Windings in superconducting magnets operating at 4.2 K are highly susceptible to quenching caused by small frictional heat inputs. Small movements in the magnet system are inevitable during ramping due to the increasing electromagnetic forces. Friction pairs of polymer based materials have been investigated at 4.2 K to gain an understanding of their sliding behavior in conditions representative of superconducting MRI systems. The results indicate that polymer-polymer pairs experience unstable sliding behavior with repeated stick-slip whereas polymer-aluminum couples have stable sliding behavior up to high contact pressures of 20 MPa.
The focus of this study is to evaluate the influence of hydrogen on the friction and wear behavior of a wide range of polymer materials. Thereby, the tribological performance of filled und unfilled polymers from different suppliers were compared at room temperature in air and hydrogen gas (H2) as well as in liquid hydrogen at -235°C (LH2).
The sliding performance of PEEK composites was investigated in vacuum environment. Tests were performed with carbon fibre reinforced PEEK composites filled with PTFE, and MoS2 or graphite as further solid lubricant. Polymer samples were tested in a pin-on-disc configuration continuously sliding against CrNi-steel. Depending on sliding speed and temperature, the MoS2 filled composites showed high wear resistance and friction coefficients as low as PVD coatings.
Besides carbon, metal sulphides are used in every standard brake pad formulation as friction stabilisers. In order to investigate their impact, various powder mixtures were tribologically stressed in a pin-on-disc device in order to produce and test artificial third bodies. containing the three main components of a real friction film, namely magnetite, graphite and a metal sulphide of interest. Since the sliding behaviour is influenced by the relative humidity the powder mixtures are tested at low, medium and high moisture levels. The tests revealed that the presence of graphite dominates the friction behaviour as well as the humidity sensitivity.
The powders were prepared by either manual mixing or high energy ball-milling. Interestingly, all ball-milled blends provided coefficients of friction within the desired range for braking, which was attributed to the effect of zirconia particles from wear debris of the milling balls. The zirconia particles prevent the formation of solid lubricant films on the surfaces and support a homogeneous mixture of all constituents of the powder. Optimum brake performance is gained by an optimum combination of solid lubricants and abrasives.
In a first test series, the friction and wear properties of 6 polymeric candidate materials for application in LNG tribosystems were tested. The most favorable properties showed PTFE composite, filled with carbon fibers and PEEK, which showed low and stable friction and a wear coefficient in the order of 10-7 mm3N-1m-1. PTFE containing PEEK composites seem to be also appropriate for LNG applications. Admixtures of graphite as solid lubricant result in lower wear. Contrary, a lubricating mechanism of MoS2 was not observed. The PI-materials showed comparatively high friction and medium wear.
In a first test series, the friction and wear properties of 6 polymeric candidate materials for application in LNG tribosystems were tested. The most favorable properties showed PTFE composite, filled with carbon fibers and PEEK, which showed low and stable friction and a wear coefficient in the order of 10-7 mm3N-1m-1. PTFE containing PEEK composites seem to be also appropriate for LNG applications. Admixtures of graphite as solid lubricant result in lower wear. Contrary, a lubricating mechanism of MoS2 was not observed. The PI-materials showed comparatively high friction and medium wear.
The tribological characteristics of pure and graphite filled polymers were investigated in gaseous hydrogen at ambient temperatures and in LH2 at -253°C. It could be shown that the tribological properties of PI and PEEK materials is related to the formation of a transfer film. The influence of both hydrogen and cryogenic temperatures will be discussed in the presentation.
High performance polymer composites have been intensively investigated for tribological applications in air, but rarely in hydrogen environment. Author's previous benchmark of composites in liquid hydrogen (LH2) showed that graphite filled polymers have beneficial friction behaviour in this extreme condition. Therefore, further investigations have been undertaken in hydrogen environment. This paper presents first results obtained with polyimide composites filled with different types (natural, synthetic) and amounts of graphite in air, vacuum and hydrogen environments. A particular attention is taken to the influence of hydrogen on graphite as well as on the polymer matrix.
This paper focuses on the influence of the counterface materials on the sliding behaviour of polymer materials in hydrogen. Polyimide (PI), polyetheretherketone (PEEK) and Polytetrafluoroethylene (PTFE) materials were investigated against hardened 52100 martensitic bearing steel and 304 austenitic stainless steel with similar roughness (Ra = 0.2 μm). Results indicate that the friction and wear of PI and PEEK materials depend on the counterface material. This effect wasn’t observed for PTFE composites. While the tribological performance of polyimide is better against 52100 in hydrogen, improved sliding behaviour of PEEK materials is observed with 304 counterface, particularly at higher sliding speed. Surface analyses of the transfer film reveal that the influence of the counterface is primarily related to the chemical nature of the steel for PI and to the thermal conductivity of the disc for PEEK materials.
The talk gives a historical introduction and introduces some of the biggest and most important research institutes in Germany dealing with tribology at Universities, scientific societies and companies. Some examples for research projects and focus areas are given. As an example for a research institute with a long history in tribological research the activities of BAM in Berlin are presented.
The tribological behavior of neat and filled PEEK and PEKK composites were compared in air and vacuum conditions. Very low friction and wear coefficient were obtained at low sliding speed while severe wear occurred at high speed. Experimental results are discussed by analysing the transfer film and wear debris.
Friction coefficients for wood-wood and wood-steel interfaces in impact limiters for transport casks
(2023)
Wood is widely used in impact limiters of transport casks for radioactive material. Encapsulated by an outer and inner steel structure, spruce wood is often applied in layers of alternating direction. The friction at the interfaces between these layers is of crucial importance for the impact and energy absorption e.g., at an accidental impact of a cask against a hard target. In order to get detailed information for corresponding numerical calculations, in this study the friction coefficient for the combinations wood-wood and wood-steel was measured in the temperature range between -40°C and 90°C according to the relevant stress conditions for such casks. Results show decreasing friction with increasing temperature, ranging from 0.43 at -40°C to 0.22 for 90°C for wood-steel combinations and from 0.3 at -40°C to 0.24 at 90°C to for a wood-wood combination.
Wood is widely used in impact limiters of Transport casks for radioactive material. Encapsulated by an outer and inner Steel structure, spruce wood is offen applied in layers of altemating direction. The friction at the interfaces between these layers is of crucial importance for the impact and energy absorption e.g., at an accidental impact of a cask against a hard component.
In order to get detailed Information for corresponding numerical calculations, in this study the friction coefficient for the combinations wood-wood and wood-steel was measured in the temperature ränge between -40 °C and 90 °C according to the relevant stress conditions for such casks. Results show decreasing friction with increasing temperature, ranging from 0.43 at -40 °C to 0.22 for 90 °C for wood-steel combinations and from 0.3 at -40 °C to 0.24 at 90 °C to for a wood-wood combination.