Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (47)
- Vortrag (9)
- Beitrag zu einem Tagungsband (7)
- Posterpräsentation (4)
- Beitrag zu einem Sammelband (2)
- Forschungsbericht (2)
- Buchkapitel (1)
Sprache
- Englisch (50)
- Deutsch (21)
- Mehrsprachig (1)
Schlagworte
- XPS (23)
- ToF-SIMS (10)
- NEXAFS (7)
- ESCA (6)
- Microarrays (5)
- Surface analysis (4)
- Carbohydrates (3)
- Plasma polymers (3)
- SIMS (3)
- Self-assembled monolayer (3)
Eingeladener Vortrag
- nein (9)
An electron effective attenuation length (EAL) of 1.68nm for Al Kα excited Pd 3d 5/2 photoelectrons with a kinetic energy of 1.152 keV has been determined experimentally using a sputtered Pd film deposited on an ultra flat fused quartz substrate. The film thickness was reduced by Ar ion sputtering several times in order to obtain different Pd film thicknesses which are used to determine experimental EAL values. These results are compared to data generated by using a Simulation of Electron Spectra for Surface Analysis (SESSA) simulation using an inelastic mean free path (IMFP) calculated with the Tanuma–Powell–Penn (TPP)-2M formula and with ‘elastic scattering on and off’. Contributions to the uncertainty budget related to the experimental approach are discussed in detail. Proposals on how to further improve the approach are suggested.
Reference materials without variations in topography are essential for the characterization of imaging XPS (X-ray Photoelectron Spectroscopy) Instruments. Therefore a new fabrication process for this kind of zero-topography reference material was developed at PTB and resulted in first prototypes. The fabrication process and first measurement results will be presented in this paper.
In this study, epoxy-terminated silicon oxide surfaces were chemically derivatized with trifluoroacetic anhydride (TFAA) and 4-(trifluoromethyl)-benzylamine (TFMBA) and analyzed by X-ray photoelectron spectroscopy, near-edge X-ray absorption fine structure spectroscopy and water contact angle measurements. TFAA was used for quantitative derivatization to determine the amount of reactive epoxy groups on these surfaces. Furthermore, epoxy-terminated surfaces were derivatized with TFMBA (a model compound for biomolecules with an amino linker) yielding secondary amines because of formation of covalent C–N bonds between TFMBA and the epoxy films. Fluorine being part of TFAA and TFMBA composition was used to follow the progress of the chemical derivatization reaction. Both derivatization agents – TFAA and TFMBA – gave comparable reaction yields of ~60% on epoxy silicon surfaces, whereas on epoxy glass slides, the derivatization yields were considerably lower (30–40%).The protocol for attachment of TFMBA (model compound) on epoxy-modified surfaces was adapted to (bio)molecules with an amino linker, e.g. carbohydrates to prepare carbohydrate-functionalized biointerfaces.
The combination of complementary characterization techniques such as SEM (Scanning Electron Microscopy), T-SEM (Scanning Electron Microscopy in Transmission Mode), EDX (Energy Dispersive X-ray Spectroscopy) and SAM (Scanning Auger Microscopy) has been proven to be a powerful and relatively quick characterization strategy for comprehensive morphological and chemical characterization of individual silica and titania nanoparticles. The selected real life test materials, silica and titania, are listed in the OECD guidance manual as representative examples because they are often used as commercial nanomaterials. Imaging by high resolution SEM and in the transmission mode by T-SEM allows almost simultaneous surface and in-depth inspection of the same particle using the same instrument. EDX and SAM enable the chemical characterization of bulk and surface of individual nanoparticles. The core–shell properties of silica based materials are addressed as well. Titania nominally coated by silane purchased from an industrial source has been found to be inhomogeneous in terms of chemical composition.
Nitrogen rich plasma polymer films (L-PPE:N) were prepared by low-pressure RF plasma using a 1:1 mixture of ethylene and ammonia and aged for 345 d in four different ambient conditions: (i) at room temperature (RT) in air; (ii) at RT in nitrogen; (iii) at -20?°C in air and; (iv) at –20 °C in nitrogen. The films were analyzed by X-ray photoelectron spectroscopy (XPS) and by time-of-flight secondary ion mass spectrometry (ToF-SIMS) at various intervals over the duration of the experiment. The ageing of primary amines, NH2, was followed by chemical derivatization with 4-trifluoromethyl benzaldehyde. Storage at –20 °C, mostly independently of ambient atmosphere, slowed down ageing to almost undetectable levels as evaluated by the analytical methods used for this study.
Different, partly complementary and partly redundant characterization methods were applied to study the transition of magnetite, graphite and MoS2 powders to mechanically alloyed nanostructures. The applied methods were: Transmission electron microscopy (TEM), Mössbauer spectroscopy (MS), Raman spectroscopy (RS), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The main objective was to prepare a model material providing the essential features of a typical tribofilm forming during automotive braking, and to assess the impact of different constituents on sliding behaviour and friction level. Irrespective of the initial grain size, the raw materials were transferred to a nanocrystalline structure and mixed on a nanoscopic scale during high energy ball milling. Whereas magnetite remained almost unchanged, graphite and molybdenum disulphide were transformed to a nanocrystalline and highly disordered structure. The observed increase of the coefficient of friction was attributed to a loss of lubricity of the latter ingredient due to this transformation and subsequent oxidation.
Methods for characterization of epoxy-functionalized substrates used for microarray applications, prepared by silanization with 3-glycidoxypropyltrimethoxysilane, have been developed. Contact angle measurements, X-ray photoelectron spectroscopy, time of flight secondary ion mass spectrometry and fluorescence based methods have been applied to investigate these epoxy-functionalized microarray substrates. The surface density of epoxy-functionalized glass slides was investigated by fluorescence labeling of surface species utilizing Rhodamine 110 as fluorescence probe.
An international interlaboratory comparison of the measurement capabilities of four National Metrology Institutes (NMIs) and one Designated Institute (DI) in the determination of the chemical composition of thin Fe-Ni alloy films was conducted via a key comparison (K-67) of the Surface Analysis Working Group of the Consultative Committee for Amount of Substance. This comparison was made using XPS (four laboratories) and AES (one laboratory) measurements. The uncertainty budget of the measured chemical composition of a thin alloy film was dominated by the uncertainty of the certified composition of a reference specimen which had been determined by inductively coupled plasma mass spectrometry using the isotope dilution method. Pilot study P-98 showed that the quantification using relative sensitivity factors (RSFs) of Fe and Ni derived from an alloy reference sample results in much more accurate result in comparison to an approach using RSFs derived from pure Fe and Ni films. The individual expanded uncertainties of the participants in the K-67 comparison were found to be between 2.88 and 3.40 atomic %. The uncertainty of the key comparison reference value (KCRV) calculated from individual standard deviations and a coverage factor (k) of 2 was 1.23 atomic %.