Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (27) (entfernen)
Schlagworte
- Laser cleaning (5)
- Femtosecond laser (4)
- Friction (3)
- Femtosecond laser ablation (2)
- Laser (2)
- Laser-induced periodic surface structures (LIPSS) (2)
- Paper (2)
- Spectroscopy (2)
- Wear (2)
- Ablation (1)
Organisationseinheit der BAM
- 6 Materialchemie (4)
- 6.2 Material- und Oberflächentechnologien (3)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 6.0 Abteilungsleitung und andere (1)
- 6.3 Strukturanalytik (1)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (1)
- 6.6 Physik und chemische Analytik der Polymere (1)
- 6.7 Materialsynthese und Design (1)
- 9 Komponentensicherheit (1)
Template Electrodeposition of Nanowire Arrays on Gold Foils Fabricated by Pulsed-Laser Deposition
(1995)
A detailed diagnostic study of the interaction of nanosecond laser pulses from the near-ultraviolet to the near-infrared wavelength range with various types of contemporary and ancient parchments is presented. The advantages of laser cleaning due to the absence of chemical agents, spectroscopic selectivity, micro-precision and computer-aided handling can only be verified when physico-chemical diagnostics guarantee destructionless processing. Scanning electron microscopy data are correlated with chemical degradation and morphological changes dependent on the laser fluence and wavelength. It is also shown how transmission electron microscopy, diffuse reflectance infrared Fourier transform spectroscopy, and pyrolysis capillary gas chromatography can be employed in the chemical diagnostics of laser cleaning of parchment. This study suggests that the ageing status of parchment artefacts plays a major role in assessing the laser cleaning limits.
The applicability of excimer laser at 308 nm and Nd:YAG laser at 532 nm with fluences below 0.86 J/cm2 for cleaning of cellulose and paper materials was evaluated. The extent of degradation of purified cotton cellulose and Fabriano paper after laser treatment as well as after a period of accelerated humid oven ageing was determined by following the changes in the degree of polymerization. While irradiation of paper with the excimer laser at 308 nm results in depolymerization of cellulose accompanied by a decrease in ISO brightness, no detrimental effects of Nd:YAG laser treatments were observed.
Single-pulse damage thresholds of hydrogenated amorphous carbon (a-C:H) films were measured for 8-ns laser pulses at 532-nm wavelength. Layer thicknesses from below the optical penetration depth to above the thermal diffusion length (60 nm13 µm) were examined. After correction of the damage-threshold values for the fraction of energy effectively absorbed by the material, the damage threshold was found to increase linearly with the layer thickness, also for film thicknesses below the optical penetration depth of a-C:H. The threshold fluence reached the bulk value for a layer thickness equal to the thermal diffusion length. The thermal diffusion coefficient was obtained from fitting the experimental data. Several phenomena like graphitization, blistering, exfoliation, and ablation were observed for different fluence regimes and film thicknesses.
Optical fibers made of fused silica are a common method of transmitting high laser pulse energies. Failure of those fibers is a significant risk. The determination of laser-induced damage thresholds (LIDT) on fiber end facets according to ISO 21254 standard is needed. In the past, single pulse nanosecond laser experiments showed an improvement of LIDT with increasing fiber core diameter for 1064 nm wavelength and a constant beam diameter of 50 µm.
This paper pays particular attention to the influence of the laser beam diameter on damage resistance. All-silica fiber types (LEONI) with different core diameters (100–600 µm) were investigated using beam diameters in a range from 30 µm to 100 µm. For comparison experiments on fused silica preform material (Heraeus F300) were performed. On one hand, surface LIDT of fused silica preform material decreases significantly with increasing beam size. A model considering a random distribution of point defects explains the experimental data qualitatively. On the other hand, LIDT of fiber end facets stays constant. White light microscopy results suggest that the point defect density on fiber end facets is lower compared to the preform surface due to an excellent surface polish quality.
Laser cleaning of delicate biological composite materials such as ancient parchment manuscripts from the 15th and 16th century and printed paper from the 19th century is demonstrated with an ultraviolet excimer pulsed laser at 308 nm. Laser fluence levels must stay below the ablation and destruction threshold of the parchment or paper substrate, and have to surpass the threshold of the contaminant matter. Foreign layers to be removed must exhibit a higher optical density than the artifact substrates. Synthetic carbonaceous dirt modelled by water-soluble black crayons showed a characteristically weak featureless laser-induced plasma spectroscopy spectrum near the noise limit. It turned out that laser-induced plasma spectroscopy is of limited use in monitoring halting points (or etch-stops) because it relies on the destruction not only of the laterally inhomogenously distributed contaminant but also of pigment phases on a microscopically rough parchment substrate. Laser-induced fluorescence spectroscopy, however, promises to be a valuable non-destructive testing technique for etch-stop monitoring.
Analyse häufig verwendeter europäischer Papiere. Im Fokus: Fasermaterial, Füllstoffe und Leimung
(2007)
Restauratoren können verschiedene Papierarten mit dem bloßen Auge aufgrund von Merkmalen in der Textur und der Oberflächenbeschaffenheit, seinem Aussehen im Durchlicht sowie an Griff und Klang grob unterscheiden. Dabei ist sich der Restaurator stets der Tatsache bewusst, dass es sich lediglich um eine erste grobe Einschätzung handeln kann. Erst bei mikroskopischen Analysen und physikalischen Experimenten treten Charakteristika zu Tage, die eine weitere Annäherung an die Zusammensetzung des Papiers und damit seiner Provenienz erlauben. Gegenstand dieser Arbeit war es, ein europäisches Hadernpapier, ein holzhaltiges Zeichenpapier und ein Whatman®-Filterpapier mit zwei mikroskopischen Methoden und einer Verbrennungstechnik zu untersuchen. Das Fasermaterial, die Füllstoffe, die Leimung und eventuelle Verunreinigungen wurden detailliert evaluiert. Neben konventioneller Lichtmikroskopie kam die weniger bekannte Umweltrasterelektronenmikroskopie (ESEM = Environmental Scanning Electron Microscopy) zum Einsatz, die neben der bildlichen Darstellung der Probenoberflächen zusätzlich eine Elementanalyse derselben gestattet. Letzteres erfordert allerdings das Vorhandensein eines zusätzlichen Röntgenspektrometers. Darüber hinaus wurden die verschiedenen Papiere trocken verascht. Es wurde eine oxidative Zerstörung der organischen Stoffe gewährleistet bis nur noch nichtbrennbare mineralische Asche zu verzeichnen war. Die Komplementarität der eingesetzten Methoden wird demonstriert und ein Einblick in die Zusammensetzung und Struktur der Papiere ermöglicht. Die Analysemethoden sind durch ihren partiell zerstörenden Charakter bzw. Limitierungen hinsichtlich der Objektgröße nur bedingt für die Untersuchung am Original geeignet, sehr wohl aber dafür, das Probenmaterial für Versuchsreihen genau zu definieren und zu standardisieren.
Characterization of laser-generated microparticles by means of a dust monitor and SEM imaging
(2006)
Nanosecond laser (1064 nm wavelength) cleaning of artificially soiled paper as a model sample simulating a real-world artwork was performed. During the cleaning process, the ejection of particles was monitored in situ by means of a dust monitor (8 size classes, ranging from 0.3 µm to >2 µm) and ex situ using a mini-cascade impactor (MKI, 5 stages). The cleaning result was analyzed by scanning electron microscopy (SEM) considering possible laser-induced damages to the substrate. Size distributions of emitted particles were measured depending on the processing parameters: laser fluence, F, and pulse number per spot, N. High numbers of large (>2 µm) particles were collected by the mini-cascade impactor indicating a gas dynamical liftoff process. Obviously, these particles were not affected by the laser-matter interaction. The different methods (SEM, MKI, and dust monitor) are compared with respect to their usefulness for a proper interpretation of the cleaning results.
Cleaning of paper is a challenging task due to the fact that a contamination should be removed and a fragile organic original material has to be preserved. Pulsed laser cleaning of artificially soiled Whatman© filter paper samples serving as models for historical paper was performed. Different cleaning strategies employing 8-ns laser pulses at 532 nm wavelength were applied to clean paper avoiding undesired effects like discoloration (yellowing) and mechanical deterioration of the substrate. Multi shot experiments with low-energy pulses were compared with single pulse investigations utilizing high pulse energies achieving a constant energy load incident on the samples in both cases. The cleaning efficiency and possible yellowing effects were evaluated by means of a multi spectral imaging system. An extensive microscopic analysis of the cleaned parts of the samples provided insight into the remaining soiling on the surface and in the bulk of the paper material after laser treatment. As a reference, a hard and a soft eraser were used to clean the samples.
Laser-induced periodic surface structures (LIPSS, ripples) were generated on stainless steel (100Cr6) and titanium alloy (Ti6Al4V) surfaces upon irradiation with multiple femtosecond laser pulses (pulse duration 30 fs, central wavelength 790 nm). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning geometry for the processing of large surface areas (5 × 5 mm²) covered homogeneously by the nanostructures. The irradiated surface regions were subjected to white light interference microscopy and scanning electron microscopy revealing spatial periods around 600 nm. The tribological performance of the nanostructured surface was characterized by reciprocal sliding against a ball of hardened steel in paraffin oil and in commercial engine oil as lubricants, followed by subsequent inspection of the wear tracks. For specific conditions, on the titanium alloy a significant reduction of the friction coefficient by a factor of more than two was observed on the laser-irradiated (LIPSS-covered) surface when compared to the non-irradiated one, indicating the potential benefit of laser surface structuring for tribological applications.
Cleaning of artificially soiled paper using nanosecond, picosecond and femtosecond laser pulses
(2010)
Cleaning of cultural assets, especially fragile
organic materials like paper, is a part of the conservation
process. Laser radiation as a non-contact tool offers
prospects for that purpose. For the studies presented here,
paper model samples were prepared using three different paper
types (pure cellulose, rag paper, and wood-pulp paper).
Pure cellulose serves as reference material. Rag and woodpulp
paper represent essential characteristics of the basic
materials of real-world artworks. The papers were mechanically
soiled employing pulverized charcoal. Pure and artificially soiled paper samples were treated with laser pulses of
28 fs (800 nm wavelength) and 8–12 ns (532 nm) duration in
a multi pulse approach. Additionally, the cellulose reference
material was processed with 30 ps (532 nm) laser pulses.
Damage and cleaning thresholds of pure and soiled paper
were determined for the different laser regimes. Laser working
ranges allowing for removal of contamination and avoiding
permanent modification to the substrate were found.
The specimens prior and after laser illumination were characterized
by light-optical microscopy (OM) and scanning
electron microscopy (SEM) as well as multi spectral imaging
analysis. The work extends previous nanosecond laser
cleaning investigations on paper into the ultra-short pulse
duration domain.
Laser-induced periodic surface structures (LIPSS, ripples) were processed on steel (X30CrMoN15-1) and titanium (Ti) surfaces by irradiation in air with linear polarized femtosecond laser pulses with a pulse duration of 30 fs at 790 nm wavelength. For the processing of large LIPSS covered surface areas (5 mm × 5 mm), the laser fluence and the spatial spot overlap were optimized in a sample-scanning geometry. The laser-processed surfaces were characterized by optical microscopy (OM), white light interference microscopy (WLIM) and scanning electron microscopy (SEM). Spatial LIPSS periods between 450 and 600 nm were determined. The nanostructured surface regions were tribologically tested under reciprocal sliding conditions against a 10-mm diameter ball of hardened 100Cr6 steel. Paraffin oil and engine oil were used as lubricants for 1000 sliding cycles at 1 Hz with a normal load of 1.0 N. The corresponding wear tracks were analyzed by OM and SEM. In particular cases, the laser-generated nanostructures endured the tribological treatment. Simultaneously, a significant reduction of the friction coefficient and the wear was observed in the laser-irradiated (LIPSS-covered) areas when compared to the non-irradiated surface. The experiments reveal the potential benefit of laser surface structuring for tribological applications.
In laser machining with ultrashort laser pulses unwanted X-ray radiation in the keV range can be generated when a critical laser intensity is exceeded. Even if the emitted X-ray dose per pulse is low, high laser repetition rates can lead to an accumulation of X-ray doses beyond exposure safety limits. For 925 fs pulse duration at a center wavelength of 1030 nm, the X-ray emission was investigated up to an intensity of 2.6 × 10^14 W/cm2. The experiments were performed in air with a thin disk laser at a repetition rate of 400 kHz. X-ray spectra and doses were measured for various planar target materials covering a wide range of the periodic table from aluminum to tungsten. Without radiation shielding, the measured radiation doses at this high repetition rate clearly exceed the regulatory limits. Estimations for an adequate radiation shielding are provided.