XPS and NEXAFS spectroscopy were used for the chemical characterization of pulsed plasma-deposited ethylene films before and after exposure to ambient air. The influence of external plasma parameters on the spectroscopic results was investigated. Information on the chemical character of the plasma-polymerized films, such as the regularity of the primary structure, the amount of long-living radicals, and branching or cross-linking or both was derived from this data. Irregularity and radical concentration for post-plasma reactions of the plasma-deposited films increased with the duty cycle or power. A decreased level of monomer fragmentation and, consequently, an increase in regularity is partially concluded from the experimental data when the monomer pressure is increased. The concentration of surface radicals available for post-plasma reactions also increased with monomer pressure. The correlation found between the degree of the post-plasma oxygen incorporation and the variation of the various external parameters agreed with earlier ToF-SSIMS findings.
Chemical properties of plasma-polymerized styrene films can be effectively controlled by the appropriate choice of external plasma parameters, such as duty cycle, power and monomer pressure. Chemical properties here are the regularity of the primary structure, the amount of long living radicals and branching or cross-linking or both in plasma polymerized styrene films, which can be indirectly monitored by X-ray photoelectron spectroscopy (XPS) and near edge X-ray absorption fine structure (NEXAFS) spectroscopy. Principally, XPS and NEXAFS spectra of plasma-polymerized styrene show all the spectroscopic fingerprints characteristic of atactic polystyrene indicating an inherent similarity of the respective primary chemical structures. There is an increase in irregularity and radical concentration for the plasma deposited films with increasing duty cycle or power. With an increase in monomer pressure, a decreased level of monomer fragmentation and, consequently, an increase in regularity must be concluded from the experimental data. The applied power regulates the fragmentation of the monomers as monitored by spectroscopic signals correlated to the aromatic rings. A trend in the extent of the post-plasma oxygen incorporation according to the variation of the various external plasma parameters was deduced, which agrees with earlier ToF-SIMS findings
Thin plasma polymer films were deposited using the pulsed plasma mode. These plasma polymers should possess a more regular structure than those produced by the conventional continuous-wave (cw) mode, because of lower monomer fragmentation caused by the plasma pulses and the chemical chain propagation during the plasmaless (free!) periods. The thermoluminescence method was applied to functional groups carrying plasma polymer layers which are used in medical technology. Examples are formation of biocompatible, biosensoric and bioactive coatings or in metal polymer composites such as adhesion-promoting interlayers.
In addition to the use of the conventional X-ray Photoelectron Spectroscopy for thin film characterization, the new method of thermoluminescence was applied to characterize undesired defects and structural specifics produced in the polymer films by pp or cw plasma mode. The main areas of focus were oxygen-containing groups produced by post-plasma oxygen introduction via auto-oxidation, oxidation of implemented unsaturations and trapped radical sites known as typical irregular structures in plasma polymers.