Filtern
Dokumenttyp
Sprache
- Englisch (11)
Schlagworte
- Hydrogen assisted cracking (11) (entfernen)
Organisationseinheit der BAM
In the present work, the influence of deuterium on the microstructure of a duplex stainless steel type EN 1.4462 has been characterized by Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS) supported by scanning electron microscopy (SEM), focused ion beam (FIB), electron back scattered diffraction(EBSD) and energy dispersive x-ray (EDX) investigations. Characterization has been carried out before and after electrochemical charging with deuterium which has been used as a tracer, due to its similar behavior to hydrogen in the steel microstructure. In a first approach, the distribution of the deuterium occurring at temperatures above 58 °C has been visualized. Further it turned out that sub-surface micro blisters are formed in the ferrite-austenite interface, followed by the formation of needle shaped plates and subsequent cracking at the ferrite surface. In the austenite phase, parallel cracking alongside twins and hexagonal close packed (martensitic) regions has been observed. In both phases and even in the apparent interface, cracking has been associated with high deuterium concentrations, as compared to the surrounding undamaged microstructure. Sub-surface blistering in the ferrite has to be attributed to the accumulation and recombination of deuterium at the ferrite-austenite interface underneath the respective ferrite grains and after fast diffusing through this phase. Generally, the present application of chemometric imaging and structural analyses allows characterization of hydrogen assisted degradation at a sub-micron lateral resolution.
Deuterium permeation and cracking in duplex steels as viewed by ToF-SIMS and HR-SEM with data fusion
(2016)
Better understanding of hydrogen assisted degradation and trapping mecha-nisms requires sufficient imaging techniques for respective hydrogen-microstructure interaction studies, in particular with multi-phase metallic micro-structures [1]. The present work is focusing on the elucidation of deuterium be-havior in two austenitic-ferritic duplex stainless steels (DSS) under the assumption that deuterium behaves in many ways similarly to hydrogen [2]. For case studies standard 2205 and lean 2101 DSSs were chosen due to the extensive use of these steels in industry [3]. The analyses were conducted by using a novel in-situ permeation and Time-of-Flight secondary ion mass spectrometry (ToF-SIMS) imaging technique or by ex-situ ToF-SIMS imaging following electrochemical charging experiments. Another pioneering procedure was data fusion (including chemometry) of results of powerful laterally resolved chemical analysis and high resolution structural characterization techniques .
Results for the ex-situ observations showed a different influence of deuterium loading on the two steel grades as well as different damage mechanisms in each phase. Formation of sub-surface blisters between the ferrite and austenite were obtained in both the standard and the lean DSS. In both steels, an increased deuterium concentration was observed around deformed regions such as cracks, confirming that they originate from the presence of deuterium [4]. The formation of parallel cracks was obtained only in the austenite within the standard duplex whereas in the lean duplex the highest intensity of deuterium was obtained in the austenite along the ferrite-austenite interphase.
In comparison, application of the novel in-situ permeation technique enabled to register and record the deuterium permeation through the material and the respective saturation sequence of the two phases as well as the interfaces. Faster diffusion of the deuterium was observed in the ferrite and a direct proof for deuterium enrichment at the austenite-ferrite interface has been given [1]. The integration of the specified techniques gives a better insight into the processes leading to hydrogen induced failure. These two experimental techniques provide very valuable tools for elucidation of respective metallurgical failure mechanisms that can be used for the validation of respective numerical models for hydrogen assisted cracking (HAC).
The explosion of hydrogen gas storage cylinders on May 25, 1894, represents one of the most spectacular failure cases during the late industrialization period in Germany. With respect to modern applications to hydrogen storage as energy carrier, it has several times been referred to as precedent failure case for the whole industrial sector. The detailed investigation reports by Martens have thus gained interest in the last years, but also, because the publications in 1896 about his expertise already provided in September 1894 document one of the first and most comprehensive investigations which can be regarded as a nucleus for modern failure analysis.
After summarizing the newspaper reports in the introduction, the present contribution provides a review of Martens' reports targeted at the development of failure analyses and materials testing procedures as well as potential failure origins.
Hydrogen might be introduced during fabrication welding or might be taken up from an environment during sour service or cathodic protection. Thus, hydrogen assisted stress corrosion and cold cracking is still a major topic regarding the reliability of welded steel components, as for instance offshore platforms and pipelines. In order to support conclusive testing and life time evaluation of welded steel components, a numerical model for hydrogen assisted cracking has been developed, particularly taking into consideration the geometrical effects of crack propagation on the respective hydrogen distribution alongside and ahead of the crack. Numerical calculations were based on finite element analysis of the hydrogen and stress-strain distribution by using a commercially available program. The model has been verified experimentally by slow strain rate experiments of supermartensitic stainless steels which are intended to be used more extensively as materials for welded flowlines in North Sea oil and gas production. As first results of such simulations the influence of the subsurface concentration provided by different H2S saturation levels in the NACE TM 0177-96 standard solution on crack propagation and the effect of crack shape on the hydrogen distribution profile are presented in this contribution.
High temperature SSRT - ductility data from cathodic hydrogen charging of 10CrMo910 and 7CrMoVTiB1010 are implemented into a mathematical model of SCC at various operational conditions including temperatures, pH and dissolved hydrogen/oxygen contents as well as global stresses and material properties. The results show that, as a consequence of experimentally verified local acidification at initial anodic path corrosion, subsequent local hydrogen assisted cracking can be a controlling factor for SCC in high temperature water. As a particular effect at global stresses close to the yield point, operational temperatures around 270°C exhibit peak crack growth rates depending on dissolved hydrogen, oxygen, pH and global stress, which has been found to be consistent for both, experimental studies and mathematical modeling.
Modeling of Hydrogen-Assisted Cracking (HAC) in Duplex Stainless Steels (DSS):
- Hydrogen causes significant degradation in DSS and consequently HAC
- Mechanisms of HAC have not been fully understood in two-phase microstructures
- Mesoscale numerical modeling for HAC in DSS was created, coupled to the macroscale, enabling simulation of HAC in both phases independent from predefined crack paths
A seamless pipe made of AISI 321 stainless steel represented a part of a transportation Pipeline system for hydrogen-containing hot gas in a hydrocarbon cracking unit. After a service period of approximately 21 months, a segment of such pipe demonstrated the cracks, causing leakage and respective fire. For clarification of a failure root cause, various metallurgical investigations combined with numerical simulations have been applied. The results revealed that the rupture of seamless pipe was evidently influenced by hydrogen assisted cracking (HAC). An increased susceptibility of the alloy to HAC had to be attributed to its sensitive microstructure which was related to the occurrence of slip bands with a high quantity in austenite grains, particularly in the specific region underneath the outer wall surface. In addition, the intensity of restraint resulting from the T-joint weld configuration caused respectively higher triaxial stresses in the confined area on the outer wall surface where the crack started. The numerical simulations of hydrogen diffusion revealed that a uniform hydrogen concentration profile over the pipe wall thickness was reached when the service period was more than 20 months. This duration agreed well to the timeto-failure of the actual component. Considering additionally that the final stage of rupture by overload was preceded by severe HAC, as confirmed by the respective intergranular fracture topography.
Literature provides a wide range of hydrogen diffusion coefficients for low alloyed steels used in power plants. In fact, experimental boundary conditions and calculation methods have influence on the determination of these coefficients. The diffusion and trapping behavior in creep-resistant steel 7CrMoVTiB10-10 has been studied. Based on experimental carrier gas hot extraction (CGHE) data, a numerical model has been developed to describe the hydrogen transport and respective hydrogen distribution at elevated temperatures. The numerical results suggest that common calculation methods for diffusion coefficients are limited for experimental data analysis. The sample preparation time before CGHE experiment influences the determined diffusion coefficients with the consequence that non-homogeneous hydrogen concentration profiles have to be considered in the simulations.