Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (54)
- Beitrag zu einem Tagungsband (15)
- Vortrag (8)
- Monografie (2)
- Beitrag zu einem Sammelband (2)
- Buchkapitel (1)
Sprache
- Englisch (82) (entfernen)
Schlagworte
- Fracture mechanics (25)
- Fatigue strength (18)
- Weldments (10)
- Fatigue crack propagation (8)
- Fatigue crack propagation threshold (7)
- Short crack propagation (7)
- Short cracks (7)
- Initial crack size (6)
- Multiple crack propagation (6)
- Crack propagation (5)
Organisationseinheit der BAM
- 9 Komponentensicherheit (40)
- 9.4 Integrität von Schweißverbindungen (39)
- 5 Werkstofftechnik (6)
- 5.1 Mikrostruktur Design und Degradation (5)
- 9.0 Abteilungsleitung und andere (5)
- 9.6 Additive Fertigung metallischer Komponenten (4)
- 8 Zerstörungsfreie Prüfung (3)
- 8.5 Röntgenbildgebung (3)
- 4 Material und Umwelt (2)
- 4.0 Abteilungsleitung und andere (1)
- 4.2 Material-Mikrobiom Wechselwirkungen (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
- 5.5 Materialmodellierung (1)
- 8.0 Abteilungsleitung und andere (1)
- 9.3 Schweißtechnische Fertigungsverfahren (1)
- S Qualitätsinfrastruktur (1)
- S.0 Abteilungsleitung und andere (1)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (8)
The paper provides an overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common K concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit as defined for 107 loading cycles and the finite life branch of the S-N curve are determined.
Besides a brief introduction into the approach, a wide range of validation examples is presented. These comprise different weldment types (butt welds, cross joints and longitudinal stiffened plates), two steels of quite different strengths, different weld geometries due to different welding techniques (TIG, MAG), as-welded and stress relieved welds and different stress ratios varying from R = -1 to R = 0.5.
Any fracture mechanics based determination of the fatigue strength of weldments requires different input information such as the local weld geometry and material data of the areas the crack is passing through during its propagation. The latter is so far not a trivial task as the fatigue crack is usually initiated at the weld toe at the transition from the weld metal to the heat affected zone and it subsequently propagates through the different microstructures of the latter to eventually grow into the base material and to cause final fracture. This paper describes how the material input information has gained particularly for heat affected zone material by thermo-mechanically simulated material specimens for two steels of quite different static strength. The data comprise the cyclic stress-strain curve, the crack closure effect-corrected crack growth characteristics, long crack fatigue crack propagation thresholds, the dependency of the parameter on the crack length and monotonic fracture resistance. The substantial experimental effort was necessary for the validation exercises of the IBESS approach, however, within the scope of practical application more easily applicable estimating methods are required. For that purpose the paper provides a number of appropriate proposals in line with its check against the reference data from the elaborate analyses.
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on productionsimilar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. In particular, the rimpeeling failure mode is considered as case study. A semi-circular surface crack is modelled at the most stressed region at the diaphragm of a turbine disk, with the crack plane perpendicular to the radial direction. The crack is therefore subjected to a biaxial stress state and grows under increasing rotational speed until it triggers the rim-peeling failure. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of -integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. Probabilistic aspects are also considered in the calculations.
An analytical fracture mechanics model for predicting the finite life fatigue strength of components is presented which Combines a number of well established and newly developed approaches such as Murakami’s and McEvily's approach for describing the transient behaviour of crack closure of short cracks, the analytical (long) crack closure function of Newman, the R6 procedure modified by a method for improving the ligament yielding correction proposed by the authors and other elements. Basic assumption is the preexistence of initial flaws such that the crack initiation or nucleation stage is small and can be neglected. The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with artificial initial defects generated by FIB technology, the size of which was fixed on the basis of fractographic investigations on broken, smooth specimens.
Starting from an introduction into important Basic questions of failure analysis and fracture mechanics, the author specifies what kind of questions in failure analysis can be effectively solved by fracture mechanics (and which can't). He illustrates his discussion with a number of case studies. Much more pronounced than in the design stage the benefit of fracture mechanics in failure analysis depends on ist accuracy. This is limited by both, intrinsic factors of the method and the availability and quality of the input information. The author discusses the various aspects and provides the participants with background information helpful for better understanding the prospects and limitations of fracture mechanics in failure analysis and the conditions of its application.
A fracture mechanics model which shall be applied to the fatigue strength determination of weldments has to focus on various aspects such as: (a) the description of mechanical and physical short fatigue crack extension which is characterised by yielding conditions which do not permit the application of the common ΔK concept and by the gradual build-up of the crack closure effect, (b) a consistent methodology for determining the initial crack size, (c) based on this, the determination of a fatigue limit, (d) the treatment of multiple crack propagation at load levels above this limit, (e) the variation of the local geometry along the weld toe, and (f) statistical effects.The paper gives alimited overview of the work the authors did in this field during the last years within the German project cluster IBESS. A model is presented and briefly discussed which covers the questions above.
In a number of previous papers, the authors have proposed a model for fracture mechanics based prediction of the S-N characteristics of metallic components with large microstructural defects. Here, an extension to materials that do not show large defects onto the fracture surfaces is provided. In such cases, an approach based on a so-called cyclic R-curve analysis is proposed for the determination of the initial flaw size, which has to be used in the calculation of fatigue crack propagation. The principle is explained and demonstrated by a first application to a welded joint.
Special aspects of welded components such as geometrical imperfections, inhomogeneity, strength mismatch and welding residual stresses have to be taken into account in a fracture mechanics analysis since they affect the crack driving force in the component as weil as the fracture resistance of the material. The treatment of components subjected to static loading is based on methods such as the European SINT AP procedure, which has been validated in a nurober of case studies. In the present paper the influence of strength mismatch and residual stresses on the fracture resistance and the assessment of a component are discussed.
Although fatigue crack propagation and fracture cause a large part of failure events in industrial practice, fracture mechanics in failure analysis seems to be still a side issue. Starting from an introduction into important basic questions of failure analysis and fracture mechanics, the authors specify what kind of questions in failure analysis can be effectively solved by fracture mechanics (and which can't). They illustrate their discussion with a number of 13 case studies from the literature. Much more pronounced than in the design stage the benefit of fracture mechanics in failure analysis depends on its accuracy. This is limited by both, intrinsic factors of the method and the availability and quality of the input information. The authors discuss the various aspects and provide the reader with some background information which, as they believe, will be helpful for better understanding the prospects and limitations of fracture mechanics in failure analysis and the conditions of its application.