Glass fiber reinforced polyamide (PA) 6T/DT flame retarded with aluminum diethylphosphinate (AlPi) was tested to assess its flame retardant properties. Models for the decomposition of PA 6T/DT with and without AlPi are presented. Thermal decomposition was measured by performing TGA with Fourier transform infrared (FTIR) spectroscopy and FTIR spectroscopy in the condensed phase. Fire behavior was studied using a cone calorimeter and flammability was tested with UL 94 and the limiting oxygen index. AlPi works as an effective flame retardant for glass fiber reinforced PA 6T/DT materials, acting in the gas phase. Also observed was condensed-phase action, which occurs especially under oxidative conditions before the samples ignite.
Sulphurous additives for polystyrene: Influencing decomposition behavior in the condensed phase
(2015)
The thermal decomposition behaviour of polystyrene (PS) containing sulphur and phosphorus additives was investigated, using thermogravimetry coupled with Fourier transform infrared spectroscopy (TGA-FTIR). It was found that the additives influence the decomposition process of the polymer in the condensed phase, resulting in a decrease in styrene monomer formation and an increase in styrene oligmer derivatives. Via reference measurements with binary mixtures it was found that the presence of sulphur additives influences the radicalic decomposition process of PS. In combination with quantum chemical calculations it was concluded that this is due to the formation of radicals that abstract hydrogen from the polymer matrix at lower temperatures, disfavouring the radicalic decomposition pathway leading to styrene.
Microplastics are increasingly entering marine, limnic and terrestrial ecosystems worldwide, where they sorb hydrophobic organic contaminants. Here, the sorption behavior of the fuel-related water contaminants benzene, toluene, ethyl benzene and xylene (BTEX) and four tertiary butyl ethers to virgin and via UV radiation aged polypropylene (PP) and polystyrene (PS) pellets was investigated. Changes in material properties due to aging were recorded using appropriate polymer characterization methods, such as differential scanning calorimetry, Fourier transform infrared spectroscopy, gel permeation chromatography, X-ray photoelectron spectroscopy, and microscopy.
Pellets were exposed to water containing BTEX and the ethers at 130-190 mg/L for up to two weeks.
Aqueous sorbate concentrations were determined by headspace gas chromatography. Sorption to the polymers was correlated with the sorbate's Kow and was significant for BTEX and marginal for the ethers.
Due to substantially lower glass transition temperatures, PP showed higher sorption than PS. Aging had no effect on the sorption behavior of PP. PS sorbed less BTEX after aging due to an oxidized surface layer.
For analysis of the gaseous thermal decomposition products of polymers, the common techniques are thermogravimetry, combined with Fourier transformed infrared spectroscopy (TGA–FTIR) and mass spectrometry (TGA–MS). These methods offer a simple approach to the decomposition mechanism, especially for small decomposition molecules. Complex spectra of gaseous mixtures are very often hard to identify because of overlapping signals. In this paper a new method is described to adsorb the decomposition products during controlled conditions in TGA on solid-phase extraction (SPE) material: twisters. Subsequently the twisters were analysed with thermal desorption gas chromatography mass spectrometry (TDS–GC–MS), which allows the decomposition products to be separated and identified using an MS library. The thermoplastics polyamide 66 (PA 66) and polybutylene terephthalate (PBT) were used as example polymers. The influence of the sample mass and of the purge gas flow during the decomposition process was investigated in TGA. The advantages and limitations of the method were presented in comparison to the common analysis techniques, TGA–FTIR and TGA–MS.
The influence of weathering on the fire retardancy of polymers is investigated by means of a cone calorimeter test, before and after artificial weathering. The surface degradation was monitored using different techniques (ATR–FTIR, microscopy, colour measurement). Different kinds of polymeric materials were chosen, all as they are used in practice: polycarbonate (PC) blends, polyamide (PA) and polypropylene (PP) flame-retarded with arylphosphate, melamine cyanurate (MC) and intumescent formulation based on ammonium polyphosphate (APP), respectively.
All samples show material degradation at the surface due to weathering. No significant weathering influence occurs on the flame retardancy when it is a bulk property, as was observed for aryl phosphates in PC blends and MC in PA. When the fire retardancy is dominated by a surface mechanism, dependence on the duration of weathering is detected: for intumescent formulations based on ammonium APP in PP, a worsening in the formation of the intumescent network was observed.