Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (29)
- Beitrag zu einem Tagungsband (9)
- Beitrag zu einem Sammelband (1)
- Vortrag (1)
- Posterpräsentation (1)
Schlagworte
- Corrosion (4)
- Residual stress (4)
- Additive manufacturing (3)
- Crystal plasticity (3)
- High temperature corrosion (3)
- TEM (3)
- Alumina coatings (2)
- Aluminiumoxid (2)
- Carburization (2)
- Corrosion protection (2)
Organisationseinheit der BAM
- 5 Werkstofftechnik (11)
- 5.1 Mikrostruktur Design und Degradation (9)
- 8 Zerstörungsfreie Prüfung (5)
- 8.5 Röntgenbildgebung (5)
- 9 Komponentensicherheit (4)
- 5.5 Materialmodellierung (3)
- 9.4 Integrität von Schweißverbindungen (3)
- 5.0 Abteilungsleitung und andere (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
- 5.6 Glas (1)
Eingeladener Vortrag
- nein (1)
Investigation of the orientation relationships of carlsbergite in the North Chile iron meteorite
(2005)
Basic research on the corrosive effect of flue gases has been performed at the BAM Federal Institute for Materials Research and Testing (Germany). Conditions at both high and low temperatures were simulated in specially designed experiments. Carburization occured in flue gases with high CO2 content and temperatures higher than 500 °C. In SO2 containing flue gases sulphur was detected in the oxide scale. At lower temperatures no corrosion was observed when gases with low humidity were investigated. Humidity higher than 1500 ppm was corrosive and all steels with Cr contents lower than 12% revealed corroded surfaces. At low temperatures below 10 °C a mixture of sulphuric and nitric acid condensed on metal surfaces. Acid condensation caused severe corrosion. Humidity, CO2, O2, and SO2 contents are the important factors determining corrosion. Below 300 °C acid condensation is the primary reason for corrosion. Low humidity and low temperatures are conditions which can be expected in the CO2 separation and treatment process. This work includes major conditions of the flue gas and CO2 stream in CCS plants and CCS technology.
Future coal power plants will in case of oxyfuel combustion be operated with altered atmospheres. Hence, corrosion attack might become more severe and steels have to be protected. An alumina-sol was used to coat X20CrMoV12-1 (X20) with alumina to test the protection. Testing was performed at 600 °C in flowing H2O–CO2–O2 and static laboratory air for 1000 h. Oxidation under air is minor compared to exposure in oxyfuel atmosphere. In both cases a multilayered oxide (hematite, magnetite, spinel) was formed on uncoated steels. Carburization appeared on uncoated X20 in H2O–CO2–O2. The coating demonstrates a high protection.
Modified Yoldas sols can be used to prepare crack-free well adherent layers on different substrate materials such as sodalime glass, corundum and metal (IN-718). These layers having thicknesses of 0.6 µm are strain tolerant and withstand thermal cycling between 810 °C and room temperature. Introducing alpha-Al2O3 filler particles into modified Yoldas sols allows the preparation of thicker layers of 1.6 µm, which as well can be thermally cycled without noticeable delaminations. Chemical bonding seems to be the predominant layer bonding mechanism.
The crystallographic orientation of carlsbergite (CrN) in the north Chile meteorite (hexahedrite) was investigated using electron backscatter diffraction and transmission electron microscopy. These studies examined the CrN crystals in the rhabdites (idiomorphic schreibersite) and in kamacite. It was found that the CrN crystals embedded in rhabdite show a number of different orientation relationships with the host crystals. These orientations can be explained based on the lattice dimensions of both coexisting crystalline materials. It was also found that both carlsbergite and kamacite are characterized by a high dislocation density (109 cm2) while rhabdite is free of dislocations. It is supposed that in spite of the deformed metallic matrix, a general connection between the orientation relation of all the phases involved exists.
Alumina coatings with differing phase compositions were deposited on Inconel-718 (IN-718) Ni-base
superalloy substrates using solgel processing. Mass gain measurements served for studying the oxidation
behavior of coated metal surfaces if exposed to 800°C and 900°C for up to 4000 h in static air. Itwas found, that
alumina coatings significantly reduce the oxidation related mass gain of IN-718 even after heating to 900°C
for 4000 h. Transmission electron microscopy (TEM) studies revealed diffusion of elements from the metal
substrate (IN-718) into the alumina coatings and to a much lower degree from the coating into the
substrate. These diffusion processes are greatly influenced by the phase composition of the coatings, especially
by the presence of alpha-alumina.