The RILEM technical committee TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ conducted a round robin testing programme to determine the validity of various durability testing methods, originally developed for Portland cement based-concretes, for the assessment of the durability of alkali-activated concretes. The outcomes of the round robin tests evaluating sulfate resistance, alkali-silica reaction (ASR) and freeze–thaw resistance are presented in this contribution. Five different alkali-activated concretes, based on ground granulated blast furnace slag, fly ash, or metakaolin were investigated. The extent of sulfate damage to concretes based on slag or fly ash seems to be limited when exposed to an Na2SO4 solution. The mixture based on metakaolin showed an excessive, very early expansion, followed by a dimensionally stable period, which cannot be explained at present. In the slag-based concretes, MgSO4 caused more expansion and visual damage than Na2SO4; however, the expansion limits defined in the respective standards were not exceeded. Both the ASTM C1293 and RILEM AAR-3.1 test methods for the determination of ASR expansion appear to give essentially reliable identification of expansion caused by highly reactive aggregates. Alkali-activated materials in combination with an unreactive or potentially expansive aggregate were in no case seen to cause larger expansions; only the aggregates of known very high reactivity were seen to be problematic. The results of freeze–thaw testing (with/without deicing salts) of alkali-activated concretes suggest an important influence of the curing conditions and experimental conditions on the test outcomes, which need to be understood before the tests can be reliably applied and interpreted.
Two fly ash-based geopolymer concretes with quartz aggregates or with expanded clay (lightweight) aggregates were exposed to the ISO 834-1 standard fire curve in a small-scale fire test set-up. Acoustic emission measurements during fire exposure and subsequent cooling were employed to study spalling events and cracking during the tests. Optical microscopy and additional acoustic measurements were conducted after the testing to better understand the crack propagation in the samples. The testing revealed that neither of the concretes were susceptible to spalling, which is particularly notable for the concrete with quartz aggregates, as it is a high-strength concrete. This behavior is attributed to the relatively high permeability of the concretes and their low amount of chemically bound water. Significant crack formation was detected only around the temperature of the alpha–beta quartz transition (573 °C) and on cooling. Because of aggregate deformations at the quartz transition temperature, deterioration after heating was more significant in the geopolymer concrete with quartz aggregates. Crack formation also occurred in the concrete with expanded clay aggregates, caused by shrinkage of the geopolymer paste on cooling. Acoustic emission measurements proved to be a valuable tool to investigate processes during high temperature exposure.