We present transmission electron microscope (TEM) tomography investigations of ruthenium-based fuel cell catalyst materials as employed in direct methanol fuel cells (DMFC). The digital three-dimensional representation of the samples not only enables detailed studies on number, size, and shape but also on the local orientation of the ruthenium particles to their support and their freely accessible surface area. The shape analysis shows the ruthenium particles deviate significantly from spherical symmetry which increases their surface to volume ratio. The morphological studies help to understand the structure formation mechanisms during the fabrication as well as the high effectiveness of these catalysts in the oxygen reduction reaction at the cathode side of fuel cells.
We present transmission electron microscope (TEM) tomography investigations of ruthenium-based fuel cell catalyst materials as employed in direct methanol fuel cells (DMFC). The digital three-dimensional representation of the samples not only enables detailed studies on number, size, and shape but also on the local orientation of the ruthenium particles to their support and their freely accessible surface area. The shape analysis shows the ruthenium particles deviate significantly from spherical symmetry which increases their surface to volume ratio. The morphological studies help to understand the structure formation mechanisms during the fabrication as well as the high effectiveness of these catalysts in the oxygen reduction reaction at the cathode side of fuel cells.
This article reports a comprehensive investigation of the average and local structure of La5.6WO12-δ, which has excellent mixed proton, electron and oxide ion conduction suitable for device applications. Synchrotron X-ray and neutron powder diffraction show that a cubic fluorite supercell describes the average structure, with highly disordered lanthanum and oxide positions. On average, the tungsten sites are sixfold coordinated and a trace [3.7 (1.3)%] of anti-site disorder is detected. In addition to sharp Bragg reflections, strong diffuse neutron scattering is observed, which hints at short-range order. Plausible local configurations are considered and it is shown that the defect chemistry implies a simple 'chemical exchange' interaction that favours ordered WO6 octahedra. The local model is confirmed by synchrotron X-ray pair distribution function analysis and EXAFS experiments performed at the La K and W L-3 edges. It is shown that ordered domains of similar to 3.5 nm are found, implying that mixed conduction in La5.6WO12-δ is associated with a defective glassy-like anion sublattice. The origins of this ground state are proposed to lie in the nonbipartite nature of the face-centred cubic lattice and the pairwise interactions which link the orientation of neighbouring octahedral WO6 sites. This 'function through frustration' could provide a means of designing new mixed conductors.
The local structure around Ni and La atoms in Al85Ni10La5 amorphous powder after ball milling was investigated by X-ray absorption spectroscopy. A continuous decrease in coordination number of Ni and La as a function of milling time was observed, while the nearest neighbour distance and the mean square atomic displacement did not change, pointing at the creation of free volume around the Ni and La atoms. These structural changes resemble those of a liquid upon temperature increase. The results are described by a shear band model in which the coordination numbers of Ni and La are different within and outside a shear band.