Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (29)
- Beitrag zu einem Tagungsband (12)
- Forschungsbericht (2)
- Beitrag zu einem Sammelband (1)
- Corrigendum (1)
- Vortrag (1)
Schlagworte
- Ringversuch (3)
- Spurenverunreinigungen (3)
- Acidity (2)
- Coating (2)
- Femtosecond laser ablation (2)
- LTCC (2)
- LTCC technology (2)
- Liquid crystals (2)
- NEXAFS (2)
- NO2 (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (1)
Amphiphilic amino acids represent promising scaffolds for biologically active soft matter. In order to understand the bulk self-assembly of amphiphilic amino acids into thermotropic liquid crystalline phases and their biological properties a series of tyrosine ionic liquid crystals (ILCs) was synthesized, carrying a benzoate unit with 0–3 alkoxy chains at the tyrosine unit and a cationic guanidinium head group. Investigation of the mesomorphic properties by polarizing optical microscopy (POM), differential scanning calorimetry (DSC) and X-ray diffraction (WAXS, SAXS) revealed smectic A bilayers (SmAd) for ILCs with 4-alkoxy- and 3,4-dialkoxybenzoates, whereas ILCs with 3,4,5-trisalkoxybenzoates showed hexagonal columnar mesophases (Colh ), while different counterions had only a minor influence. Dielectric measurements revealed a slightly higher dipole moment of non-mesomorphic tyrosine-benzoates as compared to their mesomorphic counterparts. The absence of lipophilic side chains on the benzoate unit was important for the biological activity. Thus, non-mesomorphic tyrosine benzoates and crown ether benzoates devoid of additional side chains at the benzoate unit displayed the highest cytotoxicities (against L929 mouse fibroblast cell line) and antimicrobial activity (against Escherichia coli DTolC and Staphylococcus aureus) and promising selectivity ratio in favour of antimicrobial activity.
Novel approaches of tunable devices for millimeter wave applications based on liquid crystal (LC) are presented. In the first part of the paper, a novel concept of a tunable LC phase shifter realized in Low Temperature Cofired Ceramics technology is shown while the second part of the paper deals with a tunable high-gain antenna based on an LC tunable reflectarray. The reflectarray features continuously beam scanning in between ±25°. Also first investigations on radiation hardness of LCs are carried out, indicating that LCs might be suitable for space applications.
This key comparison was performed to demonstrate the capability of NMIs to analyse the purity of methane for use as a source gas in the preparation of standard gas mixtures. This capability is an essential requirement for the preparation of accurate standards of natural gas and some other fuels.
Since it is difficult to carry out a comparison with individual samples of pure gas, the sample for this comparison was a synthetic mixture of high purity methane with selected added impurities of nitrogen, argon, carbon dioxide and ethane. These mixtures were prepared by a gas company as a batch of 10 cylinders and their homogeneity and stability were evaluated by NMIJ.
The KCRVs for the four different analytes in this key comparison are based on a consensus of values reported by participants. The uncertainties in the degrees of equivalence were calculated by combining the reported uncertainties with the homogeneity of the samples and the uncertainty of the KCRV. The results submitted are generally consistent with the KCRV within the estimated uncertainties.
Finally, this comparison demonstrates that the analysis of nitrogen, argon, carbon dioxide and ethane in methane at amount fractions of 1 µmol/mol to 5 µmol/mol is generally possible with an uncertainty of 5% to 10%.
Main text. To reach the main text of this paper, click on Final Report. Note that this text is that which appears in Appendix B of the BIPM key comparison database kcdb.bipm.org/.
The final report has been peer-reviewed and approved for publication by the CCQM, according to the provisions of the CIPM Mutual Recognition Arrangement (MRA).
DatesIssue 1A (Technical Supplement 2012)
This pilot study compares the performance of participants in analyzing gas mixtures of nitrogen dioxide in nitrogen by comparison with in-house gravimetric standards using Fourier transformed infrared spectroscopy (FT-IR). In this study the same gas mixtures were used as in the key comparison CCQM-K74, which was designed to evaluate the level of comparability of National Metrology Institutes' measurement capabilities for nitrogen dioxide (NO2) at a nominal mole fraction of 10 µmol/mol. In the comparison CCQM-K74 most of the participants used chemiluminescence, with a small number using UV absorption or FT-IR spectroscopy, and thus it is of interest to improve understanding of the comparative performance of these techniques because they do not exhibit any cross-sensitivity to nitric acid (HNO3), which was known to be present in the mixtures used for the comparison.
The results of this pilot study indicate good consistency and a level of agreement similar to that reported in the comparison CCQM-K74, demonstrating that FT-IR can be operated as a comparison method when calibrated with appropriate gas standards and can achieve similar measurement uncertainties to chemiluminescence and UV absorption techniques.
An additional pilot study, CCQM-P110-B2, was conducted on the same gas mixtures in parallel with this pilot study. The second study addressed FT-IR spectroscopy when used to measure the gas mixtures with respect to reference spectra. The results of this second study will be reported elsewhere.
Main text. To reach the main text of this paper, click on Final Report.
The final report has been peer-reviewed and approved for publication by the CCQM-GAWG.
DatesIssue 1A (Technical Supplement 2012)
The surface properties of original high strength and preoxidized high modulus carbon fibers were altered by electrocopolymerizing acryl amide and carbazole and therefore depositing a copolymer coating onto the fibers. Scanning electron microscopy and zeta-potential measurements confirmed the presence of a rough but dense and continuous electrocoating with a basic surface character. Therefore, lsquogoodrsquo adhesion behavior between the electrocoated carbon fibers and an epoxy resin matrix should be expected. The interfacial adhesion was measured using the single fiber pull-out and single fiber indentation test. It was shown that only lsquointermediatersquo adhesion was present between the carbon fibers and the electrocoating, but superior adhesion between the coating and epoxy resin exists. The single fiber model composites always failed at the fiber/electrocoating interface. However, as shown by using the indentation test, the interfacial adhesion between fibers and electrocoating can be significantly improved if preoxidized fibers are used as substrate for electropolymerization. A very high tensile strength for the electrocoating can be expected as derived from the single fiber pull-out tests.
The requirement for a metrological infrastructure to ensure the interchangability of 'nonconventional’ energy gases within existing European infrastructure1 was the driving force behind the work undertaken in the three-year EMRP Characterisation of energy gases project EMRP ENG01 (June 2010 - May 2013).
As part of work package one of the project, Standards and methods were used to perform composition and impurity measurements on samples of real energy gases collected from around Europe. The aim of this study was to compare the results obtained from different labs, and thereby provide an evaluation of the labs’ capabilities and provide insight into the feasibility of different analytical methodologies for use with future measurements.
Most studies about the interaction of nanoparticles (NPs) with cells have focused on how the physicochemical properties of NPs will influence their uptake by cells. However, much less is known about their potential excretion from cells. However, to control and manipulate the number of NPs in a cell, both cellular uptake and excretion must be studied quantitatively. Monitoring the intracellular and extracellular amount of NPs over time (after residual noninternalized NPs have been removed) enables one to disentangle the influences of cell proliferation and exocytosis, the major pathways for the reduction of NPs per cell. Proliferation depends on the type of cells, while exocytosis depends in addition on properties of the NPs, such as their size. Examples are given herein on the role of these two different processes for different cells and NPs.
A novel coordination oligo/polymer is synthesized by metal-directed self-assembly from equimolar amounts of the (dppp)M(OTf)2 precursor complexes (dppp = bis-(diphenylphosphino)-propane, OTf = triflate; M = PdII or M = PtII) and banana-shaped bidentate dipyridyl ligands. The assemblies were characterized by ESI mass spectrometry and NMR spectroscopy. The analysis of the cloudy suspension prepared by dissolving the coordination polymer in aqueous methanol solutions indicates nanosized spherical objects to form. Evidence for vesicle formation from these metallo-supramolecular oligomers comes from (cryogenic) transmission electron microscopy (TEM, cryo-TEM). Atomic force microscopy revealed stable nanospheres on hydrophilic mica and monolayer formation on hydrophobic highly oriented pyrolitic graphite (HOPG) substrates. On mica, also torus-shaped object were observed, which are rationalized by vesicles that opened during the drying procedure and released the internal solvent. Elemental analysis of the nanoassemblies by X-ray photoelectron spectroscopy (XPS) indicates uncoordinated and coordinated pyridines in the coordination polymers that form the nanospheres. Various control experiments using different metal centers and modified ligands support the conclusions.
A simple method of creating defined PMMA and poly (MMA-co-Cz) electrocoatings on carbon fibres is described. The electrodeposition of poly methylmethacrylate (PMMA) onto unsized, unmodified carbon fibres was performed by simple constant current electrolyses of methylmethacrylate (MMA) monomer in dimethylformamide (DMF) solutions and the pure liquid monomer using sodium nitrate and lithium perchlorate as supporting electrolytes. The presence of polymeric coatings successfully attached to the carbon fibres was verified by scanning electron microscopy and photoelectron spectroscopy (XPS).
Performing the electrolysis in dilute MMA in DMF solutions ([MMA] < 5 M) results in the deposition of powder-like polymer on the carbon fibre electrodes. Increasing the MMA concentration in the DMF solution results in a homogeneous PMMA coating of the carbon fibres. The degree of grafting or coating increases with increasing MMA concentration, except when pure MMA is used without solvent.
The adhesive strength between the electrocoated carbon fibres and a PMMA matrix was determined using the single fibre pull-out test. It was found that the interfacial fracture behaviour of all carbon fibre/PMMA model composites is rather brittle. The adhesion strength between the unmodified carbon fibres and the PMMA matrix was equal to the cohesive strength of the polymer matrix itself. Nevertheless, the electrodeposition of thin and homogeneous PMMA coatings resulted in much improved adhesion strengths.
Natural zeolite clinoptilolite CLIN with a framework ratio of Si/Al ≥ 4 containing mainly potassium and calcium ions in its internal channel system was used as a starting material. The acidic HCLIN catalysts were prepared under soft conditions avoiding the use of environmental less benign mineral acids. The starting material was ion exchanged using a 0.2 M aqueous ammonium nitrate solution at a temperature 80 ◦C for 2 h. The obtained NH4CLIN was converted into the acid HCLIN catalyst by calcination at 300–600 ◦C. The obtained samples were characterized by XRD, FTIR, SEM/TEM, AAS, and EDX element mapping. The state of aluminium and silicon was studied by 27Al- and 29SiMAS NMR spectroscopy. The textural properties of the catalysts were investigated by nitrogen adsorption and desorption measurements. The Brønsted acidity of the HCLIN catalysts was studied by temperature-programmed decomposition of the exchanged ammonium ions releasing ammonia as well as 1H MAS NMR, {1H–27Al} Trapdor, and {1H–27Al}
Redor experiments. The strongly agglomerated samples were crystalline and thermally stable up to >500 ◦C. Although a part of the clinoptilolite framework is maintained up to 600 ◦C, a loss of crystallinity is already observed starting from 450 ◦C. The specific surface areas of the starting CLIN and ammonium exchanged NH4CLIN are low with ca. 26 m2/g. The pores are nearly blocked by the exchangeable cations located in the zeolite pores. The thermal decomposition of the ammonium ions by calcination at 400 ◦C causes an opening of the pore entrances and a markable increase in the specific micropore area and micropore volume to ca. 163 m2/g and 0.07 cm3/g, respectively. It decreases with further rising calcination temperature indicating some structural loss. The catalysts show a broad distribution of Brønsted acid sites (BS) ranging from weak to strong sites as indicated the
thermal decomposition of exchanged ammonium ions (TPDA). The ammonium ion decomposition leaving BS, i.e., H+ located at Al–O–Si framework bridges, starts at ≥250 ◦C. A part of the Brønsted sites is lost after calcination specifically at 500 ◦C. It is related to the formation of penta-coordinated aluminium at the expense of tetrahedral framework aluminium. The Brønsted sites are partially recreated after repeated ammonium ion exchange. The catalytic performance of the acidic HCLIN
catalysts was tested in the etherification of glycerol as a green renewable resource with different C1 -C4 alcohols. The catalysts are highly active in the etherification of glycerol, especially with alcohols containing the branched, tertiary alkyl groups. Highest activity is observed with the soft activated catalyst HCLIN300 (300 ◦C, temperature holding time: 1 min). A total of 78% conversion of glycerol to mono and di ether were achieved with tert-butanol at 140 ◦C after 4 h of reaction.
The mono- and di-ether selectivity were 75% and 25%, respectively. The catalyst can be reused.
Reliability study of a tunable ka-band SIW-phase shifter based on liquid crystal in LTCC-technology
(2014)
A tunable substrate-integrated waveguide phase shifter using low-temperature co-fired ceramic (LTCC)-technology is presented in this paper. By changing the effective permittivity in the liquid crystal (LC)-filled waveguide, the differential phase can be tuned continuously. This is achieved by means of an analog signal applied to the electrodes, surrounding the LC. The design allows for precise tuning of the differential phase, which is proven with a Monte Carlo measurement resulting in phase errors of less than 3° at 28 GHz. Besides that, the ambient temperature dependency of the module is shown. The phase shifter has a high integration level and can be included into a complete and lightweight single-phased array antenna module. The phase shifter is realized with a high level of integration which is available through the multilayer process of the LTCC. It has a length of 50 and provides a differential phase shift of more than 360° at 28 GHz. The figure of merit for tunable phase shifters is >40°/dB.
XUV- and X-ray free-electron-lasers (FEL) combine short wavelength, ultrashort pulse duration, spatial coherence and high intensity. This unique combination of properties opens up new possibilities to study the dynamics of non-reversible phenomena with ultrafast temporal and nano- to atomic-scale spatial resolution. In this contribution we wish to present results of time-resolved experiments performed at the XUV-FEL FLASH (HASYLAB/Hamburg) aimed to investigate the nano-scale structural dynamics of laser-irradiated materials. Thin films and fabricated nano-structures, deposited on Si3N4-membranes, have been excited with ultrashort optical laser pulses. The dynamics of the non-reversible structural evolution of the irradiated samples during laser-induced melting and ablation has been studied in an optical pump - XUV-probe configuration by means of single-shot coherent scattering techniques (i.e. diffraction imaging [1]). In a first set of experiments we investigated the formation of laser induced periodic surface structures (LIPSS) on the surface of thin Si-films (thickness 100 nm). In a simplified view LIPPS are generated as a result of interference between the incident laser pulse and surface scattered waves which leads to a periodically modulated energy deposition. Time-resolved scattering using femtosecond XUV-pulses (with a wavelength of 13.5 nm and 7 nm) allowed us to directly follow LIPSS evolution on an ultrafast time-scale and with better than 40 nm spatial resolution. The observed scattering patterns show almost quantitative agreement with theoretical predictions [2] and reveal that the LIPSS start to form already during the 12 ps pump pulse. In the second set of measurements we studied picosecond and femtosecond laser induced ablation and disintegration of fabricated nano-structures. Correlations of coherent diffraction patterns measured at various time delays to the pattern of the undisturbed object show that order in the structure is progressively lost starting from short length scales. This structural rearrangement progresses at close to the speed of sound in the material. Under certain circumstances (e.g. adequate sampling) it became also possible to reconstruct real-space images of the object as it evolves over time [3]. The possibility of femtosecond single-shot imaging of ultrafast dynamic processes with nanoscale resolution provides yet more details of the physical processes involved. [1] H. N. Chapman et al. Nature Phys. 2, 839 (2006). [2] J. F. Young et al., Phys. Rev. B 27, 1155 (1983). [3] A. Barty et al. Nature Phot. 2, 415 (2008).
The sintering behavior and the thermoelectric performance of Ca3Co4O9 multilayer laminates were studied, and a multilayer thermoelectric generator was fabricated. Compacts and multilayer samples with anisotropic microstructure and residual porosity were obtained after conventional sintering at 920 °C, whereas dense and isotropic multilayer samples were prepared by firing at 1200 °C and reoxidation at 900 °C. A hot-pressed sample has a dense and anisotropic microstructure. Samples sintered at 920 °C exhibit low electrical conductivity due to the low density, whereas the Seebeck coefficient is not sensitive to preparation conditions. However, thermal conductivity of multilayers is very low, and, hence acceptable ZT values are obtained. A ransversal multilayer thermoelectric generator (TMLTEG) was fabricated by stacking layers of Ca3Co4O9 green tapes, AgPd conductor printing, and co-firing at 920 °C. The TMLTEG has a power output of 3 mW at ΔT =200 K in the temperature interval of 25 °C to 300 °C.
There is a high international priority attached to activities which reduce NOx in the atmosphere. The current level of permitted emissions is typically between 50 µmol/mol and 100 µmol/mol, but lower values are expected in the future. Currently, ambient air quality monitoring regulations also require the measurement of NOx mole fractions as low as 0.2 µmol/mol. The production of accurate standards at these levels of mole fractions requires either dilution of a stable higher concentration gas standard or production by a dynamic technique, for example one based on permeation tubes.
The CCQM-K74 key comparison was designed to evaluate the level of comparability of National Metrology Institutes' measurement capabilities and standards for nitrogen dioxide (NO2) at a nominal mole fraction of 10 µmol/mol.
The measurements of this key comparison took place from June 2009 to May 2010.
Seventeen laboratories took part in this comparison coordinated by the BIPM and VSL. The key comparison reference value was based on BIPM measurement results, and the standard measurement uncertainty of the reference value was 0.042 µmol/mol.
This key comparison demonstrated that the results of the majority of the participants agreed within limits of ±3% relative to the reference value. The results of only one laboratory lay significantly outside these limits. Likewise this comparison made clear that a full interpretation of the results of the comparison needed to take into account the presence of nitric acid (in the range 100 nmol/mol to 350 nmol/mol) in the cylinders circulated as part of the comparison, as well as the possible presence of nitric acid in the primary standards used by participating laboratories.
Main text. To reach the main text of this paper, click on Final Report. Note that this text is that which appears in Appendix B of the BIPM key comparison database kcdb.bipm.org/.
The final report has been peer-reviewed and approved for publication by the CCQM, according to the provisions of the CIPM Mutual Recognition Arrangement (MRA).
DatesIssue 1A (Technical Supplement 2012)
Coordination chemistry was applied to deposit pyridine-functionalized gold nanoparticles on silicon substrates. The particles were synthesized through the Brust/Schiffrin route with a subsequent ligand exchange reaction yielding well-defined particles of two different sizes. Multilayer deposition was carried out on a pyridine-terminated SAM, anchored on a hydroxyl-terminated silicon surface. Analogously, Hunter/Vögtle-type tetralactam macrocycle multilayers were deposited as well as mixed layers containing both either in an alternating sequence or as a macrocycle multilayer with a terminating nanoparticle layer. These composite layers were examined with respect to their ability to bind squaraine axles in the macrocycle cavities. The amount of guest bound is higher for the composite layer with alternating macrocycles and nanoparticles.
Continuously tuneable liquid crystal based stripline phase shifter realised in LTCC technology
(2015)
This work presents the design, fabrication and measurements of a low temperature cofired ceramic (LTCC) integrated liquid crystal (LC) phase shifter. The effective permittivity of the phase shifter and therefore its differential phase shift can be tuned continuously by orienting the LC directors with electric fields. The phase-shift demonstrator is designed for Ka-band frequencies around 30 GHz and represents a stripline filled with LC, embedded inside an LTCC multilayer structure, which provides a space-qualified and hermetically-sealed LC cavity within an RF-capable material system. The total length of the device is 37 mm while the phase shifting LC section has a length of 14.6 mm. At 30 GHz it exhibits a differential phase shift of 60° with an insertion loss around 6 dB, resulting in a figure of merit around 10°/dB. An advantage is that the insertion loss is nearly independent of the tuning state of the LC. The response time of the phase shifter, depending on the desired LC orientation, is between 62 ms and 37 s.
Improved large mesoporous ordered molecular sieves - Stabilization and acid/base functionalization
(2010)
The preparation of nanoporous materials with enhanced stability using an improved synthesis route using reactive inorganic silica and alumina species is reported. This way improved mesoporous molecular sieves were obtained. The synthesized aluminum substituted mesoporous molecular materials (Al-MMS) contain very large pores of 50200 Å size combined with an improved pore wall thickness. Increased wall thickness and Al substitution lead to an improved chemical stability against alkaline solution. The textural, structural and acid properties are investigated by physico-chemical methods. The catalytic performance acidic materials was tested in the benzoylation reaction; amino functionalized materials were studied in the base catalyzed Michael addition.