Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (15)
- Beitrag zu einem Tagungsband (10)
- Vortrag (2)
- Posterpräsentation (1)
Schlagworte
- UHPC (5)
- Hydrothermal treatment (3)
- Microstructure (3)
- Additive manufacturing (2)
- Alkali-activated materials (2)
- Alkali-silica reaction (2)
- Building Materials (2)
- Compressive strength (2)
- Concrete (2)
- Damage analysis (2)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (23)
- 7.1 Baustoffe (15)
- 7.4 Baustofftechnologie (15)
- 4 Material und Umwelt (5)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (5)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 5 Werkstofftechnik (2)
- 1.2 Biophotonik (1)
- 1.6 Anorganische Referenzmaterialien (1)
- 5.1 Mikrostruktur Design und Degradation (1)
Eingeladener Vortrag
- nein (2)
Aim of this study is to provide information about moisture dependent material behaviour of unstabilised loadbearing earth blocks and mortars. Compressive strength and Young’s modulus were investigated after conditioning in varying relative humidity reaching from 40 % up to 95 %. The material composition and physical properties were investigated to understand the influence of relative humidity onto the mechanical properties. A normalisation of strength and stiffness by the values obtained at 23 ◦C and 50 % relative humidity reveals a linear dependence of compressive strength and Young’s modulus that is regardless of the material composition.
Thus, it is possible to describe the influence of relative humidity onto the load-bearing behaviour of unstabilised earth masonry materials in a generally valid formulation.
Concrete is the most applied building material in modern times. It is present in all kinds of structures and no other material secms to rcplace concrete as the most selected building material in the near future. The prime advantages are the high performance, the easy production and a facile processability. The sustainability and durability are important requirements to concrete. Even if concrete is significantly less susceptible against factors promoting a damage, compared to other materials, there are still mechanisms affecting it. In particular, high-ways and hydraulic structures made of concrete worldwide show cases of alkali-silica reaction (ASR) damages. This article refers to experience at BAM Federal InstituteforMaterials Research and Testing for several decades to ASR research and darnage assessment. ASR is a severe darnage mechanism that can occur in concrete, when certain conditions related to composition and cxposition arise in a critical combination. The chemical reaction is based on the alkalis and the silica in the concrete and was first identified by Stanton in highway structures in California (Stanton, 1940). Actually three components are needed to initiate ASR: alkali-sensitive siliceous aggregates, alkalis coming from internal (cement or other components) or external sources (de-icing salt or sea water) and water. If all of these components are sufficiently present an alkali-silica gel could be formed (Hobbs, 1988). This gel itself needs additional space when it is formed. Furthermore it is able to swell in the presence of humidity, both processes generating an expansion pressure inside the concrete. As a consequence of intensive expansion, cracks can occur, which significantly lowers thc strength of the material. Parameters like amount and chemical composition of the gel as weil as the pattern and width of cracks can help to classify the ASR darnage (Swamy, 1992). The objective of this article is to demoostrate the microscopic work on ASR affected concrete samples, carried out to assess the damaging process or to evaluate various alkali-sensitive aggregates. It will explain the approach of ASR investigation from the macroscale to microscale, starting briefly with the condition assessment, over treatment and investigations of samples in the laboratory, to the use of different microscopical and analytical techniques. In the main part the characteristic features for identifying ASR in concrete are presented by using microscopic images. Especially the emphasis lies on the role of the aggregate.
Alkali-silica reaction (ASR) is a chemical reaction within concrete which can lead over time to cracking and spalling. Due to the complexity of the problem, it still causes damage to concrete constructions worldwide.
The publication aims to illustrate the interdisciplinary research of the German Federal Institute for Materials Research and Testing (BAM) within the last 20 years, considering all aspects of ASR topics from the macro to the micro level. First, methods for characterization and assessment of ASR risks and reaction products used at BAM are explained and classified in the international context. Subsequently the added value of the research approach by combining different, preferably nondestructive, methods across all scales is explained using specific examples from a variety of research projects. Aspects covered range from the development of new test-setups to assess aggregate reactivity, to analysis of microstructure and reaction products using microscopical, spectroscopical and X-ray methods, to the development of a testing methodology for existing concrete pavements including in-depth analysis of the visual damage indicator and the de-icing salt input using innovative testing techniques. Finally, research regarding a novel avoidance strategy that makes use of internal hydrophobization of the concrete mix is presented.
If the amount of sulfate within the mix design for concrete is not balanced, ettringite formation which first controls solidification continues while the concrete is hardening. Ettringite forms by reaction of sulfate contained in the cement or in some admixture with calcium aluminate (C3A) as cement component. The “late primary ettringite formation” promotes an increase in volume within the hardened concrete leading to cracks. To analyze the effect of substituting part of ordinary Portland cement (OPC) by a treated brown coal fly ash mortar bars were tested according to ASTM C452. This test method was originally developed to extrapolate from the internal to external sulfate attack and is based on the idea that by testing a concrete mixture containing sulfate the process of deterioration is accelerated because it does not have to diffuse into the concrete before reaction first. In addition to the samples prescribed in ASTM C452 further samples in the size of the German SVA procedure were tested also designed for accessing the external sulfate resistance. The results show that while the replacement of 25 % of cement by brown coal fly ash leads to length changes around the limit defined by ASTM, the substitution of 50 % cement exceeded the limit by a multiple. The progress of expansion is the very similar for the two geometries tested. In-situ XRD measurements confirmed that while for pastes made of OPC the formation of ettringite is completed after 20 hours, this is not true for the mixtures containing the brown coal fly ash.
In a different study the effect of hydrothermal treatment on the phase composition of ultra-high-performance concrete was analyzed. The results show that the sulfate and aluminate resulting from the decomposition of ettringite are bound into new phases.
If this binding is permanent this might allow the larger use of sulfate bearing raw materials.
The advantages of treating prefabricated components made of Ultra-High-Performance Concrete (UCPC) at 90 °C are largely recognized, while hydrothermal treatment at 185 °C and the corresponding saturation pressure of 1.1 MPa, in contrast, is not applied in building practice so far and was studied only by a few researchers.
In the research presented, the parameters pre-storage-time before treatment and dwell time in the autoclave were systematically varied. The results illustrate in which way compressive strength increases with the duration of treatment. Already samples which were only heated up and immediately cooled down show an increase in strength compared to the 28-day reference of about 10 %. After 20 h the maximum increase of about 25 % is reached. Interestingly the compressive strength of samples treated very long hardly decreases. It can be therefore concluded that for the composition investigated the achievable mechanical strength is not severely sensitive regarding the duration of the treatment.
Also, pre-storage times before autoclaving longer than 0.5 days showed no significant impact on strength development.
The phase composition measured by XRD exhibits significant changes compared to the reference. The amount of ettringite and portlandite have vanished, the cement clinker phases are substantially decreased and hydroxylellestadite and hydrogarnet are formed as new phases. The increase in strength can be assigned to an improved pozzolanic and hydraulic reaction. Contradictory to literature, there was found no tobermorite, a mineral which is known to be susceptible for disintegration at Long autoclaving duration. This explains why no significant strength loss appeared.
By the combination of an optimized granulometry, a reduced water cement ratio and the use of superplasticizers ultra-high performance concrete achieves a compressive strength of over 150 N/mm2 and a high resistance regarding acids and water-soluble salts. In different Research projects the effect of an autoclavation on the mechanical strength and the phase composition was analyzed. In systematic studies, the concrete mix and the process parameters were varied.
The results show that autoclavation leads to an improved pozzolanic and hydraulic reaction and significantly improves the mechanical strength compared to a conventional thermal treatment. If a minimum time-span for hydration is ensured, the achievable strength level is not dependent on the prestorage time. However, the duration of the autoclaving is significant. After the Maximum strength is reached there is only a very slight decrease, even if unrealistically long autoclaving times are applied.
Several studies show that thermal and hydrothermal treatment can further improve the excellent properties of UHPC in terms of mechanical strength and durability. While for the thermal treatment the increase in strength is attributed to an intensified pozzolanic and hydraulic reaction, for the hydrothermal treatment previous studies accredited it mostly to the formation of tobermorite. In the presented study thermal and hydrothermal treatment of UHPC samples was systematically varied and the phase formation analysed related to the strength development of a reference sample cured for 28 days in water. For the thermal treatment the results show that the strength increase depends on the protection against desiccation and can be ascribed to an improved pozzolanic reaction of the siliceous fillers. To achieve a significant enhancement of strength, a pre-storage time of few days and a long dwell time at elevated temperature/pressure are required. For the hydrothermal treatment already heating the specimens up to 185 °C in saturated steam followed by an immediate cooling leads to a substantial increase in compressive strength. Pre-storage time did not affect the result as far as a minimum of several hours is guaranteed. The improved performance is due to an increase in the pozzolanic and hydraulic reaction. Surprisingly, tobermorite was only found within a very thin layer at the surface of the sample, but not in the bulk. Sulphate and aluminium stemming from the decomposition of the ettringite are bound in the newly formed phases hydroxylellestadite and hydrogarnet.
This contribution presents the results of structural and compressive strength investigations on cured andhigh-temperature treated silica-based one-part geopolymer-zeolite composites. The specimens weresynthesized from two different silica sources, sodium aluminate and water. The phase content as well asthe compressive strength of the cured composites varied depending on the starting mix-design and thesilica feedstock. Besides geopolymeric gel, A-type zeolites and hydrosodalites were the major reactionproducts. One of the silica feedstocks yielded significantly higher compressive strength (19 MPa), whilethe other one appears to cause less variation in phase content. Strength testing indicated an improvementon heating up to
200–400 °C (28 MPa) followed by a moderate decrease up to 700 °C. Above 700 °C the sys-tems underwent new phase formation and shrinkage (volume decrease) deformations. After exposureat 1000 °C the different mixes consisted of a mix of several stuffed silica phases, almost pure hexago-nal nepheline or amorphous phase. Depending on the mix-design, the onset temperature of the hightemperature phase transformations varied.
UHPC (engl. ultra-high-performance concrete) bietet außergewöhnliche Eigenschaften, die sich durch eine optimierte Wärmebehandlung weiter verbessern lassen. Wie bei normalen Beton beschleunigt eine Wärmebehandlung den Aushärteprozess und reduziert das Schrumpfen. Durch Ausbildung eines dichteren Gefüges wird weiterhin die Druckfestigkeit und die Resistenz gegenüber Umwelteinflüssen erhöht.
Die Art der Wärmebehandlung wird durch die Parameter: Temperatur, Druck, Wasserdampfsättigung und Dauer definiert und hat einen entscheiden Einfluss auf die Phasenentwicklung und damit auf die makro- und mikroskopischen Eigenschaften des UHPCs. Auch die Dauer und Art der Vorlagerung des UHPCs vor der thermischen Behandlung sind von Bedeutung.
Ziel der vorgestellten Untersuchung war der Vergleich und die Optimierung verschiedener Wärmebehandlungsarten mit Blick auf die Druckfestigkeits- und Phasenentwicklung. Dafür wurden UHPC-Zylinder und Prismen hergestellt und ungeschützt bzw. in Folie eingeschweißt bei 90 °C im Ofen, im Heißwasserbad, sowie alternativ bei 185 °C und 1.1 MPa im Autoklaven wärmebehandelt. Zusätzlich wurde die Vorlagerungs- und die Behandlungszeit systematisch variiert.
Die Ergebnisse zeigen, dass eine praxisnahe Wärmebehandlung im Ofen (kurze Vorlagerungs- und Behandlungszeit, Verdunstungsschutz durch Einschweißen in Folie) zwar zu einer stark erhöhten Frühfestigkeit führt, aber die Langzeitfestigkeit wird nicht signifikant erhöht. Erst längere Behandlungszeiten verbunden mit intensiviertem Schutz gegen das Austrocknen führen darüber hinaus zu deutlich erhöhten Langzeitfestigkeiten. Nach der Autoklavierung dagegen wurden Festigkeitszuwächse von bis zu 30 % gemessen.
Die röntgenographisch nachgewiesene Phasenentwicklung wird in beiden Behandlungsarten durch die Limitierung des zur Verfügung stehenden Wassers bestimmt. Bei der Wärmebehandlung im Ofen wird das durch den Ettringitzerfall freigesetzte Wasser für die puzzolanische Reaktion der Mikrosilika verbraucht, reicht aber für eine weitere Reaktion der Klinkerphasen nicht aus. Bei der hydrothermalen Behandlung dagegen zeigen die Veränderungen im Phasenbestand sowohl eine Intensivierung der puzzolanischen als auch der hydraulischen Reaktion. Der für autoklavierte Baustoffe charakteristische Tobermorit konnte jedoch nicht im Probeninneren, sondern nur als Belag auf der Probenoberfläche nachgewiesen werden. Ursächlich hierfür ist vermutlich wiederum das zu geringe Wasserangebot im Gefüge des UHPC.
Powder X-ray diffraction is a time-consuming and challenging task, especially for preparation of sensitive phases like ettringite and calcium-silicate-hydrate (C-S-H) phases. Fine-grained ultrahigh-performance concrete (UHPC) with an average grain size <100 μm could be investigated directly without time-consuming milling. As a proof of concept, small UHPC cylinders with plain surfaces were investigated with a newly designed sample holder. The comparison with conventionally prepared powder shows the feasibility of fast qualitative phase analysis using this approach. As a great benefit, a depth-dependent analysis, as well as a comparison of surface layers and core material, was carried out.