Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (50)
- Vortrag (10)
- Beitrag zu einem Tagungsband (5)
- Beitrag zu einem Sammelband (4)
- Posterpräsentation (4)
- Buchkapitel (1)
Sprache
- Englisch (74) (entfernen)
Schlagworte
- Glass (12)
- Sintering (8)
- Crystallization (6)
- LTCC (6)
- Viscosity (5)
- Water-bearing glasses (5)
- Foaming (4)
- Glass powder (4)
- Inclusions (4)
- EBSD (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (31)
- 5.6 Glas (30)
- 6 Materialchemie (3)
- 5.1 Mikrostruktur Design und Degradation (2)
- 6.3 Strukturanalytik (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.2 Biophotonik (1)
- 1.7 Organische Spuren- und Lebensmittelanalytik (1)
- 5.0 Abteilungsleitung und andere (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
Eingeladener Vortrag
- nein (10)
Up to now, oriented surface crystallization phenomena are discussed controversially, and related studies are restricted to few glasses. For silicate glasses we found a good correlation between the calculated surface energy of crystal faces and oriented surface nucleation. Surface energies were estimated assuming that crystal surfaces resemble minimum energy crack paths along the given crystal plane. This concept was successfully applied at the Institute of Physics of Rennes in calculating fracture surface energies of glasses. Several oriented nucleation phenomena can be herby explained assuming that high energy crystal surfaces tend to be wetted by the melt. This would minimize the total interfacial energy of the nucleus. Furthermore, we will discuss the evolution of the microstructure and its effect on the preferred crystal orientation.
Development of wood-inorganic composites with enhanced properties and environmental stability
(2002)
The system Na2O.B2O3-SiO2 (NBS) is the basis of many industrial glass applications and therefore one of the most studied systems at all. Glass formation is possible over a wide compositional range, but the system also contains ranges of pronounced phase separation and crystallization tendency. Despite its importance, experimental data are limited to few compositional areas. The general understanding and modelling of glass formation, phase separation, and crystallization in this system would therefore be easier if small step melt series could be studied. The efficient melting of such glass series is now possible with the new robotic glass melting system at the Federal Institute for Materials Research and Testing (BAM, Division Glasses). Using three exemplary joins within this NBS system, the small step changes of glass transition temperature (Tg), crystallization behavior as well as glass density (Roh) was studied. Additionally, experimental Tg and Roh data were compared with their modeled counterparts using SciGlass and a newly developed DFT model, respectively.
Polyether and -ester urethanes (PU) were exposed to artificial weathering at 40 °C and artificial UV radiation in a weathering chamber. In 3 parallel exposures, humidity was varied between dry, humid, and wet conditions. Material alteration was investigated by various analytical techniques like size exclusion chromatography
(SEC), liquid chromatography-infrared spectroscopy (LC-FTIR), thermal-desorption gas chromatography-mass spectrometry (TD-GC-MS), fluorescence mapping and dynamic mechanical analysis (DMA). Our results show that depending on the weathering conditions, different degradation effects can be observed. By means of SEC an initial strong decrease of the molar masses and a broadening of the mass distributions was found. After a material dependent time span this was followed by a plateau where molar mass changes were less significant. A minor moisture-dependent degradation effect was only found for polyester PU. Fluorescence measurements on two materials revealed an increase in the luminescence intensity upon weathering process reaching a saturation level after about 500 h. The changes in the optical properties observed after different exposure conditions and times were very similar. The TD-GC-MS data showed the fate of the stabilizers and antioxidant in the course of weathering. LC-FTIR measurements revealed a change in peak intensities and the ratio of urethane and carbonyl bands.