Metal Additive Manufacturing (AM) technologies such as Laser Powder Bed Fusion (LPBF) are characterized by layer wise construction, which enable advancements of component design, leading to potential efficiency and performance improvements. However, the rapid cooling rates associated with the process consequently leads to the generation of high magnitude residual stresses (RS). Therefore, a deep understanding of the formation of RS, the influence of process parameters on their magnitude and the impact on mechanical performance is crucial for widespread application. The experimental characterization of these RS is essential for safety related engineering application and supporting the development of reliable numerical models. Diffraction-based methods for RS analysis using high energy synchrotron X-rays and neutrons enable non-destructive spatially resolved characterization of both surface and bulk residual stresses in complex components. This presentation will provide an overview of recent research conducted by the BAM at large scale facilities for the characterization of residual stresses in LPBF metallic alloys. Special focus will be given to the challenges posed by textured LPBF materials for the reliable choice of the diffraction elastic constants (DECs), which is crucial to the accurate calculation of the level of RS.
The microstructure has a great influence on short fatigue crack growth in metallic materials. Laser-based Powder Bed Fusion AlSi10Mg alloys exhibit in the as-built condition a fine fibrous Si structure and a supersaturated solid solution of Si in the α-Al matrix, which is significantly modified by heat treatments starting already at temperatures under 260 °C. This study focuses on the influence of post-process heat treatments on the microstructural evolution and the resulting fatigue crack growth resistance. As compared to the as-built condition, two heat treatments at 265 °C/1 h and at 300 °C/2 h are found to be beneficial to the fatigue crack growth resistance of the investigated material.
Large temperature gradients inherent to additive manufacturing (AM) processes induce large residual stress (RS) in the final part. Because RS can influence the tribological properties, this study focuses on the relationship between wear sliding properties and RS in IN718 coatings. Such coatings were deposited with a Laser metal deposition (LMD) machine using two different scanning strategies.
The wear resistance and RS state were investigated after surface milling. RS were measured before and after wear tests on a reciprocating sliding test apparatus.
Two different X-ray diffraction techniques were employed to measure the surface and subsurface state RS: Laboratory Energy Dispersive X-ray Diffraction (LEDXD) and Synchrotron X-ray Energy Dispersive Diffraction (SXEDD). Due to the milling process, the coatings show similar depth distributions of RS from 22 to 92 μm depth, but exhibit different magnitudes depending on the scanning strategy used. Reciprocating sliding wear tests induced high compressive residual stresses that erased the initial RS state, and a similar wear behavior was observed in the two samples. These samples possess similar texture and grain morphology. This demonstrates that the influence of RS on wear resistance is a second-order effect. Nevertheless, it was observed that RS can still impact the wear performance at the early testing stages of the repaired parts.