The thermal molecular degradation of polyamide 66 (PA 66) doped with (partially supported) metal oxide particles (Fe2O3, ZnO, Al2O3) was investigated qualitatively and quantitatively using common analysis techniques like thermogravimetry coupled with IR-spectroscopic evolved gas analysis (TGA-FTIR). Using pyrolysis coupled with gas chromatography mass spectrometry (Py-GC-MS), qualitative conclusions were drawn about the complex hydrocarbon products. However, the combination of TGA with solid-phase extraction, followed by thermal desorption gas chromatography mass spectrometry (TED-GC-MS), allows qualitative and even semi-quantitative conclusions about the decomposition pathway of PA 66 in the presence of various metal oxide particles.
The investigations under inert conditions showed that the presence of metal particles increases the rate of decarboxylation and deamination reactions, as well as the formation rate of cyclopentanone and pyridine derivatives. These species are a consequence of various condensation reactions. The condensation reactions release a large amount of water, thus triggering the hydrolysis of PA 66. Molecular thermal degradation mechanisms were developed for the main decomposition as well as for the condensation reactions and supported by quantum chemical calculations. The catalytic effect of the metal oxides in PA 66 increases in the following order: PA 66 = PA 66 – Al2O3 < PA 66 – Fe2O3 < PA 66 – ZnO.
Flame retardancy mechanisms of aluminium phosphinate in glass fiber reinforced thermoplastics
(2008)
Heterogeneous, gradual or structured morphology of fire residues plays an important role in fire retardancy of polymers. A scanning electron microscope with an attached energy dispersive X-ray spectrometer (SEM/EDX) is highlighted as a powerful tool for the advanced characterization of such complex fire residues, since it offers high resolution in combination with both good depth of field and analysis of chemical composition. Two examples are presented: First, comprehensive SEM/EDX investigation on a complex structured fire residue of glass fibre reinforced polyamide 6,6 (PA 66-GF) flame retarded by diethylaluminium phosphinate, melamine polyphosphate and some zinc borate. A multilayered surface crust (thickness ~ 24 µm) covers a rather hollow area stabilized by GF glued together. The resulting efficient thermal insulation results in self-extinguishing before pyrolysis is completed, even under forced-flaming combustion. Second, sophisticated, quasi online SEM/EDX imaging of the formation of residual protection layer in layered silicate epoxy resin nanocomposites (LSEC). Burning specimens were quenched in liquid nitrogen for subsequent analyses. Different zones were distinguished in the condensed phase characterized by distinct processes such as melting and ablation of organic material, as well as agglomeration, depletion, exfoliation and reorientation of the LS.
Using thermogravimetric analysis (TGA) with a solid-phase adsorber for thermal extraction, followed by subsequently analysing the adsorber with thermo-desorption gas chromatography mass spectrometry (TDS-GCMS) enables measurement of polymer degradation under oxidizing atmosphere, and the identification of certain complex hydrocarbon degradation products by chromatographic separation and defined mass patterns. This technique, thermal-extraction desorption gas chromatography mass spectrometry (TED-GCMS) was used to investigate the thermo-oxidative degradation of PA 66 and PA 66 doped with 2 wt% of metal oxide particles. In TGA pure PA 66 formed more residue under an oxidizing atmosphere than an inert one. In contrast to the measurements under inert atmosphere, several condensed aromatic species containing nitrogen could be identified in thermo-oxidative measurements. These degradation products were formed through condensation reactions of primary amides originating from imide hydrolysis. The formation of such highly condensed species also causes higher char formation. Four metal oxides have shown an impact on the thermo-oxidative degradation of PA 66: Fe2O3 on η-Al2O3 < pure Fe2O3 = Fe2O3 on γ-Al2O3 < pure ZnO. For ZnO even a char-stabilizing effect could be observed. A catalytic effect of these metal oxides causes more condensed cyclopentanone and pyridine derivates. Thus, more water is formed and released, resulting in increased hydrolysis of the imides and degradation at lower temperatures.