- Welding (41)
- Residual stresses (32)
- Eigenspannungen (27)
- Hydrogen (24)
- Residual stress (19)
- Restraint (17)
- Wasserstoff (17)
- Hochfester Stahl (16)
- MAG-Schweißen (16)
- High-strength steels (15)
Organisationseinheit der BAM
- 9 Komponentensicherheit (121)
- 9.4 Integrität von Schweißverbindungen (115)
- 9.2 Versuchsanlagen und Prüftechnik (53)
- 9.0 Abteilungsleitung und andere (30)
- 8 Zerstörungsfreie Prüfung (6)
- 8.5 Röntgenbildgebung (4)
- 8.4 Akustische und elektromagnetische Verfahren (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.3 Instrumentelle Analytik (1)
- 5 Werkstofftechnik (1)
Paper des Monats
- ja (6)
Carrier gas hot extraction (CGHE) is a commonly applied technique for determination of hydrogen in weld joints using a thermal conductivity detector (TCD) for hydrogen measurement. The CGHE is based on the accelerated hydrogen effusion due to thermal activation at elevated temperatures. The ISO 3690 standard suggests different specimen geometries as well as necessary minimum extraction time vs. temperature. They have the biggest influence on precise hydrogen determination. The present study summarizes the results and experience of numerous test runs with different specimen temperatures, geometries (ISO 3690 type B and small cylindrical samples), and factors that additionally influence hydrogen determination. They are namely specimen surface (polished/as-welded), limited TCD sensitivity vs. specimen volume, temperature measurement vs. effects of PI-furnace controller, as well as errors due to insufficient data assessment. Summarized, the temperature is the driving force of the CGHE. Two different methods are suggested to increase the heating rate up to the desired extraction temperature without changing the experimental equipment. Suggestions are made to improve the reliability of hydrogen determination depended on the hydrogen signal stability during extraction accompanied by Evaluation of the recorded data. Generally, independent temperature measurement with dummy specimens is useful for further data analysis, especially if this data is used for calculation of trapping kinetics by thermal desorption analysis (TDA).
Risssicherheit von Schweißnähten an Pipelines der Offshore-Industrie aus supermartensitischem Stahl
(2005)
Up to the present, the thermomechanical loads during welding and subsequent cooling under design-specific shrinkage restraint resulting from the interaction between the materials and the structure have often not been taken into consideration approperiately for weldability assessment of components. As compared to previous investigations using small specimens this report presents component weld tests under varying intensities of restraint. Online records of the reaction forces and moments demonstrate in which way the intensity of restraint affects the reaction stresses and moments and their meaning for the evaluation of the load level in welded components.
Düring the past decades, weldability studies have predominantly been concentrated on the material and the welding process. In order to achieve a closer insight into the structural effects, component weldability tests have been performed by online monitoring of the reaction forces and moments. As a particular item, the effects of different strengths of the base and filier material on the reaction force and stress build up transverse to the welding direction have been studied at a specific structural restraint. As a most relevant result for practical welding it is demonstrated that the final reaction force and also the reaction stress level in the multilayer butt welds decreases with overmatch of the weld metal.
Große Materialstärken und komplexe Strukturen bewirken eine erhebliche Schrumpfbehinderung der Schweißnaht.
Die aus dem Schweißprozess resultierenden multiaxialen Belastungen tragen maßgeblich zur Gesamteigenbeanspruchung einer Schweißkonstruktion bei und lassen sich nur unter realen Fertigungsbedingungen analysieren.
Zur wirklichkeitsnahen Simulation der komplexen Steifigkeitsverhältnisse realer Bauteile wurden hierzu in einer speziellen 3D-Prüfanlage UP-Mehrlagenschweißungen am warmfesten Stahl 13CrMoV9-10 durchgeführt. Während der schweißtechnischen Fertigung sowie der Abkühlung auf Raumtemperatur wurden die Proben an der freien Ausdehnung und Schrumpfung gehindert. Der Einfluss der Wärmeführung, d.h. Streckenenergie (E) und Vorwärm-/Zwischenlagentemperatur (T(Pli>), auf die resultierende Bauteilbeanspruchung wurde durch in-situ Messungen der Reaktionskräfte (Fy) und Biegemomente (Mx) während des Schweißens und der anschließenden Wasserstoffarmglühung untersucht. Sowohl die Reaktionskräfte als auch die Biegemomente steigen mit zunehmender Vorwärmtemperatur an und somit erhöht sich die Beanspruchung des Wurzelbereiches. Während die Vorwärm-/Zwischenlagentemperatur einen signifikanten Einfluss auf die resultierenden Reaktionskräfte hat, ist der Einfluss auf die Biegemomente nach Abkühlung auf Raumtemperatur vernachlässigbar. Eine Erhöhung der Streckenenergie wirkt sich nur geringfügig auf die Höhe der Endreaktionskraft aus, beeinflusst aber signifikant das resultierende Biegemoment nach erfolgter Abkühlung auf Raumtemperatur.
In einer speziellen 3D-Prüfanlage zur wirklichkeitsnahen Simulation von komplexen Verhältnissen an Großproben wurden UP-Mehrlagenschweißungen am warmfesten Stahl 13CrMoV9-10 durchgeführt. Während der schweißtechnischen Fertigung und der Abkühlung auf Raumtemperatur wurden die Proben an der freien Ausdehnung und Schrumpfung gehindert. Die daraus resultierenden Reaktionsspannungen führten während der Wärmenachbehandlung zu Relaxationsrissen in der Wärmeeinflusszone. Das Spannungsarmglühen wurde bei einer Temperatur von 705°C und einer Haltezeit von 8 h durchgeführt. Während der Aufheiz- und Abkühlphasen wurde die thermische Ausdehnung der Probe über die 3D-Prüfanlage kompensiert und damit das Spannungsniveau bis zum Erreichen der maximalen Glühtemperatur aufrechterhalten. Nach Erreichen der Glühtemperatur konnte die Probe relaxieren. Der Einsatz der Schallemissionsmessung ermöglichte es die Entstehung von Spannungsrelaxationsrisse, erstmalig online, nachzuweisen. Durch Synchronisierung der Schallemissionsereignisse mit den Messdaten der 3D – Prüfanlage wurde der kritische Temperaturbereich für das Auftreten von Spannungsrelaxationsrissen bestimmt. Die Rissinitiierung findet im Temperaturbereich zwischen 350°C - 500°C statt. Aussagen über das Risswachstum können auf Grund der ungünstigen Versuchsbedingungen, mit Emission von Störgeräuchen, nicht getroffen werden.
Hydrogen in metals can cause a degradation of the mechanical properties with possible subsequent hydrogen assisted cracking (HAC). Though, the mechanism of HAC is not completely understood yet and thus suitable methods for in situ investigations to characterise the crack formation are needed. X-ray computed tomography (CT) is a well-known tool for analysing these properties. However, the effective resolution of the detector system limits the detection of small defects by CT. Analyser based imaging (ABI) takes advantage of x-ray refraction at interfaces between volumes of different density, i.e. of cracks, pores, inclusions, etc., within the sample to detect defects smaller than the resolution of the detector system. In this study, measurements on an aluminium alloy weld showed that ABI allows us to resolve the 3D structure of cracks undetected by absorption based CT. Prospective investigations will analyse HAC in steels.
As an approach towards more rough industrial laser welding applications, the Nd:YAG laser welding process has been coupled to the plasma powder welding process for the first time. Process stabilities have been achieved by such hybrid welding which are even better than those known from previous coupling of the laser process with gas metal arc welding (GMAW), for instance.
The present contribution focuses on the technology and potentials of the novel laser hybrid welding technique and addresses the realisation and the perspectives for practical applications. The experimental results demonstrate that the new process coupling enables welding of austenitic stainless steels in the thickness range between 3 mm and 8 mm at various weld geometries and joint configurations and at welding speeds exceeding 2 m/min. In addition it has been proven that the laser plasma powder arc welding (LPPAW) technique can also be applied to out-of-position conditions. Continuous advancement of the welding equipment ensures a high gap bridging ability and levelling of misalignment due to higher powder feeding rates. The recent development of a new plasma powder torch even provides a higher efficiency of powder feeding and guarantees smoth weld surfaces. Up to the present, the investigations demonstrated that the novel laser plasma powder hybrid welding technique offers all perspectives for application in pipe fabrication, ship building and offshore as well as transportation industry.
Neutron imaging has become a valuable tool for measuring hydrogen distributions qualitatively and quantitatively in metals. Hydrogen mass flow can be measured inside cm thick Steel samples with 10 s temporal resolution. Hydrogen accumulations around craclcs in embrittled iron samples can be visualized three-dimensionally. The gas pressure of hydrogen in crack cavities has been measured to be in the ränge of 5 MPa to 15 MPa. This quality of information allows new insights for the analysis of damage mechanisms on a micrometer scale, e.g., of hydrogen blistering. Further, this method is nondestructive and provides local information in situ and in three dimensions with a spatial resolution of 20 µm - 30 µm.
Um den wachsenden Anforderungen an den stofflichen und konstruktiven Leichtbau sowie den Forderungen nach Ressourceneffizienz Rechnung zu tragen, werden in vielen Industriebranchen zunehmend höherfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt. Weil gerade die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften der höherfesten Feinkornbaustähle durch den beim Schweißen aufgenommenen Wasserstoff mit steigender Festigkeit zunimmt, ist auf eine geeignete Wärmeführung zu achten. Für konventionelle MAG-Schweißprozesse liegen bereits Erfahrungen und Regelwerke zur Wärmeführung und entsprechende Wasserstoffgrenzwerte vor. Moderne Invertertechnik ermöglichte die Entwicklung modifizierter Sprühlichtbögen (mod. SLB). Im Vergleich zu konventionellen Lichtbogenprozessen wird ein äußerst kurzer und richtungsstabiler Lichtbogen, eine höhere Abschmelzleistung, ein größerer Kontaktrohrabstand und ein tieferer Einbrand realisiert. Neben den bekannten Vorteilen lassen außerdem reduzierte mögliche Nahtöffnungswinkel einen anderen Lagenaufbau und unterschiedliche Geometrien der einzelnen Schweißraupen erwarten. Jedoch fehlen hierzu Aussagen über den schweißverfahrensspezifisch eingetragenen Wasserstoff und die damit einhergehende Kaltrissgefahr. Hierzu lagen in der Industrie, besonders bei den KMU, kaum Kenntnisse vor und sollten deshalb als Ziel dieses Forschungsprojektes erarbeitet werden.
Die vergleichenden Untersuchungen mit konventionellem Übergangslichtbogen und mod. SLB mit angepasster Nahtkonfiguration erfolgten an freischrumpfenden Stumpfstoßverbindungen sowohl mit Massivdraht als auch Metallpulverfülldraht. Zur Durchführung der Untersuchungen wurde eine Methodik entwickelt, die es ermöglicht, im Schweißgut realer Verbindungsschweißungen die Wasserstoffkonzentration reproduzierbar zu bestimmen. Anhand der Analysen konnte gezeigt werden, dass die Schweißprozessparameter die in das Schweißgut eingebrachte Wasserstoffkonzentration in Einlagenschweißungen beeinflussen. Auch beim Mehrlagenschweißen gestaltet sich der Wasserstoffeintrag abhängig von den Schweißprozessparametern und ist auf den unterschiedlichen Lagenaufbau zurückzuführen. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit abgesenktem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen existieren. Außerdem beinhalten Schweißgüter aus Metallpulverfülldraht höhere Wasserstoffmengen als Massivdrahtschweißungen. Geeignete Wärmeführungen führten zu einer signifikanten Reduzierung der Wasserstoffkonzentration bei dem Einsatz der Nahtkonfiguration mit abgesenktem Nahtöffnungswinkel. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend. Die Vorstellung von Zwischenergebnissen in Normungsgremien erfolgten, um mittelfristig vor allem den KMU eine sichere Verarbeitung höherfester Feinkornbaustähle zu ermöglichen.
Die dargestellten Ergebnisse stellen einen wichtigen Beitrag zur sicheren Auslegung von Schweißkonstruktionen aus höherfestem Feinkornbaustahl dar und ermöglichen den KMU die technischen und wirtschaftlichen Vorteile der mod. SLB-Prozesse auszunutzen sowie unter Berücksichtigung der wasserstoffunterstützten Kaltrissbildung kostenintensive Nacharbeiten zu reduzieren.
In order to satisfy the growing requirements towards lightweight design and resource efficiency in modern steel constructions, e.g., mobile cranes and bridges, high-strength steels with typical yield strength ≥ 690 MPa are coming into use to an increasing extent. However, these steels require special treatment in welding. The susceptibility for degradation of the mechanical properties
in the presence of hydrogen increases significantly with increasing yield strength. In case of missing knowledge about how and the amount of hydrogen that is uptaken during welding, hydrogen-assisted cracking (HAC) can be a negative consequence.
Moreover, modern weld technology like the modified spray arc process enables welding of narrower weld seams. In this context,
a reduced number of weld beads, volume, and total heat input are technical and economical benefits. This work presents the influence of welding parameters on the diffusible hydrogen content in both (1) single-pass and (2) multi-layer welds. Different
hydrogen concentrations were detected by varied contact tube distance, wire feed speed, arc length, and varied arc type (transitional
arc and modified spray arc). The results show that all welding parameters have significant influence on the diffusible hydrogen concentration in the single-pass welds. By increasing the number of weld beads in case of multi-layer welding, the
hydrogen concentration has been reduced. Whereby, differences in hydrogen concentrations between both arc types are present.
Um den wachsenden Anforderungen an den stofflichen und konstruktiven Leichtbau sowie den Forderungen nach Ressourceneffizienz Rechnung zu tragen, werden in vielen Industriebranchen zunehmend höherfeste Feinkornbaustähle mit Streckgrenzen über 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt, da die Sensibilität gegenüber einer Herabsetzung der mechanischen Eigenschaften durch den beim Schweißen aufgenommenen diffusiblen Wasserstoff mit steigender Festigkeit zunehmen kann. In den vergleichenden Untersuchungen von konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen bei reduziertem Nahtöffnungswinkel konnte gezeigt werden, dass die Schweißprozessparameter die in das Schweißgut eingebrachte Wasserstoffkonzentration beeinflussen. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit reduziertem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen vorliegen. Diese können mit geeigneten Wärmeführungen signifikant reduziert werden. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend.
Hydrogen interaction with residual stresses in steel studied by synchrotron X-ray diffraction
(2014)
The residual stress state in a material has an important role in the mechanism of cracking, induced or assisted by hydrogen. In this contribution, the beamline EDDI in BESSY II instrument in Berlin was used in order to investigate the influence of hydrogen upon the residual stresses state existing in a Supermartensitic stainless steel sample. The method used for investigating the residual stresses is the sinus square ψ method. This method involves the usage of high energy X-ray diffraction in order to measure the residual stress state and magnitude. It was found that hydrogen presence has a significant influence upon the magnitude of the residual stresses, as its value decreases with high hydrogen content. This effect is reversible, as hydrogen desorbs from the sample the residual stress magnitude gains its initial value before hydrogen charging.
Hot crack prevention in materials production and processing is an essential prerequisite for welded component safety. The causes of hot cracking can ultimately be attributed to the occurrence of metallurgical effects and to structural loads. More than 140 hot cracking test procedures have hitherto been developed for determining the hot cracking resistance. In principle, they are divided in self-restraint and externally loaded hot cracking tests with diverse process variants. Only some of the hot cracking tests are international standardized. Although various factors are known that encourage or prevent hot cracking, it is often not possible even with defined welding conditions to draw immediate conclusions about the hot cracking resistance of a welded component alone from a metallurgical composition of the base and filler materials. Based on an evaluation of the existing theories relating to hot cracking susceptibility assessment, this study summarizes the major hot cracking test procedures and highlights the application limits of the test procedures by presenting overviews along with explanations. It shows that weld hot cracking tests can generally be used to rank materials, welding consumables, and welding conditions. The evaluation of hot cracking test results and of their transferability among one another and to real components always requires consideration of the close relationships between metallurgy, welding process, and parameters, respectively, and prevailing restraint conditions.
A 20 mm thick heat resistant 13CrMoV9-10 steel was welded using a multi-pass submerged arc tandem setup on a 3-D testing facility designed to prevent shrinkage both during the welding and the subsequent cooling to room temperature. The effects of variations in pre-heating and interpass temperatures on the local stresses were monitored by in situ measurement of reaction forces and bending moments during welding and the subsequent dehydrogenation heat treatment. The austenite to bainite transformation and its effects on the overall loads were monitored through the use of a high sampling rate. Increasing the pre-heating and interpass temperatures led to a rise in reaction forces and bending moments. The bending moments originated from the eccentric force transmission over the backing, with a concomitant risk of fracture, especially in the critical root zone. Although the pre-heating and interpass temperatures had a strong effect on the reaction forces, their effect on the bending moments upon cooling to room temperature was negligible.
High-strength low-alloyed (HSLA) steels with yield strength ≥ 690 MPa have increasing importance in steel construction and civil engineering. However, weld processing of those steels is a major challenge. The susceptibility for degradation of mechanical properties of weld joints significantly increases in presence of hydrogen and can result in hydrogen assisted cracking (HAC). Generally, risk for HAC increases with increasing yield strength of HSLA steels. To minimize the incidence of HAC, it is essential to gain knowledge about both the (1) absorbed hydrogen amount and its distribution in the weld seam and (2) options to lower
the amount of introduced hydrogen. Existing standards recommend heat treatment procedures (interpass temperature or post weld heat treatment) to reduce the diffusible hydrogen concentration in weldments. In this context, different weld seam geometries should be considered. For HSLA steel fabrication weld processing with seam opening angles of 45° to 60° is typical. Modern weld technologies allow welding with seam opening angles of 30° - reduced welding time and costs. In the present study, the hydrogen distribution in multi-layer welds of a 960 MPa HSLA steel was analysed. Influence of different seam opening angles as well as heat input, interpass temperature and post weld heat treatments were investigated. The welded samples were quenched in ice water immediately after welding and subsequently stored in liquid nitrogen. After defined warming up, small specimens were machined from the weld seam by water jet cutting. The diffusible hydrogen concentration was measured by carrier gas hot extraction with coupled mass spectrometer. The results showed, that low heat input and post weld heat treatment procedures can lower hydrogen concentrations in welds. Furthermore, a gradient of the hydrogen concentration was
identified with increasing weld pool depth. By varying the seam opening angles different hydrogen concentrations were
measured.
Ausgehend vom derzeit vorrangigen Einsatz in Mobilkranen, kommen höherfeste Feinkornbaustähle mit Streckgrenzen ab 960 MPa zunehmend auch in anderen modernen Stahlkonstruktionen zur Anwendung. Dies ist aufgrund aktueller Forderungen nach Energie- und Ressourceneffizienz im Sinne des konstruktiven Leichtbaus vielfach notwendig. Die Verwendung höherfester Stähle sowie deren schweißtechnische Verarbeitung, insbesondere in sicherheitsrelevanten Tragstrukturen, erfordert ein tiefgreifendes Verständnis der Zusammenhänge zwischen Schweißverfahren, Wärmeeinbringung, Abkühlbedingungen sowie den daraus resultierenden metallurgischen Vorgängen in der Schweißnaht und den nahtnahen Bereichen. Vorwiegend werden höherfeste Güten mittels MAG-Prozess geschweißt. Bedeutende Fortschritte in der Regelungstechnik führten unter den Herstellern von Schweißstromquellen in den letzten Jahren zur Entwicklung zahlreicher modifizierter Sprühlichtbogenprozesse (mod. SLB). Diese Prozesse ähneln sich in ihren Eigenschaften und ermöglichen die bekannten positiven Aspekte, wie Einsparung an Schweißzusatz sowie Schweiß- und Rüstzeit aufgrund der Möglichkeit reduzierter Nahtöffnungswinkel. Der mod. SLB bedingt zusammen mit einer anderen Nahtgeometrie veränderte Naht- und Schweißraupenquerschnitte sowie einen abweichenden Lagenaufbau. Diese wirtschaftlich-technisch attraktive Möglichkeit reduzierter Nahtöffnungswinkel findet in den Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle unter Vermeidung von Kaltrissbildung bisher keine Berücksichtigung. Dabei gilt es, gerade die Interaktion der Haupteinflussgrößen auf die Kaltrissbildung unter reduziertem Nahtöffnungswinkel zu betrachten. Im Rahmen zweier AiF-Forschungsvorhaben (IGF-Nr. 17.978 N, 18.596 BR) wurde daher der Einfluss der Wärmeführung anhand vergleichender Mehrlagenschweißungen mittels konventionellem Übergangslichtbogen und mod. SLB mit angepasster Nahtkonfiguration auf schweißbedingte Beanspruchungen sowie auf die Wasserstoffkonzentration im Schweißgut untersucht.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system specifically developed for this purpose with a maximum capacity of 2 MN are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be simulated and quantified within the system. Additionally, X-ray diffraction can be applied to determine the resulting local residual stress distribution precisely with high spatial resolution. Two examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. It was possible to clarify why elevated working temperatures significantly increase the bending stresses in the welded joint and therefore the tensile residual stresses in the heat affected zone (HAZ). The effect of a heat treatment applied under mechanical stress resulting from welding is demonstrated by the example of a creep resistant steel. Reheat cracking is significantly increased in this case compared to small scale laboratory based tests.
Heute werden in Stahlkonstruktionen zunehmend hochfeste Baustähle (Streckgrenze ≥ 960 MPa) eingesetzt. Daher sind auch in Schweißnähten solche hohen Festigkeiten gefordert. Jedoch können hohe Eigenspannungen aufgrund geringerer plastischer Dehnungsreserven in diesen Schweißnähten die Sicherheit der Bauteile vermindern. Diese sind insbesondere im Zusammenhang mit Wasserstoff und Härtegefügen risskritisch. Niedrige Bauteilbeanspruchungen und Kosteneinsparungen lassen sich heutzutage mit modernen fokussierten Lichtbogenvarianten und engeren Nahtspalten erreichen. Die vorliegende Studie zeigt allerdings, dass diese modernen Schweißprozesse und die angepasste Nahtgeometrie höhere Wasserstoffkonzentrationen und signifikant gesteigerte oberflächennahe Zugeigenspannungsniveaus bedingen. Anhand mehrlagiger Schweißversuche an S960QL unter Variation von Wärmeführung, Lichtbogenvariante und Nahtöffnungswinkel wurden die Effekte und Wechselwirkungen unter Zuhilfenahme von Eigenspannungsanalytik mittels Röntgendiffraktometrie und Wasserstoffanalytik mittels Trägergasheißextraktion systematisch untersucht. Das Schweißgefüge führte unter kritischer mechanischer Beanspruchung und erhöhtem Gehalt an diffusiblem Wasserstoff insbesondere bei geringem Nahtöffnungswinkel und fokussiertem Lichtbogen zu einer deutlichen Ausbildung von Mikrorissen. Die Mikrorisse führten teils zu einer makroskopischen Ausprägung. Durch Analysen zur Nachwärmung aus der Schweißwärme heraus konnten suffiziente Wärmeführungsparameter für eine effektive Prävention solcher Risse erarbeitet werden. Die vorliegende Arbeit zeigt anhand des Interaktionssystems bei der wasserstoffunterstützten Kaltrissbildung Gefüge-Beanspruchung-Wasserstoff, welche Wärmeführungs- und Schweißparameter sich für die hochfesten Feinkornbaustähle zur Kaltrissvermeidung eignen.
High-strength low-alloyed (HSLA) steels with yield strength ≥ 690 MPa are gaining popularity in civil engineering and construction of heavy vehicles. With increasing yield strength, the susceptibility for degradation of the mechanical properties in the presence of diffusible hydrogen, i.e., hydrogen-assisted cracking (HAC), generally increases. HAC is a result of the critical interaction between local microstructure, mechanical load, and hydrogen concentration. In existing standards for welding of HSLA-steels, recommendations including working temperatures and dehydrogenation heat treatment (DHT) are given to Limit the amount of introduced hydrogen during welding. These recommendations are based on investigations into conventional arc welding processes. In the past decade, modern weld technologies were developed to enable welding of narrower weld seams with V-grooves of 30°, e.g., the modified spray arc process. In that connection, a reduced number of weld runs and weld volume are important technical and, economic benefits. In the present study, the hydrogen distribution in S960QL multi-layer welds with thickness of 20 mm was analyzed. The influence of different weld seam opening angles, heat input, working temperature and DHT were investigated. The results show that weldments with narrow grooves contained an increased amount of diffusible hydrogen. Hydrogen concentration has been reduced by decreasing both the heat input and working temperature. Hydrogen-free weldments were only achieved via subsequent DHT after welding. Furthermore, hydrogen distribution was experimentally determined across the weld seam thickness in HSLA gas metal arc welded multi-layer welds for the first time.
High-strength steels are increasingly applied in modern steel constructions to meet today’s lightweight requirements. Welding of these steels demands a profound knowledge of the interactions between the welding process, cooling conditions, heat input, and the resulting metallurgical occurrences in the weld and its vicinity. Additionally, welding stresses may be detrimental for the safety and performance of high-strength steel component welds during fabrication and service, especially due to the high yield ratio. For a development of strategies to adjust welding heat control, all these effects should be considered, to reach a complete exploitation of the high-strength steel potential. In recent researches at BAM, multilayer GMAW experiments were performed with high-strength steels, in which cooling conditions and resulting microstructure were analyzed for varied heat control parameters. The application of a unique 3d-operating testing facility and X-ray diffraction measurements allowed the analysis of local stresses in the weld while welding and cooling under component relevant shrinkage restraints. As a result, correlations between material behavior, welding, and cooling condition and the arising multi-axial stresses and forces were found. Based on this study, statements for the development of adapted heat control concepts were derived, which are presented by means of specific analysis examples.
Die Vermeidung von Heißrissen beim Schweißen ist für die Sicherheit geschweißter Komponenten unerlässlich. Die Entstehung von Heißrissen wird durch die komplexe Interaktion von Schweißprozess, Metallurgie und der konstruktiven Umgebung beschrieben. Bislang wurden mehr als 140 Heißrisstests entwickelt, um die Neigung gegenüber einer Rissbildung festzulegen. Grundsätzlich werden diese in selbstbeanspruchende und fremdbeanspruchte Heißrisstests eingeteilt. Der Vortrag gibt einen Überblick über Forschungsthemen der BAM, welche sich in den letzten Jahren hauptsächlich mit den metallurgischen als auch mit den konstruktiven Einflüssen auf die Rissbildung beschäftigt haben. Von austenitischen und ferritischen Werkstoffen, über neuentwickelte LTT-Legierungen bis hin zur in-situ Radiographie zur Überwachung des Risswachstums während des Schweißens wird ein breites Forschungsspektrum aufgezeigt. Zum Abschluss ist ein Ausblick für zukünftige Forschungsfelder gegeben. Diese Arbeiten konzentrieren sich auf die zwei- und dreidimensionale bildliche Charakterisierung von (Mikro-)Heißrissen in innovativen Werkstoffen zur Erweiterung bestehender Modellvorstellungen zum Rissphänomen.
High-strength steels with yield strengths ≥ 690 MPa are becoming increasingly significant for modern steel constructions. Both quenched and tempered (QT) high-strength steels and steels produced by the thermo-mechanically controlled process (TMCP) are currently available. TMCP-steels are usually provided with a typical mill scale. Apart from the manufacturing process these steels differ also in their chemical composition. The influence of these differences are investigated here with focus on the residual stresses formed during TIG welding. Bead on plate welds have shown characteristic residual stress distributions depending on the type of steel as well as on the heat input and preheat temperature. The following work demonstrates that the fluid flow, induced by the elements present in the mill scale, leads to a deeper penetration of the material. This can also lead to increased residual stresses in the surface of the weld and the HAZ. Furthermore, higher heat input and preheat temperature can induce higher tensile residual stresses − which are evident in the present study.
Beside quenched and tempered (QT) high strength steels advanced technologies in steel manufacturing provide steels produced by the thermo-mechanical controlled process (TMCP) with yield strength of 960 MPa. These steels differ in the carbon and micro-alloying element content. With variation of heat control TIG-welded dummy seams on both steel types were performed. Analyses concerning microstructure and residual stress evolution due to welding showed typical stress distributions according to common concepts. Yet, the TMCP-steel shows higher residual stresses than the QT-steel.
In modernen Schweißkonstruktionen des Stahl- und Ingenieurbaus werden zunehmend hochfeste Feinkornbaustähle eingesetzt. Grundsätzlich sind während der schweißtechnischen Verarbeitung hochfester Stahlgüten aufgrund ihres speziellen Gefüges und wegen ihres vergleichweise hohen Streckgrenzenverhältnisses engere Verfahrensgrenzen einzuhalten, als bei Stählen mit niedrigerer Festigkeit. Die Sicherheit von hochfesten Schweißverbindungen erfordert präzise Kenntnisse über die Höhe und Verteilung der schweißbedingten Beanspruchungen, da sie die erreichbare Tragfähigkeit unmittelbar beeinflussen. In den Untersuchungen wurde der Einfluss der Wärmeführung in Form der Zwischenlagentemperatur und Streckenenergie auf die Eigenspannungsausbildung und Gesamtbeanspruchung in hochfesten Schweißverbindungen ermittelt. Zur Berücksichtigung einer äußeren Bauteilsteifigkeit wurden die Proben in Nahtquerrichtung unter einem definierten Einspanngrad in einer speziellen Prüfanlage (CTW-Test) mehrlagig geschweißt. Es zeigte sich beispielsweise, dass insbesondere die Zwischenlagentemperatur einen direkten Einfluss auf die globalen Reaktionsspannungen hat. Ferner bedingt die Erhöhung der Wärmeführung ein deutliches Anheben der Zugeigenspannungen im Bereich des Schweißgutes.
Spectacular failure cases of fossil power stations in the recent years exhibited severe cracking in T24 welds. The results show that hydrogen-assisted cracking up to 200 °C cannot be excluded. Hence, it is important to gain a basic understanding on how hydrogen might affect the basic material properties in the respective weld microstructures. The present study focuses on hydrogen degradation of the respective weld microstructures, i.e., the weld metal and the coarse grained heat affected zone, where actually cracking appeared in practice. Tensile tests were carried out for coarse grain heataffected zone (CGHAZ) and the weld metal in uncharged and electrochemically hydrogen-charged condition. It turned out that both microstructures show distinct tendency for gradual degradation of mechanical properties in the presence of increasing hydrogen concentration. Already for a hydrogen concentration about and above 2 ml/100 g Fe, a significant ductility reduction has been observed. SEM investigations revealed that the fracture topography changes from ductile topography in uncharged condition to intergranular topography for the CGHAZ and to ductile-brittle mix for the weld metal (WM) in hydrogen charged condition. Ti-rich inclusions were identified as central regions of quasi-cleavage fracture areas in the WM. An approximation procedure is applied to quantify the degradation intensity.
Realization and safe operation of modern welded structures are progressively requiring for base and filler materials to cope with continually increasing loads, Analyses with a view to crack prevention therefore need to accommodate particularly the structural design (restraint intensity) and the thermomechanical effects in terms of stresses introduced during welding, Against this background, multi-run welding experiments were carried out in an IRC - (Instrumented Restraint Cracking) Test under defined restraint intensity in order to examine the influence of heat control (preheating and interpass temperatures) on the weldinq-specific forces and stresses, The experiments revealed significant rises in the reaction force and stress after welding with increasing preheating and interpass temperature, Furthermore, various concepts for calculating the preheating temperature are discussed, It is demonstrated that the hitherto existing concepts for high-strength finegrained structural steels can lead to divergent results.
Hydrogen generally causes lattice distortions and phase transformations when introduced into a metallic crystal lattice. For the investigations reported in this contribution, hydrogen thermal desorption analysis has been carried out to observe the influence of hydrogen desorption on the lattice of super martensitic stainless steel during continuous heating. The lattice expansion parameter and the phase transformations have been monitored during the thermal desorption process, and the influence of hydrogen on such characteristics has been evaluated. It was found that hydrogen has a significant influence on both the lattice parameter and on the thermal expansion. However, hydrogen has no influence on phase transformation during thermal desorption. The hydrogen's desorption behavior in this process was also observed and it turned out that hydrogen desorbs in two stages, i.e., firstly diffusible hydrogen and trapped hydrogen afterward.
This study provides an in-depth survey of current technologies and applications for assessing the cold cracking susceptibility of welded joints. From the large variety of existent cold cracking test procedures, the most important and internationally established tests are presented and evaluated in terms of their usefulness and application limits. According to the type of loading, the test procedures are classified into self-restraint and externally loaded tests. Apart from the merely metallurgical weldability tests for determining the cracking susceptibility of base materials, filler materials and weld metals, advanced test methods are presented for evaluating the cold cracking susceptibility of welded components. A salient point brought out in this respect is the fact that the level of external loading in such component weld tests can be applied independently of the welding parameters, reproducing as realistically as possible the practical application case, i.e. the level of the restraint intensity. This study includes a summarized comparison of the cold cracking procedures. It is emphasized that highly accurate consideration and reproduction of the design-specific stiffness conditions is essential in the tests for assessing the cold cracking behaviour of welded joints. Therefore, various numerical analyses are presented in a final chapter for calculating the restraint intensity as a definitive factor affecting cold cracking.
To better understand the mechanism of hydrogen assisted cracking (HAC), it is important to investigate the 3D structure of the cracks non-destructively. Since, cracks introduced by HAC are usually very small, conventional x-ray imaging methods often lack the required spatial resolution.
However, the detection of those cracks can be enhanced by taking advantage of refraction at interfaces within the sample.
To image this refractive deflection we employ analyser based imaging (ABI). In this work we aim at proving the enhanced crack detection of ABI by investigating an alluminum alloy weld.
Effects of Preheating and Interpass Temperature on Stresses in S 1100 QL Multi-Pass Butt-Welds
(2008)
In situ analysis of hydrogen behaviour in stainless steels by high energy synchrotron radiation
(2011)
Hydrogen generally causes lattice distortions and phase transformations when introduced into a metal matrix. The present contribution provides a report of first in situ investigations of hydrogen effects on the lattice of the austenite and the martensite phase in a supermartensitic stainless steel using hard synchrotron radiation for respective energy dispersion diffraction measurements. Lattice distortions, such as the planar spacing expansion, have been monitored during the complete hydrogen effusion process over 24 h and are directly correlated to the dissolved hydrogen in the metal matrix. Among other results, it turned out that hydrogen at the introduced concentration level causes a reversible lattice expansion and after hydrogen effusion the lattice nearly regained its original dimensions. Hydrogen much more significantly affects the austenite phase with respect to lattice expansion than the martensite phase, but no phase transformations occur during the hydrogen desorption process.
3D Crack analysis in hydrogen charged lean duplex stainless steel with synchrotron refraction CT
(2016)
Hydrogen in metals can cause a degradation of the mechanical properties, the so-called hydrogen embrittlement. In combination with internal stresses, hydrogen assisted cracking (HAC) can occur. This phenomenon is not completely understood yet. To better characterise the cracking behaviour, it is important to gain information about the evolution of the 3D crack network. For this purpose samples of lean duplex stainless steel were loaded with hydrogen by means of electrochemical charging and investigated by means of synchrotron refraction CT and SEM fractography after uniaxial tensile loading. Synchrotron refraction CT is an analyser-based imaging (ABI) technique. It uses a Si (111) single crystal as analyser, which is placed into the beam path between sample and detector. According to Bragg’s law only incident x-rays within a narrow range around the Bragg-angle are diffracted from the analyser into the detector. Hence, the analyser acts as an angular filter for the transmitted beam. This filtering allows to turn the refraction and scattering of x-rays into image contrast. Refraction occurs at all interfaces, where the density of the material changes and is more sensitive to density changes than the attenuation. Therefore, it is possible to detect smaller cracks than with classical x-ray imaging techniques, like CT, with comparable spacial resolution. It also visualises the 3D structure of the cracks and gains quantitative information about their morphology and distribution. Since cracks introduced by HAC are usually very small and have a small opening displacement, synchrotron refraction CT is expected to be well suited for imaging this cracking mechanism and can be a valuable tool to characterise the formation and the evolution of a 3D crack network.
Effect of cooling rate on microstructure and properties of microalloyed HSLA steel weld metals
(2015)
Two high strength Nb/Ti microalloyed S690QL steels were welded with identical filler material, varying welding parameters to obtain three cooling rates: slow, medium and fast cooling. As cooling rate increased, the predominantly acicular ferrite in Nb weld metal (WM) is substituted by bainite, with a consequence of obvious hardness increase, but in Ti WM, no great variation of acicular ferrite at all cooling rates contributed to little increment of hardness. The transition between bainite and acicular ferrite has been analysed from the point view of inclusions characteristics, chemical composition and cooling rate. Excellent Charpy toughness at 233 K was obtained with acicular ferrite as predominantly microstructure. Even with bainite weld of high hardness, the toughness was nearly enough to fulfill the minimal requirements. WM for Ti steel showed to be markedly less sensitive to the variations of cooling rate than that for Nb steel.
Höherfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa neigen bei der schweißtechnischen Fertigung zur Bildung von wasserstoffunterstützten Kaltrissen. Diese Mikrorisse entstehen aus der kritischen Interaktion von lokalem risskritischem Gefüge, lokal erhöhter Wasserstoffkonzentration und lokal erhöhter Beanspruchung bzw. Dehnung. Aktuell gültigen Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle sind Anweisungen zu entnehmen, um das Risiko einer Kaltrissbildung zu minimieren. Die Weiterentwicklung der Werkstoffe (Legierungskonzepte) und neuer Lichtbogenprozesse zur Verringerung der Nahtöffnungswinkel bei gleichzeitiger Erhöhung der Abschmelzleistung (modifizierter Sprühlichtbogen) brachten jedoch auch neue Fragen hinsichtlich der Wasserstoffmenge in der Schweißverbindung nach dem Schweißen und der Kaltrissempfindlichkeit mit sich. Mikrolegierungselemente (V, Nb und Ti) bedingen bspw. eine verlangsamte Wasserstoffdiffusion. Schweißverbindungen unter reduziertem Nahtöffnungswinkel beinhalten höhere Wasserstoffkonzentrationen. Dieser Beitrag zeigt den Einfluss von Einbrandprofil (höhere Abschmelzleistung) auf die Kaltrissempfindlichkeit an einem höherfesten Feinkornbaustahl mit artähnlichem mikrolegierten Schweißzusatzwerkstoff anhand des fremdbeanspruchten Implant-Tests.
Various test methods are available for assessing the susceptibility of materials to solidification cracking during welding. In the widely used Varestraint test, the crack length is selected as a criterion as a function of the applied bending strain.
Unfortunately, the crack length does not characterize the material behavior alone but depends to varying degrees on the individual test parameters used, which makes the interpretation of the results difficult. In addition, the crack length is not comparable under different test conditions. To overcome these disadvantages, we have developed a novel evaluation methodology that decouples the machine influence from the material behavior. The measured crack length is related to the maximum possible value specified by welding speed and deformation time. This relative crack length is calculated numerically, considering the orientation of the cracks. Experiments on two high-alloy martensitic welding consumables show that, in contrast to the conventional evaluation, a comparison of different welding parameters becomes possible. Furthermore, the strain rate proved to be a suitable crack criterion in agreement with Prokhorov's hot cracking model.
Wasserstoff kann eine Rissbildung u.U. auch noch nach Tagen in der Schweißnaht bewirken. Dabei stellen höherfeste Stähle etablierte Kaltrissprüftests vor Herausforderungen. Generell nimmt die zur Rissvermeidung tolerierbare Wasserstoffkonzentration mit zunehmender Festigkeit der Werkstoffe ab. Zudem verändern weiterentwickelte Schweißverfahren die Nahtgeometrie und Wärmeeinbringung und die Ausbildung risskritischer Mikrostrukturen (z.B. Wärmeeinflusszone). Am Beispiel des Implant- und Tekken-Tests werden die Einsatz- u. Anwendungsgrenzen bewertet. Zu berücksichtigen ist, dass beim Schweißen eine äußere mechan. Beanspruchung durch bauteilspezifische Steifigkeitsverhältnisse wirksam ist. Zusätzlich werden weiterführende Prüfverfahren zur Bestimmung der Wasserstoffkonzentration und -diffusion in Schweißnähten vorgestellt, wie die Trägergasheißextraktion (TGHE) für die Ermittlung der Wasserstoffkonzentration (ISO 3690) oder Hochtemperaturdiffusionskoeffizienten.
Diese Werte sind für die schweißtechnische Praxis von großer Bedeutung, um Haltezeiten z.B. für das Wasserstoffarmglühen abzuleiten.
While the problem of the identification of mechanisms of hydrogen assisted damage has and is being thoroughly studied, the quantitative analysis of such damage still lacks suitable tools. In fact, while, for instance, electron microscopy yields excellent characterization, the quantitative analysis of damage requires at the same time large field-of-views and high spatial resolution. Synchrotron X-ray refraction techniques do possess both features. In this work, we show how synchrotron X-ray refraction computed tomography (SXRCT) can quantify damage induced by hydrogen embrittlement in a lean duplex steel, yielding results that overperform even those achievable by synchrotron X-ray absorption computed tomography. As already reported in literature, but this time using a non-destructive technique, we show that the hydrogen charge does not penetrate to the center of tensile specimens. By the comparison between virgin and hydrogen-charged specimens, we deduce that cracks in the specimen bulk are due to the rolling process rather than hydrogen-assisted. We show that (micro)cracks propagate from the surface of tensile specimens to the interior with increasing applied strain, and we deduce that a significant crack propagation can only be observed short before rupture.
High-strength steels with yield strength of 960 MPa are susceptible to hydrogen-assisted cracking (HAC) during welding processing. In the present paper, the implant test is used to study HAC in a quenched and tempered steel S960QL and a high-strength steel produced by thermo-mechanical controlled process S960MC. Welding is performed using the gas metal arc welding process. Furthermore, diffusible hydrogen concentration (HD) in arc weld metal is determined. Based on the implant test results, lower critical stress (LCS) for complete fracture, critical implant stress for crack initiation, and embrittlement index (EI) are determined. At HD of 1.66 ml/100 g, LCS is 605 MPa and 817 MPa for S960QL and S960MC, respectively. EI is 0.30 and 0.46 for S960QL and S960MC, respectively. Fracture surfaces of S960QL show higher degradation with reduced deformation. Both, higher EI of S960MC and fractography show better resistance to HAC in the HAZ of S960MC compared to S960QL.
Einfluss von Konstruktion und Wasserstoff auf die Kaltrissbildung hochfester Feinkornbaustähle
(2020)
Der konstruktive Leichtbau erfordert den zunehmenden Einsatz hochfester Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa. Neben den durch die Wandstärkenreduzierung erreichbaren Einsparungen an Ressourcen und Fertigungszeit lässt sich eine weitere Minimierung der Schweißzeit und -kosten mittels abgesenkter Schweißnahtvolumina erreichen. Hierzu wurden moderne Lichtbogenprozesse, wie bspw. der modifizierte Sprühlichtbogen (Mod.SLB), mit erhöhter Abschmelzleistung entwickelt, mit denen auch enge Nahtspalte bzw. Nahtöffnungswinkel geschweißt werden können. Hochfeste Verbindungen unterliegen zunehmend erhöhten Anforderungen in Bezug auf die schweißtechnische Verarbeitung und der resultierenden Bauteilperformance und sicherheit. Dies gilt insbesondere beim Bauteilschweißen mittels solcher Hochleistungsverfahren in Verbindung mit engen Nahtspalten. In der vorliegenden Arbeit soll dieser Herausforderung durch Klärung der Einflüsse auf die Kaltrissbildung bei einem hochfesten Feinkornbau-stahl S960QL Rechnung getragen werden. Für die Kaltrissprüfung werden entsprechende adaptierte Proben analog dem selbstbeanspruchenden TEKKEN-Test verwendet und hinsichtlich Rissbildung, Gefüge, Gehalt an diffusiblem Wasserstoff und Eigenspannungen analysiert. Die Variation der Nahtöffnungswinkel der Prüfnähte erfolgt zwischen 30° und 60°. Zur Vermeidung wasserstoffunterstützter Kaltrissbildung wird die Wirksamkeit einer Nachwärmprozedur aus der Schweißwärme heraus untersucht. Als Ergebnis zeigen die Schweißgüter, die an reduziertem Nahtöffnungswinkel erzeugt wurden, im Mittel etwas höhere Wasserstoffkonzentrationen. Zudem ist an diesen Schweißgütern eine vermehrte Mikro- als auch Makrorissbildung festzustellen. An allen Proben, die nicht nachgewärmt wurden, treten Kerbrisse aufgrund von Kaltrissbildung auf, deren Vermeidung sich durch ein Nachwärmen unmittelbar nach dem Schweißen als besonders effektiv darstellte.
Von der Anwendung ins Prüflabor: Maßstabsgetreues Bewerten von Spannungen in geschweißten Bauteilen
(2019)
Eigenspannungen sind von zentraler Bedeutung für die Performance geschweißter Bauteile. Die Bewertung schweißbedingter Beanspruchungen im Labormaßstab ist oft nicht zielführend. Reale Bauteilschweißungen weisen geometrisch und konstruktiv bedingt meist divergente Wärmeableitungs- und Einspannbedingungen auf. Dadurch lassen sich häufig nur eingeschränkt Aussagen über Eigenspannungshöhen, -verteilungen und die wesentlichen Einflussfaktoren treffen. Dies führt oftmals zur eher konservativen Konstruktionsauslegung und damit zu einer geringerenRessourcen- und Energieeffizienz. Dieser Beitrag widmet sich den Bestrebungen, reale Randbedingungen beim Bauteilschweißen in das Labor zu übertragen. Es werden die Möglichkeiten eines speziell für diesen Zweck an der BAM entwickelten Prüfsystems mit einer maximalen Tragkraft von 2 MN aufgezeigt. Durch die konstruktive Gestaltung der Anlage lassen sich in Schweißversuchen schweißbedingte Beanspruchungen nachbilden und die komplexen Einflüsse und Wechselwirkungen durch Schweißprozess, Bauteilgeometrie und -konstruktion sowie durch die eingesetzten Grund- und Zusatzwerkstoffe quantifizieren. Darüber hinaus können mittels Röntgenbeugung die resultierenden lokalen Eigenspannungen präzise und mit hoher Ortsauflösung bestimmt werden. Anhand von Beispielen wird die Nachbildung realer Produktionsbedingungen im Labor erörtert und gezeigt, wie die Spannungen beim Schweißen hochfester Baustähle von konstruktiven, werkstoff- und prozessseitigen Randbedingungen abhängen.
So wurde geklärt, wie erhöhte Arbeitstemperaturen zum signifikanten Anstieg der Beanspruchungen führen.
The subject of this study is how, and to what extent, Varestraint/Transvarestraint test results are influenced by both testing parameters and characteristics of evaluation methods. Several different high-alloyed martensitic LTT (low Transformation temperature) filler materials, CrNi and CrMn type, were selected for examination due to their rather distinctive solidification cracking behaviour, which aroused interest after previous studies. First, the effects of different process parameter sets on the solidification cracking response were measured using standard approaches. Subsequently, microfocus X-ray computer tomography (μCT) scans were performed on the specimens. The results consistently show sub-surface cracking to significant yet varying extents. Different primary solidification types were found using wavelength dispersive X-ray (WDX) analysis conducted on filler metals with varying Cr/Ni equivalent ratios. This aspect is regarded as the main difference between the CrNiand CrMn-type materials in matters of cracking characteristics. Results show that when it comes to testing of modern highperformance alloys, one set of standard Varestraint testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
The avoidance of failures during the fabrication or operation of petrochemical reactors made of creep-resistant, low-alloy steels as 13CrMoV9-10 requires still research despite over 60 years of international investigations in the field of stress relief cracking. The quality of modern base materials and filler metals leads to the fact that previously known crack causes, such as impurities of S or P, recede into the background. Rather, the causes are increasingly to be found in the fabrication process. Investigations on the influence of heat control on the stresses in welded components and thus on the stress relief cracking sensitivity under realistic manufacturing conditions are not yet available. This work is subdivided in two parts. Part 1 of this study focused on the effect of heat control during submerged arc welding on the stresses. For this purpose, a testing facility was applied, which allows to observe the forces and moments accumulating during welding or heat treatment in a component-like specimen under shrinkage restraint. The stress acting in the specimen increases with higher preheat/interpass temperatures and higher heat input. During the heat treatment, the stresses are relieved. Nevertheless, cracks are formed already during heating. The total crack length correlates with the heat input.
Welding of 13CrMoV9-10 vanadium steel requires care due to an increased susceptibility to stress relief cracking during post weld heat treatment. Previous research into the crack formation in creep-resistant steels has focused on thermal and metallurgical factors; however, little knowledge has been gathered regarding the crack formation during post weld heat treatment considering real-life restraint conditions. This work is subdivided in two parts. Part I showed that an increasing heat input during submerged arc welding under restraint led to an increasing stress level in the joint prior to the post weld heat treatment. The magnitude of stress relief cracking observed in the heat-affected zone after the post weld heat treatment is affected by the heat input. In Part II of this work, the cracks and the associated microstructure which occurred under restraint were studied. The application of a Special acoustic emission analysis indicated that the cracks formed in a temperature range between 300 and 500 °C during the post weld heat treatment. The toughness in the heat-affected zone of the restrained welds was affected by the welding heat input.
Microstructural analyses of all specimens revealed accelerated aging due to precipitation of carbides during post weld heat treatment under restraint.
Modern arc processes, such as the modified spray arc (Mod. SA), have been developed for gas metal arc welding of high-strength structural steels with which even narrow weld seams can be welded. High-strength joints are subjected to increasingly stringent requirements in terms of welding processing and the resulting component performance. In the present work, this challenge is to be met by clarifying the influences on hydrogen-assisted cracking (HAC) in a high-strength structural steel S960QL. Adapted samples analogous to the self-restraint TEKKEN test are used and analyzed with respect to crack formation, microstructure, diffusible hydrogen concentration and residual stresses. The variation of the seam opening angle of the test seams is between 30° and 60°. To prevent HAC, the effectiveness of a dehydrogenation heat treatment (DHT) from the welding heat is investigated.
As a result, the weld metals produced at reduced weld opening angle show slightly higher hydrogen concentrations on average. In addition, increased micro- as well as macro-crack formation can be observed on these weld metal samples. On all samples without DHT, cracks in the root notch occur due to HAC, which can be prevented by DHT immediately after welding.
For higher operational temperatures and pressures required in petrochemical plants, the modified 13CrMoV9-10 steel was developed providing high resistance against creep and compressed hydrogen. Extreme care during the welding procedure is necessary for this steel, attributed to low toughness, high strength in as-welded state, and increased susceptibility to stress relief cracking (SRC) during post-weld heat treatment (PWHT). Previous research of SRC in creep-resistant steels discussed mainly thermal and metallurgical factors. Few previous findings addressed the influences of welding procedure on crack formation during PWHT considering real-life manufacturing conditions. These investigations focus on effects of welding heat control on stresses during welding and subsequent PWHT operations close to realistic restraint and heat dissipation conditions using a special 3D testing facility, which was presented in parts I and II of this contribution. Part III addresses investigations on residual stress evolution affecting crack formation and discusses the transferability of results from large-scale testing to laboratory-scale. Experiments with test set-ups at different scales under diverse rigidity conditions and an assessment of the residual stresses of the weld-specimens using X-ray (surface near) and neutron diffraction analysis (bulk) were performed. This study aims to provide a way of investigating the SRC behaviour considering component-specific residual stresses via small-scale testing concepts instead of expensive weld mock-ups.
High-strength structural steels are used in machine, steel, and crane construction with yield strength up to 960 MPa. However, welding of these steels requires profound knowledge of three factors in terms of avoidance of hydrogen-assisted cracking (HAC): the interaction of microstructure, local stress/strain, and local hydrogen concentration. In addition to the three main factors, the used arc process is also important for the performance of the welded joint. In the past, the conventional transitional arc process (Conv. A) was mainly used for welding of high-strength steel grades. In the past decade, the so-called modified spray arc process (Mod. SA) has been increasingly used for welding production. This modified process enables reduced seam opening angles with increased deposition rates compared with the Conv. A. Economic benefits of using this arc type are a reduction of necessary weld beads and required filler material. In the present study, the susceptibility to HAC in the heat-affected zone (HAZ) of the high-strength structural steel S960QL was investigated with the externally loaded implant test. For that purpose, both Conv. A and Mod. SA were used with same heat input at different deposition rates. Both conducted test series showed same embrittlement index “EI” of 0.21 at diffusible hydrogen concentrations of 1.3 to 1.6 ml/100 g of arc weld metal. The fracture occurred in the HAZ or in the weld metal (WM). However, the test series withMod. SA showed a significant extension of the time to failure of several hours compared with tests carried out with Conv. A.
The article "Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: Part I - Effect of heat control on welding stresses and stress relief cracking" was originally published in the journal "Welding in the world" Online First without Open Access. After publication in volume 64, issue 5, page 807-817 the authors decided to opt for Open Choice and to make the article an Open Access publication. Therefore, the copyright of the article has been changed to The Author(s) 2020 and the article is forthwith distributed under the terms of the Creative Commons Attribution Attribution 4. 0 International License.
The article "Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: Part II - Mechanisms of stress relief cracking during post weld heat treatment" was originally published in the journal "Welding in the world" Online First without Open Access. After publication in volume 64, issue 5, page 819-829 the authors decided to opt for Open Choice and to make the article an Open Access publication. Therefore, the copyright of the article has been changed to The Author(s) 2020 and the article is forthwith distributed under the terms of the Creative Commons Attribution Attribution 4. 0 International License.
Für eine nachhaltige und ressourceneffiziente Fertigung von Windkraftanlagen ist der Einsatz moderner hochfester Feinkornbaustähle vielfach notwendig. Bei der Montage hochfester Stahlkonstruktionen kommt es trotz anforderungsgerechter schweißtechnischer Fertigung vereinzelt zur Detektion von unzulässigen Unregelmäßigkeiten im Schweißbereich. Derzeitige Normen und Verarbeitungsrichtlinien geben hierbei kaum Informationen zu adäquaten Reparaturkonzepten, insbesondere für hochfeste Stähle. Vor diesem Hintergrund werden an der Bundesanstalt für Materialforschung und -prüfung (BAM) bauteilrelevante Untersuchungen zu den schweißbedingten Beanspruchungen und Gefügeveränderungen bei der schweißtechnischen Reparatur durch lokales thermisches Ausfugen und erneutes Schweißen durchgeführt.
Hierzu werden einige wesentliche Ergebnisse an Beispielen des Ingenieurbaus, mit Blick auf die mechanisch-technologischen Eigenschaften und Eigenspannungen erörtert. In einem aktuellen Vorhaben (FOSTA P1311, IGF 20162N) sind darauf aufbauend die Einflüsse durch die Schrumpfbehinderung und Wärmeführung beim Reparaturschweißen hochfester Feinkornbaustähle (S500MLO, S960QL) sowie die Reparaturzyklenanzahl Fokus systematischer Untersuchungen. Mittels strukturmechanischer Berechnungen ließen sich hierzu selbstbeanspruchende Probenformen identifizieren, die unterschiedliche definierte Steifigkeitsverhältnisse von Reparaturschweißnähten realer Bauteile abbilden. Schweißnähte an diesen bauteilähnlichen Proben weisen signifikant erhöhte schweißbedingte Beanspruchungen mit zunehmenden (Biege-)Einspanngraden auf. Im Vergleich mit bisherigen Erkenntnissen wird gezeigt, dass eine sichere Reparatur solcher Schweißnähte nur mittels optimaler Reparaturkonzepte und Wärmeführung gelingt, um diesen hohen Beanspruchungen und auch den speziellen Gefügen hochfester Stähle Rechnung zu tragen.
Ziel der Untersuchungen ist es letztlich, Empfehlungen für beanspruchungs- und werkstoffgerechte Reparaturkonzepte gerade für KMU abzuleiten, um Schäden und zumeist teure Nacharbeiten zu vermeiden.
Das Schweißen hochfester Feinkornbaustähle mit modifizierten Sprühlichtbögen bietet die Möglichkeit, kleinere Nahtöffnungswinkel zu schweißen.
Allerdings findet der modifizierte Sprühlichtbogen in den Regelwerken zur schweißtechnischen Verarbeitung hochfester Feinkornbaustähle unter Vermeidung von Kaltrissbildung bisher keine Berücksichtigung. Dieser Beitrag betrachtet die Wechselwirkungen der Haupteinflussgrößen auf die Kaltrissbildung beim Schweißen mit kleineren Nahtöffnungswinkeln am Beispiel des hochfesten Stahls S960QL.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system with a load capacity of 2 MN specifically developed for online monitoring of stress formation and cracking are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be quantified in-situ during welding and post weld heat treatment. Examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. Elevated working temperatures significantly increase the tensile residual stresses in the heat affected zone (HAZ). The effect of mechanical stresses resulting from welding on stress relief cracking is demonstrated by the example of a creep resistant steel. Reheat cracks were monitored online during post weld heat treatment.
Kaltrissprüfung hochfester Feinkornbaustähle beim Schweißen mit modifiziertem Sprühlichtbogen
(2019)
Der konstruktive Leichtbau erfordert den zunehmenden Einsatz hochfester Feinkornbaustähle mit Streckgrenzen bis zu 1300 MPa. Um darüber hinaus Schweißzeit, Schweißnahtvolumina und Schweißkosten zu minimieren, kam es zur Entwicklung moderner Lichtbogenprozesse mit erhöhter Abschmelzleistung, wie bspw. dem modifizierten Sprühlichtbogen (mod. SLB). Dieser Beitrag zeigt Kaltrissuntersuchungen beim Einsatz des mod. SLB unter reduziertem Nahtöffnungswinkel eines Hochfesten S960QL. Mit Hilfe des fremdbeanspruchten Implant-Tests konnte dargelegt werden, dass durch die erhöhte Abschmelzleistung ein tieferes Einbrandprofil entsteht und es dadurch zu einer zeitverzögerten Rissbildung kommt. Ergebnisse des selbstbeanspruchenden TEKKEN-Tests zeigen eine deutliche Rissbildung im Schweißgut unter reduziertem Nahtöffnungswinkel. Durch eine Nachwärmung unmittelbar nach dem Schweißen kann diese Rissbildung minimiert werden.
Einfluss der Schweiß- und Prüfparameter bei der Heißrissbewertung hochfester Schweißzusatzwerkstoffe
(2023)
Die Heißrissneigung beim Schweißen kann mittels einer ganzen Reihe von Prüfverfahren ermittelt werden. Eine etablierte Methode ist die sogenannte Varestraint-Prüfung, welche auch an der Bundesanstalt für Materialforschung und -prüfung (BAM) als modifizierter Varestraint/Transvarestraint-Test (MVT) zum Einsatz kommt. Die Ergebnisse von Varestraint-Prüfungen hängen jedoch stets in unter-schiedlichem Maße von der individuellen Prüfmaschinenauslegung und den verwendeten Prüfparametern ab. Dies kann zu einer uneinheitlichen Bewertung des Rissverhaltens führen, wenn die Risslänge konventionell als Kriterium für die Rissneigung herangezogen wird. Scheinbare Abhängigkeiten von Prozessparametern erschweren dann die Interpretation der Ergebnisse. Eine neuartige Bewertungsmethodik entkoppelt den Maschineneinfluss vom Materialverhalten und verwendet die Dehnrate als Risskriterium.
Die Bestrebungen zur Verringerung der CO2-Emissionen erfordern hochbelastbare und effiziente Komponenten aus Stahl in der Anlagen-, Verfahrens- und Kraftwerkstechnik. Hierfür sind in zunehmendem Maße auf den Anwendungsfall und Stahlwerkstoff abgestimmte Verschleißschutzschich-ten und definierte, zerspante Oberflächen notwendig. Die hohen Härten dieser Schichten und der Einsatz konventioneller Co-basierter Verschleißwerkstoffe führen oftmals zu unwirtschaftlichen Bauteilen, gerade aufgrund hohen Werkzeugverschleißes bei der Zerspanung mit geometrisch bestimmter Schneide. Er-kenntnisse über den Einsatz Ni-basierter Verschleißwerkstoffe und die Optimierung der Zerspanbarkeit mittels Legierungsmodifikationen und moderner hybrider Fräsprozesse ohne Verschlechterung der Ver-schleißschutzeigenschaften sind deshalb für die Anwender und Verarbeiter zur wirtschaftlichen Fertigung hochbelasteter Stahlbauteile wesentlich. Der vorliegende Beitrag stellt die Untersuchungsmethodik eines aktuell laufenden Vorhabens der TU Clausthal und BAM, Berlin, vor. Fokus liegt hierbei auf den hochin-strumentierten Fräsexperimenten, die eine reproduzierbare Analyse und Korrelation zwischen den mik-rostrukturellen Eigenschaften der auftraggeschweißten Legierungen, dem Zerspanprozess und der Zer-spanbarkeit, insbesondere der resultierenden Oberflächenintegrität, ermöglichen sollen.
Challenges for testing hydrogen-assisted cold cracking in weld seams of high-strength steel grades
(2024)
Hydrogen can cause weld cold cracking even days after fabrication. In this respect, higher strength steels present a challenge to established cold crack testing. In general, the tolerable hydrogen concentration for crack prevention decreases with increasing material strength. In addition, advanced welding processes require changes in weld geometry and heat input. This directly influences the formation of crack-critical microstructures, e.g. in hardened areas of the heat-affected zone. The limits of use and application of modern cold cracking tests are evaluated by (1) the externally loaded Implant-test and (2) the self-restraint Tekken-test. In particular, external mechanical stresses, which cause additional mechanical loads on the components during welding, must be considered due to the component-specific stiffness of high-strength steels. Accompanying test methods for
determining hydrogen concentration and diffusion in welds are presented, such as carrier gas hot extraction for determining hydrogen concentration (ISO 3690) or temperature-dependent diffusion coefficients. These values are of great importance for a holistic approach to the evaluation of the cold cracking sensitivity of high strength steels.
The Varestraint test and its variant Transvarestraint are one of the most widely used techniques for evaluating a material solidification cracking sensitivity during welding. The result of such tests is a crack length which is proportional to the material’s cracking susceptibility. Nevertheless, the welding and load parameters can unintentionally influence the crack length, which in some cases can distort the material evaluation. An approach is described as to how these effects can be assessed with the aid of a digital crack analysis. The crack lengths are compared position-dependently with their possible propagation due to the weld pool movement during continuous loading. The index derived from this can be used by the operator to evaluate his test parameters. In addition, a comparison of the results of different Varestraint setups is made possible. Alongside experimental results, a numerical sensitivity analysis is presented on how individual welding and loading parameters can affect the crack lengths.
Nickel base alloys are frequently applied in safety-relevant fields such as chemical plant construction or power plant engineering. Particularly on account of their cubic face-centered solidification characteristic, these materials are frequently susceptible to metallurgy-specific hot cracking during fusion welding. A classification of these materials according to their hot cracking resistance in the MVT-Test (Modified Varestraint Transvarestraint Test) is carried out by the example of a series of base and welding filler materials. Moreover, it has been proven by the MVT Test that the hot cracking resistance of nickel base alloy (Alloy 602 CA) can be improved by selecting appropriate shielding gases.
To the revision of ISO 3690 regarding the acceptance of the carrier gas hot extraction method
(2004)
Improving HAZ Toughness of High Heat Input Welded Joints by Using Boron Diffusion from Weld Metal
(2004)