- Water content (3) (entfernen)
Organisationseinheit der BAM
- 5 Werkstofftechnik (2)
- 5.6 Glas (2)
Stable crack growth was measured for nominal dry and water-bearing (6 wt%) soda-lime silicate glasses in double cantilever beam geometry and combined with DMA studies on the effects of dissolved water on internal friction and glass transition, respectively. In vacuum, a decreased slope of logarithmic crack growth velocity versus stress intensity factor is evident for the hydrous glass in line with an increase of b-relaxation intensity indicating more energy Dissipation during fracture. Further, inert crack growth in hydrous glass is found to be divided into sections of different slope, which indicates different water related crack propagation mechanism. In ambient air, a largely extended region II is observed for the hydrous glass, which indicates that crack growth is more sensitive to ambient water.
The effect of structural water on density, elastic constants and microhardness of water-bearing soda-lime-silica glasses of up to 21.5 mol% total water is studied. It is found that the Poisson ratio and the water content are positively correlated, while density and the elastic moduli decrease with increasing water content. Vickers hardness decreases by approximately 27% from the dry to the most hydrous glass. For water fractions <3 mol%, the dependencies are non-linear reflecting the non-linear change in the concentrations of OH and H2O molecules dissolved, whereas for water fractions >3 mol% linear dependencies are found. To distinguish the effect of structural water and environmental water, indentations were performed in toluene, nitrogen gas and air. Timedependent softening was evident for testing dry glasses in humid atmospheres as well as for tests of hydrous glasses in dry atmospheres. This indicates that the response times of dissolved water species are effectively equal in both scenarios.
The internal friction of hydrated soda-lime-silica glasses with total water content (CW ) up to 1.9 wt. % was studied by dynamic mechanical analysis (DMA) using temperature-frequency sweeps from 723 K to 273 K and from 1 s-1 to 50 s-1. Total water content and concentrations of H2O molecules (CH2O ) and OH groups (COH) in the DMA specimens were determined by infrared spectroscopy. For low water contents (CW ≈ COH < 0.25 wt. %) two discrete internal friction peaks below the glass transition (α relaxation) were assigned to the low-temperature motion of alkali ions (γ relaxation) and cooperative movements of dissimilar mobile species under participation of OH at higher temperature (βOH relaxation). For large water contents (CW > 1 wt. %), where significant amounts of molecular water are evident (CH2O > 0.15 wt. %), however, internal friction spectra change unexpectedly: the βOH peak heights saturate and a low temperature shoulder appears on the β-relaxation peak. This emerging relaxation mode (βH2O relaxation) was assigned to the motions of H2O molecules. βH2O relaxation was found to be faster than βOH but slower than γ relaxation. Activation energy of the different relaxation modes increased in the order γ < βH2O < βOH < α.