Concrete is the most applied building material in modern times. It is present in all kinds of structures and no other material secms to rcplace concrete as the most selected building material in the near future. The prime advantages are the high performance, the easy production and a facile processability. The sustainability and durability are important requirements to concrete. Even if concrete is significantly less susceptible against factors promoting a damage, compared to other materials, there are still mechanisms affecting it. In particular, high-ways and hydraulic structures made of concrete worldwide show cases of alkali-silica reaction (ASR) damages. This article refers to experience at BAM Federal InstituteforMaterials Research and Testing for several decades to ASR research and darnage assessment. ASR is a severe darnage mechanism that can occur in concrete, when certain conditions related to composition and cxposition arise in a critical combination. The chemical reaction is based on the alkalis and the silica in the concrete and was first identified by Stanton in highway structures in California (Stanton, 1940). Actually three components are needed to initiate ASR: alkali-sensitive siliceous aggregates, alkalis coming from internal (cement or other components) or external sources (de-icing salt or sea water) and water. If all of these components are sufficiently present an alkali-silica gel could be formed (Hobbs, 1988). This gel itself needs additional space when it is formed. Furthermore it is able to swell in the presence of humidity, both processes generating an expansion pressure inside the concrete. As a consequence of intensive expansion, cracks can occur, which significantly lowers thc strength of the material. Parameters like amount and chemical composition of the gel as weil as the pattern and width of cracks can help to classify the ASR darnage (Swamy, 1992). The objective of this article is to demoostrate the microscopic work on ASR affected concrete samples, carried out to assess the damaging process or to evaluate various alkali-sensitive aggregates. It will explain the approach of ASR investigation from the macroscale to microscale, starting briefly with the condition assessment, over treatment and investigations of samples in the laboratory, to the use of different microscopical and analytical techniques. In the main part the characteristic features for identifying ASR in concrete are presented by using microscopic images. Especially the emphasis lies on the role of the aggregate.
Several studies show that thermal and hydrothermal treatment can further improve the excellent properties of UHPC in terms of mechanical strength and durability. While for the thermal treatment the increase in strength is attributed to an intensified pozzolanic and hydraulic reaction, for the hydrothermal treatment previous studies accredited it mostly to the formation of tobermorite. In the presented study thermal and hydrothermal treatment of UHPC samples was systematically varied and the phase formation analysed related to the strength development of a reference sample cured for 28 days in water. For the thermal treatment the results show that the strength increase depends on the protection against desiccation and can be ascribed to an improved pozzolanic reaction of the siliceous fillers. To achieve a significant enhancement of strength, a pre-storage time of few days and a long dwell time at elevated temperature/pressure are required. For the hydrothermal treatment already heating the specimens up to 185 °C in saturated steam followed by an immediate cooling leads to a substantial increase in compressive strength. Pre-storage time did not affect the result as far as a minimum of several hours is guaranteed. The improved performance is due to an increase in the pozzolanic and hydraulic reaction. Surprisingly, tobermorite was only found within a very thin layer at the surface of the sample, but not in the bulk. Sulphate and aluminium stemming from the decomposition of the ettringite are bound in the newly formed phases hydroxylellestadite and hydrogarnet.