Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (53)
- Vortrag (43)
- Zeitschriftenartikel (14)
- Posterpräsentation (14)
- Beitrag zu einem Sammelband (3)
- Sonstiges (2)
- Forschungsbericht (2)
Sprache
- Deutsch (81)
- Englisch (49)
- Mehrsprachig (1)
Schlagworte
- Ultraschall (20)
- Ultrasound (14)
- Zerstörungsfreie Prüfung (13)
- Rail inspection (9)
- Zuverlässigkeit (9)
- POD (8)
- Simulation (8)
- Ultrasonic testing (7)
- Phased array (6)
- Schienenprüfung (5)
- Ultraschallprüfung (5)
- Eisenbahn (4)
- Human Factors (4)
- Non-destructive testing (4)
- Phased Array (4)
- Railway (4)
- Signal processing (4)
- Standardisierung (4)
- Tauchtechnik (4)
- Wirbelstrom (4)
- Eddy current testing (3)
- Human factors (3)
- Luftultraschall (3)
- Probability of detection (3)
- Reliability (3)
- Ultrasonics (3)
- ZfP (3)
- Eddy current (2)
- Faserverbundwerkstoffe (2)
- Fatigue (2)
- Finite element analysis (2)
- High speed (2)
- Imaging (2)
- Inspection (2)
- Mechanisierte Schienenprüfung (2)
- Modelling (2)
- NDT (2)
- Non-destructive testing (NDT) (2)
- Phased array probes (2)
- Radsatzwellen (2)
- Radsatzwellenbruch (2)
- Railway axle (2)
- Reinheitsgrad (2)
- Safety (2)
- Signalverarbeitung (2)
- Standardisation (2)
- Thermografie (2)
- Ultraschall-Hohlwellenprüfung (2)
- Ultrasonic (2)
- Wave propagation (2)
- Wellenprüfung (2)
- Wirbelstromprüfung (2)
- ACUT (1)
- Acoustical damping (1)
- Active thermography (1)
- Additive Manufacturing (1)
- Air coupled (1)
- Air-coupled (1)
- Air-coupled ultrasound (1)
- Aktive Thermografie (1)
- Analytical approach (1)
- Angle wedge (1)
- Anisotropie (1)
- Array (1)
- Arraysensoren (1)
- Artificial intelligence (1)
- Ausbildung (1)
- Austenit (1)
- Automation (1)
- Automatisierung (1)
- Axle (1)
- Axle inspection (1)
- Bahn (1)
- Bauwesen (1)
- Bruchmechanik (1)
- CFK (1)
- CFRP (1)
- Carbon-fibre-reinforced plastic (1)
- Characterisation (1)
- Characterization (1)
- Charakterisierung (1)
- Classification (1)
- Cleaniliness purity grade ultrasound non-destructive volumetric measurement standard (1)
- Cleanliness (1)
- Cologne accident (1)
- Comparison ndt methods FRP fibre reinforced plastics ultrasound (1)
- Composite (1)
- Composite materials (1)
- Computertomografie (1)
- Cone Shaped Phased Array (1)
- Crack analysis/sizing (1)
- DICONDE (1)
- Damage (1)
- Damage tolerance (1)
- Data evaluation (1)
- Data science (1)
- Datenwissenschaft (1)
- Defect sizing (1)
- Detection Assessments (1)
- Detection of Rail Defects (1)
- Digitalisierung (1)
- Digitization (1)
- Directivity pattern (1)
- Eddy Current (1)
- Eisenbahnradsatz (1)
- Eisenbahnradsatzwellen (1)
- Eisenbahnschienen (1)
- Environment (1)
- Examples for application (1)
- FEM (1)
- FRP (1)
- Faseropische Sensorik (1)
- Fatigue crack (1)
- Fatigue crack propagation (1)
- Fatigue strength (1)
- Fiber reinforced platic (1)
- Fiber resisted polymers (1)
- Fokusprüfköpfe (1)
- GFK (1)
- GFRP (1)
- Geführte Wellen (1)
- Gekrümmte Oberflächen (1)
- Gerätetechnik (1)
- Glass-fibre-reinforced (1)
- Gruppenstrahlertechnik (1)
- Gruppenstrhaler (1)
- Guideline (1)
- Guss (1)
- Head Checks (1)
- High Speed Testing (1)
- High temperature (1)
- Hochtemperaturbeständigkeit (1)
- Hollow Axle Inspection (1)
- Hollow axle (1)
- Impact (1)
- Impactschäden (1)
- In-situ Process Monitoring (1)
- Industrie 4.0 (1)
- Innenbohrung (1)
- Innenprüfung (1)
- Inspection intervals (1)
- Instandhaltung (1)
- Kegel (1)
- Kegelarray (1)
- Klebeverbindungen (1)
- Kontakttechnik Technik (1)
- Korrosion (1)
- Künstliche Intelligenz (1)
- Lutgekoppelte Ultraschallprüfung (1)
- MFC (1)
- Material characterisation (1)
- Material inspection (1)
- Materials Chemistry (1)
- Matrix Array (1)
- Matrix array (1)
- Mechanical Engineering (1)
- Mechanics of Materials (1)
- Mehrfachreflexion (1)
- Messunsicherheit (1)
- Metals and Alloys (1)
- Modeling (1)
- Modelling calculations (1)
- Nichtmetallische Einschlüsse (1)
- Nichtmetallische Einschüsse (1)
- Nickellegierung (1)
- Non-Destructive Testing (NDT) (1)
- Non-destructive Materials (1)
- Non-linear vibration (1)
- Normung Roadmap (1)
- Operational principles (1)
- Passive thermography (1)
- Phased Array Ultraschall (1)
- Phased array technique (1)
- Phased-Array-Prüfung (1)
- Probe (1)
- Probe description (1)
- Process development (1)
- Processing (1)
- Prüfkopf (1)
- Prüfung (1)
- Querfehler (1)
- Radiografie (1)
- Radsatzwelle (1)
- Radsätze von Personenverkehrszügen und Schienen (1)
- Rail (1)
- Rail Inspection (1)
- Rail Inspection Phased Array Ultrasound (1)
- Rail testing (1)
- Railway axles with a bore hole in axial direction (1)
- Richtcharakteristik (1)
- Richtlinie (1)
- Root cause (1)
- Rotation scanner (1)
- SAM (1)
- Safe life design (1)
- Schadenstoleranz (1)
- Schiene (1)
- Schienenprüfzug (1)
- Schmiedeteile (1)
- Schweißnaht (1)
- Schwingfestigkeit (1)
- Sensorik (1)
- Sensors (1)
- Sicherheit von Verkehrswegen (1)
- Signal (1)
- Sleeve shaft (1)
- Sound field (1)
- Sparse Array (1)
- Sparse array (1)
- Standardization roadmap (1)
- Steel cleanliness (1)
- Streuflussprüfung (1)
- Structural simulation (1)
- Surface breaking cracks (1)
- TFM (1)
- Testing methodologies (1)
- Testkörper (1)
- Thermographic testing (1)
- Total Focusing Method (1)
- Train (1)
- Turbinenschaufel (1)
- Ultraschall- und Wirbelstromprüfung (1)
- Ultraschallprüfsystem (1)
- Ultraschallsensorsysteme (1)
- Ultraschallwandler (1)
- Ultrasonic probe (1)
- Ultrasonic tests (1)
- Ultrasound hardware (1)
- Umformtechnik (1)
- Visualization (1)
- Volumenprüfung (1)
- Vorlaufkeile (1)
- WOLAXIM (1)
- Wheelset (1)
- Zerstörende Prüfung (1)
- Zerstörungsfreie Prüfung (ZfP) (1)
- damage tolerance (1)
- inspection (1)
- probability (1)
- railway axles (1)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (48)
- 8.4 Akustische und elektromagnetische Verfahren (42)
- 8.0 Abteilungsleitung und andere (8)
- 8.5 Röntgenbildgebung (2)
- 9 Komponentensicherheit (2)
- 4 Material und Umwelt (1)
- 4.2 Material-Mikrobiom Wechselwirkungen (1)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
Eingeladener Vortrag
- nein (43)
Advantage of a combined ultrasonic and eddy current examination for railway inspection trains
(2007)
Some years ago, two railway inspection trains (RIT) already equipped with ultrasound, had additional advanced eddy current techniques installed. Recently, a new RIT was equipped with a system that was designed, from the beginning, to employ a combination of these two techniques for non-destructive rail inspection. The eddy current technique has been developed to enable identification and evaluation of rolling contact fatigue (RCF) defects. The ultrasound technique is aimed at measurements in the rail bulk volume, which are not feasible using the eddy current technique. Experience gained from application has shown that clear improvement on rail inspection can be achieved. For example, following Deutsche Bahn DB (German Rail) AG guideline, defects which are classified as group 2 using ultrasound testing can be further labelled as 'distinguished positions' if, for example, head checking can be identified in the same position using the eddy current technique. In other words, the new technique is capable of identifying two fundamentally different types of defects occurring at the same location. Such defects can then be classified as Group 1, equivalent according to the DB AG guideline. Furthermore, problem cases in the past, such as the decision whether a weld or rail joint is present for a fishing table, can be reliably determined using additional information from the eddy current technique. In this paper, examples will be provided to demonstrate application.
High speed non-destructive rail testing with advanced ultrasound and eddy-current testing techniques
(2009)
Today the rails face increased exposure to heavy loads, higher speeds and a very dense overall traffic. A continued development of testing methods for the rail inspection trains became necessary to match the modern needs for a fast detection and detailed classification of defects. To guarantee the safe operation of rail traffic non-destructive inspection techniques with combined ultrasound and eddy current testing methods are used to detect damages on rails. One of the main actual challenges of automated rail testing is the high inspection speed which is very close to the physical limits. To overcome these limits digital signal processing algorithms have to be used which maintain resolution and detection quality independent of operation speed. This paper presents a recently developed state of the art rail inspection system which uses advanced ultrasonic and eddy current testing techniques. Testing results are shown in a newly developed so called Glassy-Rail-Diagram which is capable to present data with a fixed resolution independent of inspection speed.
High speed non-destructive rail testing with advanced ultrasound and eddy-current testing techniques
(2009)
Zur Gewährleistung des sicheren Betriebs von Schienenfahrzeugen werden bei der laufenden Instandhaltung die Radsätze (Laufräder und Radsatzwellen) mittels Ultraschall auf Fehlerfreiheit geprüft. Auf Grund der Komplexität der durchzuführenden Prüfungen an der Radscheibe von scheibengebremsten Fahrzeugen ist beim Einsatz konventioneller Techniken eine große Anzahl Ultraschallprüfköpfe erforderlich, deren Reduzierung eine technische Herausforderung darstellt. Auch bei der Prüfung von Radsatzvollwellen sind auf Grund der eingeschränkten Zugänglichkeit unterschiedliche Winkelprüfköpfe erforderlich. Ein Ziel der Untersuchungen bestand darin, die Anzahl der erforderlichen konventionellen Prüfköpfe deutlich zu reduzieren. Dazu kann die Gruppenstrahlertechnik einen Beitrag leisten.
When dealing in ultrasonic testing with inhomogeneous and anisotropic material structure such as
diverse types of components made from austenitic or nickel based cast, which are currently used
for modern power plant concepts, data interpretation is quite difficult. For better understanding of
the complex interaction between the sound field and the component under test, the mathematical
modeling of sound propagation in solids is a substantial task to increase the probability of
detection of relevant defects.
First we present a mathematical approach for modeling the three dimensional transient
particle displacement as a function of time in each point in a half space excited by an impulsive
point load at the surface. The transient ultrasonic field of a rectangular array element is calculated
with this approach by a point source synthesis. Based on this solution we model the wave
propagation of a phased array transducer by time delayed superposition of the wave field of the
transducer elements.
Next we use an electrodynamic technique to visualize the grazing sound field at the surface
of a test block radiated by a phased array probe. By detecting the grazing beam at the samples
surface with a small electrodynamic probe, we measured the particle displacement as a function of
time. It allows for measuring the displacement in all three spatial directions. This comprises the
detection of the horizontal and vertical particle displacement with respect to the surface and thus
also the detection of longitudinal and shear waves is possible.
The calculated and measured wave fields will be compared for different delay laws in
isotropic and transversely isotropic media. The results support the theoretical activities to model
the wave propagation and to find optimal testing parameters for different components and
configurations.
Am 9. Juli 2008 entgleiste ein Hochgeschwindigkeits-Triebzug der Baureihe 403, ICE3, bei der Ausfahrt aus dem Kölner Hauptbahnhof. Ursache dafür war der Schwingbruch einer Radsatzwelle. Im Auftrag der Staatsanwaltschaft Köln untersuchte die BAM die Schadensteile, insbesondere die gebrochene Treibradsatz-Hohlwelle.
Zunächst wurden das Drehgestell, der Antriebsstrang, die Räder, die Bremsen und die gebrochene Radsatzwelle visuell untersucht und deren Zustand dokumentiert.
Anschließend erfolgte die zerstörungsfreie Prüfung der beiden Bruchstücke der Hohlwelle mit teilmechanisierter Ultraschall-Handprüfung.
Vor der Zerlegung der Radsatzwelle wurden ausgewählte Maße kontrolliert und die Oberfläche eingehend untersucht. Nach der Probenahme und Präparation wurden die relevanten spezifizierten Eigenschaften des Wellenwerkstoffs überprüft.
Mittels Bruchflächenanalyse konnte die Startstelle des Schwingrisses lokalisiert, aufgrund der starken Sekundärschäden auf der Bruchfläche und an den Bruchkanten jedoch nicht direkt ausgewertet werden. Durch die Kombination von Mikro-Computertomographie und Ultraschall-Tauchtechnik wurden u. a. nahe der Schwingriss-Startstelle Inhomogenitäten erkannt, die durch metallographische Zielpräparation als nichtmetallische Einschlüsse identifiziert wurden. Die Größe dieser Einschlüsse ist gemäß gefordertem Reinheitsgrad unzulässig. Vergleichbare Einschlüsse in diesem hochbeanspruchten Bereich der Radsatzwelle haben vermutlich den Schwingriss initiiert.
Die Prüfung von anisotropen Schweißnähten auf Querfehler stellt auch heute noch eine Herausforderung für die Ultraschallprüfung dar. Das gilt insbesondere für das Auffinden kleiner rissartiger Fehlstellen in einer unbeschliffenen Wurzel. Ursachen dafür sind zum einen das ausgeprägte Beugungs-, Streuungs- und Reflexionsverhalten solcher Nähte und zum anderen die störenden Formanzeigen aus dem Wurzelbereich, die sicher von den Fehlstellen unterschieden werden müssen, um Fehlinterpretationen bei der Bewertung der Anzeigen zu vermeiden.
In der vorliegenden Arbeit werden an einer 85 mm dicken und 6 bis 10 mm breiten Engspaltschweißnaht mit stängelkristalliner Struktur rissartige Testfehler in Form erodierter Nuten untersucht. Die 2 und 4 mm tiefen Nuten sind mit 5 mm Länge kürzer als die Wurzelbreite. Die Wurzel ist nicht beschliffen und hat eine Überhöhung von ca. 2 mm. Ziel ist es, die Fehlstellen von den Form- und Gefügeanzeigen
zu unterscheiden und sicher zu detektieren. Eine Größenbestimmung ist
nicht vorgesehen.
Durch den Einsatz der Gruppenstrahlertechnik ist es möglich, optimale Einschallparameter zu finden, mit denen diese Aufgabe gelöst werden kann. Es werden zwei azimutal schwenkende lineare Gruppenstrahlerprüfköpfe mit Vorsatzkeil in SE-Technik verwendet, die so auf beiden Seiten der Schweißnaht angeordnet sind, dass sich ihre Schallfelder unabhängig von der Einschallrichtung in der Schweißnahtwurzel überlagern. Damit ist es möglich, optimale Einschallwinkel für das Prüfproblem zu finden und in einer Prüffahrt gleichzeitig in beiden Einschallrichtungen längs der Schweißnaht zu prüfen.
Die Gläserne Schiene
(2011)
Um den vermehrten Einsatz von mechanisierten Prüfeinrichtungen bei der Ultraschallprüfung in der Ausbildung Rechnung zu tragen, ist es wünschenswert, dieses Themenfeld bereits zu einem frühen Zeitpunkt in die Ultraschallkurse zu integrieren. Aus diesem Grund wurde für die Ausbildung bei der DGZfP in Zusammenarbeit mit der BAM ein teilmechanisiertes Ultraschall-Prüfsystem entwickelt.
Das System basiert auf einem handelsüblichen Ultraschallgerät für die Handprüfung und einem Netbook-Computer. Die berührungslose Positionserfassung wird über den Blenden-Ausgang des Ultraschallgerätes getriggert und die Daten werden mittels Infrarot- und Bluetoothtechnik übertragen. Dies ermöglicht einen kompakten und portablen Aufbau mit kurzen Einrichtzeiten, der sich im Rahmen einer Lehrveranstaltung effektiv einsetzen lässt. Die Ergebnisdarstellung erfolgt mit C-Bildern.
An einfachen Übungsstücken können die Kursteilnehmer, dicht an die Handprüfung angelehnt, die Methoden und Randbedingungen einer mechanisierten Prüfung erfahren.
Bei der Prüfung von gekrümmten Bauteilen in Tauchtechnik muss man die Veränderung des Schallfeldes durch die Form der Oberfläche berücksichtigen. Insbesondere bei hochauflösenden Ultraschallprüfungen mit Fokusprüfköpfen kommt es hierbei zu drastischen Verzerrungen des Schallfeldes.
Diese Verzerrungen sind bei der Empfindlichkeitseinstellung sowie bei der Auslegung von Fokuspunkt- und Spurabstand zu berücksichtigen, um eine ausreichende Prüfempfindlichkeit zu erreichen. Es werden Beispiele von Simulationsrechnungen an typischen Prüfanordnungen vorgestellt.
Die heutigen Anforderungen an Bauteile und deren Materialien werden immer höher. Somit steigen auch die Anforderungen an die notwendigen Prüfverfahren zur Qualitätsbestimmung bzw. –erhaltung. Durch den optimierten Einsatz von mechanisierten Prüfverfahren und der Verwendung von Visualisierungsalgorithmen wird es möglich, Prüfergebnisse mehrdimensional und farbcodiert z.B. als Überblicksansicht über das Volumen des geprüften Bauteils zu bekommen.
Bei der hochauflösenden Volumenprüfung eines Bauteils mittels Ultraschall-Tauchtechnikverfahren, bei dem anstelle einer einfachen Ja/Nein – Aussage eine detaillierte Analyse erforderlich ist, ist es notwendig, alle Messdaten, d.h. jedes A-Bild an jedem Ort, zu speichern.
Bei der Auswertung der Daten werden vorwiegend 2D-Darstellungen, wie z.B. das C-Bild der gescannten Fläche, B-Bilder der Scan- und Index-Ebene sowie das A-Bild an der jeweiligen Position verwendet. Um sich z.B. ein Überblick über das Volumen zu verschaffen, werden die B-Bilder der jeweiligen Ebene gescrollt. Bei diesem Verfahren erhält man zwar eine genaue Aussage in den einzelnen Ebenen, aber doch wenig Informationen über die Lage der Anzeigen im Prüfvolumen.
Eine 3D-Visualisierung der Volumenmessdaten liefert unter Berücksichtigung der Bauteilgeometrie und einer Farbcodierung der Amplitudenwerte eine übersichtliche Darstellung über Lage, Größe und Verteilung der Anzeigen im Volumen des Bauteils.
Die wiederkehrende zerstörungsfreie Prüfung von längs gebohrten
Eisenbahnradsatzwellen mit Ultraschall erfolgt im eingebauten Zustand aus der Wellenbohrung heraus. Neben den aufzufindenden Fehleranzeigen erzeugt aufgrund der geometrischen Bedingungen der Radsatzwelle hierbei jeder Querschnittsübergang eine umlaufende Formanzeige in der Ergebnisdarstellung. Durch den Prozess des Aufschrumpfens der Radscheiben auf die Sitze können weiterhin örtlich statistisch verteilte Bereiche im Sitz entstehen, die bei der Ultraschallprüfung Anzeigen hervorrufen, die so genannten Scheinanzeigen. Insbesondere in den Bereichen der Querschnittsübergänge ist zum einen die Prüfsituation sehr komplex, zum anderen ist hier die Wahrscheinlichkeit für eine Rissbildung am höchsten. Bei der Befundanalyse stößt die derzeit verwendete Prüftechnik in diesen Bereichen an ihre Grenzen, so dass nicht immer eine eindeutige Prüfaussage erfolgen kann. Im Bericht werden Lösungsansätze für Analyseverfahren vorgestellt, die auf Basis der Gruppenstrahlertechnik bzw. mit Fokusprüfköpfen in Verbindung mit dem Einsatz von Signalverarbeitung vielversprechende Ergebnisse zur Optimierung dieser Situation aufzeigen.
This paper describes the investigations, carried out during the ongoing European Project WOLAXIM. It presents the development of the non-destructive testing system for hollow axle inspection. The phased array probe is designed, the inspection parameters are determined and the required test equipment is planned according to the specifications.
As a part of the probe design, a detailed model to calculate the sound field of the conical phased array is developed. With this model the optimal geometric parameters for bore diameters from 30mm up to 70mm are determined. The first design of a conical probe with forty-eight elements is realised. Based on this design a mock-up with ten elements is produced. The first practical tests with the calculated delay laws show high sensitivity for small test flaws and offer good agreement with the modelling results. The effectiveness as well as the sensitivity with a good signal to noise ratio is verified.
The parameters for a short inspection time less than five minutes per axle are determined. A raw scanning with 1.5° circumferential and 2mm axial resolution is feasible within two minutes. That is significantly faster than comparable mechanically rotated probe systems. The remaining three minutes are sufficient for the other steps in the inspection process. The required features will be fulfilled by the COMPAS® phased array device.
The feasibility of the ultrasonic system is shown. The specification and the theoretical probe design are complete and sufficient knowledge is present that the system will be viable. The results of the modelling and first practical tests show a good agreement with the objectives. The determined probe parameters satisfy the requirements.
The paper gives an overview on safe life and damage tolerance methods applied to railway axles. It describes failure scenarios due to fatigue crack initiation and propagation. Besides common aspects of design, specific features such as corrosion and impact damage from flying ballast are discussed which may reduce the fatigue strength of axles during service. Potential effects of non-metallic inclusions from the steel manufacturing process are addressed in the context of the very high number of loading cycles railway axles are designed for. With respect to damage tolerance general lines of fracture mechanics residual lifetime analyses are introduced. More specific discussion is provided on aspects such as the threshold value of fatigue crack propagation and reliability aspects of non-destructive inspection.
High Speed Non-Destructive Rail Testing with Advanced Ultrasound and Eddy-Current Testing Techniques
(2009)
Zur Charakterisierung von luftgekoppelten Ultraschallwandlern werden mehrere verschiedene Methoden und Verfahren angewendet. Durch die unterschiedlichen Herangehensweisen werden oft unterschiedliche Prüfkopfpara-meter und Schallfeldgrößen ermittelt, was einen direkten Vergleich von Datenblättern erschwert. Für die Charakterisierung von Kontakt- und Tauchtechnikprüfköpfen hat sich ISO 22232-2:2021 bereits etabliert, allerdings ist diese Norm nicht auf die luftgekoppelten Wandlertechnologien direkt übertragbar. Daher erkannten Hersteller, Forschungseinrichtungen und Anwender den Bedarf an einer Richtlinie zur einheitlichen Charakterisierung von luftgekoppelten Wandlern. Gemeinsam arbeiten sie aktuell im Rahmen des Unterausschusses „Luftgekoppelte Ultraschallprüfung“ der DGZfP an der Erstellung einer solcher Richtlinie mit dem Anspruch, die bestehende Normung um die luftgekoppelte Prüfung zu erweitern und somit die Vereinheitlichung der Charakterisierung dieser Wandler zu erleichtern.
In diesem Beitrag wird ein Überblick über den geplanten Inhalt der Richtlinie und über die Methoden zur akustischen Charakterisierung von luftgekoppelten Ultraschallwandlern gegeben. Insbesondere werden verschiedene Methoden der Ermittlung von wichtigen Wandlerparametern wie z.B. Empfindlichkeit, Mittenfrequenz, Bandbreite, Fokusgröße und Fokusabstand dargestellt und verglichen.
Robotergeführte Ultraschallprüfung von Gasturbinenschaufeln mit adaptiver TFM im ZfP 4.0-Umfeld
(2022)
Leit- und Laufschaufeln stationärer Gasturbinen sind im Betrieb anspruchsvollen Bedingungen ausgesetzt. Die Prüfung, Wartung und Reparatur der hochbelasteten Teile sind notwendig, um Sicherheit und Effizienz über längere Zeiträume zu gewährleisten. Eine der in diesem Prozess angewandten Methoden ist die Ultraschallprüfung.
Im Zuge der fortschreitenden Digitalisierung ist es das Ziel des Projektes MRO 2.0, den Aufbereitungsvorgang um digitale Prozesse zu erweitern und somit zu modernisieren. Eine der Aufgaben ist es, dabei anstelle der konventionellen Ultraschallprüfung eine Array-Technik mit rekonstruierenden Verfahren einzusetzen und eine automatisierte, digital eingebundene Methode im Rahmen von ZfP 4.0 zu entwickeln.
Um die Ist-Geometrie der Oberfläche und die verbleibende Wanddicke flächendeckend an den Turbinenschaufeln zu bestimmen, wird ein adaptives TFM Verfahren (Total Focusing Method) in Tauchtechnik eingesetzt, welches die Brechung der Schallwellen an der Grenzfläche zum Prüfkörper in der Rekonstruktion berücksichtigt. In der hierfür entwickelten Prüfanlage führt ein Roboterarm einen Array-Prüfkopf und scannt das Bauteil normal zur inspizierten Oberfläche. Somit kann ein 3D-Modell des Ist Zustandes des zu prüfenden Bauteils erstellt werden.
Spezielle Herausforderungen an die Aufgabe stellen die komplexe Geometrie des Prüfobjektes sowie dessen geringe und ortsabhängige Wanddicke dar. Ein weiterer Fokus liegt auf der Optimierung der Prüfparameter, Verbesserung der Prüfgeschwindigkeit sowie der Zuverlässigkeit der Methode.
In diesem Beitrag werden die während des Projektes entwickelte Methode und die im zweiten Projektjahr erarbeiteten Ergebnisse vorgestellt, mit dem Schwerpunkt auf die entwickelten Rekonstruktionsalgorithmen und den Versuchsaufbau.
This guideline was drafted following and complementing the norm ISO 22232-2:2020(E) to include air-coupled ultrasonic transducers. This document specifies the characteristics of probes used for non-destructive air-coupled ultrasonic testing with center frequencies above 20 kHz, with focusing or without focusing means.
Häufig stellt sich die Frage, ob eine Materialinhomogenität kritisch für die strukturelle Integrität eines Bauteils ist. Dies ist häufig abhängig von der Größe und der Geometrie dieser Materialinhomogenität. Während die korrekte Bestimmung einer Defektgröße zweifelsfrei eine Messaufgabe darstellt, ist die Detektion eines Materialdefekts die Hauptaufgabe eines Prüfsystems. Allerdings sind manche Defekte zu klein, um detektiert zu werden. Es ist jedoch schwierig, etwas zu bemessen, was nur schwer gefunden werden kann, stellen sowohl die Detektion als auch die Fähigkeit den Defekt zu bemaßen, Teile der der Bewertung eines Prüfsystems dar. Die vorliegende Publikation beschäftigt sich zum einen mit der Notwendigkeit, die Auffindwahrscheinlichkeit von Prüfverfahren zu bewerten, und zum anderen mit den Schritten, mit denen das Konzept der Prüfunsicherheitsbewertung national und international vorangetrieben wird. Final werden die Methoden evaluiert, die den Schulterschluss zwischen Prüf- und Messunsicherheitsbestimmung ermöglichen. Ergänzt wird der Artikel mit Beispielen aus der Industrie, welche die aktuelle Relevanz des Themas untermauern.
Durch die Internationalisierung in der Standardisierung wurden die Regelwerke zur „Charakterisierung und Verifizierung der Ultraschall-Prüfausrüstung“, die bisher als europäische Regelwerke der DIN EN 12668 Reihe eingeordnet waren, überarbeitet und in internationale Regelwerke überführt. Die Regelwerke sind seit September 2021 als deutsche Übersetzung eingeführt als DIN EN ISO 22232 und ersetzen somit in Deutschland die bisher geltenden Regelwerke der DIN EN 12668 Reihe. Die drei Teile der Reihe beschäftigen sich in Teil 1 mit den Prüfgeräten, in Teil 2 mit den Prüfköpfen und in Teil 3 mit der Prüfausrüstung, die aus Prüfgerät, Prüfkopf und Kabel besteht. In dem Vortrag möchten wir neben dem historischen Werdegang darlegen, welche Gemeinsamkeiten und Unterschiede die Regelwerke aufweisen und worauf bei der Umstellung zu achten ist.
Seit 1999 existiert das MIL-HDBK 1823, die us-amerikanische Leitfaden zur Erstellung einer Probability of Detection (POD; Fehlerdetektionswahrscheinlichkeit). Obwohl das Dokument als internationaler Stand der Technik angesehen wird, ist die allgemeine Anwendung in der ZfP-Praxis von einigen Nachteilen begleitet:
1. Die beschriebenen POD‘s bilden ausschließlich die Grundlagen-POD ab, jeweils mit nur einem Fehlerparameter und einem Signalparameter. Modernere Ansätze werden hier nicht adressiert.
2. Die aktuelle Version verzichtet fast vollständig auf konkrete mathematische Formulierungen.
3. Die Richtlinie richtet sich hauptsächlich an die militärische Luftfahrt.
4. Das Dokument ist nur in englischer Sprache verfügbar.
Mit Hilfe eines BMWi-Förderprojekts wird ein weiterführendes Regelwerk auf Basis der MIL-HDBK 1823 unter deutscher Federführung erarbeitet, welches die Anwendung der POD-Berechnung auf eine breitere Basis stellt und die oben genannten Nachteile der MIL-HDBK 1823 behebt.
Das vorgestellte Projekt „normPOD“ wird eine normative, branchenübergreifend einsetzbare Beschreibung des Vorgehens bei der Berechnung einer POD zur Zuverlässigkeitsbewertung zerstörungsfreier Prüfungen entwickeln. Hierbei wird Klarheit über unterschiedliche POD-Ansätze geschaffen und anhand praktischer Beispiele aus Maschinenbau und Bauwesen ein Leitfaden für den Praxiseinsatz erarbeitet.
Das Poster gibt einen Überblick über die geplanten Arbeiten innerhalb des Projekts und lädt die Beteiligten der DGZfP-Jahrestagung zur Diskussion ein, um eine breite Basis und Akzeptanz für die entwickelten Berechnungsverfahren zu schaffen, insbesondere in Hinblick auf ZfP 4.0 und Digitalisierung.
Seit 1999 existiert das MIL-HDBK 1823, die us-amerikanische Leitfaden zur Erstellung einer Probability of Detection (POD; Fehlerdetektionswahrscheinlichkeit). Obwohl das Dokument als internationaler Stand der Technik angesehen wird, ist die allgemeine Anwendung in der ZfP-Praxis von einigen Nachteilen begleitet:
1. Die beschriebenen POD‘s bilden ausschließlich die Grundlagen-POD ab, jeweils mit nur einem Fehlerparameter und einem Signalparameter. Modernere Ansätze werden hier nicht adressiert.
2. Die aktuelle Version verzichtet fast vollständig auf konkrete mathematische Formulierungen.
3. Die Richtlinie richtet sich hauptsächlich an die militärische Luftfahrt.
4. Das Dokument ist nur in englischer Sprache verfügbar.
Mit Hilfe eines BMWi-Förderprojekts wird ein weiterführendes Regelwerk auf Basis der MIL-HDBK 1823 unter deutscher Federführung erarbeitet, welches die Anwendung der POD-Berechnung auf eine breitere Basis stellt und die oben genannten Nachteile der MIL-HDBK 1823 behebt.
Das vorgestellte Projekt „normPOD“ wird eine normative, branchenübergreifend einsetzbare Beschreibung des Vorgehens bei der Berechnung einer POD zur Zuverlässigkeitsbewertung zerstörungsfreier Prüfungen entwickeln. Hierbei wird Klarheit über unterschiedliche POD-Ansätze geschaffen und anhand praktischer Beispiele aus Maschinenbau und Bauwesen ein Leitfaden für den Praxiseinsatz erarbeitet.
Das Poster gibt einen Überblick über die geplanten Arbeiten innerhalb des Projekts und lädt die Beteiligten der DGZfP-Jahrestagung zur Diskussion ein, um eine breite Basis und Akzeptanz für die entwickelten Berechnungsverfahren zu schaffen, insbesondere in Hinblick auf ZfP 4.0 und Digitalisierung.
Während in einem konventionellen Ultraschallprüfkopf ein Kunststoffdämpfungskörper mit Kleber oder Öl an einen Piezoschwinger angekoppelt ist, werden als Hochtemperaturlösung feinporöse sintermetallische Dämpfungsmaterialien mit einer Flüssigglasankopplung eingesetzt. Um dabei das Sintermetall vor dem korrosiven Angriff der Glasschmelze zu schützten, wird am Dämpfungskörper gegenwärtig Gold- oder Platinfolie zeit- und kostenaufwendig appliziert.
In der aktuellen Arbeit wurde eine Methode zum Korrosionsschutz der sintermetallischen Oberfläche aus rostfreiem Stahl mittels Laser-Pulverauftragschweißen entwickelt. Im Laufe einer Schweißparameterstudie auf dem Substratmaterial aus massivem rostfreiem Stahl wurde die Eignung unterschiedlicher Auftragsmaterialien auf Nickel- und Kobaltbasis untersucht. Dabei wurde zunächst der Einfluss verschiedener Schweißparameter wie Laserleistung, Vorschubgeschwindigkeit und Pulvermenge auf die Auftragsqualität (Nahtform, Vermischungsgrad, Porosität) metallografisch bewertet. Anschließend wurden die aufgetragenen Schichten hinsichtlich ihrer Korrosionsbeständigkeit getestet. Der Kontakt mit einer flüssigen Glasmischung bei 500 °C hat bei keiner der beschichteten Proben sichtbare Korrosionswirkung gezeigt. Als Resultat der Schweißparameterstudie haben sich besonders die nickelbasierten Pulver als gut geeignete Materialien für den Prozess gezeigt. Die identifizierten Schweißparameter wurden im nächsten Schritt erfolgreich an das sintermetallische Substrat angepasst.
Menschliche Faktoren sind ein häufig genanntes Thema, wenn wir über
die Zuverlässigkeit der zerstörungsfreien Prüfung (ZfP) sprechen. Die Probability of Detection (POD), das üblicherweise verwendete Maß für die Zuverlässigkeit der ZfP, betrachtet jedoch nur die technische Fähigkeit eines ZfP-Systems, einen Fehler zu entdecken. Nach mehreren Jahrzehnten der Erforschung des Einflusses der menschlichen Faktoren auf die Zuverlässigkeit der ZfP gibt es immer noch keinen allgemein akzeptierten Ansatz, um menschliche Faktoren in der Zuverlässigkeitsbewertung sichtbar zu machen. Dieser Beitrag gibt einen Überblick über verschiedene verfügbare Methoden zur Einbeziehung menschlicher Faktoren in die Zuverlässigkeitsbewertung. Das Thema ist ein essenzieller Bestandteil des laufenden WIPANO-Projekts "normPOD", das sich als Ziel gesetzt hat, die Standardisierung der Zuverlässigkeitsbewertung in Deutschland voranzutreiben und im Vergleich zu den schon bekannten internationalen Normen einen Fokus auf den Umgang mit den menschlichen Faktoren zu legen.
Bei der simulationsunterstützten Planung kritischer Ultraschallprüfaufgaben ist die detaillierte Kenntnis der Parameter der eingesetzten Prüfköpfe von entscheidender Bedeutung. Durch die, in den Regelwerken (DIN EN ISO 22232-2) zugelassenen Toleranzen bei der Herstellung der Prüfköpfe sind einige Prüfkopfparameter nur ungefähr bekannt. Durch die Alterung von Prüfköpfen und Verschleiß können auch Parameter variieren, die nicht vollständig durch die erforderliche Justierung ausgeglichen werden können. Daher sind zusätzlichen Vorversuche oft unvermeidlich. In dieser Arbeit wurden nach einer statistischen Versuchsplanung (DoE) Untersuchungen zur relativen Echo-Empfindlichkeit von konventionellen Prüfköpfen durchgeführt. Die Auswertung wurde für prüfkopfbezogene und personenbezogene Stichproben durchgeführt. Es wird gezeigt, wie weit die Daten um den Zentralwert herum verteilt sind bzw. wie sehr sich das Testobjekt im untersuchten Merkmal unterscheidet. Gerade in Hinblick auf die Beurteilung der intrinsischen Fähigkeit von Prüfverfahren und der Human Factors wird das POD-Analysekonzept zur quantitativen Bewertung der Zuverlässigkeit weiterentwickelt. Die HF-Quantifizierung bezieht sich auf verschiedene Faktoren und Methoden, die in der Veröffentlichung von M. Bertovic et al. [1] ausführlich beschrieben wurden. Die Schritte, die für das Bewertungsverfahren zur POD-Analyse erforderlich sind, werden in der Veröffentlichung von D. Kanzler et al. [2] detailliert dargestellt. Die grundlegenden Anforderungen an die Testkörpersätze für die POD-Analyse wurden in der Publikation von A. Jüngert et al. [3] zusammengefasst. Diesbezüglich wurden mit Hilfe von Simulationsrechnungen die möglichen Abweichungen an Beispielen der im Projekt norm- POD ausgewählten Prüfanordnungen dargestellt. Die Ergebnisse wurden Messungen an Testkörpern gegenübergestellt.
Im Rahmen des WIPANO Vorhabens „normPOD“ wird eine Richtlinie zur experimentellen und simulationsgestützten Zuverlässigkeitsbewertung erstellt. In der Richtlinie wird die Zuverlässigkeitsbewertung beispielhaft für zwei praktische Anwendungsfälle vorgestellt. Ein Anwendungsfall beschäftigt sich mit konventionellen Ultraschallprüfungen an ferritischen Stählen und deren
Schweißnähten.
Zur Berechnung von Probability-Of-Detection (POD)-Kurven ist es notwendig, dass ein geeigneter Testkörpersatz zur Verfügung steht, der sowohl leicht zu findende Fehlstellen als auch Fehlstellen, die an der Grenze der Detektierbarkeit liegen, enthält.
Im Vorhaben kommen verschiedene Testkörper zum Einsatz, die entweder Ersatzfehler wie Nuten und Bohrungen oder künstlich eingebrachte realistische Fehlstellen wie Risse und Schweißfehler enthalten.
Zur Erstellung eines möglichst allgemeinen Leitfadens zur Testkörperherstellung für die Zuverlässigkeitsbewertung werden verschiedene Möglichkeiten betrachtet. Es wird ein Testkörpersatz mit Ersatzfehlern hergestellt und durch Testkörper mit realistischen Fehlstellen ergänzt. Mit Hilfe von Simulationen mit CIVA sollen die optimalen Konfigurationen und Anordnung von realistischen Fehlstellen und Ersatzfehlern identifiziert, und anschließend mithilfe geeigneter Fertigungsverfahren eingebracht und validiert werden. Neben den Testkörpern, die gezielt für das Vorhaben hergestellt werden, kommen außerdem kommerziell erhältliche Testkörpersätze mit realistischen Fehlstellen zum Einsatz.
Die Prüfaussage einer Ultraschallprüfung hängt weiterhin wesentlich von den Informationen ab, die dem Prüfpersonal vor Ort zur Verfügung steht. Es muss ein ausgewogenes Maß zwischen zu wenig und zu viel Informationen gefunden werden.
Im letzten Schritt wird deshalb eine geeignete Vorlage für eine Prüfanweisung erstellt, die so formuliert ist, dass die Wahrscheinlichkeit menschlicher Fehler (z. B. Missverständnis, Fehlinterpretation, Überspringen von Schritten usw.) möglichst gering ist.
Seit beinahe 50 Jahren werden Zuverlässigkeitsbewertungen zerstörungsfreier Prüfverfahren erfolgreich in unterschiedlichen Industriebranchen eingesetzt. Dennoch gibt es weiterhin viele Vorbehalte, da die Bewertungsgrundlage nicht standardisiert ist und konkrete Handlungsanweisungen fehlen. Dem gegenüber steht die Anerkennung in der ZfP-Community. Es ist bisher nur Wenigen bekannt, dass dem Wissen über die Zuverlässigkeit eines zerstörungsfreien Prüfverfahren eineSchlüsselfunktion für die ZfP 4.0 zukommt.
Im Vortrag wird die Notwendigkeit für eine Norm oder eine Richtlinie zum Thema Zuverlässigkeitsbewertungen aufgezeigt. Es wird darauf eingegangen, warum es bisher (in Deutschland) noch keine Richtlinie gab und gibt und was der:die Anwender:innen aus einer Richtlinie zur Zuverlässigkeitsbewertung von ZfP-Prüfverfahren erwarten kann.
Es werden konkrete Schritte und Vorgehensweisen zur Bewertung der Zuverlässigkeit eines Verfahrens aufgezeigt; von der Definition eines Anwendungsfalls, über die Herstellung geeigneter Testkörper bis hin zur Durchführung und Bewertung von Prüfungen unter Einbeziehung von menschlichen Einflüssen. Die Beispiele umfassen sowohl Anwendungen aus dem Bauwesen als auch aus dem Maschinen- und Anlagenbau.
Der Vortrag fasst die bisherigen und geplanten Arbeiten in dem WIPANO Projekt „Normung für die probabilistische Bewertung der Zuverlässigkeit für zerstörungsfreie Prüfverfahren“ zusammen.
Ultrasonic probes for high-temperature applications are provided with metallic wedges, which can withstand the contact with the high temperature of the inspected structure. The ultrasonic signal travels within the wedge and gets reflected from its boundaries, causing interference signals called “ghost echoes”. The current work presents an investigation of the additional damping effect provided by porous sintered metal plates applied onto the surface of the wedge. In particular, the study evaluates the effect of damping plate thickness on the interference signal level at different transmission frequencies. Damping plates made of sintered metal SIKA-R 15 AX were attached to a wedge prototype made of steel 1.4301. The study revealed, that the most effective thickness of damping plates in the selected frequency interval of 1 to 4 MHz is equal to 4 mm. The evaluation of the interference signal has shown that the application of such damping plates to the wedge surface contributes to an additional attenuation of an interference signal of 10 to 30 dB after 500 μs of signal propagation.
Die regelmäßige Überprüfung von Eisenbahnradsatzwellen auf betriebsbedingte Schädigungen ist ein fester Bestandteil des Instandhaltungskonzeptes von Eisenbahnfahrzeugen. Insbesondere bei hohen Achslasten und hohen Rotationsgeschwindigkeiten ist eine detaillierte regelmäßige Prüfung notwendig. In den letzten Jahren wurden für diese Prüfaufgabe mechanisierte Ultraschallprüfsysteme entwickelt, erfolgreich eingeführt und etabliert. Für eine Weiterentwicklung dieser Technologie stehen die Themen Erhöhung der Auflösung, Reduzierung von Oberflächen- und Störeinflüssen, Verkürzung von Prüfzeiten, Verbesserung der POD, Verlängerung von Inspektionsintervallen, Vereinfachung der Auswertung und die Möglichkeit der Durchführung von Analyseprüfungen im Vordergrund. Es werden Ansätze und neue Konzepte zur Lösung dieser Herausforderungen vorgestellt.