Filtern
Dokumenttyp
- Vortrag (11)
- Zeitschriftenartikel (9)
- Posterpräsentation (7)
Schlagworte
- DCB (11)
- Glass (8)
- Crack growth (7)
- Water speciation (6)
- Ontologie (5)
- Glas (4)
- Simulation (4)
- Soda-lime silicate glass (4)
- Water content (4)
- Bildanalyse (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (25)
- 5.6 Glas (25)
In the past few years, a new phase, Ba0.5Sr0.5Zn2Si2O7 with negative thermal expansion has been described in the literature. Some excess of SiO2 is necessary to produce glasses from which the Ba0.5Sr0.5Zn2Si2O7 phase can be crystallized.
Unfortunately, in such glasses usually surface crystallization occurs; however, the addition of nucleating agents such as trace quantities of platinum or relatively high quantities of ZrO2 is necessary to achieve bulk nucleation. These additional components also affect the crystal growth velocity, which furthermore is different for crystal growth from the surface and in the bulk. In this paper, three different chemical compositions containing different ZrO2 concentrations, where one composition additionally contains 100 ppm platinum, are studied with respect to their crystallization behaviour. Although the compositions do not differ much, the crystallization behaviour and also the Crystal growth velocities are surprisingly different.
Crack growth velocity in alkali silicate glasses was measured in vacuum across 10 orders of magnitude with double cantilever beam technique. Measured and literature crack growth data were compared with calculated intrinsic fracture toughness data obtained from Young´s moduli and the theoretical fracture surface energy estimated from chemical bond energies. Data analysis reveals significant deviations from this intrinsic brittle fracture behavior. These deviations do not follow simple compositional trends. Two opposing processes may explain this finding: a decrease in the apparent fracture surface energy due to stress-induced chemical changes at the crack tip and its increase due to energy dissipation during fracture.
Stable crack growth was measured for nominal dry and water-bearing (6 wt%) soda-lime silicate glasses in double cantilever beam geometry and combined with DMA studies on the effects of dissolved water on internal friction and glass transition, respectively. In vacuum, a decreased slope of logarithmic crack growth velocity versus stress intensity factor is evident for the hydrous glass in line with an increase of b-relaxation intensity indicating more energy Dissipation during fracture. Further, inert crack growth in hydrous glass is found to be divided into sections of different slope, which indicates different water related crack propagation mechanism. In ambient air, a largely extended region II is observed for the hydrous glass, which indicates that crack growth is more sensitive to ambient water.
Glass strength and fatigue is limited by surface cracks. As subcritical crack growth (SCCG) is governed by ambient humidity, stress corrosion at the crack tip is widely accepted to be the underlying mechanism. However, as water is known to have decisive effect on glass properties and can rapidly enter the crack tip near glass region, SCCG could be affected by such water related phenomena. We tried to mimic these effects studying water dissolution and speciation, mechanical properties, and SCCG in water-bearing glasses. For this purpose, glasses up to 8 wt% water have been prepared by means of high-pressure melting of glass powder - water mixtures.
As part of this effort, SCCG in dry and hydrous commercial micros¬cope slide glass (CW = 6 wt%) was studied in double cantilever beam (DCB) geometry and sub-Tg relaxation was measured by Dynamic Mechanical Analysis (DMA).
For SCCG in ambient air (24% r.h.), SCCG was promoted by the presence of 6wt% bulk water with respect to the dry glass. On the other hand, stress intensity values, KI, required to cause slow crack growth (v < 10-6 ms-1) resemble literature findings for float glass of similar composition in liquid water, which might represent the maximum possible promoting effect of ambient water on SCCG.
For SCCG in vacuum (10-3 mbar), dissolved bulk water causes even more pronounced effects. Most strikingly, it strongly decreases the slope of the log v(KI)-curve, which is a measure of dissipated energy during fracture. A strong increase of sub-Tg relaxation with increasing water content was confirmed by DMA. As a consequence, slow crack growth occurs at KI values as measured in the dry glass whereas fast crack growth occurs at much larger KI than that of the dry glass. Kinks and shoulders shown by the inert log v(KI)-curve indicate that bulk water does not simply affect bulk mechanical properties.
Compared to its intrinsic strength, the practical strength of glasses is substantially
lowered by microscopic flaws. Their sub critical growth from the surface is strongly
affected by ambient humidity.
A new device was designed to enable the observation of sub critical crack growth
(SCCG) in vacuum and controlled atmosphere. It allows measurements in transparent and
semi-transparent materials in double cantilever beam (DCB) geometry. The aim of the
present work is to study the effect of crystals on crack growth.
Die Festigkeit von Gläsern wird durch die Oberflächenqualität beeinflusst. Kommt es neben dem Auftreten von Defekten zusätzlich zum Risswachstum ausgehend hiervon, wird die Festigkeit minimiert. Das Wachstum hängt dabei maßgeblich von der Luftfeuchtigkeit ab. Dieses Ermüdungsverhalten von Gläsern besser zu verstehen und dabei die Mechanismen und den Einfluss von im Volumen eingebauten Wasser auf das unterkritische Risswachstum zu untersuchen, ist Ziel der Arbeiten. Als Teilprojekt im Rahmen des DFG Schwerpunktprogramms SPP 1594 „Ultrastrong glasses“ soll der Einfluss des im Volumen eingebauten Wassers auf die Rissspitze untersucht werden. Zusammen mit der Leibniz Universität Hannover und der TU Clausthal werden hierfür hochwasserhaltige Gläser (bis zu 8 Gew%) bei 8 kbar über die Flüssigphase synthetisiert, die makroskopisch den hohen Wasseranteil nachstellen. Die Charakterisierung erfolgt hinsichtlich des Wassereinbaus, der mechanischen Eigenschaften und des Risswachstums. Die Arbeiten in Berlin beziehen sich hierbei auf die Messungen des unterkritischen Risswachstums in Luft und Vakuum, sowie Verlustwinkelmessungen.
Erste Ergebnisse zeigen Unterschiede im korrosionsbeeinflussten (langsames) und inerten (schnelles und im Vakuum stattfindendes) Risswachstumsverhalten der untersuchten Gläsern. Die Rissgeschwindigkeit beim Übergang vom korrosionsbeeinflussten zum inerten Risswachstum ist hin¬gegen für alle Gläser ähnlich und folglich ein kinetisch durch den äußeren Wassertransport an die Rissspitze bestimmter Prozess. Der Widerstand gegen Risswachstum steigt mit Tg und zusätzlich kann anhand der Verlustwinkelmessungen ein Zusammenhang zwischen der Netzwerk- und der β-Relaxation ermittelt werden. Je höher der Wassergehalt im Glas ist, desto niedriger wird Tg und einfacher das Risswachstum, welches sich durch längere Risse kennzeichnet. Besonders stark tritt dieser Effekt bei einem Überschuss an molekularem Wasser auf.
Premature failure of glass under load is caused by sub-critical crack growth (SCCG) originate from microscopic flaws at the surface. While SCCG is related to the humidity of the ambient atmosphere, leading to stress corrosion phenomena at the crack tip, the detailed mechanism and the effect of different network formers are still not fully understood. For more clarity, various soda silicate glasses with a second network former were investigated by double cantilever beam technique: Na2O*Al2O3*SiO2 (NAS), Na2O*B2O3*SiO2 (NBS), Na2O*PbO*SiO2 (NPbS).
Three effects on the crack growth velocity, v, versus stress intensity, KI, curves were found out. The slope in region I, which is limited by corrosion, increases in the order NAS < NBS ≲ NPbS. The velocity range of region II reflecting the transition between corrosion effected and inert crack growth (region III), varies within one order of magnitude between the glasses. The KI region of inert crack growth strongly scatters between 0.4 and 0.9 MPam1/2. For comparison, crack growth at different humidity in commercial soda lime silicate glass (NCS) was measured.