Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (57)
- Vortrag (40)
- Beitrag zu einem Tagungsband (32)
- Monografie (3)
- Buchkapitel (2)
- Beitrag zu einem Sammelband (2)
- Forschungsbericht (2)
Schlagworte
- Fracture mechanics (25)
- Fatigue strength (19)
- Bruchmechanik (16)
- Schwingfestigkeit (14)
- Weldments (10)
- Fatigue crack propagation (9)
- Fatigue crack propagation threshold (7)
- Short crack propagation (7)
- Short cracks (7)
- FITNET (6)
- IBESS (6)
- Initial crack size (6)
- Multiple crack propagation (6)
- Railway axles (6)
- S-N curve (6)
- SINTAP (6)
- Schadenstoleranz (6)
- Crack propagation (5)
- Cyclic R-curve (5)
- Fatigue (5)
- Flaw assessment (5)
- Limit load (5)
- Reference load (5)
- Crack closure (4)
- Damage tolerance (4)
- Non-metallic inclusions (4)
- R6 procedure (4)
- Additive manufacturing (3)
- Component assessment (3)
- Constraint (3)
- Cyclic J-integral (3)
- Defects (3)
- Kitagawa-Takahashi diagram (3)
- Residual stresses (3)
- Rissarrest (3)
- Safe life design (3)
- Selective Laser Melting (SLM) (3)
- Structural integrity (3)
- Turbine disk (3)
- Werkstoffeigenschaften (3)
- Zyklische R-Kurve (3)
- Ausgangsriss (2)
- Bauteilbewertung (2)
- Bruchmechanische Bauteilbewertung (2)
- Burst (2)
- Corrosion (2)
- Crack driving force (2)
- Cyclic R-curve analysis (2)
- Damage tolerance design (2)
- Endurance limit (2)
- Experimental determination (2)
- Experimental procedure (2)
- Fail-safe (2)
- Failure analysis (2)
- Fatigue crack growth (2)
- Fatigue life (2)
- Flying ballast impact (2)
- Fracture (2)
- Fracture resistance (2)
- Fracture toughness (2)
- Inclusions (2)
- Korrosion (2)
- Material defects (2)
- Mehrfachriss (2)
- Micro-shrinkages (2)
- Multiple cracks (2)
- Nichtmetallische Einschlüsse (2)
- Pores (2)
- R6 (2)
- Radsatzwellen (2)
- Railway rails (2)
- Reference stress method (2)
- Residual lifetime (2)
- Schweißverbindungen (2)
- Sichere Lebensdauer (2)
- Steinschlag (2)
- Strength mismatch (2)
- Weld toe geometry (2)
- Welded joints (2)
- Welding residual stresses (2)
- Zerstörungsfreie Inspektion (2)
- (Residual) lifetime (1)
- 316L (1)
- AM 316L stainless steel (1)
- ASTM E647 (1)
- Accompanying measures (1)
- Achsschenkel (1)
- Additive Fertigung (1)
- Additive Manufacturing (1)
- Analytisches Modell (1)
- BS 7910 (1)
- Bauteilauslegung (1)
- Biaxial loading (1)
- Biaxial tensile loading (1)
- Bruch (1)
- Bruchmechanische Auslegung (1)
- Bruchmechanische Kennwerte (1)
- Bruchmechanische Konzepte (1)
- Burst test (1)
- Butt welds (1)
- Chapetti’s and IBESS model (1)
- Characterisation (1)
- Codes and standards (1)
- Compression pre-cracking (1)
- Constraint faktor (1)
- Contact fatigue (1)
- Corrosion pits (1)
- Crack Tip Opening Displacement (CTOD) (1)
- Crack arrest (1)
- Crack closure effect (1)
- Crack closure mechanisms (1)
- Crack closure phenomenon (1)
- Crack initation (1)
- Crack-closure (1)
- Critical distance (1)
- Critical speed (1)
- Cyclic R curve (1)
- Cyclic stress-strain curve (1)
- Damage tolerant component design (1)
- Data evaluation methods (1)
- Defekte Eigenspannung (1)
- Derailment (1)
- Druckanschwingen (1)
- EPRI method (1)
- EPRI-Methode (1)
- Effective crack propagation data (1)
- Einflussfaktoren auf Rissfortschrittsdaten (1)
- Einschlüsse (1)
- Elastic follow-up (1)
- Elastic-plastic fracture mechanics (1)
- Environment (1)
- Environmental conditions (1)
- Environmental effect (1)
- Environmental effects (1)
- Ermüdungsrissausbreitung (1)
- Ermüdungsrissfortschritt (1)
- FAT class (1)
- FAT class approach (1)
- FAT class concept (1)
- FEM (1)
- FKM-Richtlinie (1)
- FORM (1)
- FORM/SORM (1)
- Fail-safe design (1)
- Failure Assessment Diagram (1)
- Failure probability (1)
- Fatigue S-N curve (1)
- Fatigue crack (1)
- Fatigue crack initiation (1)
- Fatigue crack propagation stages (1)
- Fatigue crack propagation stagesdefects (1)
- Fatigue life prediction (1)
- Fatigue loading (1)
- Fatigue strength and life (1)
- Finite element (FE) (1)
- Flaw assessment procedures (1)
- Flaw interaction (1)
- Flawed rotors (1)
- Foot crack (1)
- Fracture Mechanics (1)
- Fracture assessment (1)
- Fracture of weldments (1)
- Global stability criterion (1)
- Graphite modules (1)
- Grenzlast (1)
- HAZ (1)
- HCF (1)
- Heat affected zone (1)
- IBESS-Prozedur (1)
- ISO 12108 (1)
- Impact damage (1)
- In-situ Process Monitoring (1)
- Inclusion cluster (1)
- Inclusion size (1)
- Influencing factors (1)
- Initial flaw size (1)
- Inspection intervals (1)
- Intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung (1)
- J-Integral (1)
- J-integral (1)
- Kerbschlagarbeit (1)
- Korrelation (1)
- Kritische Last (1)
- Kurz- und Langriss-Ermüdungsbruchmechanik (1)
- Kurzrissbruchmechanik (1)
- Kurzrisswachstum (1)
- L-PBF (1)
- LCF (1)
- Lastabsenkung (1)
- Life prediction (1)
- Ligamentplastifizierung (1)
- Load decreasing (1)
- L‐PBF (1)
- Material inhomogeneity (1)
- Mechanische Bewertung (1)
- Metallic components (1)
- Mis-match (1)
- Mismatch (1)
- Monotonic and cyclic crack driving force (1)
- Multiple crack initiation (1)
- Multiple cracking (1)
- Non-destructive Materials (1)
- Non-destructive inspection (1)
- Non-destructive testing (1)
- Non-propagating cracks (1)
- Non-sharp defects (1)
- Notch fatigue (1)
- Notch sensitivity (1)
- Notches (1)
- Nuclear reactor systems (1)
- Numerische Analyse (1)
- Oberflächenschädigung (1)
- Overspeed (1)
- Oxide-induced crack closure (1)
- Peak stress method (PSM) (1)
- Pipes (1)
- Plastic collapse (1)
- Poren (1)
- Primär- und Sekundärspannungen (1)
- Process development (1)
- R-curve analysis (1)
- R6-Routine (1)
- Radioaktives Material (1)
- Railway axle (1)
- Rauheit (1)
- Reference yield load (1)
- Referenzlast (1)
- Referenzspannungsmethode (1)
- Reliability (1)
- Representative material properties (1)
- Repräsentative Werkstoffeigenschaften (1)
- Restlebensdauer (1)
- Rissausbreitung (1)
- Rissausbreitungsstadien (1)
- Rissschließeffekte (1)
- Rissschließfunktion (1)
- Rissschließphenomen (1)
- Rissspitzenbelastung (1)
- Risswiderstand (1)
- Root cause (1)
- Safety (1)
- Safety assessment (1)
- Schadenstolerante Bauteilauslegung (1)
- Schadenstolerante Bauteilauslegung, (1)
- Schadenstolerante Bauteilauslegung, Restlebensdauer, intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung (1)
- Schweißeigenspannungen (1)
- Schweißeigenspannungs-Tiefen-Profile (1)
- Schwellenwert (1)
- Schwellenwert gegen Ermüdungsrissausbreitung (1)
- Scratches (1)
- Secondary stresses (1)
- Service loading fatigue (1)
- Short crack (1)
- Short fatigue-cracks (1)
- Shrinkages (1)
- Stabilität von Eigenspannungen (1)
- Standardisation (1)
- Statistics (1)
- Steel (1)
- Steel 316L (1)
- Stiffness (1)
- Strength mis-match (1)
- Stress analysis (1)
- Stress intensity factor (1)
- Stretch-Zone (1)
- Structures (1)
- Struktur Integrität (1)
- Surface roughness (1)
- SN curve (1)
- Tearing instability (1)
- Testing parameters (1)
- Threshold (1)
- Transferability to components (1)
- Turbinenscheibe (1)
- Weld fatigue (1)
- Weld geometry (1)
- Weld toes (1)
- Werstoff- und geometrische Imperfektion (1)
- Zerstörungsfreie Prüfung (1)
- Zuverlässigkeit (1)
- damage tolerance (1)
- fatigue crack propagation (1)
- fatigue strength (1)
- fracture mechanics (1)
- inspection (1)
- probability (1)
- railway axles (1)
Organisationseinheit der BAM
- 9 Komponentensicherheit (52)
- 9.4 Integrität von Schweißverbindungen (49)
- 9.0 Abteilungsleitung und andere (7)
- 5 Werkstofftechnik (6)
- 5.1 Mikrostruktur Design und Degradation (5)
- 9.6 Additive Fertigung metallischer Komponenten (5)
- 8 Zerstörungsfreie Prüfung (3)
- 8.5 Röntgenbildgebung (3)
- 4 Material und Umwelt (2)
- 9.3 Schweißtechnische Fertigungsverfahren (2)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (40)
The two-part paper provides an overview on the state-of-the-art in the application of engineering fracture mechanics to weldments. This, of course, cannot be exhaustive but is limited to butt and fillet welds with crack initiation at weld toes. In the present first pari, the authors briefly focus on the susceptibility of welds to cracks and other defects. Following this, they discuss in more detail the consequences of material inhomogeneity across the weld for fracture mechanics. Inhomogeneity causes scatter in fracture toughness and strength mis-match effects which both have to be considered in fracture toughness testing, crack driving force determination and fracture assessment of welded components. Part 2 of the paper series will add a discussion of welding residual stresses and questions of applying fracture mechanics to residual as well as total lifetime estimation of welds under cyclic loading.
The presentation provides a discussion and damage tolerant assessment of metallic AM components. In the focus are problems of the determination of representative material data, the effect of material defects and residual stresses. Starting with the actual state-of-the-art in the field, options and possibilities of a damage tolerant design for AM are discussed.
A discussion is provided on demands that must be met in order to apply fracture mechanics to the determination of overall fatigue lifetime and strength, i.e., S-N curves and fatigue limits. These comprise the determination of the cyclic crack driving force for all stages of fatigue crack propagation, in particular for the short crack stage where the crack driving force has to be determined for elastic-plastic deformation and the gradual build-up of the crack closure phenomenon. Special emphasis is put on a fatigue damage relevant specification of the initial crack size. Different approaches in the literature are discussed. Another important aspect is the adequate treatment of multiple crack propagation. Finally, the discussion is illustrated by an example of a butt weld made of a medium strength steel.
Der Vortrag thematisiert die Behandlung von Schweißeigenspannungen bei der Auslegung geschweißter Bauteile. Ausgehend von Fragen der Klassifizierung unterschiedlicher Typen von Eigenspannungen wird auf Fragen der Behandlung von Primär- und Sekundärspannungen, der Ermittlung und Aussagefähigkeit von Eigenspannungs-Tiefen-Profilen und der Stabilität der Eigenspannungen bei zyklischer Beanspruchung eingegangen. Neben der Auslegung auf Bruch wird die Beschreibung der Ermüdungsrissausbreitung bei Vorhandensein von Eigenspannungen diskutiert, wobei neben der klassischen Langrissbruchmechanik auch Besonderheiten der Kurzrissbruchmechanik angesprochen werden.
The acronym IBESS stands for "Integrale Bruchmechanische Ermittlung der Schwingfestigkeit von Schweißverbindungen" which, translated from German, means "integral fracture mechanics determination of the fatigue strength of welds". the method introduced in this study is the outcome of a German Research cluster in which eight partners were involved. A list of them is found at the end this study. The IBESS method is characterized by a number of partially novel aspects and elements of fracture mechanics applied to the evaluation of fatigue stength of welds. The most important ones are: (a) Determination of fatigue crack propagation for mechanically/physically short and long cracks. (b) Determination of an elastic-plastic crack driving force for the treatment of mechanically short cracks. To that purpose an analytical expression for the cyclic J-integral was developed and validated against finite element results. (c) The gradual build-up of the crack closure phenomenon is determined by using cyclic R-curves which describe the crack size dependency of the fatigue crack propagation threshold in the physically short crack growth regime. (d) A physically meaningful initial crack size is defined for total life consideration. It is based on a two-criteria approach. Based on a cyclic R-curve analysis, the crack size at crack arrest is determined as a lower bound. If, however, a pre-existing crack-like defect is larger than this, its dimensions define the initial crack size. (e) Multiple crack propagation at the weld toe is considered. (f) In conjunction with this, the variation of the weld toe geometry is considered in a stochastic model. (g) As a result, both the fatigue limit (defined for 107 loading cycles) and the finite life (high cycle) fatigue S-N curve are obtained statistically. (h) At various analysis steps, parametric equations have been developed which allow for analytical calculations instead of complete stochastic analyses based on finite elements which are unrealistic even at present. (i) The method has been validated with a large number of S-N curves including two materials, three weldment types with two geometries, each referring to differnt manufacturing technologies and the as-welded and stressrelieved state. (j) Althrough not finally solved, an extended discussion is provided on the issue of welding residual stresses including their redistribution under cyclic loading. (k) A number of simplifications is proposed at lower analyses levels which, however, partly lack complete validation by now.
This book provides a comprehensive and thorough guide to those readers who are lost in the often-confusing context of weld fatigue. It presents straightforward information on the fracture mechanics and material background of weld fatigue, starting with fatigue crack initiation and short cracks, before moving on to long cracks, crack closure, crack growth and threshold, residual stress, stress concentration, the stress intensity factor, J-integral, multiple cracks, weld geometries and defects, microstructural parameters including HAZ, and cyclic stress-strain behavior. The book treats all of these essential and mutually interacting parameters using a unique form of analysis.
This third part of the review on defects as root cause of fatigue failure addresses cavities (pores, micro-shrinkages, unmelted regions), defective microstructures and microcracks as material defects and defects due to local damage during manufacturing, service and maintenance such as dents, scratches and localized corrosion. In addition, damage due to contact fatigue and the effect of surface roughness are discussed in the context of fatigue failure. Also addressed is the competition between different kinds of defects in controlling the initiation and early growth of fatigue cracks.
According to the definition of the ASM handbook [1,3], a defect is "an imperfection. that can be shown to cause failure by a quantitative analysis and that would not have occurred in the absence of the imperfection". The topic of the present three-part review is a discussion of defects which can cause failure in cyclically loaded structures. The features discussed comprise material defects such as non-metallic inclusions, pores or micro-shrinkages, etc. and geometric defects such as surface roughness and secondary notches which have their origin in manufacturing, and defects such as surface damage due to scratches, impact events or contact fatigue as well as corrosion pits which arise in service. In this first part, the discussion is prefaced by an introduction to basic aspects which are essential for a deeper understanding of the characteristics and mechanisms how the defects influence fatigue crack initiation and propagation. These include the life cycle of a fatigue crack from initiation up to fracture, crack arrest, multiple crack initiation and coalescence, and the material and geometrical properties affecting these.
Defects as a root cause of fatigue failure of metallic components. II: Non-metallic inclusions
(2019)
This second part of the review on defects as root cause of fatigue failure comprises the origin, the nature and the effects of non-metallic inclusions. Topics addressed are the different kinds of inclusions formed during the manufacturing process, various types of mis-match causing local stresses and, as a consequence, fatigue crack initiation, and effects of characteristics such as size, morphology, localization, spatial distribution and orientation of the defects on the fatigue behavior. Methods for inclusion counting and sizing are discussed along with statistical aspects necessary to be considered when evaluating structural components.
Analytical flaw assessment
(2018)
The paper provides a review on analytical flaw assessment methods with the focus on fracture under monotonic loading and fatigue crack propagation. The first topic comprises linear elastic as well as elastic-plastic fracture mechanics approaches. It essentially follows their historical development. Topics which are separately discussed are reference/Limit loads, the treatment of secondary stresses, strength mismatch, constraint, unstable crack propagation (monotonic R-curve analyses) and statistical aspects. With respect to fatigue crack propagation the analytical treatment of crack closure and constraint and the Determination of the cyclic elastic-plastic crack driving force is discussed. Finally, cyclic Rcurve analyses are briefly addressed.
Foreword
(2018)
The subject of this Special Issue is the fracture mechanics-based determination of the fatigue strength of weldments. Except for one, all papers were written in closer or wider relation to a methodology developed within the framework of the German Project cluster IBESS. Some of them provide background or supplementary information needed in that context but which is also relevant in a wider frame of research activities. The acronym IBESS stands for the topic of this Special Issue (in German: „Integrale Methode zu Bruchmechanischen Ermittlung der Schwingfestigkeit von Schweißverbindungen). Eight partners were involved. The cluster was cooperatively founded by the German Research Foundation (Deutsche Forschungsgemeinschaft) and by the German AiF Network (Arbeitsgemeinschaft industrieller Forschungsvereinigungen) for industrial research.
The work presents the procedure developed within the German research project IBESS, which allows for the fracture mechanics-based prediction of the fatigue strength of welded joints under constant amplitude loading. Based on the experimental observations of the crucial failure mechanisms, the approach focuses on the short crack propagation, where elastic-plastic fracture mechanics and the build-up of closure effects must be considered as well as the variability of the local geometry at the weld toe and the modelling of multiple crack interaction. Analytical solutions are provided for the approximation of the through-thickness stress profiles at the weld toe and for the determination of the crack driving force in the form of a plasticity-corrected stress intensity factor range ∆K_p. Proposals for the determination of the initial crack size and the crack closure factor are also included.
The approach is validated against a large number of experimental data, which comprises fatigue tests on individual cracks monitored by heat tinting and beach-marking techniques, as well as stress life curves. Three kinds of welded joints, two steels of significant different strengths and three stress ratios are considered. The results show that the procedure provides good estimations of the statistical distribution of the fatigue strength of welded joints both for the finite and infinite life regime. Furthermore, the predictions are compared with available benchmark data for structural steels.
Any fracture mechanics based determination of the fatigue strength of weldments requires different input information such as the local weld geometry and material data of the areas the crack is passing through during its propagation. The latter is so far not a trivial task as the fatigue crack is usually initiated at the weld toe at the transition from the weld metal to the heat affected zone and it subsequently propagates through the different microstructures of the latter to eventually grow into the base material and to cause final fracture. This paper describes how the material input information has gained particularly for heat affected zone material by thermo-mechanically simulated material specimens for two steels of quite different static strength. The data comprise the cyclic stress-strain curve, the crack closure effect-corrected crack growth characteristics, long crack fatigue crack propagation thresholds, the dependency of the parameter on the crack length and monotonic fracture resistance. The substantial experimental effort was necessary for the validation exercises of the IBESS approach, however, within the scope of practical application more easily applicable estimating methods are required. For that purpose the paper provides a number of appropriate proposals in line with its check against the reference data from the elaborate analyses.
The so-called cyclic R curve, i.e. the crack size dependence of the fatigue crack propagation threshold in the physically short crack regime, is a key parameter for bringing together fatigue strength and fracture mechanics concepts. Its adequate determination is of paramount importance. However, notwithstanding this relevance, no test guideline is available by now and only very few institutions have spent research effort on cyclic R curves so far. The aim of the present paper is to give an overview on the state-of-the-art. Besides an introduction into the basic principles, the discussion will concentrate on the experimental determination on the one hand and questions of its application on the other hand.
The cyclic J-integral (∆J-integral) is a crack tip parameter of elastic-plastic fracture mechanics which can be used as governing parameter for the description of fatigue crack growth (FCG) in metallic structures. In this contribution, it is applied for modelling FCG in weldments. The ∆J-integral is determined by means of analytical approximation formulas as well as numerical methods. An analytical solution, which takes into account effects of the local ligament plasticity, was derived. This solution is based on well established methods such as R6, BS7910 and SINTAP which were modified for cyclic loading. It incorporates methods for the description of short crack closure behaviour as well as the well known analytical (long) crack closure function of Newman. A specific code was written to evaluate the ∆J-integral numerically in the course of finite element based crack growth simulations. The code was first validated for an infinite plate with centre crack by applying elastic and elastic-plastic material behaviour. Next, the ∆J-integral was calculated for cracks in various butt and cruciform welded joints. The results were compared with the results of the derived analytical approximation formula. A good accordance was achieved between the results.
The paper provides an application of the IBESS approach to the investigation of the influence of various parameters of the global and local weld geometry as well as material defects on the fatigue strength of weldments. For this purpose, the global weld parameters, such as the weld toe radius, the flank angle, the excess weld metal, local secondary notches (in the present study as a measure of surface imperfections) and inclusions sizes have been determined as statistical distributions for different joint types and geometries and two steels of different strengths. The results are in line with literature data and reveal the potential of the theoretical approach to predict the correct trends. The combination with an advanced weld quality system has been demonstrated to be possible.
Ein Defekt ist „eine Imperfektion …, für die in einer quantitativen Analyse gezeigt werden kann, dass sie Versagen verursacht hat, welches ohne die Imperfektion nicht aufgetreten wäre“. Defekte in diesem Sinn können einerseits Werkstoffimperfektionen wie nichtmetallische Einschlüsse, Poren und Porennester, Nichtdurchschweißungen oder Bereiche defekter Mikrostruktur, andererseits unbeabsichtige geometrische Imperfektionen wie Kratzer, Eindrücke, Korrosionsgrübchen, Einbrandkerben, zu große Oberflächenrauheit u.a. sein. Sie können in der Fertigung, im Betrieb oder auch bei der Wartung entstehen. Nicht jede Imperfektion ist ein Defekt im oben genannten Sinn. Entscheidend ist zumeist nicht, dass an ihr ein oder mehrere Risse initiiert werden, sondern dass wenigstens ein Riss wachstumsfähig bleibt und so innerhalb der projektierten Lebensdauer zum Bruch oder anderweitigem Versagen führt. Aufgrund des begrenzten Umfangs bleibt die vorliegen-de Übersicht beschränkt.
Welding residual stresses have an impact on the performance of welded structures, on their fracture resistance, their resistance against fatigue crack propagation and, most important, their fatigue strength and fatigue lifetime. The present paper provides an overview on the issue mainly from the point of view of the application of fracture mechanics to the determination of the fatigue strength as the topic of this Special issue. Besides own experimental and theoretical data a comprehensive discussion is provided in that context which includes the definition and interaction of short- and long-range (or reaction) residual stresses, the effect of cyclic mechanical loading and its treatment in fracture and fatigue analyses.
Common fracture mechanics based fatigue considerations are usually limited to the residual lifetime determination of so-called long cracks. The extension of this concept to the total lifetime, as in the S-N curve approach, requires an adequate description of short crack propagation which cannot be based on the Delta K concept, and it must consider the crack closure phenomenon as well as its gradual build-up at the short crack stage. Further, it has to provide a meaningful definition of initial crack dimensions and a solution for the multiple crack problem at stress levels higher than the fatigue limit as it is specific for some configurations such as weldments. This paper aims at a discussion of all these points and offers possible solutions which are illustrated by examples taken from the German IBESS project on fracture mechanics based determination of the fatigue strength of weldments, the results of which will be discussed in more detail in this Special issue.
Unter der zyklischen R-Kurve versteht man die Abhängigkeit des Schwellenwertes gegen Ermüdungsrissausbreitung von der Risstiefe im Kurzrissbereich. Bei Spannungsverhältnissen R = omin/omax < ca. 0,7 erhöht sich der Schwellenwert AKltl ausgehend von einer intrinsischen, werkstoffspezifischen Untergrenze mit zunehmender Risstiefe, bis er einen risslängenunabhängigen Wert erreicht.
Ursache ist der graduelle Aufbau unterschiedlicher Rissschließeffekte. Die besondere Bedeutung des Kurzrisswachtums allgemein und der zyklischen R-Kurve speziell besteht darin, dass sie ein physikalisches Bindeglied zwischen der konventionellen Schwingfestigkeit (Wöhlerkurve) und der Bruchmechanik repräsentieren. Der Beitrag befasst sich sowohl mit der experimentellen Ermittlung der zyklischen R-Kurve als auch mit ihrer Anwendung auf Rissarrest im Zusammenhang mit Schwingfestigkeitsbetrachtungen.
Die experimentelle Ermittlung der zyklischen R-Kurve erfordert einen experimentellen Aufwand, der deutlich über den der Langrissbruchmechanik hinausgeht. Insbesondere im Anfangsbereich ist eine sehr genaue Messung der Risstiefe erforderlich, was eine Verbesserung etwa der konventionellen Potentialmethode erforderlich macht. Von wesentlicher Bedeutung ist auch, dass der Ausgangsriss vor
Beginn des eigentlichen Versuchs keine Rissschließeffekte gesehen haben darf. Realisiert wird das durch eine vorgeschaltete Phase von sog. „Compression Pre-cracking“, d.h. durch Anschwingen komplett im Druckbereich.
Die Präsentation diskutiert Besonderheiten von Schweißnähten bei der Bestimmung der Zähigkeit bei monotoner Belastung, bei der Ermittlung des zyklischen Rissfortschritts und bei der Ermittlung der Gesamtlebensdauer/Schwingfestigkeit mittels moderner bruchmechanischer Methoden. Besonderes Augenmerk liegt auf der Inhomogenität des Werkstoffs in den einzelnen Nahtbereichen, die sich statistisch (stochastische Verteilung von Gefügeschwachstellen) und systematisch (Effekte von Festigkeits-Mismatch) auswirkt. Als weiterer Faktor kommen Schweißeigenspannungen hinzu, bei denen für die bruchmechanische Analyse eine Fallunterscheidung in primäre und sekundäre Eigenspannungen vorgenommen werden muss. Diskstiert werden die Konsequenzen für die Zähigkeitsermittlung und die Bauteilbewertung.
The Topic of the presentationis a discussion on defects which can cause failure in cyclically loaded metallic components. Although also touching Features such as material defects such as pores or micro-shrinkages, etc. and geometric defects such as surface roughness and secondary notches (which are not considered in the design process) which origin in manufacturing, and others the presentation concentrates on non-metallic inclusions. It is prefaced by an introduction to the life cycle of a fatigue crack from initiation up to fracture. Special emphasis is put on the fact that only cracks which are not arrested during one of their distinct Propagation stages can grow to a critical size.
The paper provides an overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common ΔK concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit and the finite life branch of the S-N curve are determined.
Besides a brief introduction into the approach, validation examples are presented. These comprise different weldment types (butt welds, cross joints and longitudinal stiffened plates), two steels (S355NL and S960QL) of quite different strengths, different weld geometries due to different welding techniques (WIG, MAG), as-welded and stress relieved welds and different stress ratios varying from R = -1 to R = 0.5.
The paper provides an overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common K concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit as defined for 107 loading cycles and the finite life branch of the S-N curve are determined.
Besides a brief introduction into the approach, a wide range of validation examples is presented. These comprise different weldment types (butt welds, cross joints and longitudinal stiffened plates), two steels of quite different strengths, different weld geometries due to different welding techniques (TIG, MAG), as-welded and stress relieved welds and different stress ratios varying from R = -1 to R = 0.5.
Um bruchmechanisch Schwingfestigkeiten ermitteln zu können, sind einige Voraussetzungen erforderlich:
(a) Das Wachstum sowohl langer als auch mechanisch und physikalisch kurzer Risse muss adäquat beschrieben werden. Das erfordert die Anwendung elastisch plastischer Konzepte zur Beschreibung der zyklischen Rissspitzenbeanspruchung sowie die Modellierung des graduellen Aufbaus der Rissschließeffekte im Kurzrissbereich.
(b) Es müssen physikalisch sinnvolle Ausgangsrissgrößen für die bruchmechanische Analyse bestimmt werden.
(c) Bei Spannungen oberhalb der Dauerfestigkeit respektive der Versagensspannung bei 107 Lastwechseln muss gegebenenfalls Mehrfachrisswachstum berücksichtigt werden.
Der Vortrag diskutiert diese Punkte und zeigt Lösungswege auf.
Um bruchmechanisch Schwingfestigkeiten ermitteln zu können, sind einige Voraussetzungen erforderlich:
(a) Das Wachstum sowohl langer als auch mechanisch und physikalisch kurzer Risse muss adäquat beschrieben werden. Das erfordert die Anwendung elastisch plastischer Konzepte zur Beschreibung der zyklischen Rissspitzenbeanspruchung sowie die Modellierung des graduellen Aufbaus der Rissschließeffekte im Kurzrissbereich.
(b) Es müssen physikalisch sinnvolle Ausgangsrissgrößen für die bruchmechanische Analyse bestimmt werden.
(c) Bei Spannungen oberhalb der Dauerfestigkeit respektive der Versagensspannung bei 107 Lastwechseln muss gegebenenfalls Mehrfachrisswachstum berücksichtigt werden. Der Vortrag diskutiert diese Punkte und zeigt Lösungswege auf.
If fracture mechanics shall be applied to the total lifetime respectively the fatigue limit of components (within the meaning of the S-N curve approach) it has to address four challenges:
(a) It has to adequately describe so-called short crack propagation, which cannot be based on the common long crack concepts for principle reasons. Since the crack size is in the order of the plastic zone size, the modelling of short crack propagation cannot be based on the common linear elastic Delta K concept. Instead, an elastic-plastic parameter such as the cyclic J integral has to be applied. A second point is that the crack closure concept has to be modified in that the crack opening stress is not a constant, crack size- independent parameter but shows a transient behaviour with increasing short crack size.
(b) It has to provide a meaningful definition of the initial crack dimensions as the starting point for an S-N curve relevant (residual) lifetime analysis. This can be based either on the (statistical) size of material defects which can be treated as cracks or by the size of the crack which would arrest subsequent to early crack propagation, whatever is larger.
(c) It has to cope with the problem of multiple cracks for load levels higher than the fatigue limit such as it occurs in many applications in the absence of very large initial defects.
(d) This requires consequent statistical treatment taking into account variations in the local geometry of the area where crack initiation has to be expected as well as the scatter in the initial crack size and in the material data used for the analyses.
If fracture mechanics shall be applied to the total lifetime respectively the fatigue limit of components (within the meaning of the S-N curve approach) it has to address four challenges:
(a) It has to adequately describe so-called short crack propagation, which cannot be based on the common long crack concepts for principle reasons. Since the crack size is in the order of the plastic zone size, the modelling of short crack propagation cannot be based on the common linear elastic Delta K concept. Instead, an elastic-plastic parameter such as the cyclic J integral has to be applied. A second point is that the crack closure concept has to be modified in that the crack opening stress is not a constant, crack size- independent parameter but shows a transient behaviour with increasing short crack size.
(b) It has to provide a meaningful definition of the initial crack dimensions as the starting point for an S-N curve relevant (residual) lifetime analysis. This can be based either on the (statistical) size of material defects which can be treated as cracks or by the size of the crack which would arrest subsequent to early crack propagation, whatever is larger.
(c) It has to cope with the problem of multiple cracks for load levels higher than the fatigue limit such as it occurs in many applications in the absence of very large initial defects.
(d) This requires consequent statistical treatment taking into account variations in the local geometry of the area where crack initiation has to be expected as well as the scatter in the initial crack size and in the material data used for the analyses.
Approximation of the crack driving force for cracks at notches under static and cyclic loading
(2017)
The work deals with the efficient calculation of the elastic-plastic crack driving force (J-integral for monotonic loading andΔJ-integral under cyclic loading) for short cracks at notches as essential parameter for the reliable static and fatigue assessment of notched structures. The J- or ΔJ-integral is calculated based on analytical solutions for stress intensity factors, estimated by means of well-known weight function solutions in the case of cracks under power-law stress distributions. A plasticity-correction function is applied to the stress intensity factors to obtain the final expression of the crack driving force. The comparison between analytical solutions and finite element calculations in case of cracks at the weld toe in welded joints shows good agreement.
The presentation provides a brief overview on results obtained in the context of fracture mechanics based flaw assessment particularly in the context of short crack propagation. Background is the planned updating of international fitness-for-service procedures such as BS 7910. Specific topics addressed are the determination of the cyclic elastic-plastic crack driving force, the description of the gradual build-up of the crack closure phenomenon at the short crack stage, cyclic R curve analysis and residual stresses.
Der Vortrag bietet eine Übersicht über die im Rahmen des IBESS-Projektes entwickelte Methodik zur bruchmechanischen Ermittlung der Schwingfestigkeit von Schweißverbindungen. Schwerpunkte sind die Beschreibung des Wachstums kurzer Risse, die mit den klassischen linear-elastischen Bruchmechanik-Konzepten nicht möglich ist, die Ermittlung einer physikalisch sinnvollen Ausgangsrissgröße für das Bruchmechanik-Modell, die Ermittlung der Bauteildauerfestigkeit und des Zeitfestigkeitsastes diverser Schweißnahtgeometrien und eine Diskussion der Eigenspannungsproblematik. Die Ergebnisse werden mittels Validierungsbespielen illustriert.
The present paper provides a discussion on all these topics and it offers solutions for it. The authors present an analytical solution of a Delta J based crack driving force based on an R6 type approach but modified for cyclic loading. The gradual build-up of the crack closure effect is modelled by the so-called cyclic R curve which describes the crack size dependency of the fatigue crack propagation threshold in the short crack regime. It is explained how the cyclic R curve is experimentally determined and how it can be estimated by a modified Kitagawa-Takahashi approach.
Unterschiedliche Werkstoffeigenschaften reagieren auf jeweils spezifische Weise auf Gittertyp, Gefüge und Defekte. Für die schadenstolerante Betrachtung von Werkstoff und Bauteil ist das Verständnis dieser Zusammenhänge essentiell. Der Beitrag gibt mit Hinblick auf additiv gefertigte metallische Bauteile mittels Selective Laser Melting einen kurzen, keineswegs vollständigen Überblick über Faktoren, die die Steifigkeit, Festigkeit, Duktilität, Zähigkeit, Ermüdungsrissausbreitung und Schwingfestigkeit beeinflussen. Es wird aufgezeigt, wie die bruchmechanische Betrachtung zur Quantifizierung der Zusammenhänge beitragen kann.
The additive manufacturing technology of Selective Laser Melting (SLM) experiences a rapid development within an increasing marked of quite different application fields. The properties of SLM materials and structures are influenced by a number of tech-nological parameters such as the metal powder (particle size, homogeneity, cleanliness), the laser tool (power, beam diameter, pulse lengths), the scanning operation (speed, sequence and orientation of melting paths), parameters of the over-all equipment (design and preheating of the base plate, currents and turbulence in the protective gas atmosphere) and, last not least, the hatching strategy including the build-up direction of the structure with respect to the loading direction of the component.
For the perspective use of SLM structures as load carrying, safety-relevant components the knowledge of their mechanical properties is necessary. It is essential to understand these in the context of the manufacturing-related features and at the back-ground of the basic characteristics of metallic materials: crystal lattice, microstructure and material defects. The paper provides an overview on factors which affect the mechanical parameters stiffness, strength, ductility, toughness, fatigue crack propagation and fatigue strength in the context of selective laser melting.
Damage development and damage tolerance of structures manufactured by selective laser melting
(2017)
The additive manufacturing technology of Selective Laser Melting (SLM) experiences a rapid development within an increasing marked of quite different application fields. The properties of SLM materials and structures are influenced by a number of tech-nological parameters such as the metal powder (particle size, homogeneity, cleanliness), the laser tool (power, beam diameter, pulse lengths), the scanning operation (speed, sequence and orientation of melting paths), parameters of the over-all equipment (design and preheating of the base plate, currents and turbulence in the protective gas atmosphere) and, last not least, the hatching strategy including the build-up direction of the structure with respect to the loading direction of the component.
For the perspective use of SLM structures as load carrying, safety-relevant components the knowledge of their mechanical properties is necessary. It is essential to understand these in the context of the manufacturing-related features and at the back-ground of the basic characteristics of metallic materials: crystal lattice, microstructure and material defects. The paper provides an overview on factors which affect the mechanical parameters stiffness, strength, ductility, toughness, fatigue crack propagation and fatigue strength in the context of selective laser melting.
A fracture mechanics model which shall be applied to the fatigue strength determination of weldments has to focus on various aspects such as: (a) the description of mechanical and physical short fatigue crack extension which is characterised by yielding conditions which do not permit the application of the common ΔK concept and by the gradual build-up of the crack closure effect, (b) a consistent methodology for determining the initial crack size, (c) based on this, the determination of a fatigue limit, (d) the treatment of multiple crack propagation at load levels above this limit, (e) the variation of the local geometry along the weld toe, and (f) statistical effects.The paper gives alimited overview of the work the authors did in this field during the last years within the German project cluster IBESS. A model is presented and briefly discussed which covers the questions above.
Based on a large set of 2D finite element analyses, parametric equations for weld toe stress concentration factors and through-thickness stress profiles are provided for butt-welded plates. These cover Single-Vand Double-V joints subject to tensile and bending loading. Compared to the most widespread solutions in the literature, which have also been tested against the finite element data in this work, the application range is extended particularly with respect to the weld toe radius(0.1≤ρ≤4 mm)andangle(10 °≤α≤60 °). Furthermore, two values of excess weld metal are considered (h=0.75;2.5mm). The analyses are performed for a plate thickness of 10 mm. Besides the extended validity range, the proposed equations show also an improved accuracy compared to the existing solutions.
Semi-probabilistic method for residual lifetime of aluminothermic welded rails with foot cracks
(2016)
One of the most frequent and dangerous failure modes in continuous welded rails is fatigue crack Propagation terminated by brittle fracture. Due to the brittleness of the weld material and HAZ and the scatter in its mechanical properties, a statistical approach is necessary. The paper deals with surface cracks at the foot base of aluminothermic welded rails, developing a probabilistic methodology for determining the day by day prospective failure probability. The investigations presented here comprise weld material characterization, simulation of fatigue crack propagation and finally the determination of the failure probability using the Monte Carlo method. The effect of various parameters, such as axle weight, Initial crack size, residual stresses, fatigue crack propagation threshold and date of inspection were analyzed.
The results show that, independent of the date of the last inspection, almost any failure event happens in wintertime. This is in accordance with practical experience. However, from the proposed analysis it is evident that the main parameter controlling rail fracture is not only the minimum local temperature, but the temperature range over the whole year. Finally, the results are compared to the standard rail classification method.
Starting from an introduction into important Basic questions of failure analysis and fracture mechanics, the author specifies what kind of questions in failure analysis can be effectively solved by fracture mechanics (and which can't). He illustrates his discussion with a number of case studies. Much more pronounced than in the design stage the benefit of fracture mechanics in failure analysis depends on ist accuracy. This is limited by both, intrinsic factors of the method and the availability and quality of the input information. The author discusses the various aspects and provides the participants with background information helpful for better understanding the prospects and limitations of fracture mechanics in failure analysis and the conditions of its application.
Unterschiedliche Werkstoffeigenschaften reagieren auf jeweils spezifische Weise auf Gittertyp, Gefüge und Defekte. Für die schadenstolerante Betrachtung von Werkstoff und Bauteil ist das Verständnis dieser Zusammenhange essentiell. Der Beitrag gibt mit Hinblick auf additiv gefertigte metallische Bauteile (Selective Laser Melting) einen kurzen, keineswegs vollständigen Überblick über Faktoren, die die Steifigkeit, Festigkeit, Duktilität, Zähigkeit, Ermüdungsrissausbreitung und Schwingfestigkeit beeinflussen. Es wird aufgezeigt, wie die bruchmechanische Betrachtung zur Quantifizierung der zusammenhänge beitragen kann.
A discussion is provided on the relation between non-destructive testing (NDT) and fracture mechanics. The basic tasks behind this are to guarantee the safety of a component at a potential hazard loading event, to specify inspection intervals or, alternatively, of demands on NDT for a fixed inspection regime, to plan accompanying measures for cases of temporary continued operation of structures in which cracks have been detected, and, finally, fatigue strength considerations which take into account initial defects.
Unterschiedliche Werkstoffeigenschaften reagieren auf jeweils spezifische Weise auf Gittertyp, Gefüge und Defekte. Für die schadenstolerante Betrachtung von Werkstoff und Bauteil ist das Verständnis dieser Zusammenhänge essentiell. Der Beitrag gibt mit Hinblick auf additiv gefertigte metallische Bauteile(Selective Laser Melting) einen kurzen, keineswegs vollständigen Überblick über Faktoren, die die Steifigkeit, Festigkeit, Duktilität, Zähigkeit, Ermüdungsrissausbreitung und Schwingfestigkeit beeinflussen. Es wird aufgezeigt, wie die bruchmechanische Betrachtung zur Quantifizierung der Zusammenhänge beitragen kann
The fatigue crack propagation threshold ΔKth is of paramount importance for any kind of damage tolerant design, but in contrast to this importance, the determination and application of the parameter is not on the firm ground as previously assumed. The paper discusses questions of its experimental determination as well as of its application to components. In both fields, new questions have been raised with the potential to challenge or modify long-standing knowledge. Against this background, the paper is an attempt to systematize the established knowledge as well as questions and open issues.
The paper deals with the prediction of the fatigue Limit of notched specimens. Some authors in the literature have shown that this issue can be solved by employing an approach based on critical distances, others used elastic fracture mechanics. In this paper the fatigue limit of notched specimens is given by the non-propagating condition of mechanically small surface cracks. According to the so-called cyclic R-curve method, the crack driving force of a growing small crack is compared to its resistance force, which incorporates the gradual build-up of crack closure. The fatigue limit is determined by that applied nominal stress, for which the tangency condition of crack driving and resistance force is satisfied. The approach has been modified to incorporate plasticity effects in the mechanically short crack Regime and it has been applied to a mild and a high-strength steel, in case of an infinite plate with circular hole under remote tensile stress. The method has been successfully applied to the evaluation of fatigue notch-sensitivity in case of surface roughness.
Analytische bruchmechanische Ermittlung der Schwingfestigkeit von Schweißverbindungen (IBESS-A3)
(2016)
Ziel des DFG-AiF-Forschungsclusters IBESS war die Entwicklung einer Methodik zur bruchmechanischen Ermittlung von Wöhlerkurven in Schweißverbindungen. Dem vorliegenden Teilprojekt A3 kamen dabei zwei Aufgaben zu: die Entwicklung einer analytischen bruchmechanischen Methodik und die Koordinierung des insgesamt acht Partner umfassenden Clusters. Dieser Bericht fasst die Ergebnisse der erstgenannten Aufgabe zusammen. Die bruchmechanische Methode ist durch folgende Aspekte charakterisiert. (a) Sie beschreibt sowohl Kurz- als auch Langrisswachstum. Ersteres umfasst mechanisch und physikalisch kurze Risse. Mechanisch kurze Risse weisen Abmessungen in der Größenordnung der plastischen Zone auf, weshalb sie zwar bruchmechanisch, nicht jedoch auf der Basis des linear-elastischen K-Konzepts charakterisiert werden können. Im Projekt wurde entsprechend eine Methode zur Bestimmung eines „plastizitätskorrigierten“ zyklischen K-Faktors entwickelt, die auf dem zyklischen J-Integral beruht. Physikalisch kurz bedeutet, dass die Rissschließeffekte im Ausgangsstadium der Rissentwicklung zunächst noch nicht vorhanden sind, dann jedoch graduell aufgebaut werden, bis sie mit Erreichen des Langrissstadiums eine risstiefenunabhängig konstante Größe erreichen. Beschrieben wird dieser Effekt durch die Anwendung der sogenannten zyklischen R-Kurve, der Funktion des Schwellenwerts gegen Rissausbreitung von der Risstiefe. Mittels Rissarrestbetrachtungen des kurzen Risses werden (b) die Ausgangsrissgröße für die weitere Bruchmechanikanalyse und (c) die für N = 107 definierte Dauerfestigkeit der Bauteile bestimmt. Die Analyse erfolgt (d) statistisch, Schwankungen der lokalen Nahtgeometrie entlang des Nahtübergangs über ein Modell äquidistanter Abschnitte einbezogen werden. (e) Eigenspannungen werden sowohl im unbehandelten Schweißzustand als auch nach zyklischer Belastung berücksichtigt. Das Modell wird an insgesamt 33 Wöhlerkurven validiert, die an drei Schweißverbindungsformen (Stumpfstoß, Kreuzstoß, Längssteife) mit je zwei unterschiedlichen Ausführungen, zwei Werkstoffen (S355NL und S960QL), sowie im spannungsarmgeglühten und ungeglühten Zustand experimentell ermittelt wurden.
Kernstück der angestrebten IBESS-Prozedur ist eine analytische Methode zur bruchmechanischen Beschreibung der Rissausbreitung unter Schwingbelastung. Da man es im Bereich der Schwingfestigkeit mit kurzen Rissen zu tun hat, auf die die etablierten Methoden der Langrissbruchmechanik nicht anwendbar sind, werden Lösungen entwickelt, die es erlauben, sowohl die rissnahen Plastizitätsverhältnisse als auch die mit wachsendem Riss graduell zunehmenden Rissschließeffekte quantitativ zu beschreiben. Unter Einbeziehung der sogenannten "zyklischen R-Kurve", deren experimentelle Methodik ebenfalls im Rahmen des Projekts weiterentwickelt wird, ist es zudem möglich, Ausgangsrissgrößen vorherzusagen, die auf Dauerfestigkeitsniveau gerade so noch arretieren würden. Dies erlaubt umgekehrt eine Abschätzung der Dauerfestigkeit an realen Bauteilen wie eben Schweißnähten sowie die statistisch basierte, analytische Vorhersage des Zeitfestigkeitsastes der Wöhlerkurve. Die im Modell berücksichtigten Parameter bzw. deren statistische Verteilung schließen Werkstoffdaten und die lokale Nahtgeometrie (Nachtübergangsradius, Nahtanstiegswinkel, Einbrandkerben oder Oberflächenrauhigkeit) ein. Im Vortrag wird das analytische Modell vorgestellt und vor dem Hintergrund der im IBESS-Cluster bereitgestellten experimentellen Information diskutiert.
Bruchmechanischen Bewertungsmethoden liegt stets eine tatsachlich vorhandene oder fiktive Anfangsrisslange zu Grunde. Schweißverbindungen sind mit strukturellen Imperfektionen wie beispielsweise lnhomogenitaten in der Mikrostruktur und den Werkstoffeigenschaften behaftet, welche auf der Werkstoffseite berücksichtigt werden können. Imperfektionen wie der Kantenversatz und der Nahtübergangsradius, die als außere geometrische Imperfektionen aufgefasst werden können, haben vor allem Auswirkungen auf den Spannungszustand und werden daher auf der Lastseite erfasst. Innere geometrische Imperfektionen wie Einschlüsse oder Poren, von welchen Risse initiieren und sich ausbreiten, können als Ausgangsrissgröße aufgefasst werden. Im Teilprojekt A1 des Forschungsclusters IBESS wurden außere geometrische Imperfektionen an Schweißverbindungen ermittelt und statistisch ausgewertet. Des Weiteren wurden Schweißverbindungen fraktografisch im Rasterelektronenmikroskop (REM) bezüglich innerer geometrischer Imperfektionen untersucht, jedoch konnten aufgrund der hohen Schweißgütekeine schadigungsrelevanten inneren Imperfektionen (Ausgangsdefekte) detektiert werden.
Um dennoch eine Ausgangsrisskonfiguration zu bestimmen, wurden "Heat-Tinting" Versuche eingesetzt, mit denen auf der Bruchflache verschiedene Anrissstadien markiert werden können. Mit dem .Heat-Tinting" Verfahren können sehr kleine Anrisse detektiert und in Abhangigkeit von der Beanspruchung frühe Anrisskonfigurationen ermittelt werden.
Des Weiteren haben Zerbst und Madia im Teilprojekt A3 ein Modell entwickelt, mit dem für den Grundwerkstoff mittels zyklischer R-Kurven eine Ausgangsrissgröße rechnerisch ermittelt werden kann. Unter Verwendung der Ergebnisse aus den Versuchen zur Ermittlung der Anrissstadien soll dieses Modell validiert werden, um auch für Schweißverbindungen Anwendung zu finden.
Die Projektbezeichnung IBESS steht für .Integrale Bruchmechanische Ermittlung der Schwingfestigkeit von Schweißverbindungen". Ziel des von acht Partnern vorangetriebenen AiF-DFG-Forschungsclusters IBESS ist die Entwicklung eines Ansatzes zur bruchmechanischen Ermittlung der Schwingfestigkeit von Schweißverbindungen. Die Arbeiten umfassen grundlegende Untersuchungen zum Wachstum und Arrest kurzer Risse, zur Ausbildung und Beeinflussung von Schweißeigenspannungen unter zyklischer Last, zum Einfluss der lokalen Nahtgeometrie auf die Rissausbreitung, zum Mehrfachriss-Phänomen oberhalb des Dauerfestigkeitsniveaus sowie zum Koaleszenzverhalten benachbarter Risse. Die gewonnenen Erkenntnisse fließen in ein analytisches Modell zur Ermittlung der Schwingfestigkeit ein, das physikalisch begründete und mithin sehr viel individuellere Vorhersagen des Ermüdungsverhaltens von Schweißnähten ermöglichen soll, als das auf konventioneller Basis bislang möglich ist. Ein nicht geringer Teil der Aktivitäten des Clusters ist mit der Bereitstellung von Daten zur Validierung befasst. Diese wird auf verschiedenen Ebenen vorgenommen, von der Beschreibung des Wachstuns von Einzelrissen über ihr Zusammenwachsen bis hin zur kompletten Wöhlerkurve. Ziel dieses Vortrags ist ein kurzer Überblick über das IBESS-Gesamtprojekt, das dem Zuhörer eine Einordnung der im IBESS-Vortragsblock vorgestellten Einzelaktivitäten ermöglichen soll.
Special aspects of welded components such as geometrical imperfections, inhomogeneity, strength mismatch and welding residual stresses have to be taken into account in a fracture mechanics analysis since they affect the crack driving force in the component as weil as the fracture resistance of the material. The treatment of components subjected to static loading is based on methods such as the European SINT AP procedure, which has been validated in a nurober of case studies. In the present paper the influence of strength mismatch and residual stresses on the fracture resistance and the assessment of a component are discussed.
Bruchmechanik: Konzepte, Kennwertermittlung, Bauteilbewertung. Kurzeinführung Betriebsfestigkeit
(2015)
Bei der Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung, K111, oft entscheidende Bedeutung zu. Dabei ist seine Anwendung weniger gesichert als bislang angenommen. Der Vortrag diskutiert Fragen der experimentellen Ermittlung des Schwellenwertes sowie seiner Anwendung auf Bauteile. Auf beiden Gebieten haben sich in den letzten Jahren Probleme ergeben, die bestehendes Wissen teilweise wieder in Frage stellen oder modifizieren. Im Beitrag diskutiert werden der Einfluss unterschiedlicher Rissschließmechanismen auf K111, Konsequenzen, die sich daraus hinsichtlich der Ermittlung und Übertragung des Kennwertes ergeben, sowie die Effekte von Einflussgrößen wie Spannungsverhältnis und Rissgröße, aber auch des Werkstoffgefüges und der damit korrelierten mechanischen Eigenschaften.
Recently three of the authors of this paper presented analytical solutions for reference loads of plate geometries with semi-elliptical surface cracks subjected to tension, bending, combined tension-bending and biaxial tension. These solutions were shown to provide more accurate crack driving force estimates than the conventional limit load solutions available in the literature, and the method behind them allowed for a wider application range. Within the present paper a methodology for the fracture analysis of thick-wall pressurized pipes using the R6 assessment method and considering both, biaxial and combined tension-bending loading is developed and validated. The analyses are carried out analytically, and the comparison between the predicted critical loads and experimental burst test failure loads shows satisfying agreement, this way demonstrating the potential of the proposed method.
ln den letzten Jahren hat sich gezeigt, dass die Ermittlung des Schwellenwertes DeltaKth nach den bestehenden Standardvorschriften für verschiedene Materialien zu nichtkonservativen Werten führt. Das ergibt sich im Vergleich mit Schwellenwerten, die man mit Anrissen erhält, die hinsichtlich der Ober- und der Unterlast komplett im Druckbereich erzeugt wurden. Dort, wo die Diskrepanz auftritt, verstärkt sie sich mit abnehmendem Spannungsverhältnis. ln der vorliegenden Studie wurden an einem mittel- und einem hochfesten Stahl bei unterschiedlichen Spannungsverhältnissen Schwellenwerte bestimmt. Anwendung fanden die konventionelle Lastabsenkungsmethode nach ASTM-Standard und ein Verfahren, bei dem der Langrissscbwellenwert als Endpunkt der sogenannten Zyklischen R-Kurve erhalten wird. Dieses folgt im Wesentlichen der von Pippan et al. entwickelten Methode, ergänzt diese jedoch durch eine eigene Verfahrensvariante.
In a number of previous papers, the authors have proposed a model for fracture mechanics based prediction of the S-N characteristics of metallic components with large microstructural defects. Here, an extension to materials that do not show large defects onto the fracture surfaces is provided. In such cases, an approach based on a so-called cyclic R-curve analysis is proposed for the determination of the initial flaw size, which has to be used in the calculation of fatigue crack propagation. The principle is explained and demonstrated by a first application to a welded joint.
Konventionell wird in der Bauteilauslegung zwischen Konzepten der Schwing- und Betriebsfestigkeit auf der einen und der Bruchmechanik auf der anderen Seite unterschieden. Werden in der Schwingfestigkeitsbewertung Gesamtlebensdauern ermittelt, so sind es in der Bruchmechanik Restlebensdauern bei Vorhandensein eines größeren, d.h., bereits zerstörungsfrei auffindbaren Risses. Daneben gibt es seit längerem Bestrebungen, bruchmechanische Ansätze auch für die Ermittlung der Gesamtlebensdauer fruchtbar zu machen. Der besondere Wert einer solchen Kombination besteht darin, dass die Bruchmechanik die explizite theoretische Behandlung von Eingangsparametern (Kerben, Oberflächenrauhigkeit, Mittelspannung, etc.) erlaubt, die in den konventionellen Ansätzen mit vergleichsweise hoher Ungenauigkeit halbempirisch einbezogen werden. Der Beitrag stellt einen von den Autoren entwickelten bruchmechanischen Ansatz zur Ermittlung von Wöhlerkurven vor, der eine Reihe innovativer Merkmale wie die Anwendung der elastischplastischen Bruchmechanik auf kurze Risse, die Ermittlung der Ausgangsrissgröße aus Rissarrestbetrachtungen, die Beschreibung der transienten Entwicklung des Rissschließeffekts mit Hilfe zyklischer R-Kurven (Risslängenabhängigkeit des Schwellenwertes von der Risstiefe), die theoretische Erfassung von Mehrfachrisswachstum bei Lastniveaus oberhalb der Dauerfestigkeit und statistische Aspekte umfasst. Das diskutierte Beispiel ist eine Schweißverbindung (Stumpfnaht) und wurde im Rahmen des laufenden Cluster-Projektes IBESS (Integrale bruchmechanische Ermittlung der Schwingfestigkeit von Schweißverbindungen) generiert.
Although fatigue crack propagation and fracture cause a large part of failure events in industrial practice, fracture mechanics in failure analysis seems to be still a side issue. Starting from an introduction into important basic questions of failure analysis and fracture mechanics, the authors specify what kind of questions in failure analysis can be effectively solved by fracture mechanics (and which can't). They illustrate their discussion with a number of 13 case studies from the literature. Much more pronounced than in the design stage the benefit of fracture mechanics in failure analysis depends on its accuracy. This is limited by both, intrinsic factors of the method and the availability and quality of the input information. The authors discuss the various aspects and provide the reader with some background information which, as they believe, will be helpful for better understanding the prospects and limitations of fracture mechanics in failure analysis and the conditions of its application.
The idea to determine the fatigue strength of weldments by means fracture mechanics was originally based on the empirical observation that the major portion of the fatigue life in weldments is frequently spent in crack propagation. The present paper gives a brief overview on the basic principles of fracture mechanics-based determination of fatigue strength and on special features which have to be considered for weldments. Based on this information, the ongoing research project IBESS is introduced and briefly reviewed.
Die Sicherheit von Radsatzwellen beruht gegenwärtig auf zwei Säulen: der Schwingfestigkeitsauslegung und periodischen Inspektionen. Ausgehend von einem Schadensfall, der gebrochenen ICE 3-Welle von Köln, 2008, werden ausgewählte Aspekte dieser beiden Säulen diskutiert und Vorschläge zur weiteren Verbesserung gemacht. Diese betreffen u. a. Fragen einer Betriebszeitbegrenzung, Veränderungen der Schwingfestigkeit während des Betriebs infolge von Korrosion und Steinschlag, den Einfluss von Korrosion auf Schwingrissinitiierung und -fortschritt, den potenziellen Einfluss nichtmetallischer Einschlüsse auf die Schwingfestigkeit, die Möglichkeiten, sie im Rahmen der Qualitätssicherung zu detektieren, sowie Fragen der Bruchmechanik und der Zuverlässigkeit zerstörungsfreier Schwingriss-Prüfverfahren im Rahmen eines Konzepts regelmäßiger Inspektionen.
Recently two of the authors of the present paper proposed a model for a fracture mechanics
based prediction of the S–N characteristics of metallic components with large microstructural
defects and supported this by a validation exercise on tensile plates made of an aluminium
alloy AL5380 H321. Here the authors extend the study using a number of further
data sets from the literature for which data were available at different R ratios. These data
include two aluminium alloys, Al 2024-T3 and Al 7075-T6, and a ductile cast iron, EN-GJS-
400-18-LT. Despite of necessary assumptions for the compensation of partially missing
input information the results were fairly reasonable with the exception of one data set.
The authors identify high applied stress levels in combination with potential multiple crack
initiation as the probable root of the problem and propose a scheme how the model can be
extended for taking into account crack initiation.
The yield or limit load is a key parameter with respect to the accuracy of flaw assessment based on R6 type procedures such as the R6 routine, the SINTAP and FITNET method, the standard BS 7910 and others. In a number of previous papers two of the present authors proposed the use of a reference load instead of the common limit load, which not only provided more exact fracture mechanics predictions, but showed also a wider and more general application range than the conventional parameter. Here the method has been extended to biaxial tensile loading and it has been successfully validated by a thorough comparison with finite element results and alternative solutions available in the literature.
The Fatigue Crack Propagation threshold as a design criterion - actual developments and open issues
(2014)
The burst of a disc in rotating machinery can cause catastrophic damage of the equipment and, more importantly, it can represent a mortal threat to anyone in the sphere of influence of the event. In order to minimize the danger associated to a rotating component failure, burst testing is required by the authorities in order to set safety margins to the normal operating speeds. Moreover more accurate predicting tools are required for designing the components. This paper presents the results of a numerical and analytical study on the assessment of the crack driving force for discs containing surface flaws. The aim is to provide a simple, though reliable, tool in order to be able to calculate the possible dangerous in-service speed for a rotating component and, therefore, to set burst margins above the normal operating conditions of the equipment. An R6-like flaw assessment procedure is adopted considering different assumptions in the definition of the critical speed and the analytical predictions are compared with the results of elastic-plastic finite element analysis of disc. In particular, the validity and potentiality of the method is proved for surface flaws in different positions in the disc.
Welding is one of the most common methods in industrial practice for joining components. Its main advantages are high speed in manufacturing combined with low costs and, usually, a high degree of flexibility, integrity and reliability. Nevertheless, welding is a highly complex metallurgical process and, therefore, weldments are susceptible to material discontinuities, flaws and residual stresses which may lead to structural failure and life time reduction. As a consequence weldments are an important field of fracture mechanics methods although its application is more complex than for homogeneous or non-welded structures. The aim of the paper is to provide an overview on the current state of fracture mechanics application to weldments. It starts by discussing the specific features which any fracture mechanics analysis of weldments has to take into account. Then, the experimental determination of fracture toughness, fatigue crack propagation and tensile properties of weldments is addressed. Finally, the analytical determination of the crack driving force in components and structural integrity assessment approaches for weldments are presented.
The idea to determine the fatigue strength of weldments by means fractuie mechanics was originally based on the empirical observation that the major portion of the fatigue life in weldments is frequently spent in crack propagation. The present paper gives a brief OverView on the basic principles of fracture mechanics-based determination of fatigue strength and on special features which have to be considered for weldments. Based on this Information, the ongoing research project IBESS is introduced and briefly reviewed.
The determination of the fatigue life in technical alloys containing large and small defects must rely on a propagation model which accounts for short and long crack growth. Recently an analytical model which incorporates propagation in the short crack regime and plastic correction for the crack driving force has been presented by two of the authors.
This work is intended to show further validation of the model, taking into account data sets for different materials with different testing conditions.
Despite the assumptions about missing parameters, the value of which had to be taken from the literature, the predictions showed a fairly good approximation of the fatigue lives. A possible interpretation of the results in terms of multiple crack initiation and propagation at higher loads is proposed.
The paper gives an overview on safe life and damage tolerance methods applied to railway axles. It describes failure scenarios due to fatigue crack initiation and propagation. Besides common aspects of design, specific features such as corrosion and impact damage from flying ballast are discussed which may reduce the fatigue strength of axles during service. Potential effects of non-metallic inclusions from the steel manufacturing process are addressed in the context of the very high number of loading cycles railway axles are designed for. With respect to damage tolerance general lines of fracture mechanics residual lifetime analyses are introduced. More specific discussion is provided on aspects such as the threshold value of fatigue crack propagation and reliability aspects of non-destructive inspection.
An analytical fracture mechanics model for predicting the finite life fatigue strength of components is presented which Combines a number of well established and newly developed approaches such as Murakami’s and McEvily's approach for describing the transient behaviour of crack closure of short cracks, the analytical (long) crack closure function of Newman, the R6 procedure modified by a method for improving the ligament yielding correction proposed by the authors and other elements. Basic assumption is the preexistence of initial flaws such that the crack initiation or nucleation stage is small and can be neglected. The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with artificial initial defects generated by FIB technology, the size of which was fixed on the basis of fractographic investigations on broken, smooth specimens.
On July 9, 2008 a high speed train derailed in Cologne main Station, Germany at a low speed because an axle was broken. Fortunately, the derailment happened at a low speed so that nobody was injured. The reason for the broken axle was investigated and it turned out that most likely large inclusions located shortly undemeath the surface in a T-transition were the origin of the final crack. Basing on that result, a systematic investigation on existing safety assessments of railway axles was performed. This results in an analysis of the production process of axles and in a critical review of existing of existing assessments. Improvements and future developments are outlined.
The safety assessment of railway axles is based on a two-stage approach: fatigue strength design and regular inspections which, in terms of a general safety philosophy refer to safe-life and damage tolerance concepts. Starting with a recent failure case, a broken axle of a German high speed train, a discussion is presented on issues of both safety levels. These include ideas for finite life design, the treatment of in-service effects on the fatigue strength due to flying ballast damage and corrosion pits, the effect of corrosion on fatigue crack initiation and propagation, potential effects of non-metallic inclusions in steels, the way to detect them by quality control measures and reliability aspects of non-destructive testing with respect to the detection of fatigue cracks. Proposals are made how the safety level could be further improved.
In the design approval of transport packages for radioactive materials, the mechanical and thermal safety assessment is carried out in Germany by competent authority BAM. In recent years BAM was involved in several licensing procedures of new spent fuel and HLW package designs, where the cask body is of Ductile Cast Iron (DCI). According to IAEA regulations package designs have to fulfill requirements for specific conditions of transport. Type B(U) packages must withstand the defined accident conditions of transport. The temperature range from -40°C up to the operational temperature has to be considered. For the cask material DCI, it is necessary to determine safety against brittle fracture. The German guideline BAM-GGR 007 defines requirements for fracture mechanics of packagings made of DCI. Due to complex cask body structure and the dynamic loading a fracture mechanical assessment by analytical approaches is not always possible. Experience of recent design approval procedures show that the application of numerical calculations are applicable to determine the stresses and stress intensity factors in the cask body. At the first step a numerical analysis has to be done to identify
the loading state at the whole cask body. Secondly an analysis of a detail of the cask body is made considering the displacement boundary conditions of the global model. An artificial flaw is considered in this detailed model to calculate the fracture mechanical loading state. The finite element mesh was strongly refined in the area of the flaw. The size of the artificial flaw is based on the ultrasonic inspection acceptance criteria applied for cask body manufacture. The
applicant (GNS) developed additional analysis tools for calculation of stress intensity factor and/or J-Integral. The assessment approach by BAM led to the decision to develop own tools to the possibility for independent proof of the results.
The paper describes the authority assessment approach for DCI fracture mechanics analysis. The validation procedure incl. the development of own tools is explained. BAM developed a postprocessor to determine the fracture mechanical loads. A horizontal 1 m puncture bar drop test is used to give a detailed description of the assessment procedure.
Die Sicherheit von Radsatzwellen beruht gegenwärtig auf zwei Säulen: der Schwingfestigkeitsauslegung und periodischen Inspektionen. Ausgehend von einem Schadensfall, der gebrochenen ICE 3-Welle von Köln, 2008, sollen ausgewählte Aspekte beider Säulen diskutiert und Vorschläge zur weiteren Verbesserung gemacht werden. Diese betreffen u.a. Fragen einer Betriebszeitbegrenzung, Veränderungen der Schwingfestigkeit während des Betriebs infolge von Korrosion und Steinschlag, den Einfluss von Korrosion auf Schwingrissinitiierung und -fortschritt, den potentiellen Einfluss nichtmetallischer Einschlüsse auf die Schwingfestigkeit, die Möglichkeiten sie im Rahmen der Qualitätssicherung zu detektieren sowie Fragen der Bruchmechanik und der Zuverlässigkeit zerstörungsfreier Schwingriss-Prüfverfahren im Rahmen eines Konzepts regelmäßiger Inspektionen.
Ermüdungsrisse gehen in technischen Materialien in der Regel von Werkstoffdefekten auf oder nahe der Oberfläche aus. Bei Schweißverbindungen können Schweißnahtdefekte, z. B. oberflächennahe Schlackeneinschlüsse die Risseinleitungsphase erheblich verkürzen, so dass der Hauptteil der Lebensdauer auf die Phase der Kurzriss- und zu geringerem Anteil auf die Langrissausbreitung entfällt. Bei nichtgeschweißten Bauteilen aus technischen Werkstoffen starten Ermüdungsrisse häufig an Einschlüssen, oberflächennahen Poren oder anderen Ungänzen. Einerseits ermöglicht dies prinzipiell die Anwendung bruchmechanischer Methoden zur Ermittlung der Schwingfestigkeit, andererseits müssen die Methoden in der Lage sein, spezielle Aspekte des Kurzrisswachstums wie den graduellen Aufbau des Rissschließeffekts und die lokale Rissspitzenplastizität zu erfassen. Im Beitrag werden ein geeignetes analytisches Modell sowie erste Validierungen an Proben aus verschiedenen Aluminiumlegierungen vorgestellt. Der abschließende Teil des Beitrags geht auf Besonderheiten von Schweißverbindungen (Schweißnahtdefekte, Eigenspannungen etc.) im Kontext des vorgestellten Modells ein. Eine Erweiterung des Modells für Schweißverbindungen aus Stahl wird im Rahmen eines kürzlich gestarteten DFG-AiF-Clusterprojekts erfolgen.
Two of the authors of the present paper proposed a definition of a reference load F0 which can be used as an alternative option to the common limit load for cases where the definition of the latter might be problematic in the frame of flaw assessment procedures such as R6, BS 7910, SINTAP or FITNET. The reference load is defined as that load at which the ligament yielding parameter Lr approaches one. F0, in general, varies along the crack front. It has to be obtained by finite element analyses but the results can be approximated by analytical expressions. In a previous study of the authors such a solution was presented for tension loaded plates with semi-elliptical surface cracks. In the present paper it is extended to pure bending and to combined bending and tension.
An analytical fracture mechanics model for predicting the finite life fatigue strength of components is
presented which combines a number of well established and newly developed approaches such as
Murakami's and McEvily's approach for describing the transient behaviour of crack closure of short
cracks, the analytical (long) crack closure function of Newman which became part of the widely used
NASGRO approach, the R6 procedure, a method for improving the ligament yielding correction f(Lr ) of
R6 proposed by the authors of the present paper and other elements. Basic assumption is the preexistence
of initial flaws such that the crack initiation or nucleation stage is small and can be neglected.
The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with
artificial initial defects generated by FIB technology, the size of which was fixed on the basis of
fractographic investigations on broken, smooth specimens.
The net section limit load FY necessary for assessment at static loading is a key input for the accuracy of any elasticplastic flaw assessment procedure of the R6 type. Unfortunately available limit load solutions are of variable quality since they have been obtained over decades by different methods. As a consequence the results of the fracture analyses such as the critical load or crack size are limited in their accuracy and are often significantly conservative. Further, common limit load solutions based on ligament yielding are inadequate in a number of cases even for through crack configurations and should be replaced by some kind of local yielding solutions. In the present paper a simple and straightforward reference load definition is proposed instead of the limit load which strictly corresponds to a ligament yielding parameter Lr = 1 in the R6 Routine and similar approaches such as the European SINTAP and FITNET methods. This can be determined by finite element simulation for any geometry. In addition to a previous study on thin wall notched plates the method is applied to plates containing shallow semi-elliptical surface cracks. The results demonstrate that the approach provides a suitable extension and improvement of the existing methods.
In the approval procedure of transport packages for radioactive materials, the mechanical and thermal safety assessment is carried out in Germany by competent authority BAM. In recent years BAM was involved in several licensing procedures of new spent fuel and HLW package designs, where the cask body was made of Ductile Cast Iron (DCI). According to IAEA regulations package designs have to fulfill requirements for specific conditions of transport. Type B(U) packages must withstand the defined accident conditions of transport. The temperature range from -40°C up to the operational temperature has to be considered. For the cask material DCI, it is necessary to determine the brittle fracture behavior. The German guideline BAM-GGR 007 defines requirements for the fracture mechanics of DCI. Due to complex structure of the cask body and the dynamic loading a fracture mechanical assessment in an analytical kind is not always possible. Experience of recent design approval procedures show that the application of numerical calculations are applicable to determine the fracture mechanical load in the cask body. At the first step a numerical analysis has to be done to identify the loading state at the whole cask body. Secondly an analysis of a detail of the cask body is made considering the displacement boundary conditions of the global model. An artificial flaw is considered in this detailed model to calculate the fracture mechanical loading state. The finite element mesh was strongly refined in the area of flaw. The size of the artificial flaw is characterized by the ultrasonic inspection used for the quality assurance of the package. The applicant developed additional analysis tools for calculation of stress intensity factor and/or J-Integral. The assessment approach by BAM led to the decision to develop own tools to the possibility for independent check of the results.
The paper describes the authority assessment approach for the DCI fracture mechanics analysis. The validation procedure incl. the development of own tools is explained. BAM developed a post-processor called JINFEM to determine the fracture mechanical loads. The regulatory 1 m puncture bar drop test is used to give an example of the assessment procedure.