Detection of suspended nanoparticles with near-ambient pressure x-ray photoelectron spectroscopy
(2017)
Two systems of suspended nanoparticles have been studied with near-ambient pressure x-ray photoelectron spectroscopy: silver nanoparticles in water and strontium fluoride—calcium fluoride core-shell nanoparticles in ethylene glycol. The corresponding dry samples were measured under ultra high vacuum for comparison. The results obtained under near-ambient pressure were overall comparable to those obtained under ultra high vacuum, although measuring silver nanoparticles in water requires a high pass energy and a long acquisition time. A shift towards higher binding energies was found for the silver nanoparticles in aqueous Suspension compared to the corresponding dry sample, which can be assigned to a change of surface potential at the water-nanoparticle interface. The shell-thickness of the core-shell nanoparticles was estimated based on simulated spectra from the National Institute of Standards and Technology database for simulation of electron spectra for surface analysis. With the instrumental set-up presented in this paper, nanoparticle suspensions in a suitable Container can be directly inserted into the analysis chamber and measured without prior sample preparation.
Near-ambient pressure x-ray photoelectron spectroscopy (NAP-XPS) is a less traditional form of XPS that allows samples to be analyzed at relatively high pressures, i.e., at greater than 2500 Pa. With NAP-XPS, XPS can probe moderately volatile liquids, biological samples, porous materials, and/or polymeric materials that outgas significantly. In this submission, we show survey, C 1s, O 1s, and N
1s narrow scans from an aqueous solution of a common protein, bovine serum albumin. The C 1s peak envelope is well fit to four symmetric peaks of equal width that correspond to carbon bonded to carbon and hydrogen (C-1), carbon singly bonded to oxygen (C-2), carbonyl and/or amide carbon (C-3), and carboxyl carbon (C-4). Two possible peak fits are considered for the N 1s and O 1s peak envelopes. The N 1s signal is fit to four peaks that correspond to amine (—NH2), Amide (OvCZNH2), ammonium (—NH3 +), and N2(g) nitrogen, and alternatively to three peaks that correspond to amine, amide, and N2(g) nitrogen. The O 1s peak envelope is similarly fit to three and four components.