-life and damage tolerance concepts. Starting with a recent failure case, a broken axle of a German high speed train, a discussion is presented on issues of both safety levels. These include ideas for finite life design, the treatment of in-service effects on the fatigue strength due to flying ballast damage and corrosion pits, the effect of corrosion on fatigue crack initiation and propagation, potential effects of non-metallic inclusions in steels, the way to detect them by quality control measures and reliability aspects of non-destructive testing with respect to the detection of fatigue cracks. Proposals are made how the safety level could be further improved.
In the design approval of transport packages for radioactive materials, the mechanical and thermal safety assessment is carried out in Germany by competent authority BAM. In recent years BAM was involved in several licensing procedures of new spent fuel and HLW package designs, where the cask body is of Ductile Cast Iron (DCI). According to IAEA regulations package designs have to fulfill requirements for specific conditions of transport. Type B(U) packages must withstand the defined accident conditions of transport. The temperature range from -40°C up to the operational temperature has to be considered. For the cask material DCI, it is necessary to determine safety against brittle fracture. The German guideline BAM-GGR 007 defines requirements for fracture mechanics of packagings made of DCI. Due to complex cask body structure and the dynamic loading a fracture mechanical assessment by analytical approaches is not always possible. Experience of recent design approval procedures show that the application of numerical calculations are applicable to determine the stresses and stress intensity factors in the cask body. At the first step a numerical analysis has to be done to identify
the loading state at the whole cask body. Secondly an analysis of a detail of the cask body is made considering the displacement boundary conditions of the global model. An artificial flaw is considered in this detailed model to calculate the fracture mechanical loading state. The finite element mesh was strongly refined in the area of the flaw. The size of the artificial flaw is based on the ultrasonic inspection acceptance criteria applied for cask body manufacture. The
applicant (GNS) developed additional analysis tools for calculation of stress intensity factor and/or J-Integral. The assessment approach by BAM led to the decision to develop own tools to the possibility for independent proof of the results.
The paper describes the authority assessment approach for DCI fracture mechanics analysis. The validation procedure incl. the development of own tools is explained. BAM developed a postprocessor to determine the fracture mechanical loads. A horizontal 1 m puncture bar drop test is used to give a detailed description of the assessment procedure.
Die Sicherheit von Radsatzwellen beruht gegenwärtig auf zwei Säulen: der Schwingfestigkeitsauslegung und periodischen Inspektionen. Ausgehend von einem Schadensfall, der gebrochenen ICE 3-Welle von Köln, 2008, sollen ausgewählte Aspekte beider Säulen diskutiert und Vorschläge zur weiteren Verbesserung gemacht werden. Diese betreffen u.a. Fragen einer Betriebszeitbegrenzung, Veränderungen der Schwingfestigkeit während des Betriebs infolge von Korrosion und Steinschlag, den Einfluss von Korrosion auf Schwingrissinitiierung und -fortschritt, den potentiellen Einfluss nichtmetallischer Einschlüsse auf die Schwingfestigkeit, die Möglichkeiten sie im Rahmen der Qualitätssicherung zu detektieren sowie Fragen der Bruchmechanik und der Zuverlässigkeit zerstörungsfreier Schwingriss-Prüfverfahren im Rahmen eines Konzepts regelmäßiger Inspektionen.
The robust determination of the threshold against fatigue crack propagation DKth is of paramount importance in fracture mechanics based fatigue assessment procedures. The standards ASTM E647 and ISO 12108 introduce operational definitions of DKth based on the crack propagation rate da/dN and suggest linear fits of logarithmic DK– da/dN test data to calculate DKth. Since these fits typically suffer from a poor representation of the actual curvature of the crack propagation curve, a method for evaluating DKth using a nonlinear function is proposed. It is shown that the proposed method reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density.
Bei der Auslegung von Achsschenkeln für Nutzfahrzeuge wird für den Überlastfall ein fail-safe-Kriterium (kontrolliertes Versagen) als Basisphilosophie angesetzt. Gefordert wird, dass sich der Achsschenkel auch unter Akzeptanz begrenzten Risswachstums hinreichend elastisch-plastisch verformen kann, ohne dass es zum Bruch kommt. Der Fahrer soll anschließend anhand der bleibenden Verformungen bemerken können, dass mit seinem Fahrzeug etwas nicht in Ordnung ist. Eine Voraussetzung für dieses Bauteilverhalten ist eine hinreichende Bruchzähigkeit des Werkstoffs. Diese, wie auch die Rissspitzenbeanspruchung, müssen ermittelt werden, um den bruchmechanischen Sicherheitsnachweis führen zu können. Zur Ermittlung der mechanisch-technologischen und bruchmechanischen Werkstoffeigenschaften wurde ein Prüfkonzept entwickelt, bei dem die Proben an der potenziell kritischen Stelle direkt aus den geschmiedeten Achsschenkeln entnommen werden. Die experimentelle Werkstoffcharakterisierung bildet dann die Beanspruchungsbedingungen beim Überlastereignis ab. Im Rahmen der Produktion stehen jedoch nur Kerbschlagarbeitswerte zur Verfügung und aufwändige bruchmechanische Versuche sollen vermieden werden. Deshalb wurde eine Korrelation zur Abschätzung der vorhandenen Bruchzähigkeit aus der Kerbschlagarbeit herangezogen. Es ergibt sich eine Ergebnismatrix, die die Einflussgrößen Versagenswahrscheinlichkeit, Temperatur und Bruchzähigkeit verknüpft. Abschließend wird ein erster Vergleich der abgeschätzten mit den experimentell ermittelten Bruchzähigkeitswerten gezogen. Dieser weist aus, dass die abgeschätzten Werte geringfügig konservativ sind.
In the framework of the fatigue assessment of welded components, several methods are available in design standards such as the nominal stress, hot-spot stress, notch stress and linear elastic fracture mechanics approaches. The present paper aims at comparing two advanced local approaches for the fatigue strength assessment of different welded joints made of steel. The first one is IBESS which is based on short crack fracture mechanics. The second one is the PSM which instead involves the strain energy density approach. Both methods will be briefly presented, and the fatigue life prediction results discussed. The results obtained for the joint geometries considered in this work show advantages and drawbacks of the approaches, which are thoroughly analysed as well.
The effect of the environmental conditions on the threshold against fatigue crack propagation
(2022)
The threshold against fatigue crack propagation (ΔKth) is a crucial parameter for the damage tolerance assessment of engineering components subjected to cyclic loading and it is composed by two distinct components, one intrinsic, dependent on the elastic material properties and the lattice type, and one extrinsic, related to the occurrence of crack closure effects. An important issue is that several factors can influence ΔKth and, in general, the fatigue crack propagation behavior. In this work, the influence of the experimental procedure, air humidity, stress ratio and test frequency on da/dN-ΔK data has been investigated. Results are discussed with their potential causes and consequences on the calculations of the residual lifetime.
The Kitagawa-Takahashi (KT) diagram is a proven concept for describing the fatigue limit in presence of a defect or crack. It can be determined empirically with great experimental effort. It can also be estimated by means of the El Haddad relationship if the endurance limit and the long fatigue crack propagation threshold are available in reasonable accuracy. A third option is the determination using the cyclic R-curve, which describes the dependency of the fatigue crack propagation threshold on the crack growth at the short crack propagation stage. This can be experimentally determined using a closure-free initial pre-crack. It can then be applied to the determination of crack arrest for a given applied load and a given defect or crack size. Compared to the other two methods mentioned above, this option has considerable advantages: It can be applied to any component and any stress ratio. It allows the treatment of multiple cracks and provides estimations of the S-N curve in the finite life regime as well as at the endurance limit. Compared to the empirical determination of the KT diagram, the experimental effort is significantly lower and compared to the El Haddad approach it avoids problems such as the use of non-conservative long fatigue crack propagation thresholds (when the conventional load reduction method is applied to materials prone to corrosion) and the mathematical predetermination of the curve shape. The work introduces the method and provides a critical discussion as well as quantitative comparison between the different methods.
Additive manufacturing (AM) is becoming increasingly important in engineering applications due to the possibility of producing components with a high geometrical complexity allowing for optimized forms with respect to the in-service functionality. Despite the promising potential, AM components are still far from being used in safety-relevant applications, mainly due to a lack of understanding of the feedstock-process-properties-performance relationship. This work aims at providing a full characterization of the fatigue behavior of the additively manufactured AISI 316L austenitic stainless steel and a direct comparison with the fatigue performance of the wrought steel. To this purpose, a set of specimens has been produced by laser powder bed fusion (L-PBF) and subsequently heat treated at 900 °C for 1 hour for complete stress relief, whereas a second set of specimens has been machined out of hot-rolled plates. Low cycle fatigue (LCF) and high cycle fatigue (HCF) tests have been conducted for characterizing the fatigue behavior. The L-PBF material had a higher fatigue limit and better finite life performance compared to wrought material. Both, LCF and HCF-testing revealed an extensive cyclic softening.