In a number of previous papers, the authors have proposed a model for fracture mechanics based prediction of the S-N characteristics of metallic components with large microstructural defects. Here, an extension to materials that do not show large defects onto the fracture surfaces is provided. In such cases, an approach based on a so-called cyclic R-curve analysis is proposed for the determination of the initial flaw size, which has to be used in the calculation of fatigue crack propagation. The principle is explained and demonstrated by a first application to a welded joint.
The determination of the fatigue life in technical alloys containing large and small defects must rely on a propagation model which accounts for short and long crack growth. Recently an analytical model which incorporates propagation in the short crack regime and plastic correction for the crack driving force has been presented by two of the authors.
This work is intended to show further validation of the model, taking into account data sets for different materials with different testing conditions.
Despite the assumptions about missing parameters, the value of which had to be taken from the literature, the predictions showed a fairly good approximation of the fatigue lives. A possible interpretation of the results in terms of multiple crack initiation and propagation at higher loads is proposed.