The failure of laminates is originated in plies loaded transverse to the fiber direction, e.g. in the 90° ply of a cross ply laminate. The initiation of failure is due to the debonding of individual fibers At some point the interface crack kinks into the matrix and propagates towards the inter-face of the neighbouring fiber. The cracks then continue propagating through the full ply. The interface failure obviously is the dominating process of the failure of plies in high fiber volume fraction composites. Several authors investigated the interfacial crack propagation on model systems. First, Varna and Paris studied the debonding process on a single fiber embedded in pure matrix under transverse ten-sion by fracture mechanical analyses. Correa and Paris performed experimental as well as numerical studies by calculating the mixed mode energy release rate under different loading conditions. These analyses were extended to fibers surrounded by a composite material by the present authors. Among others, Comninou as well as Sun and Jih have shown that the separation into a mode I and mode II energy release rate is not universal but the mixed mode ratio depends on the length of the crack increment. Comninou developed a solution of an interface crack between dissimilar media which reveals the even a small contact zone is found near the crack tip. As a result, the mode I part of the energy release rate vanishes because no opening of the crack takes place. The contact zone, however, is extremely small. If these mathematical phenomena, however, are relevant for physical problems is not verified.
Pore annihilation during hot isostatic pressing (HIP) was investigated in the single-crystal nickel-base superalloy CMSX-4 experimentally by interrupted HIP tests at 1288 °C/103 MPa. The kinetics of pore annihilation was determined by density measurement and quantitative metallography. Transmission electron microscopy of a HIPed specimen showed that the pores shrink via dislocation movement on octahedral glide planes. Theoretically pore closure under HIP condition was modelled by the finite element method using crystal plasticity and large strain theories. The modelling gives a similar kinetics of pore annihilation as observed experimentally, however somewhat higher annihilation rate.
The determination of the strength and the failure behaviour of fiber reinforced composites is a complex task. This is mainly due to the anisotropy and the inhomogeneiety of the material on the microscale. The strength or the fracture toughness of the interface between fiber and matrix is the key factor controlling the failure process on microscale, especially under loads transverse to the fiber axes.
The ultimate failure of a laminate is a complex process consisting of a large number of different subprocesses. Due to its highly dynamic nature on one hand and the microscopical scale on the other it is not possible to observe the ultimate failure directly or even to analyse it theoretically. However, long before ultimate failure occurs a large number of elementary failure processes take place in a rather
static manner or at least at low crack Propagation speed.