This study provides an in-depth survey of current technologies and applications for assessing the cold cracking susceptibility of welded joints. From the large variety of existent cold cracking test procedures, the most important and internationally established tests are presented and evaluated in terms of their usefulness and application limits. According to the type of loading, the test procedures are classified into self-restraint and externally loaded tests. Apart from the merely metallurgical weldability tests for determining the cracking susceptibility of base materials, filler materials and weld metals, advanced test methods are presented for evaluating the cold cracking susceptibility of welded components. A salient point brought out in this respect is the fact that the level of external loading in such component weld tests can be applied independently of the welding parameters, reproducing as realistically as possible the practical application case, i.e. the level of the restraint intensity. This study includes a summarized comparison of the cold cracking procedures. It is emphasized that highly accurate consideration and reproduction of the design-specific stiffness conditions is essential in the tests for assessing the cold cracking behaviour of welded joints. Therefore, various numerical analyses are presented in a final chapter for calculating the restraint intensity as a definitive factor affecting cold cracking.
Effects of Preheating and Interpass Temperature on Stresses in S 1100 QL Multi-Pass Butt-Welds
(2008)
The increased application of higher-strength steels and filler materials necessitates a more profound understanding of the interactions between the welding process, the heat input, the cooling conditions and the resulting metallurgical processes in the weid and its surroundings. Strategies, which help to improve the strength properties and life-time of welded stmctures to such an extent that the utilisation of higher-strength materials can be justified and their lightweight construction potential can thus be exploited to the füll, can only be derived from the interaction between all the influencing factors. Examples of a few investigations on welded joints between higher-strength fine-grained structural steels with regard to the interactions between the main variables influencing the cold cracking are presented in this article.
The increased application of higher-strength steels and filler materials necessitates a more profound understanding of the interactions between the welding process, the heat input, the cooling conditions and the resulting metallurgical processes in the weid and its surroundings. Strategies, which help to improve the strength properties and life-time of welded stmctures to such an extent that the utilisation of higher-strength materials can be justified and their lightweight construction potential can thus be exploited to the füll, can only be derived from the interaction between all the influencing factors. Examples of a few investigations on welded joints between higher-strength fine-grained structural steels with regard to the interactions between the main variables influencing the cold cracking are presented in this article.
Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were – for the first time – detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 µm. The residual stresses show significant distributions dependent on Ms temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent.
Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms-temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were — for the first time — detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 μm. The residual stresses show significant distributions dependent on the Ms-temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent.
The application of high-strength fine-grained structural steels with yield stress ≥ 690 MPa permits significant weight reductions and cost savings. Since welding is the major joining technology, e.g. in mobile crane industry, the sustainable and economical application of these grades depends on the load-bearing capacity and safety of the welds. An economical processing of high-strength steels is determined above all by the avoidance of cold cracking, apart from achieving demand-oriented mechanical properlies in the weid area. High tensile residual stresses are disadvantageaus regarding the cold cracking resistance and strength of welded components. Furthermore, high restraints commonly appearing in component welds increase residual stresses. Hence, in this research the influences of heat control on residual stresses and the overall structural Ioad of welded structures were quantified. The relationship between the weid thermal cycle and the resulting residual stress under additional shrinkage restraint was analysed by a successive augmentation of the restraint intensity. This was achieved by systematic low Ioad and component weid tests. lt was observed that the heat control significantly affects the local residual stresses and the overall structural Ioad of welded structures. A high interpass temperature increases the global and local welding stresses in particular. Moreover, the transferability of experimental welding results obtained from small specimens according to applicable codes to real component geometries was investigated. With the help of these findings it is possible to improve existing heat control concepts for high-strength steel welding.
Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods, or jackets. These components are typically constructed using submerged arc welding (SAW) with high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen-assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicates the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam/layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with over 20 passes and a seam length of 1000 mm. Additional welded stiffeners simulated the effect of a high restraint, to achieve critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of up to 48 h after the completion welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modeling allowed the qualitative estimation of the hydrogen diffusion in the weld. No noticeable HAC occurrence was identified and confirms the high cracking resistance of the investigated material. Finally, the applicability of the MWT concept should be critically discussed.