Windings in superconducting magnets operating at 4.2 K are highly susceptible to quenching caused by small frictional heat inputs. Small movements in the magnet system are inevitable during ramping due to the increasing electromagnetic forces. Friction pairs of polymer based materials have been investigated at 4.2 K to gain an understanding of their sliding behavior in conditions representative of superconducting MRI systems. The results indicate that polymer-polymer pairs experience unstable sliding behavior with repeated stick-slip whereas polymer-aluminum couples have stable sliding behavior up to high contact pressures of 20 MPa.
The sliding performance of PEEK composites was investigated in vacuum environment. Tests were performed with carbon fibre reinforced PEEK composites filled with PTFE, and MoS2 or graphite as further solid lubricant. Polymer samples were tested in a pin-on-disc configuration continuously sliding against CrNi-steel. Depending on sliding speed and temperature, the MoS2 filled composites showed high wear resistance and friction coefficients as low as PVD coatings.
High performance polymer composites have been intensively investigated for tribological applications in air, but rarely in hydrogen environment. Author's previous benchmark of composites in liquid hydrogen (LH2) showed that graphite filled polymers have beneficial friction behaviour in this extreme condition. Therefore, further investigations have been undertaken in hydrogen environment. This paper presents first results obtained with polyimide composites filled with different types (natural, synthetic) and amounts of graphite in air, vacuum and hydrogen environments. A particular attention is taken to the influence of hydrogen on graphite as well as on the polymer matrix.
This paper focuses on the influence of the counterface materials on the sliding behaviour of polymer materials in hydrogen. Polyimide (PI), polyetheretherketone (PEEK) and Polytetrafluoroethylene (PTFE) materials were investigated against hardened 52100 martensitic bearing steel and 304 austenitic stainless steel with similar roughness (Ra = 0.2 μm). Results indicate that the friction and wear of PI and PEEK materials depend on the counterface material. This effect wasn’t observed for PTFE composites. While the tribological performance of polyimide is better against 52100 in hydrogen, improved sliding behaviour of PEEK materials is observed with 304 counterface, particularly at higher sliding speed. Surface analyses of the transfer film reveal that the influence of the counterface is primarily related to the chemical nature of the steel for PI and to the thermal conductivity of the disc for PEEK materials.
The tribological behavior of neat and filled PEEK and PEKK composites were compared in air and vacuum conditions. Very low friction and wear coefficient were obtained at low sliding speed while severe wear occurred at high speed. Experimental results are discussed by analysing the transfer film and wear debris.
Wood is widely used in impact limiters of Transport casks for radioactive material. Encapsulated by an outer and inner Steel structure, spruce wood is offen applied in layers of altemating direction. The friction at the interfaces between these layers is of crucial importance for the impact and energy absorption e.g., at an accidental impact of a cask against a hard component.
In order to get detailed Information for corresponding numerical calculations, in this study the friction coefficient for the combinations wood-wood and wood-steel was measured in the temperature ränge between -40 °C and 90 °C according to the relevant stress conditions for such casks. Results show decreasing friction with increasing temperature, ranging from 0.43 at -40 °C to 0.22 for 90 °C for wood-steel combinations and from 0.3 at -40 °C to 0.24 at 90 °C to for a wood-wood combination.