Laser-induced periodic surface structures (LIPSS) were generated on two types of steel (100Cr6, X30CrMoN15-1) and two types of titanium (Ti, Ti6A14V) surfaces upon irradiation with multiple linear polarized femtosecond laser pulses in air environment (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz, Gaussian beam shape). Teh conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning geometry for the processing of large surface areas covered homogeneously by two different types of LIPSS - either near wavelength or sub-100 nm structures. The tribological performance of the nanostructured surfaces was characterized under reciprocating sliding at 1 Hz against a ball of hardened steel using different lubricants and normal forces. After 1000 cycles the corresponding wear tracks were characterized by optical and scanning electron microscopy. For specific conditions, the wear was strongly reduced and laser-generated nanostructures endured the tribological treatment. Simultaneously, a significant reduction of the friction coefficient was observed in the laser-irradiated LIPSS-covered areas, indicating the benefit of laser surface structuring for tribological applications. The spatially Gaussian shaped beam used for the laser processing was transformed via beam shaping into a top hat distribution at the surface of the samples for optimization. The tribological performance of the laser-induced nanostructures is discussed on the basis of different physical and chemical mechanisms.
Various methods have been used for introducing fire retardant additives into polymers. Deposition of thick fire retardant coatings directly onto polymer substrates is an alternative technique. An important advantage of the coating technique is the preservation of the physical and chemical integrity of the polymer material. Moreover, the fire retardancy of the polymer materials can be achieved following their production. Suitable coating materials are inorganics, intumescent, char-forming, oxygendiluting, and cooling or radical quenching layers. The most important problem is to achieve sufficient coating thickness to withstand the direct attack of flame and to protect the polymer bulk from pyrolysis, otherwise blistering of coating, caused by emitted pyrolysis gases, is often observed. To avoid blistering of coating, the adhesion between polyolefin substrate and fire retardant coating has to be extraordinarily high.
In order to achieve such a high level of adhesion, the polymer surface has to be modified with adhesion-promoting functional groups. The deposition of thin plasma polymers as adhesion-promoting layers with NH2, OH or COOH groups has been the most suited method. These functional groups are able to form covalent bonds and other interactions between the fire-resistant coating and the plasma-modified polyolefin substrate. Additionally, the plasma polymer counteracts the strong mechanical stresses in the laminate on exposure to high temperatures by its flexibility.