Filtern
Erscheinungsjahr
Dokumenttyp
Sprache
- Englisch (73)
Referierte Publikation
- ja (73) (entfernen)
Schlagworte
- Microplastics (9)
- Flame retardance (7)
- Pyrolysis (7)
- Fire retardancy (6)
- Flame retardancy (6)
- Microplastic (6)
- Degradation (5)
- Cone calorimeter (4)
- Thermogravimetric analysis (4)
- Thermosets (4)
Organisationseinheit der BAM
- 6 Materialchemie (13)
- 6.6 Physik und chemische Analytik der Polymere (13)
- 1 Analytische Chemie; Referenzmaterialien (6)
- 1.7 Organische Spuren- und Lebensmittelanalytik (4)
- 1.4 Prozessanalytik (3)
- 5 Werkstofftechnik (2)
- 5.3 Polymere Verbundwerkstoffe (2)
- 4 Material und Umwelt (1)
- 4.3 Schadstofftransfer und Umwelttechnologien (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
Paper des Monats
- ja (1)
Summary: The decomposition of novel phosphorus-containing poly(oxyphenylene-sulfonyl-phenylene-oxy-diphenyl phenylene phosphine oxide) (PSU_I), 2,5-dihydroxy-1-biphenylene-phosphine oxide based polysulfone (PSU_II), poly(sulfonyl-diphenylphenylene phosphonate) (PSU_P) and bisphenol A-based polysulfone (PSU) is studied. The influence of the chemical structure, charring and phosphorus release is discussed based on the mass loss, kinetics and products. The pyrolysis and fire behaviour of blends with epoxy resin (EP) are studied. For EP-PSU_II, phosphorus initiates water elimination and changes the decomposition pathway of EP. The fire behaviour of EP-PSU shows some improvements, whereas the heat release rate is crucially reduced for EP-PSU_II due to simultaneous char formation and flame inhibition.
A comparative evaluation of systematically tailored chemical structures of various phosphorus-containing aminic hardeners for epoxy resins was carried out. In particular, the effect of the oxidation state of the phosphorus in the hardener molecule on the curing behavior, the mechanical, thermomechanical, and hot-wet properties of a cured bifunctional bisphenol-A based thermoset is discussed. Particular attention is paid to the comparative pyrolysis of neat cured epoxy resins containing phosphine oxide, phosphinate, phosphonate, and phosphate (with a phosphorus content of about 2.6 wt %) and of the fire behavior of their corresponding carbon fiber-reinforced composites. Comparatively faster curing thermosetting system with an enhanced flame retardancy and adequate processing behavior can be formulated by taking advantage of the higher reactivity of the phosphorus-modified hardeners. For example, a combination of the high reactivity and of induced secondary crosslinking reactions leads to a comparatively high Tg when curing the epoxy using a substoichiometric amount of the phosphinate-based hardener. The overall mechanical performance of the materials cured with the phosphorus-containing hardeners is comparable to that of a 4,4-DDS-cured reference system. While the various phosphorus-containing hardeners in general provide the epoxy-based matrix with enhanced flame retardancy properties, it is the flame inhibition in the gas phase especially that determines the improvement in fire retardancy of carbon fiber-reinforced composites. In summary, the present study provides an important contribution towards developing a better understanding of the potential use of such phosphorus-containing compounds to provide the composite matrix with sufficient flame retardancy while simultaneously maintaining its overall mechanical performance on a suitable level.
The fire retardancy mechanisms of aluminium diethylphosphinate in combination with melamine polyphosphate and zinc borate was analysed in glass-fibre reinforced polyamide 6,6. The influence of phosphorus compounds on the polyamide decomposition pathways was characterized using thermal analysis (TG), evolved gas analysis (TGFTIR), and FTIRATR analysis of the residue. The Lewis acidbase interactions between the flame retardants, the amide unit, and the metal ions control the decomposition. The flammability (LOI, UL 94) and performance under forced-flaming conditions (cone calorimeter using different irradiations) were investigated. Fire residues were analysed with FTIRATR, SEMEDX, and NMR. Aluminium phosphinate in polyamide 6,6 acts mainly by flame inhibition. Melamine polyphosphate shows some fuel dilution and a significant barrier effect. Using a combination of aluminium phosphinate and melamine polyphosphate results in some charring and a dominant barrier effect. These effects are improved in the presence of zinc borate due to the formation of boronaluminium phosphates instead of aluminium phosphates.
The pyrolysis and fire behavior of glass-fiber reinforced poly(butylene terephthalate) (PBT/GF) with two different metal phosphinates as flame retardants in combination with and without melamine cyanurate (MC) were analyzed by means of thermogravimetry, thermogravimetry coupled with infrared spectroscopy, flammability, and cone calorimeter tests as well as scanning electron microscopy/energy dispersive X-ray spectroscopy and X-ray fluorescence spectroscopy. In PBT/GF, dosages of 13-20% of the halogen-free flame retardant aluminum phosphinate or aluminum phosphinate in combination with MC fulfill the requirements for electrical engineering and electronics applications (UL 94 = V-0; LOI > 42%), whereas the use of the same amount of zinc phosphinate or zinc phosphinate in combination with MC does not improve the fire behavior satisfactorily (UL 94 = HB; LOI = 27-28%). The performance under forced flaming conditions (cone calorimeter) is quite similar for both of the metal phosphinates. The use of aluminum and zinc salts results in similar flame inhibition predominantly due to the release of the phosphinate compounds in the gas phase. Both metal phosphinates and MC interact with the polymer changing the decomposition characteristics. However, part of the zinc phosphinate vaporizes as a complete molecule. Because of the different decomposition behavior of the metal salts, only the aluminum phosphinate results in a small amount of thermally stable carbonaceous char. In particular, the aluminum phosphinate-terephthalate formed is more stable than the zinc phosphinate-terephthalate. The small amount of char has a crucial effect on the thermal properties and mechanical stability of the residue and thus the flammability.
A systematic and comparative evaluation of the pyrolysis of halogen-free flame-retarded epoxy resins containing phosphine oxide, phosphinate, phosphonate, and phosphate (phosphorus contents around 2.6 wt.%) and the fire behaviour of their carbon fibre composites is presented. Decomposition pathways are proposed based on the thermal analysis (TG), TG coupled with evolved gas analysis (TG-FTIR), kinetics and analysis of the residue with FTIR and XPS. All organophosphorus-modified hardeners containing phenoxy groups lead to a reduced decomposition temperature and mass loss step for the main decomposition of the cured epoxy resin. With increasing oxidation state of the phosphorus the thermally stable residue increases, whereas the release of phosphorus-containing volatiles decreases. The flammability of the composites was investigated with LOI and UL 94 and the fire behaviour for forced-flaming conditions with cone calorimeter tests performed using different irradiations. The flame retardancy mechanisms are discussed. With increasing oxidation state of the phosphorus additional charring is observed, whereas the flame inhibition, which plays the more important role for the performance of the composites, decreases. The processing and the mechanical performance (delamination resistance, flexural properties and interlaminar bonding strength) of the fibre-reinforced composites containing phosphorus were maintained at a high level and, in some cases, even improved. The potential for optimising flame retardancy while maintaining mechanical properties is highlighted in this study.
A novel phosphorus-modified polysulfone (P-PSu) was employed as a combined toughness modifier and a source of flame retardancy for a DGEBA/DDS thermosetting system. In comparison to the results of a commercially available polysulfone (PSu), commonly used as a toughness modifier, the chemorheological changes during curing measured by means of temperature-modulated DSC revealed an earlier occurrence of mobility restrictions in the P-PSu-modified epoxy. A higher viscosity and secondary epoxy-modifier reactions induced a sooner vitrification of the reacting mixture; effects that effectively prevented any phase separation and morphology development in the resulting material during cure. Thus, only about a 20% increase in fracture toughness was observed in the epoxy modified with 20 wt.% of P-PSu, cured under standard conditions at 180 °C for 2 h. Blends of the phosphorus-modified and the standard polysulfone (PSu) were also prepared in various mixing ratios and were used to modify the same thermosetting system. Again, no evidence for phase separation of the P-PSu was found in the epoxy modified with the P-PSu/PSu blends cured under the selected experimental conditions. The particular microstructures formed upon curing these novel materials are attributed to a separation of PSu from a miscible P-PSuepoxy mixture. Nevertheless, the blends of P-PSu/PSu were found to be effective toughness/flame retardancy enhancers owing to the simultaneous microstructure development and polymer interpenetration.
Thermal, thermo-oxidative and fire residues of high impact polystyrene/magnesium hydroxide/red phosphorus (HIPS/Mg(OH)2/Pr) are investigated by solid-state NMR and compared with the results for the binary subsystem Mg(OH)2/Pr. The influences of oxygen, nitrogen and temperature are discussed. For a thermal decomposition and pyrolysis during combustion, the main pyrolysis of HIPS takes place while the remaining residue is a rather intact polymer, with a major share of the embedded Pr still present. Subsequently, mainly amorphous phosphates and a slight amount of crystalline Mg3(PO4)2 and Mg2P2O7 are formed at the highest temperatures. Only with increasing mass loss does the remaining polystyrene structure decompose and graphitic structures occur. The influence of oxygen on the decomposition mechanism is most obvious for the binary system Mg(OH)2/Pr. Pr vanishes more rapidly and crystalline, oxygen-rich magnesium phosphates are formed. In HIPS/Mg(OH)2/Pr systems the polymer acts as a barrier to reaction by the embedded particles, so that major characteristics of an anaerobic decomposition are found. Significant amounts of phosphorus are retained in the condensed phase through a reaction of Pr with Mg(OH)2 to mostly amorphous phosphates. This formation of amorphous inorganic magnesium phosphates can act as an additional physical barrier. This study outlines some advanced approaches for controlling the condensed-phase mechanisms of phosphorus and underlines that solid-state NMR is a most powerful tool for investigating the organic and inorganic residues.
The pyrolysis of an epoxy resin and the fire behavior of corresponding carbon fiber-reinforced composites, both flame-retarded with either 10-ethyl-9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide or 1,3,5-tris[2-(9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide-10-)ethyl]1, 3,5-triazine-2,4,6(1H,3H,5H)-trione, are investigated. The different fire retardancy mechanisms are discussed, and their influence on the fire properties assessed, in particular for flammability (limiting oxygen index, UL 94) and developing fires (cone calorimeter with different external heat fluxes of 35, 50, and 70 kW m-2). Adding the flame retardants containing 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide affects the fire behavior by both condensed phase and gas phase mechanisms. Interactions between the additives and the epoxy resin result in a change in the decomposition pathways and an increased char formation. The release of phosphorous products results in significant flame inhibition. The fire properties achieved are thus interesting with respect to industrial exploration.
The flame retardancy mechanisms of aluminium diethylphosphinate (AlPi) and its combination with melamine cyanurate (MC) in glass-fibre-reinforced poly(butylene terephthalate) (PBT/GF) were analysed using TGA including evolved gas analysis (TGA-FTIR), cone calorimeter measurements using various irradiations, flammability tests (limited oxygen index, LOI, UL 94) and chemical analyses of residues (FTIR, SEM/EDX). AlPi decomposed mainly through the formation of diethylphosphinic acid and aluminium phosphate and influenced the decomposition of the PBT only slightly. AlPi acted mainly through flame inhibition. A halogen-free V-0 PBT/GF material was achieved with a LOI of 44%. Additional charring influenced the flammability. MC decomposed independently of the polymer and showed some fuel dilution effects.