Filtern
Erscheinungsjahr
Dokumenttyp
Referierte Publikation
- ja (21) (entfernen)
Schlagworte
- Laser cleaning (5)
- Femtosecond laser (4)
- Friction (3)
- Femtosecond laser ablation (2)
- Laser (2)
- Laser-induced periodic surface structures (LIPSS) (2)
- Paper (2)
- Wear (2)
- Ablation (1)
- Biomaterials (1)
Organisationseinheit der BAM
- 6 Materialchemie (4)
- 6.2 Material- und Oberflächentechnologien (3)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 6.0 Abteilungsleitung und andere (1)
- 6.3 Strukturanalytik (1)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (1)
- 6.6 Physik und chemische Analytik der Polymere (1)
- 6.7 Materialsynthese und Design (1)
- 9 Komponentensicherheit (1)
Template Electrodeposition of Nanowire Arrays on Gold Foils Fabricated by Pulsed-Laser Deposition
(1995)
A detailed diagnostic study of the interaction of nanosecond laser pulses from the near-ultraviolet to the near-infrared wavelength range with various types of contemporary and ancient parchments is presented. The advantages of laser cleaning due to the absence of chemical agents, spectroscopic selectivity, micro-precision and computer-aided handling can only be verified when physico-chemical diagnostics guarantee destructionless processing. Scanning electron microscopy data are correlated with chemical degradation and morphological changes dependent on the laser fluence and wavelength. It is also shown how transmission electron microscopy, diffuse reflectance infrared Fourier transform spectroscopy, and pyrolysis capillary gas chromatography can be employed in the chemical diagnostics of laser cleaning of parchment. This study suggests that the ageing status of parchment artefacts plays a major role in assessing the laser cleaning limits.
The applicability of excimer laser at 308 nm and Nd:YAG laser at 532 nm with fluences below 0.86 J/cm2 for cleaning of cellulose and paper materials was evaluated. The extent of degradation of purified cotton cellulose and Fabriano paper after laser treatment as well as after a period of accelerated humid oven ageing was determined by following the changes in the degree of polymerization. While irradiation of paper with the excimer laser at 308 nm results in depolymerization of cellulose accompanied by a decrease in ISO brightness, no detrimental effects of Nd:YAG laser treatments were observed.
Censorship of parts of written text was and is a common practice in totalitarian regimes. It is used to destroy information not approved by the political power. Recovering the censored text is of interest for historical studies of the text. This paper raises the question, whether a censored postcard from 1942 can be made legible by applying multispectral imaging in combination with laser cleaning. In the fields of art conservation (e.g. color measurements), investigation (e.g. Analysis of underdrawings in paintings), and historical document analysis, multispectral imaging techniques have been applied successfully to give visibility to information hidden to the human eye.
The basic principle of laser cleaning is to transfer laser pulse energy to a contamination layer by an absorption process that leads to heating and evaporation of the layer. Partial laser cleaning of postcards is possible; dirt on the surface can be removed and the obscured pictures and writings made visible again. We applied both techniques to the postcard. The text could not be restored since the original ink seems to have suffered severe chemical damage.
Optical fibers made of fused silica are a common method of transmitting high laser pulse energies. Failure of those fibers is a significant risk. The determination of laser-induced damage thresholds (LIDT) on fiber end facets according to ISO 21254 standard is needed. In the past, single pulse nanosecond laser experiments showed an improvement of LIDT with increasing fiber core diameter for 1064 nm wavelength and a constant beam diameter of 50 µm.
This paper pays particular attention to the influence of the laser beam diameter on damage resistance. All-silica fiber types (LEONI) with different core diameters (100–600 µm) were investigated using beam diameters in a range from 30 µm to 100 µm. For comparison experiments on fused silica preform material (Heraeus F300) were performed. On one hand, surface LIDT of fused silica preform material decreases significantly with increasing beam size. A model considering a random distribution of point defects explains the experimental data qualitatively. On the other hand, LIDT of fiber end facets stays constant. White light microscopy results suggest that the point defect density on fiber end facets is lower compared to the preform surface due to an excellent surface polish quality.
Laser cleaning of delicate biological composite materials such as ancient parchment manuscripts from the 15th and 16th century and printed paper from the 19th century is demonstrated with an ultraviolet excimer pulsed laser at 308 nm. Laser fluence levels must stay below the ablation and destruction threshold of the parchment or paper substrate, and have to surpass the threshold of the contaminant matter. Foreign layers to be removed must exhibit a higher optical density than the artifact substrates. Synthetic carbonaceous dirt modelled by water-soluble black crayons showed a characteristically weak featureless laser-induced plasma spectroscopy spectrum near the noise limit. It turned out that laser-induced plasma spectroscopy is of limited use in monitoring halting points (or etch-stops) because it relies on the destruction not only of the laterally inhomogenously distributed contaminant but also of pigment phases on a microscopically rough parchment substrate. Laser-induced fluorescence spectroscopy, however, promises to be a valuable non-destructive testing technique for etch-stop monitoring.
Cleaning of paper is a challenging task due to the fact that a contamination should be removed and a fragile organic original material has to be preserved. Pulsed laser cleaning of artificially soiled Whatman© filter paper samples serving as models for historical paper was performed. Different cleaning strategies employing 8-ns laser pulses at 532 nm wavelength were applied to clean paper avoiding undesired effects like discoloration (yellowing) and mechanical deterioration of the substrate. Multi shot experiments with low-energy pulses were compared with single pulse investigations utilizing high pulse energies achieving a constant energy load incident on the samples in both cases. The cleaning efficiency and possible yellowing effects were evaluated by means of a multi spectral imaging system. An extensive microscopic analysis of the cleaned parts of the samples provided insight into the remaining soiling on the surface and in the bulk of the paper material after laser treatment. As a reference, a hard and a soft eraser were used to clean the samples.
Laser-induced periodic surface structures (LIPSS, ripples) were generated on stainless steel (100Cr6) and titanium alloy (Ti6Al4V) surfaces upon irradiation with multiple femtosecond laser pulses (pulse duration 30 fs, central wavelength 790 nm). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning geometry for the processing of large surface areas (5 × 5 mm²) covered homogeneously by the nanostructures. The irradiated surface regions were subjected to white light interference microscopy and scanning electron microscopy revealing spatial periods around 600 nm. The tribological performance of the nanostructured surface was characterized by reciprocal sliding against a ball of hardened steel in paraffin oil and in commercial engine oil as lubricants, followed by subsequent inspection of the wear tracks. For specific conditions, on the titanium alloy a significant reduction of the friction coefficient by a factor of more than two was observed on the laser-irradiated (LIPSS-covered) surface when compared to the non-irradiated one, indicating the potential benefit of laser surface structuring for tribological applications.
Cleaning of artificially soiled paper using nanosecond, picosecond and femtosecond laser pulses
(2010)
Cleaning of cultural assets, especially fragile
organic materials like paper, is a part of the conservation
process. Laser radiation as a non-contact tool offers
prospects for that purpose. For the studies presented here,
paper model samples were prepared using three different paper
types (pure cellulose, rag paper, and wood-pulp paper).
Pure cellulose serves as reference material. Rag and woodpulp
paper represent essential characteristics of the basic
materials of real-world artworks. The papers were mechanically
soiled employing pulverized charcoal. Pure and artificially soiled paper samples were treated with laser pulses of
28 fs (800 nm wavelength) and 8–12 ns (532 nm) duration in
a multi pulse approach. Additionally, the cellulose reference
material was processed with 30 ps (532 nm) laser pulses.
Damage and cleaning thresholds of pure and soiled paper
were determined for the different laser regimes. Laser working
ranges allowing for removal of contamination and avoiding
permanent modification to the substrate were found.
The specimens prior and after laser illumination were characterized
by light-optical microscopy (OM) and scanning
electron microscopy (SEM) as well as multi spectral imaging
analysis. The work extends previous nanosecond laser
cleaning investigations on paper into the ultra-short pulse
duration domain.
Laser-induced periodic surface structures (LIPSS, ripples) were processed on steel (X30CrMoN15-1) and titanium (Ti) surfaces by irradiation in air with linear polarized femtosecond laser pulses with a pulse duration of 30 fs at 790 nm wavelength. For the processing of large LIPSS covered surface areas (5 mm × 5 mm), the laser fluence and the spatial spot overlap were optimized in a sample-scanning geometry. The laser-processed surfaces were characterized by optical microscopy (OM), white light interference microscopy (WLIM) and scanning electron microscopy (SEM). Spatial LIPSS periods between 450 and 600 nm were determined. The nanostructured surface regions were tribologically tested under reciprocal sliding conditions against a 10-mm diameter ball of hardened 100Cr6 steel. Paraffin oil and engine oil were used as lubricants for 1000 sliding cycles at 1 Hz with a normal load of 1.0 N. The corresponding wear tracks were analyzed by OM and SEM. In particular cases, the laser-generated nanostructures endured the tribological treatment. Simultaneously, a significant reduction of the friction coefficient and the wear was observed in the laser-irradiated (LIPSS-covered) areas when compared to the non-irradiated surface. The experiments reveal the potential benefit of laser surface structuring for tribological applications.
In laser machining with ultrashort laser pulses unwanted X-ray radiation in the keV range can be generated when a critical laser intensity is exceeded. Even if the emitted X-ray dose per pulse is low, high laser repetition rates can lead to an accumulation of X-ray doses beyond exposure safety limits. For 925 fs pulse duration at a center wavelength of 1030 nm, the X-ray emission was investigated up to an intensity of 2.6 × 10^14 W/cm2. The experiments were performed in air with a thin disk laser at a repetition rate of 400 kHz. X-ray spectra and doses were measured for various planar target materials covering a wide range of the periodic table from aluminum to tungsten. Without radiation shielding, the measured radiation doses at this high repetition rate clearly exceed the regulatory limits. Estimations for an adequate radiation shielding are provided.
A great number of Central Asian wall paintings, archeological materials, architectural fragments, and textiles, as well as painting fragments on silk and paper, make up the so called Turfan Collection at the Asian Art Museum in Berlin. The largest part of the collection comes from the Kucha region, a very important cultural center in the third to ninth centuries. Between 1902 and 1914, four German expeditions traveled along the northern Silk Road. During these expeditions, wall paintings were detached from their original settings in Buddhist cave complexes. This paper reports a technical study of a wall painting, existing in eight fragments, from the Buddhist cave no. 40 (Ritterhöhle). Its original painted surface is soot blackened and largely illegible. Grünwedel, leader of the first and third expeditions, described the almost complete destruction of the rediscovered temple complex and evidence of fire damage. The aim of this case study is to identify the materials used for the wall paintings. Furthermore, soot deposits as well as materials from conservation interventions were of interest. Non-invasive analyses were preferred but a limited number of samples were taken to provide more precise information on the painting technique. By employing optical and scanning electron microscopy, energy dispersive X-ray spectroscopy, micro X-ray fluorescence spectroscopy, X-ray diffraction analysis, and Raman spectroscopy, a layer sequence of earthen render, a ground layer made of gypsum, and a paint layer containing a variety of inorganic pigments were identified.
Sub-100-nm laser-induced periodic surface structures (LIPSS) were processed on bulk titanium (Ti) surfaces by femtosecond laser pulse irradiation in air (30 fs pulse duration, 790 nm wavelength). The laser peak fluence, the spatial spot overlap, and the number of overscans were optimized in a sample-scanning geometry in order to obtain large surface areas (5 mm × 5 mm) covered homogeneously by the LIPSS. The laser-processed regions were characterized by optical microscopy (OM), white light interference microscopy (WLIM) and scanning electron microscopy (SEM). The friction coefficient of the nanostructured surfaces was tested during 1000 cycles under reciprocal sliding conditions (1 Hz, 1.0 N normal load) against a 10-mm diameter ball of hardened 100Cr6 steel, both in paraffin oil and in engine oil used as lubricants. Subsequently, the corresponding wear tracks were qualified by OM, SEM, and energy dispersive X-ray analyses (EDX). The results of the tribological tests are discussed and compared to that obtained for near wavelength-sized fs-LIPSS, processed under somewhat different irradiation conditions. Some constraints for a beneficial effect of LIPSS on the tribological performance are provided.
Titanium nitride (TiN) was coated on different substrate materials, namely pure titanium (Ti), titanium alloy (Ti6Al4V) and steel (100Cr6), generating 2.5 μm thick TiN layers. Using femtosecond laser pulses (30 fs, 790 nm, 1 kHz pulse repetition rate), large surface areas (5 mm × 5 mm) of laser-induced periodic surface structures (LIPSS) with sub-wavelength periods ranging between 470 nm and 600 nm were generated and characterized by optical microscopy (OM), white light interference microscopy (WLIM) and scanning electron microscopy (SEM). In tribological tests, coefficients of friction (COF) of the nanostructured surfaces were determined under reciprocating sliding conditions (1 Hz, 1.0 N normal load) against a 10-mm diameter ball of hardened 100Cr6 steel during 1000 cycles using two different lubricants, namely paraffin oil and engine oil. It turned out that the substrate material, the laser fluence and the lubricant are crucial for the tribological performance. However, friction and wear could not be significantly reduced by LIPSS on TiN layers in comparison to unstructured TiN surfaces. Finally, the resulting wear tracks on the nanostructured surfaces were investigated with respect to their morphology (OM, SEM), depth (WLIM) and chemical composition by energy dispersive X-ray spectroscopy (EDX) and, on one hand, compared with each other, on the other hand, with non-structured TiN surfaces.
Until the end of the 1980s many wooden artworks underwent surface treatment by liquid preservatives, e.g. Hylotox-59. DDT (dichlorodiphenyltrichloroethane) crystal structures are formed on the wooden surfaces by the "blooming" of chlorine compounds by time. In addition to an aesthetic disturbance, it is assumed that DDT represents a health risk. Therefore, the removal of DDT crystals from the surfaces is requested. Contaminated wood with natural biocide ageing, gilded and wood carved elements and wooden samples with paint layers were provided by the Schlossmuseum Sondershausen, Germany. Laser cleaning on selected surface areas on the objects was done by means of femtosecond and nanosecond laser pulses. For the same object, cleaning results using 30-fs laser pulses at 800 nm wavelength are compared to findings utilizing 10-ns laser pulses at 1064 nm wavelength. Before and after laser treatment, chlorine measurements at the same surface position were done by X-ray fluorescence analysis (XRF) as an indicator for the presence of DDT. In this way, pointwise chlorine depletion rates can be obtained for the different pulse duration regimes and wavelengths. Additionally, the object surfaces were examined using optical microscopy and multi spectral imaging analysis.
Noble metal-free nanoparticles (NPs) based on multi-principal element alloys (MPEAs) were synthesized using a one-step pulsed laser ablation in liquids (PLALs) method for the electrochemical reduction of CO2. Laser ablation was performed in pure water or poly-(diallyldimethylammonium chloride) (PDADMAC)-containing an aqueous solution of Al8Cr17Co17Cu8Fe17Ni33 MPEA targets. Transmission electron microscopy (TEM) measurements combined with energy dispersive X-ray (EDX) mapping were used to characterize the structure and composition of the laser-generated MPEA nanoparticles (MPEA-NPs). These results confirmed the presence of a characteristic elemental distribution of a core-shell phase structure as the predominant NP species. The electrocatalytic performance of the laser-generated MPEA-NPs was characterized by linear sweep voltammetry (LSV) demonstrating an enhanced electrocatalytic CO2 activity for PDADMAC-stabilized NPs. The findings of these investigations indicate that MPEAs have great potential to replace conventional, expensive noble metal electrocatalysts.
Noble metal-free nanoparticles (NPs) based on multi-principal element alloys (MPEAs) were synthesized using a one-step pulsed laser ablation in liquids (PLALs) method for the electrochemical reduction of CO2. Laser ablation was performed in pure water or poly-(diallyldimethylammonium chloride) (PDADMAC)-containing an aqueous solution of Al8Cr17Co17Cu8Fe17Ni33 MPEA targets. Transmission electron microscopy (TEM) measurements combined with energy dispersive X-ray (EDX) mapping were used to characterize the structure and composition of the laser-generated MPEA nanoparticles (MPEA-NPs). These results confirmed the presence of a characteristic elemental distribution of a core-shell phase structure as the predominant NP species. The electrocatalytic performance of the laser-generated MPEA-NPs was characterized by linear sweep voltammetry (LSV) demonstrating an enhanced electrocatalytic CO2 activity for PDADMAC-stabilized NPs. The findings of these investigations indicate that MPEAs have great potential to replace conventional, expensive noble metal electrocatalysts.