In the last decade, high-strength fine grained steels and welding consumables have gained a strong raise of application ranging from mobile cranes to bridge constructions. However, the cracking susceptibility of these steels increases significantly in correspondence with the achieved improvements in yield strength and the loss in plastic deformation reserves.
In order to determine this behavior a series of different standardized cold cracking tests has been developed. One remaining major problem of these tests is the uncertainty about the quantitative intensity of the restraint conditions as well as the corresponding welding residual stresses.
Consequently, the comparison of different tests and welding conditions as well as the transferability of the results onto real parts is difficult at best. The main topic of this paper is the analysis of the restraint conditions and their link with the welding induced residual stresses. The importance of the given standardized selfrestrained tests and first results about the transferability of
results onto real parts are discussed. The influence of the test specimen geometry on the restraint conditions of the test is investigated for a selected test with numerical Simulation using commercial FEA software. Additionally, the residual stresses caused by the welding process are measured and linked with the restraint conditions which are defined mainly by the geometry parameters.
Finally the transferability of the selected cold cracking test results is validated experimentally. The test results of a multilayer weld on high-strength fine grained steel of real size weldments are investigated. For these experiments a 16 MN large scale testing facility is used which is capable of applying the high reaction forces and clamping conditions found at large scale demonstrator parts.
The results show the importance of the quantitative knowledge of the restraint conditions and the welding residual stresses on the cold cracking resistance.
Kornfeinung im Schweißgut kann die mechanischen Eigenschaften der Schweißnaht und die Schweißeignung des Grundwerkstoffs deutlich verbessern. Eine Möglichkeit korngefeintes Schweißgut zu erreichen, ist das Versetzen des Schmelzbades mit kornfeinenden Mitteln. In dieser Studie wird gezeigt wie Titan- und Borzusätze Korngröße und -struktur von WIG-Schweißnähten der Al-Legierung 5083 (Al Mg4,5Mn0,7) beeinflussen. Dazu wurden in einem Gießprozess stäbchenförmige Einlagen hergestellt, die aus Grundwerkstoff und definierten Zusätzen der Kornfeinungslegierung Al Ti5B1 bestanden. Sie wurden als Ersatz für einen Schweißzusatzwerkstoff in einer Nut im Grundwerkstoff untergebracht und im WIG-Verfahren überschweißt. Durch die Steigerung des Titan- und Borgehalts im Schweißgut konnte dessen mittlere Korngröße deutlich verringert werden. Außerdem wurde eine Änderung der Kornstruktur beobachtet. Die Ergebnisse können als Grundlage genutzt werden, um die empfohlene chemische Zusammensetzung von Schweißzusätzen für Lichtbogenschweißen von Aluminium anzupassen.