3D Crack analysis in hydrogen charged lean duplex stainless steel with synchrotron refraction CT
(2016)
Hydrogen in metals can cause a degradation of the mechanical properties, the so-called hydrogen embrittlement. In combination with internal stresses, hydrogen assisted cracking (HAC) can occur. This phenomenon is not completely understood yet. To better characterise the cracking behaviour, it is important to gain information about the evolution of the 3D crack network. For this purpose samples of lean duplex stainless steel were loaded with hydrogen by means of electrochemical charging and investigated by means of synchrotron refraction CT and SEM fractography after uniaxial tensile loading. Synchrotron refraction CT is an analyser-based imaging (ABI) technique. It uses a Si (111) single crystal as analyser, which is placed into the beam path between sample and detector. According to Bragg’s law only incident x-rays within a narrow range around the Bragg-angle are diffracted from the analyser into the detector. Hence, the analyser acts as an angular filter for the transmitted beam. This filtering allows to turn the refraction and scattering of x-rays into image contrast. Refraction occurs at all interfaces, where the density of the material changes and is more sensitive to density changes than the attenuation. Therefore, it is possible to detect smaller cracks than with classical x-ray imaging techniques, like CT, with comparable spacial resolution. It also visualises the 3D structure of the cracks and gains quantitative information about their morphology and distribution. Since cracks introduced by HAC are usually very small and have a small opening displacement, synchrotron refraction CT is expected to be well suited for imaging this cracking mechanism and can be a valuable tool to characterise the formation and the evolution of a 3D crack network.
Hydrogen in metals can cause a degradation of the mechanical properties with possible subsequent hydrogen assisted cracking (HAC). Though, the mechanism of HAC is not completely understood yet and thus suitable methods for in situ investigations to characterise the crack formation are needed. X-ray computed tomography (CT) is a well-known tool for analysing these properties. However, the effective resolution of the detector system limits the detection of small defects by CT. Analyser based imaging (ABI) takes advantage of x-ray refraction at interfaces between volumes of different density, i.e. of cracks, pores, inclusions, etc., within the sample to detect defects smaller than the resolution of the detector system. In this study, measurements on an aluminium alloy weld showed that ABI allows us to resolve the 3D structure of cracks undetected by absorption based CT. Prospective investigations will analyse HAC in steels.
Einfluss von Konstruktion und Wasserstoff auf die Kaltrissbildung hochfester Feinkornbaustähle
(2020)
Der konstruktive Leichtbau erfordert den zunehmenden Einsatz hochfester Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa. Neben den durch die Wandstärkenreduzierung erreichbaren Einsparungen an Ressourcen und Fertigungszeit lässt sich eine weitere Minimierung der Schweißzeit und -kosten mittels abgesenkter Schweißnahtvolumina erreichen. Hierzu wurden moderne Lichtbogenprozesse, wie bspw. der modifizierte Sprühlichtbogen (Mod.SLB), mit erhöhter Abschmelzleistung entwickelt, mit denen auch enge Nahtspalte bzw. Nahtöffnungswinkel geschweißt werden können. Hochfeste Verbindungen unterliegen zunehmend erhöhten Anforderungen in Bezug auf die schweißtechnische Verarbeitung und der resultierenden Bauteilperformance und sicherheit. Dies gilt insbesondere beim Bauteilschweißen mittels solcher Hochleistungsverfahren in Verbindung mit engen Nahtspalten. In der vorliegenden Arbeit soll dieser Herausforderung durch Klärung der Einflüsse auf die Kaltrissbildung bei einem hochfesten Feinkornbau-stahl S960QL Rechnung getragen werden. Für die Kaltrissprüfung werden entsprechende adaptierte Proben analog dem selbstbeanspruchenden TEKKEN-Test verwendet und hinsichtlich Rissbildung, Gefüge, Gehalt an diffusiblem Wasserstoff und Eigenspannungen analysiert. Die Variation der Nahtöffnungswinkel der Prüfnähte erfolgt zwischen 30° und 60°. Zur Vermeidung wasserstoffunterstützter Kaltrissbildung wird die Wirksamkeit einer Nachwärmprozedur aus der Schweißwärme heraus untersucht. Als Ergebnis zeigen die Schweißgüter, die an reduziertem Nahtöffnungswinkel erzeugt wurden, im Mittel etwas höhere Wasserstoffkonzentrationen. Zudem ist an diesen Schweißgütern eine vermehrte Mikro- als auch Makrorissbildung festzustellen. An allen Proben, die nicht nachgewärmt wurden, treten Kerbrisse aufgrund von Kaltrissbildung auf, deren Vermeidung sich durch ein Nachwärmen unmittelbar nach dem Schweißen als besonders effektiv darstellte.
High-strength low-alloyed (HSLA) steels with yield strength ≥ 690 MPa have increasing importance in steel construction and civil engineering. However, weld processing of those steels is a major challenge. The susceptibility for degradation of mechanical properties of weld joints significantly increases in presence of hydrogen and can result in hydrogen assisted cracking (HAC). Generally, risk for HAC increases with increasing yield strength of HSLA steels. To minimize the incidence of HAC, it is essential to gain knowledge about both the (1) absorbed hydrogen amount and its distribution in the weld seam and (2) options to lower
the amount of introduced hydrogen. Existing standards recommend heat treatment procedures (interpass temperature or post weld heat treatment) to reduce the diffusible hydrogen concentration in weldments. In this context, different weld seam geometries should be considered. For HSLA steel fabrication weld processing with seam opening angles of 45° to 60° is typical. Modern weld technologies allow welding with seam opening angles of 30° - reduced welding time and costs. In the present study, the hydrogen distribution in multi-layer welds of a 960 MPa HSLA steel was analysed. Influence of different seam opening angles as well as heat input, interpass temperature and post weld heat treatments were investigated. The welded samples were quenched in ice water immediately after welding and subsequently stored in liquid nitrogen. After defined warming up, small specimens were machined from the weld seam by water jet cutting. The diffusible hydrogen concentration was measured by carrier gas hot extraction with coupled mass spectrometer. The results showed, that low heat input and post weld heat treatment procedures can lower hydrogen concentrations in welds. Furthermore, a gradient of the hydrogen concentration was
identified with increasing weld pool depth. By varying the seam opening angles different hydrogen concentrations were
measured.
Neutron cameras allow visualizing hydrogen distributions with radiographic or tomographic imaging methods in iron and steel. The necessary contrast between hydrogen and iron stems from the high difference in the total neutron cross section of both elements. This allows e.g. the in situ measurement of hydrogen mass flow inside cm thick steel samples with a temporal resolution of 20 s using neutron radiography as well as the quantitative measurement of hydrogen accumulations at the crack’s inner surfaces in hydrogen embrittled iron samples with neutron tomography. We could detect directly gaseous hydrogen in the crack cavities and we measured the gas pressure. This new quality of the information on a micrometer scale allows new insights for the analysis of hydrogen-induced damage mechanisms. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20-30 µm. In this contribution, we show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography methods in order to visualize and quantify hydrogen accumulations at cracks. The measurements were performed at the research reactor BER II of the HZB in Berlin and at the FRM II reactor of the neutron source Heinz Maier-Leibnitz in Garching.
Ausgehend vom derzeit vorrangigen Einsatz in Mobilkranen, kommen höherfeste Feinkornbaustähle mit Streckgrenzen ab 960 MPa zunehmend auch in anderen modernen Stahlkonstruktionen zur Anwendung. Dies ist aufgrund aktueller Forderungen nach Energie- und Ressourceneffizienz im Sinne des konstruktiven Leichtbaus vielfach notwendig. Die Verwendung höherfester Stähle sowie deren schweißtechnische Verarbeitung, insbesondere in sicherheitsrelevanten Tragstrukturen, erfordert ein tiefgreifendes Verständnis der Zusammenhänge zwischen Schweißverfahren, Wärmeeinbringung, Abkühlbedingungen sowie den daraus resultierenden metallurgischen Vorgängen in der Schweißnaht und den nahtnahen Bereichen. Vorwiegend werden höherfeste Güten mittels MAG-Prozess geschweißt. Bedeutende Fortschritte in der Regelungstechnik führten unter den Herstellern von Schweißstromquellen in den letzten Jahren zur Entwicklung zahlreicher modifizierter Sprühlichtbogenprozesse (mod. SLB). Diese Prozesse ähneln sich in ihren Eigenschaften und ermöglichen die bekannten positiven Aspekte, wie Einsparung an Schweißzusatz sowie Schweiß- und Rüstzeit aufgrund der Möglichkeit reduzierter Nahtöffnungswinkel. Der mod. SLB bedingt zusammen mit einer anderen Nahtgeometrie veränderte Naht- und Schweißraupenquerschnitte sowie einen abweichenden Lagenaufbau. Diese wirtschaftlich-technisch attraktive Möglichkeit reduzierter Nahtöffnungswinkel findet in den Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle unter Vermeidung von Kaltrissbildung bisher keine Berücksichtigung. Dabei gilt es, gerade die Interaktion der Haupteinflussgrößen auf die Kaltrissbildung unter reduziertem Nahtöffnungswinkel zu betrachten. Im Rahmen zweier AiF-Forschungsvorhaben (IGF-Nr. 17.978 N, 18.596 BR) wurde daher der Einfluss der Wärmeführung anhand vergleichender Mehrlagenschweißungen mittels konventionellem Übergangslichtbogen und mod. SLB mit angepasster Nahtkonfiguration auf schweißbedingte Beanspruchungen sowie auf die Wasserstoffkonzentration im Schweißgut untersucht.
Kaltrissprüfung hochfester Feinkornbaustähle beim Schweißen mit modifiziertem Sprühlichtbogen
(2019)
Der konstruktive Leichtbau erfordert den zunehmenden Einsatz hochfester Feinkornbaustähle mit Streckgrenzen bis zu 1300 MPa. Um darüber hinaus Schweißzeit, Schweißnahtvolumina und Schweißkosten zu minimieren, kam es zur Entwicklung moderner Lichtbogenprozesse mit erhöhter Abschmelzleistung, wie bspw. dem modifizierten Sprühlichtbogen (mod. SLB). Dieser Beitrag zeigt Kaltrissuntersuchungen beim Einsatz des mod. SLB unter reduziertem Nahtöffnungswinkel eines Hochfesten S960QL. Mit Hilfe des fremdbeanspruchten Implant-Tests konnte dargelegt werden, dass durch die erhöhte Abschmelzleistung ein tieferes Einbrandprofil entsteht und es dadurch zu einer zeitverzögerten Rissbildung kommt. Ergebnisse des selbstbeanspruchenden TEKKEN-Tests zeigen eine deutliche Rissbildung im Schweißgut unter reduziertem Nahtöffnungswinkel. Durch eine Nachwärmung unmittelbar nach dem Schweißen kann diese Rissbildung minimiert werden.
Heute werden in Stahlkonstruktionen zunehmend hochfeste Baustähle (Streckgrenze ≥ 960 MPa) eingesetzt. Daher sind auch in Schweißnähten solche hohen Festigkeiten gefordert. Jedoch können hohe Eigenspannungen aufgrund geringerer plastischer Dehnungsreserven in diesen Schweißnähten die Sicherheit der Bauteile vermindern. Diese sind insbesondere im Zusammenhang mit Wasserstoff und Härtegefügen risskritisch. Niedrige Bauteilbeanspruchungen und Kosteneinsparungen lassen sich heutzutage mit modernen fokussierten Lichtbogenvarianten und engeren Nahtspalten erreichen. Die vorliegende Studie zeigt allerdings, dass diese modernen Schweißprozesse und die angepasste Nahtgeometrie höhere Wasserstoffkonzentrationen und signifikant gesteigerte oberflächennahe Zugeigenspannungsniveaus bedingen. Anhand mehrlagiger Schweißversuche an S960QL unter Variation von Wärmeführung, Lichtbogenvariante und Nahtöffnungswinkel wurden die Effekte und Wechselwirkungen unter Zuhilfenahme von Eigenspannungsanalytik mittels Röntgendiffraktometrie und Wasserstoffanalytik mittels Trägergasheißextraktion systematisch untersucht. Das Schweißgefüge führte unter kritischer mechanischer Beanspruchung und erhöhtem Gehalt an diffusiblem Wasserstoff insbesondere bei geringem Nahtöffnungswinkel und fokussiertem Lichtbogen zu einer deutlichen Ausbildung von Mikrorissen. Die Mikrorisse führten teils zu einer makroskopischen Ausprägung. Durch Analysen zur Nachwärmung aus der Schweißwärme heraus konnten suffiziente Wärmeführungsparameter für eine effektive Prävention solcher Risse erarbeitet werden. Die vorliegende Arbeit zeigt anhand des Interaktionssystems bei der wasserstoffunterstützten Kaltrissbildung Gefüge-Beanspruchung-Wasserstoff, welche Wärmeführungs- und Schweißparameter sich für die hochfesten Feinkornbaustähle zur Kaltrissvermeidung eignen.
Höherfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa neigen bei der schweißtechnischen Fertigung zur Bildung von wasserstoffunterstützten Kaltrissen. Diese Mikrorisse entstehen aus der kritischen Interaktion von lokalem risskritischem Gefüge, lokal erhöhter Wasserstoffkonzentration und lokal erhöhter Beanspruchung bzw. Dehnung. Aktuell gültigen Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle sind Anweisungen zu entnehmen, um das Risiko einer Kaltrissbildung zu minimieren. Die Weiterentwicklung der Werkstoffe (Legierungskonzepte) und neuer Lichtbogenprozesse zur Verringerung der Nahtöffnungswinkel bei gleichzeitiger Erhöhung der Abschmelzleistung (modifizierter Sprühlichtbogen) brachten jedoch auch neue Fragen hinsichtlich der Wasserstoffmenge in der Schweißverbindung nach dem Schweißen und der Kaltrissempfindlichkeit mit sich. Mikrolegierungselemente (V, Nb und Ti) bedingen bspw. eine verlangsamte Wasserstoffdiffusion. Schweißverbindungen unter reduziertem Nahtöffnungswinkel beinhalten höhere Wasserstoffkonzentrationen. Dieser Beitrag zeigt den Einfluss von Einbrandprofil (höhere Abschmelzleistung) auf die Kaltrissempfindlichkeit an einem höherfesten Feinkornbaustahl mit artähnlichem mikrolegierten Schweißzusatzwerkstoff anhand des fremdbeanspruchten Implant-Tests.
Neutron imaging has become a valuable tool for measuring hydrogen distributions qualitatively and quantitatively in metals. Hydrogen mass flow can be measured inside cm thick Steel samples with 10 s temporal resolution. Hydrogen accumulations around craclcs in embrittled iron samples can be visualized three-dimensionally. The gas pressure of hydrogen in crack cavities has been measured to be in the ränge of 5 MPa to 15 MPa. This quality of information allows new insights for the analysis of damage mechanisms on a micrometer scale, e.g., of hydrogen blistering. Further, this method is nondestructive and provides local information in situ and in three dimensions with a spatial resolution of 20 µm - 30 µm.