A discussion is provided on demands that must be met in order to apply fracture mechanics to the determination of overall fatigue lifetime and strength, i.e., S-N curves and fatigue limits. These comprise the determination of the cyclic crack driving force for all stages of fatigue crack propagation, in particular for the short crack stage where the crack driving force has to be determined for elastic-plastic deformation and the gradual build-up of the crack closure phenomenon. Special emphasis is put on a fatigue damage relevant specification of the initial crack size. Different approaches in the literature are discussed. Another important aspect is the adequate treatment of multiple crack propagation. Finally, the discussion is illustrated by an example of a butt weld made of a medium strength steel.
Any fracture mechanics based determination of the fatigue strength of weldments requires different input information such as the local weld geometry and material data of the areas the crack is passing through during its propagation. The latter is so far not a trivial task as the fatigue crack is usually initiated at the weld toe at the transition from the weld metal to the heat affected zone and it subsequently propagates through the different microstructures of the latter to eventually grow into the base material and to cause final fracture. This paper describes how the material input information has gained particularly for heat affected zone material by thermo-mechanically simulated material specimens for two steels of quite different static strength. The data comprise the cyclic stress-strain curve, the crack closure effect-corrected crack growth characteristics, long crack fatigue crack propagation thresholds, the dependency of the parameter on the crack length and monotonic fracture resistance. The substantial experimental effort was necessary for the validation exercises of the IBESS approach, however, within the scope of practical application more easily applicable estimating methods are required. For that purpose the paper provides a number of appropriate proposals in line with its check against the reference data from the elaborate analyses.
This book provides a comprehensive and thorough guide to those readers who are lost in the often-confusing context of weld fatigue. It presents straightforward information on the fracture mechanics and material background of weld fatigue, starting with fatigue crack initiation and short cracks, before moving on to long cracks, crack closure, crack growth and threshold, residual stress, stress concentration, the stress intensity factor, J-integral, multiple cracks, weld geometries and defects, microstructural parameters including HAZ, and cyclic stress-strain behavior. The book treats all of these essential and mutually interacting parameters using a unique form of analysis.
Welding residual stresses have an impact on the performance of welded structures, on their fracture resistance, their resistance against fatigue crack propagation and, most important, their fatigue strength and fatigue lifetime. The present paper provides an overview on the issue mainly from the point of view of the application of fracture mechanics to the determination of the fatigue strength as the topic of this Special issue. Besides own experimental and theoretical data a comprehensive discussion is provided in that context which includes the definition and interaction of short- and long-range (or reaction) residual stresses, the effect of cyclic mechanical loading and its treatment in fracture and fatigue analyses.