Pyrolysis and fire behavior of high impact polystyrene (HIPS) containing red phosphorus and melamine polyphosphate were investigated. The thermal and thermo-oxidative decomposition were characterized using thermogravimetry coupled with FTIR and MS, respectively. The fire behavior was monitored with a cone calorimeter using different external heat fluxes and determining the LOI. Red phosphorus reduced the heat release in HIPS due to radical trapping in the gas phase. The reduction in effective heat of combustion was accompanied by an increase of incomplete combustion products such as smoke and carbon monoxide. Melamine polyphosphate in HIPS acted in the condensed phase with barrier formation. The heat release rate was reduced, whereas the total heat evolved, smoke and carbon monoxide formation were not influenced significantly. Using both fire retardants, the resulting fire retardancy was characterized mainly by superposition.
Flame Retardant Mechanisms of Red Phosphorus and Magnesium Hydroxide in High Impact Polystyrene
(2004)
The flame retardant mechanisms of red phosphorus, magnesium hydroxide and red phosphorus combined with magnesium hydroxide were studied in high impact polystyrene by means of comprehensive decomposition studies and combustion tests. The study is intended to illuminate prerequisites and the potential of red phosphorus as a fire retardant for hydrocarbon polymers in the condensed phase and in the gas phase. Thermal and thermo-oxidative decomposition, decomposition kinetics and the product gases evolved were characterized using thermogravimetry coupled with Fourier transform infrared spectroscopy and mass spectroscopy, respectively. Fire behaviour was investigated with a cone calorimeter using different external heat fluxes, whereas the flammability was determined by limited oxygen indices. The combustion residues were analysed using XPS. Red phosphorus reduced the heat release in HIPS due to radical trapping in the gas phase. Magnesium hydroxide influenced fire behaviour by heat sink mechanisms, release of water and the formation of a magnesia layer acting as a barrier. The combination of both flame retardants in HIPS nearly resulted in a superposition. A slight synergy in barrier characteristics was due to the formation of magnesium phosphate, whereas a slight anti-synergism occurred in flammability and in the gas phase action. The latter effect is controlled by a decreased fuel rate due to the barrier layer rather than by an initiation of red phosphorus oxidation in the condensed phase.
The exploration of condensed phase mechanisms such as charring and intumescence has been pushed forward in the last decades, since it is believed that focusing on these concepts will bring materials closer to an efficient and ecologically friendly fire retardancy. They promise to concentrate efficient fire retardancy at the key position between pyrolysis zone and gas phase. Examples of residue/char forming and intumescent materials are used to illustrate the influence of mass and heat barrier effects on the fire behavior of materials and general results are presented. A comprehensive understanding of the mechanisms and structure-property relationships in fire retardancy is presented.