First results of an inter-laboratory comparison (27 participants in Europe, Japan and USA) of XPS data obtained with non-conducting samples are presented. Binding energies of Al 2s for alumina, N 1s and imide C 1s for Kapton and Sr 3p3/2 for a strontium titanate film on glass were obtained after static charge referencing with the help of 15 nm gold particles deposited at the surface of the test samples. For the alumina sample C 1s static charge referenced data are also presented. Repeat standard deviations (sr), between standard deviations (sb), reproducibility standard deviations (sR) and total means are evaluated from the experimental data. It can be stated that although the repeat standard deviation is as small as 0.05 eV in the best case, the standard deviation characterizing the reproducibility of the method is obviously not better than 0.15 eV in the best case at the present time. The knowledge of these standard deviations is important for metrology, validations of analytical procedures relying on qualitative photoelectron spectroscopy and XPS databanking.
A combined XPS, NEXAFS, and ToF-SIMS chemical surface characterization of carbohydrate-functionalized gold and glass surfaces is presented. Spot shape and chemical composition across a spot surface are provided by surface-sensitive methods as ToF-SIMS and XPS, used in their imaging modes. Moreover, the feasibility of this multimethod approach to control relevant production steps of a carbohydrate microarray prototype is demonstrated.
Carbohydrate films on gold based on dimannoside thiols (DMT) were prepared, and a complementary surface chemical analysis was performed in detail by X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS), near-edge X-ray absorption fine structure (NEXAFS), FT-IR, and contact angle measurements in order to verify formation of ω-carbohydrate-functionalized alkylthiol films. XPS (C 1s, O 1s, and S 2p) reveals information on carbohydrate specific alkoxy (C–O) and acetal moieties (O–C–O) as well as thiolate species attached to gold. Angle-resolved synchrotron XPS was used for chemical speciation at ultimate surface sensitivity. Angle-resolved XPS analysis suggests the presence of an excess top layer composed of unbound sulfur components combined with alkyl moieties. Further support for DMT attachment on Au is given by ToF-SIMS and FT-IR analysis. Carbon and oxygen K-edge NEXAFS spectra were interpreted by applying the building block model supported by comparison to data of 1-undecanethiol, poly(vinyl alcohol), and polyoxymethylene. No linear dichroism effect was observed in the angle-resolved C K-edge NEXAFS.
Self-assembled octadecyltrichlorosilane (CH3(CH2)17SiCl3, OTS) films were deposited on an oxidized silicon wafer. They were carefully exposed to a low-pressure oxygen direct current (dc) plasma and/or Cr vapor. Subsequently, they were characterized by X-ray photoelectron spectroscopy, near-edge X-ray absorption fine structure spectroscopy, and atomic force microscopy. Detailed information on the oxygen functionalization and the molecular conformation of the OTS films was obtained. The main result was that functionalization conditions can be found where the order of the film remains almost unaffected. Similarly, Cr evaporation of pure OTS films revealed only slight effects on the order in the film. Cr evaporation of an ordered but functionalized OTS film immediately changes its state toward a fully isotropic one. In the course of interaction, oxygen sites at the surface of the functionalized OTS film are reduced whereas Cr becomes oxidized. A redox reaction scheme is proposed for this interfacial reaction. Finally, it is concluded that the given study should be of importance for advanced plasma processing of polyolefins.
Neues vom Urkilogramm
(1999)
Overlayers of SiO2 (nominally 4, 6 and 8 nm thick) on silicon, prepared by thermal oxidation, were investigated using x-ray photoelectron spectroscopy (XPS). The thickness of these overlayers was obtained from a measurement of the photoelectron intensities originating from the substrate and the oxide overlayer by applying an appropriate quantitative model. The uncertainty budget of that thickness measurement method is given. The relative combined standard uncertainty of the method was found to be 15%. The effective attenuation lengths or the corresponding electron inelastic mean free paths are of considerable importance for both the estimated values of overlayer thickness and combined standard uncertainties. The XPS results were compared with ellipsometry data.