Hydrogen might be introduced during fabrication welding or might be taken up from an environment during sour service or cathodic protection. Thus, hydrogen assisted stress corrosion and cold cracking is still a major topic regarding the reliability of welded steel components, as for instance offshore platforms and pipelines. In order to support conclusive testing and life time evaluation of welded steel components, a numerical model for hydrogen assisted cracking has been developed, particularly taking into consideration the geometrical effects of crack propagation on the respective hydrogen distribution alongside and ahead of the crack. Numerical calculations were based on finite element analysis of the hydrogen and stress-strain distribution by using a commercially available program. The model has been verified experimentally by slow strain rate experiments of supermartensitic stainless steels which are intended to be used more extensively as materials for welded flowlines in North Sea oil and gas production. As first results of such simulations the influence of the subsurface concentration provided by different H2S saturation levels in the NACE TM 0177-96 standard solution on crack propagation and the effect of crack shape on the hydrogen distribution profile are presented in this contribution.
Hydrogen assisted stress corrosion and cold cracking represent still a major topic regarding the safety of welded steel components against failure in many industrial branches. Hydrogen might be introduced during fabrication welding or might be taken up from an environment during sour service or at cathodic protection. Additionally, understanding and avoidance of hydrogen entry into weld microstructures from gaseous pressurized environments becomes increasingly important for renewable energy components. There are two types of metallurgical mechanisms associated with hydrogen assisted cracking, i.e. the cracking as well as hydrogen transport and trapping mechanisms. For numerical modelling, it has to be considered that both types are not independent of each other, that the mechanisms are not yet completely clarified and that validation of such models strongly depends on implementation of the correct hydrogen related materials properties. However, quite significant achievements have been made in modelling of hydrogen assisted cracking by indirect coupling of thermal, stress-strain as well as hydrogen uptake and diffusion analyses. After a brief introduction into the subject and by revisiting various proposed cracking mechanisms, the present contribution focuses on recent developments of a numerical model based on a comparison of actual hydrogen concentrations and mechanical loads with respective hydrogen dependent material properties as crack initiation and propagation criteria. The basic procedure for numerical simulation of crack initiation and propagation is outlined and it is shown how such numerical simulations can be validated experimentally. Furthermore, it is highlighted how such a procedure has been extended to a comprehensive model for life time prediction of welded steel pipeline components and experimentally verified. Finally, it is outlined how the model can be extended to simulate cracking in heterogeneous steel microstructures on the different scales.