The aging management system for the mechanical components of nuclear power plants (NPPs) must be established and used by the licensee in such a way that the quality of safety relevant components is guaranteed for the completely designed lifetime of the NPP. This demands an extensive plant life management with special emphases on the knowledge of the degradation in material properties. The basic safety concept in Germany observes this circumstance. Lifetime extension of the German NPPs is an aim of the current valid coalition agreement of the German government. Operational extension of interim storage facilities requires, in comparison to the aging management system for NPP, an aging management system adapted to the Special circumstances of spent fuel storage casks. Extension of interim storage periods for spent fuel casks beyond the designed lifetime requires, in comparison to the components of an NPP, an increasing knowledge of material degradation with potential impact on cask integrity, e.g. leak tightness. Dry interim storage in Germany has been approved for 40 years. After that time, according to the present strategy, a final repository should be available. However, until now, such a final facility still does not exist, and the German exploration and licensing process is heavily delayed. Currently, discussions are continuing regarding further exploration of the Gorleben salt mine. There is willingness to overcome this situation that is clearly described in the available coalition agreement of the federal government. Anyway, however, the prediction is viewed; a repository for heat generating radioactive waste in Germany will not be available in the near future and may not be available when first storage facilities and casks reach their 40 years of approved lifetime, which will occur in ~25 years starting from now. Therefore, the question must be asked:
what has to be done with the existing storage casks in the interim facilities? May these casks be fit for continued use, with an extension of the storage period? One option is to have an aging management system, which creates enough information about the technical condition of safety relevant cask properties. This is the basis for safety evaluation for extended storage periods. In the present paper, possible aging mechanisms for high level waste storage casks are discussed, as well as the influence of the time dependent changes of the component properties.
Metal seals are in common use as an essential component for the leak tight closure of transport and storage casks for spent fuel and vitrified high active waste from reprocessing. They are placed between the massive monolithic cask body made of ductile cast iron or forged steel and the primary and secondary lids, which are fixed with screws around the lid circumference, in order to ensure long term safe enclosure of the radioactive cask inventory. Hereby, long term reliable pressure forces in combination with a tight surface contact are as important as well maintained seal and surface qualities and dry and clean conditions during seal assembly and operation. A few years ago BAM started systematic investigation on the long term seal behavior with re-spect to longer storage periods and seal behavior in accidental cask scenarios with dynamic de-formations of the seal groove geometry or short term drop in pressure force up to lid lifting. BAM has developed test flanges for seals with full scale cross section diameter but much small-er outer diameter to gain representative data for metal-sealed lid systems. They are placed in appropriate testing machines for relevant mechanical loading under static and dynamic condi-tions with the ability to measure the standard helium leakage rate continuously during each test phase. This paper focuses on BAM long term tests of different seal types with aluminum and silver jackets at three different temperatures of +20°C, +100°C and +150°C under static conditions over longer periods of time. Due to creeping effects, a reduction of the pressure force does ap-pear during loading and unloading depending on prior holding times. So far, test results of up to 2 years indicate a clear correlation between seal pressure forces and holding time, temperature and seal type allowing for extrapolating to much longer periods of time. The paper presents basic correlations, test and evaluation procedures as well as important provisional results and gives an outlook on further investigations.