The focus of this study is to evaluate the influence of hydrogen on the friction and wear behavior of a wide range of polymer materials. Thereby, the tribological performance of filled und unfilled polymers from different suppliers were compared at room temperature in air and hydrogen gas (H2) as well as in liquid hydrogen at -235°C (LH2).
The tribological characteristics of pure and graphite filled polymers were investigated in gaseous hydrogen at ambient temperatures and in LH2 at -253°C. It could be shown that the tribological properties of PI and PEEK materials is related to the formation of a transfer film. The influence of both hydrogen and cryogenic temperatures will be discussed in the presentation.
The development of hydrogen technologies is a key strategy to reduce greenhouse gas emission worldwide. Power-to-Gas is a challenging solution, in which hydrogen and methane can be used in mobility, industry, heat supply and electricity generation applications. This presentation deals with the tribological behaviour of polymer materials in hydrogen and methane, both in gas and in liquefied form.
The development of hydrogen technologies entails high safety requirements in distribution and dispensing infrastructure. Therefore, it is necessary to pursue research on material compatibility in hydrogen, especially for critical parts with tribological issues.
The focus of this study is to evaluate the influence of hydrogen on a wider range of commercially available polymer materials. Thereby, the friction and wear behavior of different grades of TPE, POM, PA66, PA12, PPA, PEEK, PPS, PTFE, PAI, PI and PBI were investigated against a rotating steel disk (AISI 304). Filled and unfilled polymers from different suppliers were evaluated at room temperature in air, vacuum and hydrogen gas (H2) as well as in liquid hydrogen at - 253°C (LH2).
The sliding behavior of the polymer materials is discussed by means of surface analyses, whereby special attention is paid to the formation of a transfer film.
According to the results at ambient temperature, the effect of hydrogen environment on the tribological behavior of neat polymers may be related to lack of moisture, but also to saturated hydrocarbons in gaseous hydrogen. In liquid hydrogen, the best tribological performances were achieved with neat PA polymers as well as PPS and PI composites.
In the development of hydrogen technology, special attention is paid to the technical problems of
hydrogen storage. One possible way is cryogenic storage in liquid form. Generally cryotechnical
machines need components with interacting surfaces in relative motion such as bearings, seals or
valves, which are subjected to extreme conditions. Materials of such systems have to be resistant to
friction-caused mechanical deformation at the surface, low temperatures and hydrogen environment.
Since materials failure can cause uncontrolled escape of hydrogen, new material requirements are
involved for these tribo-systems, in particular regarding operability and reliability. In the past few
years several projects dealing with the influence of hydrogen on the tribological properties of friction
couples were conducted at the Federal Institute for Materials Research and Testing, (BAM), Berlin.
This paper reports some investigations carried out with polymer composites. Friction and wear were
measured for continuous sliding and analyses of the worn surfaces were performed after the
experiments. Tests were performed at room temperature in hydrogen as well as in liquid hydrogen.
The influence of hydrogen environment on the friction and wear behavior of polyimide (PI) composites was investigated for two different PI-types (PI1 and PI2) filled with natural or synthetic graphite. Sliding tests were run against AISI 52100 steel and the worn surfaces as well as the transfer film were analyzed by means of SEM, EDX and Infrared Spectroscopy. Results indicate that the chemical structure of the polyimide has a major influence on the tribological behavior. While the friction of PI2 remains rather stable in all environments, PI1 showed very low friction in hydrogen without any lubricant. The lubricity of graphite was found to be more effective in hydrogen than in moist air.
Die tribologischen Eigenschaften von graphitgefüllten Polyimiden gegen Stahl 100Cr6 wurden an Luft, im Hochvakuum (l0⁻ ³ Pa) und in Wasserstoffumgebung bei verschiedenen Drücken (10³ Pa, 10⁴ Pa und 10⁵ Pa) untersucht. Zwei unterschiedliche Polyimid-Typen wurden eingesetzt, wobei Typ und Menge des Graphits variiert wurden.
Die Experimente wurden bei 3,1 MPa Kontaktdruck und einer Gleitgeschwindigkeit von 0,2 m/s bzw. 1 m/s durchgeführt. Die verschlissenen Oberflächen und die Morphologie des Materialübertrags auf die Stahl-Gegenfläche wurden mittels Lichtmikroskopie, REM, TEM und FTIR untersucht. Die Untersuchung zeigt, dass sowohl die Matrix als auch der Graphitanteil einen deutlichen Einfluss auf das Reibverhalten von Verbundwerkstoffen in Wasserstoffumgehungen haben können.