Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (66)
- Vortrag (49)
- Zeitschriftenartikel (13)
- Forschungsbericht (5)
- Beitrag zu einem Sammelband (4)
- Posterpräsentation (2)
- Dissertation (1)
Schlagworte
- Ring Compression Test (13)
- Cladding Embrittlement (10)
- Spent Nuclear Fuel (10)
- Cladding (9)
- Drop test (9)
- Safety assessment (9)
- Ductile iron (8)
- Numerical analysis (8)
- Simulation (8)
- Fracture mechanics (7)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (49)
Mechanical drop test scenarios for Type B (U) packages according to the IAEA regulations have to be carried out onto the so-called “unyielding target” (usually with cask impact limiters) and onto the puncture bar respectively. They are predefined and do not require any further investigation of scenarios that really could happen on transportation routes. Cask accident scenarios in the framework of approval procedures for interim storage sites are derived from a detailed analysis of the handling procedures necessary from arrival of cask at the site to its storing position.
In that case, casks are usually handled without impact limiters. Dependent on possible drop heights, drop positions and floor properties, conservative cask accident scenarios are derived for further safety proofs.
According to the mechanical assessment concept of the considered approval procedure numerical calculations have to be provided by the applicant to demonstrate mechanical cask safety. Stresses and strains in the cask body as well as in the lid System have to be identified and assessed. Using the example of a 3-mvertical-drop of a transport and storage cask for spent fuel elements onto the floor construction made of damping concrete covered by screed, BAM developed a finite element model. The finite element code ABAQUS/Explicit™ was used. Results of experimental investigations are not available. Therefore parameter studies are necessary to identify the sensitivity of the finite element model to significant Parameters and to verify the finite element models according to the requirements of the Guidelines for the Numerical Safety Analyses for the Approval of Transport and Storage Casks for Radioactive Materials (BAM GGR-008).
The paper describes the modeling of the material behavior and attachment of bottom side cask components. Questions concerning the modeling of a crack length limiting reinforcement in the screed layer are discussed. The influence of the mesh density of the screed layer and its strength is considered as well. Finally, the developed finite element model can be used for a numerical safety assessment. It can help to understand the complex mechanisms of the interaction between the cask components and floor construction.
Existing spent nuclear fuel (SF) and high active waste (HAW) management policies and practices worldwide are the result of past presumptions that sufficient reprocessing and/or disposal capacity would be available in the near term. Consequently, in the past many countries have developed specific solutions for different periods of time due to their individual national nuclear policies.
In Germany the concept of dry interim storage in dual purpose metal casks before disposal is being pursued for SF and HAW management and transport and storage licenses have been issued accordingly. The current operation licenses for existing storage facilities have been granted for a storage period of up to 40 years. This concept has demonstrated its suitability for over 20 years so far. Relevant safety requirements have been assessed for the short-term as well as for the long-term for site-specific operational and accidental storage conditions. But in the meantime significant delays in the national repository siting procedure occurred which will make extended storage periods necessary in the future.
Die sicherheitstechnische Auslegung von Behältern aus duktilem Gusseisen mit erhöhten Reststoffanteilen wird untersucht. Ausgehend von den zu gewährleistenden Anforderungen an Transport- und Lagerbehälter für radioaktive Abfälle werden Referenzbeanspruchungs- situationen definiert. Für einen ausgewählten Referenzfall (bestehend aus der Kombination der Behälterbauart Gusscontainer Typ VI, einem Absturz aus 5 m Höhe auf ein hartes Endlagergestein simulierendes Betonfundament als repräsentativer Störfall und vorgegebenen Werkstoffeigenschaften) wird eine numerische Spannungsanalyse durchgeführt. Die Berechnungen erfolgen mit der Methode der finiten Elemente an dreidimensionalen Modellen, deren numerische Stabilität und Genauigkeit überprüft wird. Zur Berechnung der Behälterbeanspruchungen in Abhängigkeit vom Reststoffanteil werden dynamische Fließkurven für definiert legierte Testabgüsse angegeben.
In the present study, ductile cast iron from an original DCI container with a wide variety of microstructure was
investigated in order to determine the materials fracture toughness under impact loading conditions. Three-point bending
specimens with thickness of 140 mm from a cubic DCI container were investigated at elevated loading rates to
provide reliable fracture toughness parameters for the assessment procedures. In contrast to static fracture behaviour,
the fracture toughness values of thick-walled DCI at higher loading rates show a remarkable reduction with decreasing
temperature up to 50 °C and a significant shift of the transition range. The lower bound fracture toughness value used
in the BAM DCI safety concept was confirmed for impact loading conditions by these fracture mechanics tests using
large specimens. These measurements are relevant to the licensing tests for storage containers without shock absorbers,
especially to the assessment of the dynamic behaviour of crack-like defects inside a cask structure under drop test conditions.
Using extensive dynamic numerical analyses it could be shown, that for special crack configurations the dynamic
crack tip parameter (KI, or J) may be estimated by static formulae even under mechanical impact. These results
of the safety assessment were verified according to the German Konrad repository acceptance criteria by a drop test
with a cubic waste container with artificial crack-like defects from 5 m height onto a representative storage facility
foundation.