Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (94)
- Beitrag zu einem Tagungsband (16)
- Beitrag zu einem Sammelband (8)
- Forschungsbericht (6)
- Monografie (1)
- Buchkapitel (1)
Sprache
- Englisch (126) (entfernen)
Schlagworte
- XPS (15)
- Welding (9)
- Residual stress (8)
- Nanoparticles (6)
- NEXAFS (5)
- Additive manufacturing (4)
- CCQM (4)
- Fluorescence (4)
- Low transformation temperature (4)
- Residual stresses (4)
Organisationseinheit der BAM
- 9 Komponentensicherheit (16)
- 9.4 Integrität von Schweißverbindungen (12)
- 6 Materialchemie (10)
- 6.1 Oberflächen- und Dünnschichtanalyse (8)
- 1 Analytische Chemie; Referenzmaterialien (7)
- 7 Bauwerkssicherheit (4)
- 9.0 Abteilungsleitung und andere (4)
- 1.4 Prozessanalytik (3)
- 7.2 Ingenieurbau (3)
- 9.2 Versuchsanlagen und Prüftechnik (3)
Paper des Monats
- ja (3)
The present work shows results on elemental distribution analyses in Cu(In,Ga)Se2 thin films for solar cells performed by use of wavelength-dispersive and energy-dispersive X-ray spectrometry (EDX) in a scanning electron microscope, EDX in a transmission electron microscope, X-ray photoelectron, angle-dependent soft X-ray emission, secondary ion-mass (SIMS), time-of-flight SIMS, sputtered neutral mass, glow-discharge optical emission and glow-discharge mass, Auger electron, and Rutherford backscattering spectrometry, by use of scanning Auger electron microscopy, Raman depth profiling, and Raman mapping, as well as by use of elastic recoil detection analysis, grazing-incidence X-ray and electron backscatter diffraction, and grazing-incidence X-ray fluorescence analysis. The Cu(In,Ga)Se2 thin films used for the present comparison were produced during the same identical deposition run and exhibit thicknesses of about 2 µm. The analysis techniques were compared with respect to their spatial and depth resolutions, measuring speeds, availabilities, and detection limits.
Solid-state phase transformations and the evolution of thermal and elastic strains in novel low temperature transformation (LTT) weld filler materials in the near surface region are monitored in real time by means of an innovative experimental set-up at the PDIFF (powder diffraction) beamline at the synchrotron light source ANKA (Angströmquelle Karlsruhe) at the KIT (Karlsruhe Institute for Technology). The key components of the diffraction set-up are two fast microstrip line detectors, which enables the strain evolution to be followed as a function of time and temperature for a 0.5?s counting time. During controlled heating and cooling cycles, as well as during near welding cycles, the martensite–austenite–martensite phase transitions are analysed. The transformation kinetics are monitored during resistance heating of small chips of the pure LTT alloys and during gas tungsten arc welding of simplified LTT welds using a specially designed welding rig for in-situ studies on the diffraction instruments. Under the mechanically unconstrained condition allowing free thermal expansion and shrinkage, the LTT alloys are found to exhibit decreasing transformation temperatures Ac and MS and increasing phase fraction of retained austenite for increasing Ni content. The strain evolution during welding reveals increased compressive stresses upon welding, which is attributed to the martensite formation upon cooling, which counteracts the thermal contraction strains. Comparison of the transformation temperatures reveals higher values than in the pure LTT alloys, but no variation between the different alloys. On the one hand, this is attributed to preferred grain orientation affecting the diffraction measurements and the determination of the transformation temperatures. On the other hand, it is possible that with the different chemical compositions of the LTT alloys and the mechanical constraints during welding, the evolution of the residual strain and stress may vary and result in counteracting affects with respect to lowered martensite start temperatures.
We discuss the stability of weld residual strain under static and quasi cyclic transverse tensile loading in the elastic and elastic–plastic region. The test welds were joined with low transformation temperature weld filler materials with 10 wt% Cr and varying Ni-content from 8 to 12 wt%. Using neutron diffraction the residual lattice strain in the martensitic α'- and austenitic γ-phase in the fusion zone as well as the ferritic α-phase in the heat affected zone and base metal as induced by welding, superimposed by stepwise tensile loading and after unloading was measured. The amount of retained austenite in the fusion zone increases with increasing Ni-content, but it decreases with increasing load level due to stress induced martensite formation. In the as-welded condition the transverse macroscopic residual lattice strain was found to be in low compression in the fusion zone in each weld, while the heat affected zone was in tension. Local plastic deformation of the γ-phase as a result of yielding during tensile loading in combination with the change in phase fraction resulted in increased macroscopic compression in the fusion zone. The reduced yield strength in the heat affected zone resulted in plastic deformation and a considerable shift into compression. Comparison with the cross weld distribution of the hardness and FWHM of the neutron diffraction interference lines supported the assumption of plastic deformation of the γ- and α-phase in the fusion and heat affected zone, respectively, while the α'-phase in the fusion zone was stressed within the elastic regime only. Microstructural observations as well as measurement of the local γ-phase fraction by means of laboratory X-ray diffraction in the fusion zone strengthen these observations.
A recent approach to measure electron radiation doses in the kGy range is the use of phosphors with an irradiation dose-dependent luminescence decay time. However, the applicability of the previously investigated material NaYF4:Yb3+,Er3+ is limited as it shows pronounced fading. Therefore, in this work, a modified SrF2 synthesis is presented that results in SrF2 nanoparticles codoped with Yb and either Er, Hm, or Tm. To assess their suitability as dosimeter material, dose response, as well as its degree of fading over 50 up to 140 days after irradiation were measured. Fading rates as small as 5% in SrF2:Er,Yb and 4% in SrF2:Ho,Yb were derived, which are comparable to established dosimeter materials. A combination of spectroscopy, diffraction and DFT calculations was used to elucidate the effect of irradiation, pointing towards the formation of a secondary phase of Yb2+ that we predict could be Yb2OF2. This irreversible formation of a secondary phase is considered to be the explanation for the low fading behavior in SrF2-based phosphors compared to NaYF4:Yb, Er, a highly attractive feature for electron beam dosimetry.
Due to the recent widespread application of nanomaterials to biological systems, a careful consideration of their physiological impact is required. This demands an understanding of the complex processes at the bio–nano interface. Therefore, a comprehensive and accurate characterization of the material under physiological conditions is crucial to correlate the observed biological impact with defined colloidal properties. As promising candidates for biomedical applications, two SiO2-based nanomaterial systems were chosen for extensive size characterization to investigate the agglomeration behavior under physiological conditions. To combine the benefits of different characterization techniques and to compensate for their respective drawbacks, transmission electron microscopy, dynamic light scattering and asymmetric flow field-flow fractionation were applied. The investigated particle systems were (i) negatively charged silica particles and (ii) poly(organosiloxane) particles offering variable surface modification opportunities (positively charged, polymer coated). It is shown that the surface properties primarily determine the agglomeration state of the particles and therefore their effective size, especially under physiological conditions. Thus, the biological identity of a nanomaterial is clearly influenced by differentiating surface properties.
Recently, time-of-flight secondary ion mass spectrometry (ToF-SIMS) and X-ray photoelectron spectroscopy (XPS) instrumentation has been used to address areas of interest within micro-fluidic devices providing full access to the surface chemistry established at the bottom of micro-channels therein. After careful calibration, information on surface chemistry as obtained by ToF-SIMS or XPS can be interpreted in terms of wettability expressed as contact angles which are then characteristic for the inner walls of micro-channels. Standard contact angle measurement is not applicable in micro-channels. The approach has been demonstrated to be successful with two different micro-fluidic devices hot embossed into high-end quality poly(methyl methacrylate) (PMMA) or Polycarbonate wafers. A pre-selected surface chemistry at micro-channel walls can be established by plasma technologies but ageing and rinsing effects have to be under control. A combination of ToF-SIMS, XPS and contact angle measurement techniques has been demonstrated to provide the required information. Finally, it is shown by ToF-SIMS and XPS analysis that in the production of micro-fluidic parts during practical processing using hot embossing technologies, material originating from cover foils will reside on the polymer wafer's surface. Moreover, residues of releasing agents as silicone oil used during processing can be detected by ToF-SIMS. Both cover foil residues and silicones are issues of trouble shooting in micro-fluidics because they will change contact angles efficiently.
The wettability of the surfaces inside the microchannels of a microfluidic device is an important property considering a liquid flows through them. Contact angle measurements usually applied to test the wettability of surfaces cannot be used for an analysis of microchannel walls within microfluidic devices. A workaround is the use of surface analytical methods, which are able to reach points of interest in microchannels and may provide information on the surface chemistry established there. In calibrating these methods by using flat polymer wafers, where the contact angle can be measured as usual, data measured in real microchannels can be evaluated in terms of wetting properties. Reference wafers of bisphenol-A polycarbonate, a polymeric material that is often used in fluidic microdevice fabrication, were treated under different oxygen plasma conditions. The modified surfaces were characterized by using XPS, time of flight (ToF)-SIMS and atomic force microscope (AFM). Surface chemistry and surface topography have been correlated with contact angle measurements. In addition, effects of ageing or rinsing after plasma treatment have also been investigated.
The interest in (micro)porous systems is greater than ever before with microporous polymers finding application in areas such as gas storage/separation and catalysis. In contrast to the vast majority of publications on microporous polymers seeking ever higher values for surface area or uptake capacity for a particular gas, this work presents a means to render a microporous system responsive to electromagnetic stimuli. The incorporation of a diarylethene (DAE) derivative in the backbone of a polymer of intrinsic microporosity (PIM) produces a microporous system that exhibits photochromism as proven by UV–vis absorption and NMR studies. In the resulting DAE-PIM, surface area is not a fixed unalterable property but can be influenced by the external and nondestructive stimulus light in a reversible manner. Furthermore, in combination with Matrimid, free-standing membranes can be produced that display light-switchable diffusivity and permeability for carbon dioxide and oxygen. In this way, material scientists are offered the potential to employ only one system that can assume several states with different properties for each.