Filtern
Dokumenttyp
- Zeitschriftenartikel (5) (entfernen)
Sprache
- Englisch (5)
Referierte Publikation
- ja (5)
Schlagworte
- Flame retardance (2)
- WPC (2)
- Aluminum phosphinate (1)
- Cone calorimeter (1)
- Decking boards (1)
- Degradation (1)
- Disflamoll TP LXS 51064 (1)
- Fire behaviour (1)
- Flame retardancy (1)
- Flame retardants (1)
- Fourier transform infrared - attenuated total reflexion (FTIR-ATR) spectroscopy (1)
- Fungal decay (1)
- Halogen free (1)
- High tmeperature polyamide 6T/DT (1)
- Microscopy (1)
- Renewable resources (1)
- Thermogravimetric analysis (TGA) (1)
- Wood-plastic composite (1)
- Wood-plastic composite (WPC) (1)
- Wood-plastic composites (1)
- Wood-plastic composites (WPC) (1)
Glass fiber reinforced polyamide (PA) 6T/DT flame retarded with aluminum diethylphosphinate (AlPi) was tested to assess its flame retardant properties. Models for the decomposition of PA 6T/DT with and without AlPi are presented. Thermal decomposition was measured by performing TGA with Fourier transform infrared (FTIR) spectroscopy and FTIR spectroscopy in the condensed phase. Fire behavior was studied using a cone calorimeter and flammability was tested with UL 94 and the limiting oxygen index. AlPi works as an effective flame retardant for glass fiber reinforced PA 6T/DT materials, acting in the gas phase. Also observed was condensed-phase action, which occurs especially under oxidative conditions before the samples ignite.
Combinations of different common flame retardants in wood–plastic composites (WPCs) are tested to identify synergistic or antagonistic effects with the goal of improving the fire performance of WPCs. Flame retardants investigated are expandable graphite (EG), ammonium polyphosphate (APP), and red phosphorus (RP) and combinations of two of them are used. The fire behavior is studied by cone calorimetric measurements. Additional thermogravimetry is used for further investigations. The fire tests show that EG has the highest potential for flame retardancy, but due to its expansion it cracks the formed residue layer. Combinations of EG with RP or with high amounts of APP are able to suppress this cracking.
A new flame retardant based on an ammonium phosphonate is studied with respect to its thermal decomposition and its mode of action in wood-plastic composites (WPCs). The measurements are carried out by means of fire tests (cone calorimeter) and pyrolysis investigations (thermogravimetry, infrared spectroscopy). The flame retardant acts mainly in the condensed phase by increasing the amount of residue formed by the wood part in the WPC. Additional flame dilution is achieved by the release of water, ammonia and carbon dioxide during the decomposition of the flame retardant.
In this study, we investigated the basic knowledge necessary to develop flame-retarded woodplastic composite (WPC) materials by focusing on decking boards. Therefore, the respective effects of geometry, material composition, and moisture were studied by performing cone calorimetric measurements. Using hollow-shaped geometries removes combustible material and reduces the fire load but simultaneously increases fire propagation. The best results were achieved by using high-wood contents. The addition of talc can reduce the intensity of burning. Moisture also has a positive effect on burning behavior. Apart from the well-known mechanism of water, a change was observed in the resultant residue.
Flame retarded wood-plastic composites (WPCs) should allow safe application in areas of fire risk. Halogen-free flame retardants can contain high amounts of nitrogen, phosphorus or sulphur, which may serve as nutrition source for wood degrading fungi and accelerate wood decay. Therefore, the material resistance of WPCs with each of four flame retardants against both fire or fungal decay was examined in comparison to WPC without flame retardant. Expandable graphite showed the best performance against fire in cone calorimetry and radiant panel testing. Two ammonium polyphosphates and a third nitrogen-containing flame retardant were not as effective. Contrary to the possibility that flame retardants might enhance fungal decay of WPC, the opposite effect occurred in case of the wood-degrading fungi Trametes versicolor and Coniophora puteana according to determination of mass loss and decrease of bending modulus of elasticity. Only the surface mould Alternaria alternata slightly increased the degradation of WPCs with nitrogen-containing flame retardants compared to WPC without flame retardant according to mass loss data and FTIR-ATR analyses. Finally, WPC including expandable graphite as flame retardant was effective against both fire and fungal decay.