Two commercial polyethylene grades were exposed to water at elevated temperatures and enhanced oxygen pressure. To characterize their aging behavior laser-induced photoluminescence spectroscopy was applied. Additionally, aging characterization was performed by established methods such as tensile testing, infrared (IR) spectroscopy, high performance liquid chromatography (HPLC), differential scanning calorimetry (DSC) and UV–VIS spectroscopy. During the initial stages of aging, the overall concentration of phenolic antioxidants as well as oxidation onset temperatures decreased exponentially. Simultaneously, significant discoloration due to the formation of conjugated degradation products from phenolic antioxidants (e.g., quinone methides) was detected. After the consumption of antioxidants, photoluminescence started to grow continuously presumably due to the formation of photoluminescent unsaturated carbonyls. In the final stages of aging, embrittlement of the materials as characterized by the degradation of mechanical properties (i.e., loss in ductility) coincided with rising carbonyl index values as well as an increase in crystallinity due to chemicrystallization. Between integrated photoluminescence intensity and carbonyl index, a linear correlation was established. In the induction period, the photoluminescence method exhibited a significantly higher sensitivity to reflect aging induced material changes.
After some months of operation, a number of PV modules develop a discolouration defect called 'snail trails', or 'snail traces', which appear as irregular dark stripes across the cells. Whereas these traces were soon identified as discoloured silver contacts along the cell edges or at micro cracks, the chemical and mechanistic reasons for this phenomenon have not yet been resolved in detail. In this work we show that silver nanoparticles accumulating within the encapsulation foil cause the brownish discolouration, and that certain additives of encapsulation and back sheet foils trigger the formation of these nanoparticles.
Cure monitoring of epoxy films by heatable in situ FTIR analysis: Correlation to composite parts
(2014)
The curing mechanism of an epoxy film containing dicyandiamide (DICY) and an epoxy formulation based on diglycidyl ether of Bisphenol A (DGEBA) polymer was studied as a function of various temperature programs. The investigation was performed in situ, using a thin film of the epoxy mixture on a silicon wafer substrate in a heatable transmission tool of a FTIR spectrometer. Based on these model-curing experiments, a major curing mechanism was proposed, taking into account the appearance, the decrease, and the development of characteristic bands at various temperatures. The conclusions of the model curing were correlated to FTIR measurements on a real, 50-mm-thick glass fiber reinforced component composite part from a technical process. It could be shown that characteristic bands that develop at curing temperatures above 150°C appear especially in the center of the thick sample. From the chemical or molecular point of view, this demonstrates the established technician's understanding that temperature control inside a large-scale fiber composite of, for example, aircraft, wind-turbine, automotive applications component is of major importance.
After several months of operation, many photovoltaic (PV) modules develop a discolouration defect called snail trails which appear as irregular dark traces across the cells. These traces are caused by silver nanoparticles accumulating within the encapsulation foil directly above the grid finger. In this work we systematically investigate combinations of encapsulation and back-sheet foils with respect to their susceptibility for snail trails. We can show that certain additive compositions within the encapsulation and back sheet foils are critical for the formation of the discolouring silver nanoparticles. We suggest a reaction model explaining the formation of snail trails from a chemical point of view. This fundamental understanding allows the rapid testing of foils for their snail trail sensitivity as well as the special design of resistant foils.
A flexible, sustainable, one-step thermal decomposition route for the synthesis of hierarchical, heteroatom doped carbon foams is presented. Task-specific semi-organic crystals combine functions for three different purposes: the carbon and heteroatom source, a foaming agent (CO2) and an in situ generable template (NaCl). Insights to the decomposition pathway were gained through FTIR/MS coupled TGA and an ultrafast out-of-furnace heating procedure and the products were analysed with (HR)SEM/TEM, EELS, FTIR, and N2 sorption. The resulting macroporous carbon foams are excellent supports for metallic nanoparticles due to their hierarchical structure, high surface area and tuneable heteroatom contents. This was demonstrated for catalytically active copper or the magnetic CoNi alloy for water purification.